Synthesis of PbTiO3 by use of polymeric precursors

Lead titanate powders were synthesized through the use of polymeric precursors according to the Pechini Process. The polymeric precursor was calcined at temperatures ranging from 300 to 600°C for 1 or 2 h. X-ray diffraction (XRD) showed that lead titanate crystallizes from the precursor at temperatures as low as 400°C. No intermediate carbonate phase was detected by Fourier transform infrared spectroscopy (FTIR) or by XRD. A powder with mean particle size of 150 nm was obtained after calcination of the precursor at 600°C for 1 h. © 1998 Elsevier Science B.V. All rights reserved.

Preparation and characterization of SrBi2Nb2O9 thin films made by polymeric precursors

A polymeric precursor solution was employed in preparing SrBi2Nb2O9 (SBN) powder and thin films dip coated onto Si(100) substrate. XRD results show that the SBN perovskite phase forms at temperatures as low as 600°C through an intermediate fluorite phase. This fluorite phase is observed for samples heat-treated at temperatures of 400 and 500°C. After heat treatment at temperatures ranging from 300 to 800°C, thin films were shown to be crack free. Grazing incident angle XRD characterization shows the occurrence of the fluorite intermediate phase for films also. The thickness of films, measured by MEV, was in the order of 80-100 nm.

Electrical properties of a composite of Polyurethane and ferroelectric ceramics

Ferroelectric ceramic particles based on lead titanate zirconate (PZT) were dispersed in a polymer matrix based on castor oil. After the poling process, the pyroelectric activity of this composite was measured using a direct method in which a linear heating rate was applied to the pre-poled samples. The pyroelectric coefficient at 343 K is comparable with that of a PZT-poly(vinylidene fluoride) (PVDF) composite and significantly higher than that of PVDF. © 1998 Kluwer Academic Publishers.

Piezoelectric effect in composite polyurethane-ferroelectric ceramics

Flexible and free-standing films of piezoelectric composites made up of lead zirconate titanate (PZT) ceramic powder dispersed in a castor oil-based polyurethane (PU) matrix were obtained by spin coating and characterized as materials for sensor applications. The piezoelectric coefficients d 31 and d 33 were measured with the usual technique. The piezoelectric charge constant d 33 yields values up to ≤24 pC/N, even at lower PZT content (33 vol%). Some desirable properties like piezoelectricity, flexibility and good mechanical resistance show this new material to be a good alternative for use as sensors and actuators.

Release of formaldehyde by 4 endodontic sealers

Objective. The purpose of this study was to evaluate the release of formaldehyde by some root canal filling materials. Study design. Two older endodontic sealers, AH 26 and Endomethasone, and 2 recently available sealers, AH Plus and Top Seal, were analyzed. Infrared and electronic spectroscopy were used to determine formaldehyde content after set of the materials. Results. Analysis showed that the AH 26 and Endomethasone sealers released formaldehyde. Although the AH Plus and Top Seal sealers have similar chemical composition, they released formaldehyde in a minimal concentration. Conclusions. The AH 26 and Endomethasone sealers released formaldehyde after setting; however, a minimum release was observed for the AH Plus and Top Seal sealers. Copyright © 1999 by Mosby, Inc.

Evaluation of cell culture cytotoxicity of five root canal sealers

The cytotoxicity of four calcium hydroxide-based root canal sealers (Sealapex, CRCS, Apexit, and Sealer 26) and one zinc oxide-eugenol-based sealer (Fill Canal) was evaluated microscopically for morphological changes in rat peritoneal macrophages. The least cytotoxic sealer was Fill Canal, followed in increasing order of cytotoxicity by CRCS, Sealer 26, Apexit, and Sealapex. Copyright © 2000 by The American Association of Endodontists.

Preparation and properties of ferroelectric BaTiO3 thin films produced by the polymeric precursor method

Ferroelectric barium titanate thin films were produced by the polymeric precursor method. In this technique, the desired metal cations are chelated in a solution using a hydroxycarboxylic acid as the chelating agent. Barium carbonate and titanium IV isopropoxide were used as precursors for the citrate solution. Ethylene glycol and citric acid were used as polymerization/complexation agents for the process. The crystalline structure of the film annealed at 700 °C had a single perovskite phase with a tetragonal structure. The BaTiO3 film showed good P-E hysteresis loops and C-V characteristics due to the switched ferroelectric domains.

Preparation and characterization of BaBi2Nb2O9(BBN) ceramics synthetized by polymeric precursors method

Pure BBN powders and with addition of 1 and 2 wt% in excess of bismuth were obtained by Pechini Method. The powders calcined at 300°C/4h were analyzed by TG/DTA to study the temperature of organic matter decomposition. A systematic study of calcination temperature and time to the formation of the BBN phase was performed and the phase formation was accompanied by XRD. The calcined powders at 800°C during 2h were analyzed by infrared spectroscopy and by BET. The powders were isostaticaly pressed and sintered at temperatures ranging from 900°C to 1000°C. The ceramics were characterized by XRD to control the crystalline phase and by SEM to analyze the microstructure.

