Low temperature synthesis, structure and properties of alkali-doped La2NiO4, LaNiO3 and LaNi0.85Cu0.15O3 from alkali hydroxide fluxes

We report a low-temperature synthesis of La1.95Na0.05NiO4 from NaOH flux, La0.97K0.03NiO3 and La0.95K0.05Ni0.85Cu0.15O3 phases from KOH flux at 400 degreesC. Alkali-doped LaNiO3 can be prepared in KOH, but not in NaOH flux and La2NiO4 can be prepared in NaOH, but not in KOH flux. The flux-grown oxides were characterized by powder X-ray Rietveld profile analysis and electron microscopy. Sodium doped La2NiO4 crystallizes in orthorhombic structure and potassium doped LaNiO3-phases crystallizes in rhombohedral structure. La1.95Na0.05NiO4 is weakly paramagnetic and semiconducting while La0.97K0.03NiO3 and La0.95K0.05Ni0.85Cu0.15O3 show Pauli paramagnetic and metallic behavior. (C) 2002 Editions scientifiques et medicales Elsevier SAS. All rights reserved.

Novel Mn-doped chalcopyrites

Heavily Mn-doped II-VI-V-2 semiconductors, such as CdGeP2 and ZnGeP2 have been prepared by depositing Mn on single crystalline substrate at nearly 400 T in an ultra high vacuum chamber. Well-defined ferromagnetic hysteresis with a saturation behavior appears in the magnetization curve up to above room temperature. The chemical states of the ZDGeP(2):Mn interface has been clarified by a careful in situ photoemission spectroscopy. The as-prepared surface consists of Ge-rich, metallic Mn compound. In and below the sub-surface region, dilute divalent Mn species as precursors of the DMS phase exist. No MnP phase was observed at any stage of the depth profile. Theoretical band-calculation suggests that the system with vacancies (Cd, V-c, Mn)GeP2 or a non-stoichiometric (Cd, Ge, Mn)GeP2 are ferromagnetic and energetically stable although ferromagnetism is not stable in a stoichiometric compound (Cd, Mn)GeP2. (C) 2003 Elsevier Ltd. All rights reserved.

Synthesis and photoluminescent properties of ZnS nanocrystals doped with copper and halogen

A novel wet-chemical precipitation method is optimized for the synthesis of ZnS nanocrystals doped with Cu+ and halogen. The nanoparticles were stabilized by capping with polyvinyl pyrrolidone (PVP). XRD studies show the phase singularity of ZnS particles having zinc-blende (cubic) structure. TEM as well as XRD line broadening indicate that the average crystallite size of undoped samples is similar to2 nm. The effects of change in stoichiometry and doping with Cu+ and halogen on the photoluminescence properties of ZnS nanophosphors have been investigated. Sulfur vacancy (Vs) related emission with peak maximum at 434 nm has been dominant in undoped ZnS nanoparticles. Unlike in the case of microcrystalline ZnS phosphor, incorporation of halogens in nanoparticles did not result V-Zn related self-activated emission. However, emission characteristics of nanophosphors have been changed with Cu+ activation due to energy transfer from vacancy centers to dopant centers. The use of halogen as co-activator helps to increase the solubility of Cu+ ions in ZnS lattice and also enhances the donor-acceptor type emission efficiency. With increase in Cu+ doping, Cu-Blue centers (CuZn-Cui+), which were dominant at low Cu+ concentrations, has been transformed into Cu-Green (Cu-Zn(-)) centers and the later is found to be situated near the surface regions of nanoparticles. From these studies we have shown that, by controlling the defect chemistry and suitable doping, photoluminescence emission tunability over a wide wavelength range, i.e., from 434 to 514 nm, can be achieved in ZnS nanophosphors. (C) 2003 Elsevier B.V. All rights reserved.

The Drude parameters for metallic PF6 doped polypyrrole

We measured the two components of the complex dielectric function of insulating and metallic PF6 doped polypyrrole up to 4 meV simultaneously. These data are used as an input performed Kramers-Kronig analysis on the higher energy reflection data. This has helped to clarify those results, which were previously deduced from the FIR and UV/VIS data, that could be artifacts.

