Multiple melting behavior of isotactic polypropylene and poly(propylene-co-ethylene) after stepwise isothermal crystallization

The multiple melting behavior of several commercial resins of isotactic polypropylene (iPP) and random copolymer, poly(propylene-co-ethylene) (PPE), after stepwise isothermal crystallization (SIC) were studied by differential scanning calorimeter and wide-angle X-ray diffraction (WAXD). For iPP samples, three typical melting endotherms appeared after SIC process when heating rate was lower than 10 degreesC/min. The WAXD experiments proved that only alpha-form crystal was formed during SIC process and no transition from alpha1- to alpha2-form occurred during heating process. Heating rate dependence for each endotherm was discussed and it was concluded that there were only,two major crystals with different thermal stability. For the PPE sample, more melting endotherms appeared after stepwise isothermal crystallization. The introduction of ethylene comonomer in isotactic propylene backbone further decreased the regularity of molecular chain, and the short isotactic propylene sequences could crystallize into gamma-form crystal having a low melting temperature whereas the long sequences crystallized into alpha-form crystal having high melting temperature.

Novel polyimides derived from 2,3,3 ',4 '-benzophenonetetracarboxylic dianhydride

A series of polyimides (PIs) based on 2,3,3',4'-benzophenonetetracarboxylic dianhydride (2,3,3',4'-BTDA) and 3,3',4,4'-BTDA were prepared by the conventional two-step process. The properties of the 2,3,3',4'-BTDA based polyimides were compared with those of polyimides prepared from 3,3',4,4'-BTDA. It was found that PIs from 2,3,3,4'-BTDA have higher glass transition temperature and better solubility without sacrificing their thermal properties. Furthermore the theological properties of PMR-15 type polyimide resins based on 2,3,3',4'-BTDA showed lower melt viscosity and wider melt flow region (flow window) compared with those from 3,3',4,4'-BTDA. The structure-property relations resulted from isomerism were discussed.

Morphology and thermal and mechanical properties of PBT/HIPS and PBT/HIPS-g-GMA blends

The modification of high-impact polystyrene (HIPS) was accomplished by melt-grafting glycidyl methacrylate (GMA) on its molecular chains. Fourier transform infrared spectroscopy and electron spectroscopy for chemical analysis were used to characterize the formation of HIPS-g-GMA copolymers. The content of GMA in HIPS-g-GMA copolymer was determined by using the titration method. The effect of the concentrations of GMA and dicumyl peroxide on the degree of grafting was studied. A total of 1.9% of GMA can be grafted on HIPS. HIPS-g-GNU was used to prepare binary blends with poly(buthylene terephthalate) (PBT), and the evidence of reactions between the grafting copolymer and PBT in the blends was confirmed by scanning electron microscopy (SEM), dynamic mechanical analysis, and its mechanical properties. The SEM result showed that the domain size in PBT/HIPS-g-GMA blends was reduced significantly compared with that in PBT/HIPS blends; moreover, the improved strength was measured in PBT/HIPS-g-GMA blends and results from good interfacial adhesion. The reaction between ester groups of PBT and epoxy groups of HIPS-g-GMA can depress crystallinity and the crystal perfection of PBT.

Effects of rubber content and temperature on unstable fracture behavior in ABS materials with different particle sizes

The fracture behavior of ABS materials with a particle diameter of 110 nm and of 330 nm was studied using instrumented Charpy impact tests. The effects of rubber content and temperature on fracture behavior, deformation mode, stable crack extension, plastic zone size, J-integral value, and crack opening displacement were investigated. In the case of a particle size of 110 nm, the material was found to break in a brittle manner, and the dominant crack mechanism was unstable crack propagation. Fracture toughness increases with increasing rubber content. In the case of a particle size of 330 nm, brittle-to-tough transition was observed. The J-integral value first increases with rubber content, then levels off after the rubber content is greater than 16 wt %. The J-integral value of a particle diameter of 330 nm was found to be much greater than that of 110 nm. The J-integral value of both series first increased with increasing temperature until reaching the maximum value, after which it decreased with further increasing temperature. The conclusion is that a particle diameter of 330 nm is more efficient than that of 110 nm in toughening, but for both series the effectiveness of rubber modification decreases with increasing temperatures higher than 40 degreesC because of intrinsic craze formation in the SAN matrix at temperatures near the glass transition of SAN. (C) 2000 John Wiley & Sons, Inc.

Efforts to decrease crosslinking extent of polyethylene in a reactive extrusion grafting process

Grafting of acrylic acid and glycidyl methacrylate onto low density polyethylene (LDPE) was performed by using a corotating twin-screw extruder. The effects of residence time and concentration of initiator and monomers on degree of grafting and gel content of grafting LDPE were studied systematically. Paraffin, styrene, p-benzoquinone, triphenyl phosphite, tetrachloromethane, and oleic acid were added to try to decrease the extent of crosslinking of LDPE. 4-hydroxyl-2,2,6,6-tetramethyl-1-piperidinyloxy (4-hydroxyl-TEMPO) and dipentamethylenethiuram tetrasulfide were also tried to inhibit crosslinking reaction of LDPE during its extruding grafting process. It was found that p-benzoquinone, triphenyl phosphite and tetrachloromethane were good inhibitors for crosslinking of LDPE. (C) 2000 John Wiley & Sons, Inc.

