Weak epitaxy growth affording high-mobility thin films of disk-like organic semiconductors

Thin films of phthalocyanine compounds show weak epitaxial growth on a monodomain film of a rod-like molecule (see figure). The resulting organic electronic devices exhibit high charge carrier mobilities close to those of the single-crystal devices.

Thickness dependence of mobility in CuPc thin film on amorphous SiO2 substrate

Hole mobility in a copper-phthalocyanine (CuPc)-based top-contact transistor has been studied with various organic layer thicknesses. It is found that the transistor performance depends on the thickness of the CuPc layer, and the mobility increases with the increase in the CuPc layer and saturated at the thickness of 6 ML. The upper layers do not actively contribute to the carrier transport in the organic films. The morphology of the organic layer grown on the bare SiO2/Si substrate is also presented. The analysis of spatial correlations shows that the CuPc films grow on the SiO2 according to the mixed-layer mode.

High-mobility pentacene thin-film transistors with copolymer-gate dielectric

Pentacene thin-film transistors have been obtained using polymethyl-methacrylate-co-glyciclyl-methacrylate (PNIMA-GMA) as the gate dielectric. The optimum active layer thickness in thin-film transistors (OTFTs) was investigated. The present devices show a wide operation voltage range. The on/off current ratio is as high as 10(5). In linear region (V-DS = -2V), the field-effect mobility of device increases with the increase in gate field at low-voltage region (V-G < - 20 V), and a mobility of 0.33 cm(2)/Vs can be obtained when V-G > 20 V. In saturation region, the mobility increases linearly with the gate field, and a high mobility of 1.14 cm(2)/Vs can be obtained at V-G = -95V. The influence of voltage on mobility of device was investigated.

Confined intra-molecular clustering in orientated polyethylene after annealing

Deuterated polyethylene tracer molecules with small amount of branches (12 C2H5- branches per 1000 backbone carbon atoms) were blended with a hydrogenated polyethylene matrix to form a homogenous mixture. The conformational evolution of the deuterated chains in a stretched semi-cry stall me film was observed via online small angle neutron scattering measurements during annealing at high temperatures close to the melting point. Because the sample was annealed at a temperature closely below its melting point, the crystalline lamellae were only partially molten and the system could not fully relax. The global chain dimensions were preserved during annealing. Recrystallization of released polymeric chain segments allows for local phase separation thus driving the deuterated chain segments into the confining interlamellar amorphous layers giving rise to an interesting intra-molecular clustering effect of the long deuterated chain. This clustering is deduced from characteristic small angle neutron scattering patterns. The confined phase separation has its origin in primarily the small amount of the branches on the deuterated polymers which impede the crystallization of the deuterated chain segments.

Naphthyl end-capped quarterthiophene: A simple organic semiconductor with high mobility and air stability

An organic semiconductor that can be mass produced is synthesized by end-capping quaterthiophene with naphthyl units (NaT4). An organic thin-film transistor (OTFT, see figure) has been fabricated using this organic semiconductor, and exhibits stability under ambient conditions with a mobility of up to 0.40 cm(2) V-1 s(-1).

Ambipolar organic field-effect transistors with air stability, high mobility, and balanced transport

Ambipolar organic field-effect transistors (OFETs) based on the organic heterojunction of copper-hexadecafluoro-phthalocyanine (F16CuPc) and 2,5-bis(4-biphenylyl) bithiophene (BP2T) were fabricated. The ambipolar OFETs eliminated the injection barrier for the electrons and holes though symmetrical Au source and drain electrodes were used, and exhibited air stability and balanced ambipolar transport behavior. High field-effect mobilities of 0.04 cm(2)/V s for the holes and 0.036 cm(2)/V s for the electrons were obtained. The capacitance-voltage characteristic of metal-oxide-semiconductor (MOS) diode confirmed that electrons and holes are transported at F16CuPc and BP2T layers, respectively. On this ground, complementary MOS-like inverters comprising two identical ambipolar OFETs were constructed.