The effect of host glass on optical absorption and fluorescence of Nd3+ in xNa(2)O-(30-x)K2O-70B(2)O(3) glasses

The effect of host glass composition on the optical absorption and fluorescence spectra of Nd3+ has been studied in mixed alkali borate glasses of the type xNa(2)O-(30-x)K2O-69.5B(2)O(3)-0.5Nd(2)O(3) (X = 5,10,15,20 and 25). Various spectroscopic parameters such as Racah (E-1, E-2 and E-3), spin-orbit (xi(4f)) and configuration interaction (alpha, beta) parameters have been calculated. The Judd-Ofelt intensity parameters (Omega(lambda)) have been calculated and the radiative transition probabilities (A(rad)), radiative lifetimes (tau(r)), branching ratios (beta) and integrated absorption cross sections (Sigma) have been obtained for certain excited states of the Nd3+, ion and are discussed with respect to x. From the fluorescence spectra, the effective fluorescence line widths (Deltalambda(eff)) and stimulated emission cross sections (sigma(p)) have been obtained for the three transitions F-4(3/2) --> I-4(9/2), F-4(3/2) --> I-4(11/2) and F-4(3/2) --> I-4(13/2) of Nd3+. The stimulated emission cross section (sigma(p)) values are found to be in the range (2.0-4.8) x 10(-2)0 cm(2) and they are large enough to indicate that the mixed alkali borate glasses could be potential laser host materials.

Transient analysis in Al-doped barium strontium titanate thin films grown by pulsed laser deposition

Thin films of (Ba0.5Sr0.5)TiO3 (BST) with different concentrations of Al doping were grown using a pulsed laser deposition technique. dc leakage properties were studied as a function of Al doping level and compared to that of undoped BST films. With an initial Al doping level of 0.1 at. % which substitutes Ti in the lattice site, the films showed a decrease in the leakage current, however, for 1 at. % Al doping level the leakage current was found to be relatively higher. Current time measurements at elevated temperatures on 1 at. % Al doped BST films revealed space-charge transient type characteristics. A complete analysis of the transient characteristics was carried out to identify the charge transport process through variation of applied electric field and ambient temperature. The result revealed a very low mobility process comparable to ionic motion, and was found responsible for the observed feature. Calculation from ionic diffusivity and charge transport revealed a conduction process associated with an activation energy of around 1 eV. The low mobility charge carriers were identified as oxygen vacancies in motion under the application of electric field. Thus a comprehensive understanding of the charge transport process in highly acceptor doped BST was developed and it was conclusive that the excess of oxygen vacancies created by intentional Al doping give rise to space-charge transient type characteristics. © 2001 American Institute of Physics.

Interacting magnetic sublattices and ferrimagnetism in Sr-doped DyMnO3

We present the magnetic properties of polycrystalline Dy1−xSrxMnO3 (0.1 ≤ x ≤ 0.4) with an orthorhombic (o) crystal structure. The parent compound, o-DyMnO3, undergoes an incommensurate antiferromagnetic ordering of the Mn spins at 39 K, followed by a spiral order at 18 K. A further antiferromagnetic transition at 5 K marks an ordering of the Dy-sublattice. Doping of divalent Sr ions results in diverse magnetization phenomena. The zero-field cooled (ZFC) and field cooled (FC) magnetization curves display the presence of strongly interacting magnetic sublattices. For x = 0.1 and 0.2, a bifurcation between the ZFC and FC magnetization sets in at around 30 and 32 K, respectively. The ZFC magnetization peaks at about 5 K, indicating antiferromagnetic Dy-couplings similar to the case of o-DyMnO3. For x = 0.3, clear signatures of ferrimagnetism and strong anisotropy are found, including negative magnetization. The compound with x = 0.4 behaves as a spin glass, similar to Dy0.5Sr0.5MnO3.

Synthesis, Structure, Negative Thermal Expansion, and Photocatalytic Property of Mo Doped ZrV(2)O(7)

A new series of compounds identified in the phase diagram of ZrO(2)-V(2)O(8)-MoO(3) have been synthesized via the solution combustion method. Single crystals of one of the compounds in the series, ZrV(1.50)Mo(0.50)O(7.25), were grown by the melt-cool technique from the starting materials with double the MoO(3) quantity. The room temperature average crystal structure of the grown crystals was solved using the single crystal X-ray diffraction technique. The crystals belong to the cubic crystal system, space group Pa (3) over bar (No. 205) with a = 8.8969 (4) angstrom, V = 704.24 (6) angstrom(3), and Z = 4. The final R(1) value of 0.0213 was achieved for 288 independent reflections during the structure refinement. The Zr(4+) occupies the special position (4a) whereas V(5+) and Mo(6+) occupy two unique (8c) Wyckoff positions. Two fully occupied O atoms, (24d) and (4b), one partially occupied 0 atom (8c) have been identified for this molybdovanadate, which is a unique feature for these crystals. The structure is related to both ZrV(2)O(7) and cubic ZrMo(2)O(8). The temperature dependent single crystal studies show negative thermal expansion above 370 K. The compounds have been characterized by powder X-ray diffraction, solid-state UV-vis diffuse reflectance spectra, scanning electron microscopy (SEM), and transmission electron microscopy (TEM). The photocatalytic activity of these compounds has been investigated for the degradation of various dyes, and these compounds show specificity toward the degradation of non-azoic dyes.