Effect of thermal treatment on the morphology of PLZT thin films prepared from polymeric precursor method

Lead lanthanum zirconate titanate (PLZT) thin films with (9/65/35) stoichiometry were prepared by dip coating from polymeric precursor method. The films deposited on silicon (100) substrates, were thermally treated from 450° to 700°C for 6 hours in order to study the influence of thermal treatment on the crystallinity, microstructure, grain size and roughness of the final film. X-ray diffraction results showed that PLZT phase crystallizes at low temperature (500°C) and present preferential orientation. It was observed by scanning electron microscopy (SEM) that it is possible to obtain dense thin films at temperatures around 650°C. The atomic force microscopy (AFM) studies showed that the grain size and roughness are strongly influenced by the annealing temperature.

Preparation of 9.5/65/35 PLZT powders by organic precursor method

In this study the preparation of 9.5/65/35 PLZT ceramic powders were investigated. The powders with the formula Pb0.905La0.095(Zr0.65 Ti0.35)0.976O3 + 3.5 w% PbO were prepared using Pechini process and partial oxalate method. The powder phase formation, powder morphology, and green density of PLZT were shown.

Pressure-induced phase transitions in Zr-rich PbZr1-xTixO3 ceramics

A Raman study of structural changes in the Zr-rich PbZr1-x TixO3 (PZT) system under hydrostatic pressures up to 5.0 GPa is presented. We observe that externally applied pressure induces several phase transitions in PZT ceramics among phases with orthorhombic (Ao), rhombohedral low-temperature (RLT), and rhombohedral high-temperature (RHT) symmetries (all found in PZT at ambient pressure and room temperature). Each of the compositions investigated (0.02 ≤ x ≤ 0.14) exhibits a high-pressure phase with orthorhombic (OI′) symmetry. We further report a detailed study of the pressure dependence of Raman frequencies to elucidate the phase transitions and to provide a set of pressure coefficients for the high-pressure phases.

Ferroelectric SBN thin films grown by an SBN/Bi2O3 PLD sequential process

Ferroelectric SrBi2Nb2O9 (SBN) thin films were prepared by pulsed laser deposition (PLD) on Pt/Ti/SiO2/Si(100) using a sequential deposition process from two SBN and Bi2O3 targets. This route allows for bismuth enrichment of the film composition in order to improve the ferroelectric characteristics. Structural and microstructural characterizations were performed by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The composition of films and targets was determined by energy dispersive X-ray spectrometry (EDX). The deposition temperature, which provided well-crystallized layered perovskite SBN phase films in situ, was found to be 700°C. The results were compared with those obtained for SBN films deposited at 400°C and then crystallized ex situ. For an ex situ annealing temperature of 750°C, a remanent polarization value (Pr) of 23.2 μc/cm2 and a coercive field (Ec) of 112 kV/cm were measured. © 2001 Elsevier Science Ltd. All rights reserved.

Influence of barium and strontium addition on the ratio c/a of PZT obtained by the polymeric precursor method

Lead zirconate titanate powder, with Zr/Ti ratio of 50/50 was prepared by Pechini method after adding up to 10,0 mol% of Ba +2 and Sr +2 ions. Tetragonal phase is favored by the increase of barium and strontium concentration in the LiNbO 3 crystal lattice. The ratio c/a for tetragonal phase increases with the content of Ba +2 and Sr +2.

Crystallographic, dielectric and optical properties of SrBi 2Ta2O9 thin films prepared by the polymeric precursor method

Strontium bismuth tantalate thin films were prepared on several substrates (platinized silicon (Pt/Ti/SiO 2 /Si), n -type (100)-oriented and p -type (111)-oriented silicon wafers, and fused silica) by the solution deposition method. The resin was obtained by the polymeric precursor method, based on the Pechini process, using strontium carbonate, bismuth oxide, and tantalum ethoxide as starting reagents. Characterizations by XRD and SEM were performed for structural and microstructural evaluations. The electrical measurements, carried on the MFM configuration, showed P r values of 6.24 μC/cm 2 and 31.5 kV/cm for the film annealed at 800 C. The film deposited onto fused silica and treated at 700 C presented around 80% of transmittance. © 2002 Taylor & Francis.

The use of pulsed electric acoustic technique for measuring the polarization reversal in ferroelectric ceramic samples

The pulsed electric acoustic technique, PEA, has been usually applied to probe space charge profiles in polymers. Preliminary PEA results using a ferroelectric ceramic are presented. If the reverse applied electric field i of the order of the coercive field the switching polarization process occurs in a period larger than hundreds of seconds. Such a slow process allows one to use the PEA setup to follow the polarization switching dynamics and determine the electric field profile. The PEA signal obtained in the lead zirconate-titanate doped with niobium ceramic, PZTN, indicates that the polarization distribution and field are not uniform during the switching period. We were also able to observe that the acoustic wave velocity and attenuation depends on the stage of the polarization switching, which agrees with results obtained using the ultrasonic method.