Sonochemical synthesis of Ce1-xFexO2-delta (0 <= x <= 0.45) and Ce0.65Fe0.33Pd0.02O2-delta nanocrystallites: oxygen storage material, CO oxidation and water gas shift catalyst

Nanocrystalline Ce1-xFexO2-delta (0 <= x <= 0.45) and Ce0.65Fe0.33Pd0.02O2-delta of similar to 4 nm sizes were synthesized by a sonochemical method using diethyletriamine (DETA) as a complexing agent. Compounds were characterized by powder X-ray diffraction (XRD), X-ray photo-electron spectroscopy (XPS) and transmission electron microscopy (TEM). Ce1-xFexO2-delta (0 <= x <= 0.45) and Ce0.65Fe0.33Pd0.02O2-delta crystallize in fluorite structure where Fe is in +3, Ce is in +4 and Pd is in +2 oxidation state. Due to substitution of smaller Fe3+ ion in CeO2, lattice oxygen is activated and 33% Fe substituted CeO2 i.e. Ce0.67Fe0.33O1.835 reversibly releases 0.31O] up to 600 degrees C which is higher or comparable to the oxygen storage capacity of CeO2-ZrO2 based solid solutions (Catal. Today 2002, 74, 225-234). Due to interaction of redox potentials of Pd2+/0(0.89 V) and Fe3+/2+ (0.77 V) with Ce4+/3+ (1.61 V), Pd ion accelerates the electron transfer from Fe2+ to Ce4+ in Ce0.65Fe0.33Pd0.02O1.815, making it a high oxygen storage material as well as a highly active catalyst for CO oxidation and water gas shift reaction. The activation energy for CO oxidation with Ce0.65Fe0.33Pd0.02O1.815 is found to be as low as 38 kJ mol(-1). Ce0.67Fe0.33O1.835 and Ce0.65Fe0.33Pd0.02O1.815 have also shown high activity for the water gas shift reaction. CO conversion to CO2 is 100% H-2 specific with these catalysts and conversion rate was found to be as high 27.2 mu moles g(-1) s(-1) and the activation energy was found to be 46.4 kJ mol(-1) for Ce0.65Fe0.33Pd0.02O1.815.

Reactions of Mixed-Valent Palladium (IV,II) Complexes of Tetradentate Schiff-Bases Involving Bond Isomerization

Reactions of [PdIVB-(AI)2]++ [PdIICl4]-- (i) B-(AI)2 = dianion of N,N'-ethylene-/i-propylene-/n-propylene-bis(acetyl-acetoneimine) with some π-acceptor ligands, aliphatic primary amines and nitrosating reagents have been investigated. In all these reactions except nitrosation, 1:1 adducts having the formula, [PdIVB-(AI)2.X] [PdIICl4] [X = triphenylphosphine (TPP), triphenylarsine (TPA), pyridine (Py), methylamine (CH3NH2) or ethylamine (C2H5NH2)] are obtained. The formation of these complexes is associated with a bond isomerization - from Pd-Cxo-π -allylic bond prevailing in [PdIVB-(AI)2]2+ to PdIV-O bonding.Reaction of (i) with nitrosating reagents reduces PdIV to PdII and subsequently transform the γ-CH group, into an ambidentate isonitroso group (°C = NOH). The latter enters into coordination with PdII by dislodging the already coordinated carbonyl group. Further, selective nitrosation (mono- and dinitrosation) has been carried out by controlling the amount of the nitrosating reagent and the reaction time. The complexes have been characterized by elemental analyses, electrical conductivity, magnetic susceptibility and ir spectral data.

Assignment of Fundamental Vibrations of Hydrazo Derivatives. Carbohydrazide and Diprotonated Carbohydrazide

The Infrared spectra of carbohydrazide, diprotonated carbohydrazide and their deuterated compounds have been measured in the solid state. From the results on thio- and selenocarbohydrazides and other related molecules and normal coordinate analyses using a Urey-Bradley force field assignments of the fundamental vibrational frequencies and a description of the normal modes of carbohydrazide, diprotonated carbohydrazide and their deuterated species are given.

Synthesis and characterization of flexible epoxy nanocomposites reinforced with amine functionalized alumina nanoparticles: a potential encapsulant for organic devices

Research on conducting polymers, organic light emitting diodes and organic solar cells has been an exciting field for the past decade. The challenge with these organic devices is the long term stability of the active material. Organic materials are susceptible to chemical degradation in the presence of oxygen and moisture. The sensitivity of these materials towards oxygen and moisture makes it imperative to protect them by encapsulation. Polymer nanocomposites can be used as encapsulation materials in order to prevent material degradation. In the present work, amine functionalized alumina was used as a cross-linking and reinforcing material for the polymer matrix in order to fabricate the composites to be used for encapsulation of devices. Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy and Raman spectroscopy were used to elucidate the surface chemistry. Thermogravimetric analysis techniques and CHN analysis were used to quantify grafting density of amine groups over the surface of the nanoparticles. Mechanical characterizations of the composites with various loadings were carried out with dynamic mechanical analyzer. It was observed that the composites have good thermal stability and mechanical flexibility, which are important for an encapsulant. The morphology of the composites was evaluated using scanning electron microscopy and atomic force microscopy.