Characterization and properties of biodegradable poly(hydroxyalkanoates) and 4,4-dihydroxydiphenylpropane blends: Intermolecular hydrogen bonds, miscibility and crystallization

Intermolecular hydrogen bonds, miscibility, crystallization and thermal stability of the blends of biodegradable poly(3-hydroxybutyrate) (PHB), poly(3-hydroxybutyrate-co-3-hydroxyhexanoate) [P(3HB-3HHx)] with 4,4-dihydroxydiphenylpropane (DOH2) were investigated by FTIR, C-13 Solid state NMR, DSC, WAXD and TGA. Intermolecular hydrogen bonds were found in both blend systems, which resulted from the carbonyl groups in the amorphous phase of both polyesters and the hydroxyl groups of DOH2. The intermolecular interaction between P(3HB-3HHx) and DOH2 is weaker than that between PHB and DOH2 owing to the steric hindrance of longer 3HHx side chains. Because of the effect of the hydrogen bonds, the chain mobility of both PHB and P(3HB-3HHx) components was limited after blending with DOH2 molecules. Single glass transition temperature depending on the composition was observed in all blends, indicating that those blends were miscible in the melt. The addition of DOH2 suppressed the crystallization of PHB and P(3HB-3HHx) components. Moreover, the crystallinity of PHB and P(3HB-3HHx) components also decreased with increasing DOH2 content in the blends.

Enhanced efficiency of light-emitting polymers through intra-molecular energy transfer

To enhance the photoluminescence and electroluminescence efficiency, light-emitting polymers with energy transferring chromophores including N,N,N'N'-phenylene-diamine, naphthalene-imide, oxadiazole, meta-phenylene vinylene are designed and synthesized.

A dinuclear aluminum 8-hydroxyquinoline complex with high electron mobility for organic light-emitting diodes

A dinuclear aluminum 8-hydroxyquinoline complex (DAlq(3)) with improved electron mobility was designed for organic light-emitting diodes. The electron mobility in DAlq(3) was determined via transient electroluminescence (EL) from bilayer devices with structure of indium tin oxide (ITO)/N,N-'-di(naphthalene-1-yl)-N,N-'-diphenyl-benzidine (NPB)/DAlq(3)/Mg:Ag. It was found that the electron mobility in DAlq(3) is between 3.7-8.4x10(-6) cm(2)/Vs at electric fields ranging between 1.2x10(6) and 4.0x10(6) V/cm, which is a factor of two higher than that in Alq(3). The DAlq(3) also shows a higher EL efficiency of 2.2 cd/A (1.2 Lm/W), as compared to Alq(3) with an EL efficiency of 2.0 cd/A (1.0 Lm/W), which is attributed to more balanced electron and hole recombination due to the improved electron mobility of DAlq(3).

Charge carrier mobility and electroluminescence in a green-emitting alternating block copolymer with a methoxy Bi-substituted chromophore

We determine the mobility of positive and negative charge carriers in a soluble green-emitting alternating block copolymer with, a methoxy bi-subsbituted conjugated segment. The negative charge carrier mobility of 6 x 10(-11) cm(2)/V.s is directly determined using space-charge-limited current analytical expressions. Positive charge carrier transport is also space-charge-limited, with a mobility of I x 10(-8) cm(2)/V.s. The electron trap distribution is exponential, with a characteristic energy of similar to 0.12 eV. A hole trap with energy similar to 0.4 eV was observed. This copolymer is used as emissive material in organic light-emitting diodes that present brightness of similar to 900 cd/m(2) at 12.5 V.

The effect of chain flexibility and chain mobility on radiation crosslinking of polymers

Radiation crosslinking of polymers mainly depends on the structure of polymer chain. The flexibility and mobility of chain directly influence the possibility of the reactive radicals recombination. Flexible chain is easier to crosslink than rigid-chain polymer. The latter must be crosslinked at high temperature, as most polymers can only crosslink above their melting point. Structural effect also influences the mechanism of radiation crosslinking of polymers. We find from the results in literature and in our laboratory that, the flexibility chain polymer mainly crosslinked with H type, but the rigid chain polymer mainly crosslinked with Y type. (C) 2001 Published by Elsevier Science Ltd.