Crosslinking of polyimides via spirodilactone unit in polymer backbone

A new approach for the crosslinking of polyimides via the lactamization of spirodilactone unit in polyimide backbone was studied by two means: model reaction and the comparison of the properties of the polyimide precursors to those of the crosslinking polymers. Polyimides 4 and 5 were soluble in N,N'dimethylacetamide (DMAc), dimethylformamide (DMF), dimethylsulfoxide (DMSO), N'-methylpyrrolidone (NMP), and other common organic solvents, whereas their corresponding crosslinking polymers were insoluble in these solvents. The glass transition temperatures for polyimide 5 and its crosslinking polymer were 262 degrees C and 291 degrees C, whereas those for polyimide 4 and its crosslinking polymer were 265 degrees C and 360 degrees C. The weight-loss rate of the crosslinling polymers was apparently slower than that of the precursors when the temperature was >400 degrees C. The 10% weight-loss temperature for the polyimides 4 and 5 was <500 degrees C, whereas that for the crosslinking polymers was close to or above 600 degrees C. The results indicate that this type of crosslinking polymer has good thermal properties. The temperature for the formation of lactam was above 180 degrees C. (C) 1999 John Wiley & Sons, Inc.

Polyaniline as marine antifouling and corrosion-prevention agent

Conductive polyaniline was found to have special marine antifouling property. The coating from conducting polyaniline and epoxy resin(or polyurethane) can last 6-9 months in Southern China sea, i.e., less than 10% of the coating surface was fouled during this period. The conducting polyaniline has special synergetic antifouling effect on other antifouling agents like cuprous oxide or 4, 4'-dichlorodiphenyltrichloroethane. The conductivity of the polyaniline was found to be extremely important for its antifouling effect. Moreover, employing aliphatic polyamine as solvent of emeraldine base and curing agent of epoxy resin, a new technique to process corrosion prevention coating containing emeraldine base was developed, therefrom the emeraldine base and epoxy resin was in molecular level blending. This technique was solvent free and extremely effective, i.e., only 1wt% of emeraldine base in the coating can have good corrosion prevention property.

Studies on the interfacial adhesion between functionalized polypropylene and polyamide 1010

The interface behavior of polyamide 1010 (PA1010) and polypropylene (PP) was studied. In order to improve their interfacial adhesion, functional PP was prepared by means of grafting glycidyl methacrylate (GMA) on PP main chains and used instead of plain PP. Several technological characterizations were performed here on their interfaces. ESCA was used to confirm that some kind of reaction occurred between end groups of PA1010 and epoxy species of PP-g-GMA. The peel test was adopted to measure interfacial adhesion. It was found that the fracture energy of interfaces between PA1010 and PP-g-GMA was dramatically increased with the content of GMA. Their interfaces were observed as being blurred by using SEM and TEM and a crack that could be seen in the case of the interfaces of the PA1010 and the plain PP disappeared.

The characterization of the interfacial reaction in polyamide 1010 poly(propylene)-graft-(glycidylmethacrylate) blends

Binary blends of polyamide 1010/poly(propylene) and polyamide 1010 (PA1010)/poly(propylene)-graft-(glycidyl methacrylate) (PP-g-GMA) were prepared. The epoxy groups in PP-g-GMA react with the amino end-groups in PA1010, thus a PA1010-graft-PP copolymer is formed and acts as a compatibilizer between PA1010 and PP-g-GMA. The reaction was confirmed by electron spectroscopy for chemical analysis (ESCA) and attenuated total reflection (ATR)-FTIR spectroscopic analysis, and also evaluated by the stability of the suspension obtained by dissolving the blends in formic acid and by the morphologies of the blends.

Extraction and separation of heavy rare earth (III) with Extraction Resin containing di(2,4,4-trimethyl pentyl) phosphinic acid (Cyanex 272)

Extraction resins, of the type of;levextrel, (which is a collective term for styrene/divinylbenzene based copolymers of predominantly macroporous structure that contain a selective extractant) are important for the recovery and separation of metal ions, as they combine features of solvent extraction and ion exchange resins. This paper presents the results of the adsorption of heavy rare earth ions (Ho(III), Er(III), Tm(III), Yb(III), Lu(III) and Y(III)) from hydrochloric acid solutions at 0.2 mol/L ionic strength and 50 degrees C by the extraction resin containing di (2,4,4-trimethyl pentyl) phosphinic acid (Cyanex 272) and the chromatographic separation of (Er(III), Tm(III) and Yb(III)). Technological separation products, with purity and yield of Tm2O3 >99.97%, >80%, Er2O3 >99.9%, >94% and Yb2O3 >99.8%, >80% respectively, have been obtained from a feed having the composition Tm2O3 60%, Er2O3 10%, and Yb2O3 3%, the others 27%. The distribution coefficients, extraction equilibrium constants and separation factors have been determined as a function of acidity, loading of the resin and rare earths, flow rates and column ratios. The resolutions and efficiencies of separation of Er/Tm/Yb each other have been calculated. The stoichiometry of the extraction of rare earth ions has been suggested as well.