Texture and grain-size dependence of tensile properties in warm rolled cadmium

The development of crystallographic texture and the change in the grain size during warm rolling (300 deg K) and their effect on the tensile yield strength at 77 and 300 deg K are studied in 99.9% pure Cd. Both longitudinal and transverse specimens are tested. The yield strength obeys the Hall--Petch relation. The Hall--Petch slope, k, is lower and the intercept sigma o is higher in the warm worked material in comparison with the corresponding values for annealed Cd. The differences are attributed to the change in 1013 < and 0001 textures that are developed during warm rolling.26 refs.--AA

Structural Relationships in 2,3-Bis-n-decyloxyanthracene and 12-Hydroxystearic Acid Molecular Gels and Aerogels Processed in Supercritical CO2

Supercritical carbon dioxide is used to prepare aerogels of two reference molecular organogelators, 2,3-bis-n-decyloxyanthracene (DDOA) (luminescent molecule) and 12-hydroxystearic acid (HSA). Electron microscopy reveals the fibrillar morphology of the aggregates generated by the protocol. SAXS and SANS measurements show that DDOA aerogels are crystalline materials exhibiting three morphs: (1) arrangements of the crystalline solid (2D p6m), (2) a second hexagonal morph slightly more compact, and (3) a packing specific of the fibers in the gel. Aggregates specific of the aerogel (volume fraction being typically phi approximate to 0.60) are developed over larger distances (similar to 1000 angstrom) and bear fewer defaults and residual strains than aggregates in the crystalline and gel phases. Porod, Scherrer and Debye-Bueche analyses of the scattering data have been performed. The first five diffraction peaks show small variations in position and intensity assigned to the variation of the number of fibers and their degree of vicinity within hexagonal bundles of the related SAFIN according to the Oster model. Conclusions are supported by the guidelines offered by the analysis of the situation in HSA aerogels for which the diffraction pattern can be described by two coexisting lamellar-like arrangements. The porosity of the aerogel, as measured by its specific surface extracted from the scattering invariant analysis, is only 1.8 times less than that of the swollen gel and is characteristic of a very porous material.

Synthetic and physicochemical studies of uranium complexes with semicarbazone and hydrazone

Uranyl complexes of two Schiff bases, semicarbazone and hydrazone containing OON donor atoms have been synthesized and characterized on the basis of NMR, IR and electronic spectral studies, conductance, magnetic susceptibility and thermogravimetric data. The 1H NMR spectrum of the semicarbazone complex shows low field signals due to OH, NH and ---CH=N groups at 10.23, 9.31 and 8.17 ppm, respectively. The aromatic protons appear in the range 7.74–7.40 ppm. On complexation with U(VI) the signals due to OH and NH disappear evidently due to their participation in coordination. The coordination number of the o-vanillin semicarbazone (oVSC) complex is 6 whereas, that of the o-vanillin isonicotinic acid hydrazone (oVINAH) complex is 8, in addition to the two oxygen atoms already bonded to U(VI) in each species. The thermograms show the presence of 3 and 2 water molecules in these complexes, respectively and the IR spectral data also support the above conclusion. Suitable structures have been assigned.

The effect of structure on the dilute solution properties of branched polysaccharides studied with SEC and AsFlFFF