Study of the conductivity and side chain mobility of a comb-like polymer electrolyte using the dynamic mechanical method

Using poly(styrene-co-maleic anhydride) as a backbone and poly(ethylene glycol) methyl ether (PEGME) with different molecular weights as side chains, three comb-like polymers and their Li salt complexes were synthesized. The dynamic mechanical properties and conductivities were investigated. Results showed that the polymer electrolytes possess two glass transitions: alpha -transition and beta -transition, and the temperature dependence of the ionic conductivity shows WLF (Williams-Landel-Ferry) behavior. Based on the time-temperature equivalence principle, a master curve was constructed by selecting T-beta as reference temperature. The values of the WLF parameters (C-1 and C-2) were obtained and were found to be almost independent of the length of the PEGME side chain and the content of Li salt. By reference to T-0 = 50 degreesC. the relation between log tau (c) and c was found to be linear. The master curves are displaced progressively to higher frequencies as the molecular weight of the side chain is increased. The relation between log tau (n) and the molecular weight of the side chain is also linear. (C) 2001 Elsevier Science B.V. All rights reserved.

Determination of electron mobility in a blue-emitting alternating block copolymer by space-charge-limited current measurements

In this communication we analyse current versus voltage data obtained using one carrier injection at metal/polymer/metal structures, The used polymer is a soluble blue-emitting alternating block copolymer, Our experimental results demonstrate that the electron current is limited by a large amount of traps with exponential energy distribution in the copolymer. The electron ;mobility of 5.1 x 10(-10) cm(2)/V s is directly determined by space-charge-limited current measurements. The electron mobility is at least three orders of magnitude smaller than that for holes in the copolymer. (C) 1999 Elsevier Science Ltd. All rights reserved.

THE EFFECT OF MOBILITY OF MOLECULES ON RADIATION-INDUCED CHAIN SCISSION AND RACEMIZATION OF ISO-POLY(METHYL METHACRYLATE)

The radiation-induced chain-scission and racemization of isotactic poly(methylmethacrylate)(iso-PMMA) in amorphous and semi-crystalline state as well as in solution have been studied with nuclear magnetic resonance and molar mass deter-mination. It is shown that the chain-scission is dominant for iso-PMMA in dilute solution while the racemization reaction is not favorable in this case. On the contrary, the racemization is favorable when iso-PMMA was irradiated in its crystalline state while chain-scission is not. Such experimental results could be well explained by the mobility of molecules and "cage effect". The hypothesis, we proposed previously that the chain-scission, racemization and recombination are in competition and the final result depends on the state of molecular motion at which iso-PMMA was irradiated, has been verified verified once again.

Extra- and intra-cellular ice formation of red seabream (Pagrus major) embryos at different cooling rates

The ice crystal formation is assumed as the most lethal factor for the failure of fish embryo cryopreservation and intracellular ice formation (IIF) plays a central role in cell injury during cooling. The objectives were to observe the morphological changes of red seabream (Pagrus major) embryo during the cooling-thawing process, and to examine the effect of cryoprotectant and cooling rate on the temperatures of oil globule ice formation (T-OIF), extra-cellular ice formation (T-EIF) and intracellular ice formation (T-IIF) using cryomicroscope. After thawing, the morphological changes of embryos were observed and recorded by the video attachment and monitor under the microscope. During the cooling process, three representative phenomena were observed: oil globule gradually turned bright firstly, then the whole field of view flashed and the embryo blackened. Cooling rate affect the temperature of both extra- and intra-cellular ice formations. T-EIF and T-IIF at high cooling rate were much lower than that at low cooling rate. And the value of T-EIF - T-IIF increased from 0.45 to 11.11 degrees C with the increase of cooling rate from 3 to 130 degrees C/min. Taken together, our results suggested that high cooling rate with proper cryoprotectant would be a good option for red seabream embryo cryopreservation. (C) 2009 Elsevier Inc. All rights reserved.