Toughening of nylon with epoxidised ethylene propylene diene rubber

Blends of nylon-6 and epoxidised ethylene propylene diene (eEPDM) rubber were prepared through reactive mixing. It is found that the toughness of nylon-6 can be much improved by this method, and that the particle size of eEPDM is much smaller than that of unexpoxidised EPDM (uEPDM) rubber in a nylon-6 matrix. This indicates that the epoxy group in eEPDM could react with a nylon-6 end group to form a graft copolymer which could act as an interfacial compatibiliser between the nylon-6 and the eEPDM rubber dispersed phase. (C) 1998 Elsevier Science Ltd. All rights reserved.

In situ epoxidation of ethylene propylene diene rubber by performic acid

In this paper, epoxidation of ethylene propylene diene rubber by in situ generated performic acid is discussed. The samples have been characterized by infra-red and H-1-nuclear magnetic resonance analyses. Quantitative analysis of the reaction products is made possible by using the methyl deformation band at 1377 cm(-1) as internal standard. The conversion of double bonds increases rapidly within the first 1 h, then gradually, over 2 h, has only a slight increase. The maximum conversion ratio of double bonds is about 70%. The relative content of epoxy groups has a top value at about 7 h. The side reactions are also discussed. (C) 1997 Elsevier Science Ltd.

Toughening of poly(butylene terephthalate) with epoxidized ethylene propylene diene rubber

In this paper, unepoxidized ethylene propylene diene rubber (uEPDM) was first epoxidized with formic acid and H2O2, and then the epoxidized ethylene propylene diene rubber (eEPDM) was melt-mixed with PET resin in a Brabender-like apparatus. Toughening of PET matrix was achieved by this method. The dispersion of rubber particles and phase structure of the blends were also observed by SEM. It has been suggested that the epoxy groups in the eEPDM could react with PET end groups to form a graft copolymer which could act as an interfacial compatibilizer between the PBT matrix and eEPDM rubber dispersed phase. This is beneficial to the improvement of the impact performance of PBT. (C) 1997 Elsevier Science Ltd.

Miscibility and phase behavior in blends containing random copolymers of poly(ether ether ketone) and phenolphthalein poly(ether ether ketone)

The miscibility and phase behavior of polysulfone (PSF) and poly(hydroxyether of bisphenol A) (phenoxy) with a series of copoly(ether ether ketone) (COPEEK), a random copolymer of poly(ether ether ketone) (PEEK), and phenolphthalein poly(ether ether ketone) (PEK-C) was studied using differential scanning calorimetry. A COPEEK copolymer containing 6 mol % ether ether ketone (EEK) repeat units is miscible with PSF, whereas copolymers containing 12 mol % EEK and more are not. COPEEK copolymers containing 6 and 12 mol % EEK are completely miscible with phenoxy, but those containing 24 mol % EEK and more are immiscible with phenoxy. Moreover, a copolymer containing 17 mol % EEK is partially miscible with phenoxy; the blends show two transitions in the midcomposition region and single transitions at either extreme. Two T(g)s were observed for the 50/50 blend of phenoxy with the copolymer containing 17 mol % EEK, whereas a single composition-dependent T-g appeared for all the other compositions. An FTIR study revealed that there exist hydrogen-bonding interactions between phenoxy and the copolymers. The strengths of the hydrogen-bonding interactions in the blends of the COPEEK copolymers containing 6 and 12 mol % EEK are the same as that in the phenoxy/PEK-C blend. However, for the blends of copolymers containing 17, 24, and 28 mol % EEK, the hydrogen-bonding interactions become increasingly unfavorable and the self-association of the hydroxyl groups of phenoxy is preferable as the content of EEK units in the copolymer increases. The observed miscibility was interpreted qualitatively in terms of the mean-field approach. (C) 1996 John Wiley & Sons, Inc.

FRACTURE-TOUGHNESS OF PHENOLPHTHALEIN POLYETHER KETONE

The static and impact fracture toughness of phenolphthalein polyether ketone (PEK-C) were studied at different temperatures. The static fracture toughness of PEK-C was evaluated via the linear elastic fracture mechanics (LEFM) and the J-integral analysis. Impact fracture toughness was also analyzed using the LEFM approach. Temperature and strain rate effects on the fracture toughness were also studied. The enhancement in static fracture toughness at 70 degrees C was thought to be caused by plastic crack tip blunting. The increase in impact fracture toughness with temperature was attributed two different mechanisms, namely, the relaxation process in a relatively low temperature and thermal blunting of the crack tip at higher temperature. The temperature-dependent fracture toughness data obtained in static tests could be horizontally shifted to match roughly the data for impact tests, indicating the existence of a time-temperature equivalence relationship. (C) 1995 John Wiley & Sons, Inc.