Cereal arabinoxylans, guar galactomannans, and dextrans produced by lactic acid bacteria(LAB) are a structurally diverse group of branched polysaccharides with nutritional and industrial functions. In this thesis, the effect of the chemical structure on the dilute solution properties of these polysaccharides was investigated using size-exclusion chromatography(SEC) and asymmetric flow field-flow fractionation (AsFlFFF) with multiple-detection. The chemical structures of arabinoxylans were determined, whereas galactomannan and dextran structures were studied in previous investigations. Characterization of arabinoxylans revealed differences in the chemical structures of cereal arabinoxylans. Although arabinoxylans from wheat, rye, and barley fiber contained similar amounts of arabinose side units, the substitution pattern of arabinoxylans from different cereals varied. Arabinoxylans from barley husks and commercial low-viscosity wheat arabinoxylan contained a lower number of arabinose side units. Structurally different dextrans were obtained from different LAB. The structural effects on the solution properties could be studied in detail by modifying pure wheat and rye arabinoxylans and guar galactomannan with specific enzymes. The solution characterization of arabinoxylans, enzymatically modified galactomannans, and dextrans revealed the presence of aggregates in aqueous polysaccharide solutions. In the case of arabinoxylans and dextrans, the comparison of molar mass data from aqueous and organic SEC analyses was essential in confirming aggregation, which could not be observed only from the peak or molar mass distribution shapes obtained with aqueous SEC. The AsFlFFF analyses gave further evidence of aggregation. Comparison of molar mass and intrinsic viscosity data of unmodified and partially debranched guar galactomannan, on the other hand, revealed the aggregation of native galactomannan. The arabinoxylan and galactomannan samples with low or enzymatically extensively decreased side unit content behaved similarly in aqueous solution: lower molar mass samples stayed in solution but formed large aggregates, whereas the water solubility of the higher-molar-mass samples decreased significantly. Due to the restricted solubility of galactomannans in organic solvents, only aqueous galactomannan solutions were studied. The SEC and AsFlFFF results differed for the wheat arabinoxylan and dextran samples. Column matrix effects and possible differences in the separation parameters are discussed, and a problem related to the non-established relationship between the separation parameters of the two separation techniques is highlighted. This thesis shows that complementary approaches in the solution characterization of chemically heterogeneous polysaccharides are needed to comprehensively investigate macromolecular behavior in solution. These results may also be valuable when characterizing other branched polysaccharides.

A thermodynamic protocol for explaining subcriticality and other subtle features in self-deflagrating solids

A novel universal approach to understand the self-deflagration in solids has been attempted by using basic thermodynamic equation of partial differentiation, where burning mte depends on the initial temperature and pressure of the system. Self-deflagrating solids are rare and are reported only in few compounds like ammonium perchlorate (AP), polystyrene peroxide and tetrazole. This approach has led us to understand the unique characteristics of AP, viz. the existence of low pressure deflagration limit (LPL 20 atm), hitherto not understood sufficiently. This analysis infers that the overall surface activation energy comprises of two components governed by the condensed phase and gas phase processes. The most attractive feature of the model is the identification of a new subcritical regime I' below LPL where AP does not burn. The model is aptly supported by the thermochemical computations and temperature-profile analyses of the combustion train. The thermodynamic model is further corroborated from the kinetic analysis of the high pressure (1-30 atm) DTA thermograms which affords distinct empirical decomposition rate laws in regimes I' and 1 (20-60 atm). Using Fourier-Kirchoff one dimensional heat transfer differential equation, the phase transition thickness and the melt-layer thickness have been computed which conform to the experimental data.

Characterization and evaluation of melibiose as novel excipient in tablet compaction

Lactose is probably the most used tablet excipient in the field of pharmacy. Although lactose is thoroughly characterized and available in many different forms there is a need to find a replacer for lactose as a filler/binder in tablet formulations because it has some downsides. Melibiose is a relatively unknown disaccharide that has not been thoroughly characterized and not previously used as an excipient in tablets. Structurally melibiose is close to lactose as it is also formed from the same two monosaccharides, glucose and galactose. Aim of this research is to characterize and to study physicochemical properties of melibiose. Also the potential of melibiose to be used as pharmaceutical tablet excipient, even as a substitute for lactose is evaluated. Current knowledge about fundamentals of tableting and methods for determinating of deformation behavior and tabletability are reviewed. In this research Raman spectroscopy, X-ray powder diffraction (XRPD), near-infrared spectroscopy (NIR) and Fourier-transform infrared spectroscopy (FT-IR) were used to study differences between two melibiose batches purchased from two suppliers. In NIR and FT-IR measurements no difference between materials could be observed. XPRD and Raman however found differences between the two melibiose batches. Also the effects of moisture content and heating to material properties were studied and moisture content of materials seems to cause some differences. Thermal analytical methods, differential scanning calorimetry (DSC) and thermogravimetry (TG) were used to study thermal behaviour of melibiose and difference between materials was found. Other melibiose batch contains residual water which evaporates at higher temperatures causing the differences in thermal behaviour. Scanning electron microscopy images were used to evaluate particle size, particle shape and morphology. Bulk, tapped and true densities and flow properties of melibiose was measured. Particle size of the melibiose batches are quite different resulting causing differences in the flowability. Instrumented tableting machine and compression simulator were used to evaluate tableting properties of melbiose compared to α-lactose monohydrate. Heckel analysis and strain-rate sensitivity index were used to determine deformation mechanism of melibiose monohydrate in relation to α–lactose monohydrate during compaction. Melibiose seems to have similar deformation behaviour than α-lactose monohydrate. Melibiose is most likely fragmenting material. Melibiose has better compactibility than α – lactose monohydrate as it produces tablets with higher tensile strength with similar compression pressures. More compression studies are however needed to confirm these results because limitations of this study.

Casting and heat treatment variables of Al–7Si–Mg alloy

A review of the research work that has been carried out thus far relating the casting and heat treatment variables to the structure and mechanical properties of Al–7Si–Mg (wt-%) is presented here. Although specifications recommend a wide range of magnesium contents and a fairly high content of iron, a narrow range of magnesium contents, closer to either the upper or lower specified limits depending on the properties desired, and a low iron content will have to be maintained to obtain optimum and consistent mechanical properties. A few studies have revealed that the modification of eutectic silicon slightly increases ductility and fracture toughness and also that the effect of modification is predominant at low iron content. Generally, higher solidification rates give superior mechanical properties. Delayed aging (the time elapsed between quenching and artificial aging during precipitation hardening) severely affects the strength of the alloy. The mechanism of delayed aging can be explained on the basis of Pashley's kinetic model. It has been reported that certain trace additions (cadmium, indium, tin, etc.) neutralise the detrimental effect of delayed aging. In particular, it should be noted that delayed aging is not mentioned in any of the specifications. With reference to the mechanism by which trace additions neutralise the detrimental effect of delayed aging, various hypotheses have been postulated, of which impurity–vacancy interaction appears to be the most widely accepted.

Solvation and axial ligation properties of (2,3,7,8,12,13,17,18-octabromo-5,10,15,20-tetraphenylporphyrinato)zinc(II)

he solvation of (2,3,7,8,12,13,17,18-octabromo-5,10,15,20-tetraphenylporphyrinato)zinc(II)[Zn(obtpp)], in twelve different solvents results in large red shifts of the B and Q bands of the porphyrin accompanied by enhanced absorbance ratios of the Q bands. These observations are ascribed to the destabilisation of the highest occupied molecular orbital a2u of the porphyrin arising from a flow of charge from the axial ligand to the porphyrin ring through the zinc(II) ion. The binding constants of adducts of [Zn(obtpp)] with neutral bases have been found to be an order of magnitude greater than those observed for the corresponding adducts of (5,10,15,20-tetraphenylporphyrinato)-zinc and vary in the order piperidine > imidazole > pyridine > 3-methylpyridine > pyridine-3-carbaldehyde. The enhanced binding constants and large spectral shifts are interpreted in terms of the electrophilicity of [Zn(obtpp)] induced by the electron-withdrawing bromine substituents in the porphyrin core. The structure of [Zn(obtpp)(PrCN)2] has been determined; it reveals six-co-ordinated zinc(II) with two long Zn–N distance [2.51(4), 2.59(3)Å]. The porphyrin is non-planar and displays a saddle-shaped conformation.

Structural, dielectric and ferroelectric properties of multilayer lithium tantalate thin films prepared by sol-gel technique

Multilayer lithium tantalate thin films were deposited on Pt-Si Si(111)/SiO2/TiO2/Pt(111)]substrates by sol-gel process. The films were annealed at different annealing temperatures (300, 450 and 650 degrees C) for 15 min. The films are polycrystalline at 650 degrees C and at other annealing conditions below 650 degrees C the films are in amorphous state. The films were characterized using X-ray diffraction, atomic force microscopy (AFM) and Raman spectroscopy. The AFM of images show the formation of nanograins of uniform size (50 nm) at 650 degrees C. These polycrystalline films exhibit spontaneous polarization of 1.5 mu C/cm(2) at an application of 100 kV/cm. The dielectric constant of multilayer film is very small (6.4 at 10 kHz) as compared to that of single crystal. (C) 2010 Elsevier B.V. All rights reserved.

Optical properties change in amorphous (As2S3)(0.87)Sb-0.13 thin films by photo and thermal induced process

Exposure with above band gap light and thermal annealing at a temperature near to glass transition temperature, of thermally evaporated amorphous (As2S3)(0.87)Sb-0.13 thin films of 1 mu m thickness, were found to be accompanied by structural effects, which in turn, lead to changes in the optical properties. The optical properties of thin films induced by illumination and annealing were studied by Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy and Raman spectroscopy. Photo darkening or photo bleaching was observed in the film depending upon the conditions of the light exposure or annealing. These changes of the optical properties are assigned to the change of homopolar bond densities. (C) 2010 Elsevier B.V. All rights reserved.

Ultrafast laser spectroscopy-A tool chemists and biologists

Application of ultrafast lasers to chemistry and biology has been an active area of research in the international scene for over a decade for physical and biophysical chemists. Perhaps, ultrafast laser spectroscopy is one of the most versatile tools available today to experimentally study structure and dynamics in the time domain of nanoseconds (10(-9) sec) to femtoseconds (10(-15) sec). In this article we attempt to highlight some of the recent developments in ultrafast laser spectroscopy with particular reference to vibrational spectroscopy, viz. infrared and Raman spectroscopy, in the above time domain.