Synthesis and characterization of K2Ca5(SO4)6· H2O, the equivalent of görgeyite, a rare evaporite mineral

Görgeyite, K2Ca5(SO4)6··H2O, is a very rare monoclinic double salt found in evaporites related to the slightly more common mineral syngenite. At 1 atmosphere with increasing external temperature from 25 to 150 °C, the following succession of minerals was formed: first gypsum and K2O, followed at 100 °C by görgeyite. Changes in concentration at 150 °C due to evaporation resulted in the formation of syngenite and finally arcanite. Under hydrothermal conditions, the succession is syngenite at 50 °C, followed by görgyeite at 100 and 150 °C. Increasing the synthesis time at 100 °C and 1 atmosphere showed that initially gypsum was formed, later being replaced by görgeyite. Finally görgeyite was replaced by syngenite, indicating that görgeyite is a metastable phase under these conditions. Under hydrothermal conditions, syngenite plus a small amount of gypsum was formed, after two days being replaced by görgeyite. No further changes were observed with increasing time. Pure görgeyite showed elongated crystals approximately 500 to 1000 µ m in length. The infrared and Raman spectra are mainly showing the vibrational modes of the sulfate groups and the crystal water (structural water). Water is characterized by OH-stretching modes at 3526 and 3577 cm–1 , OH-bending modes at 1615 and 1647 cm–1 , and an OH-libration mode at 876 cm–1 . The sulfate 1 mode is weak in the infrared but showed strong bands at 1005 and 1013 cm–1 in the Raman spectrum. The 2 mode also showed strong bands in the Raman spectrum at 433, 440, 457, and 480 cm–1 . The 3 mode is characterized by a complex set of bands in both infrared and Raman spectra around 1150 cm–1 , whereas 4 is found at 650 cm–1.

Raman spectroscopic study of vivianites of different origins

Raman spectroscopy has been used to study a selection of vivianites from different origins. A band is identified at around 3480 cm-1 whose intensity is sample dependent. The band is attributed to the stretching vibration of Fe3+ OH units which are formed through the autooxidation of the vivianite minerals either by self-oxidation or by photocatalytic oxidation according to the reaction: (Fe2+)3(PO4)2·8H2O + 1/2O2 (Fe2+)3– x(Fe3+)x(PO4)2(OH)x·(8–x)H2O in which some of the water of crystallization is converted to hydroxyl anions. Complexity of the OH stretching region through the overlap of broad bands is reflected in the water HOH deformation modes at 1660 cm–1. Using the infrared bands at 3281, 3105 and 3025 cm–1, hydrogen bond distances of 2.734(5), 2.675(2) and 2.655(2) Å are calculated. Vivianites are characterised by an intense band at 950 cm–1 assigned to the PO4 symmetric stretching vibration. Low Raman intensity bands are observed at ~1077, ~1050, 1015 and ~ 985 cm–1 assigned to the phosphate PO4 antisymmetric stretching vibrations. Multiple antisymmetric stretching vibrations are due to the reduced tetrahedral symmetry. This loss of degeneracy is also reflected in the bending modes. Two bands are observed at ~ 423 and ~ 456 cm–1 assigned to the2bending modes. For the vivianites four bands are observed at ~ 584, ~ 571, ~ 545 and ~ 525 cm–1 assigned to the 4modes of vivianite.

Raman spectroscopy of kaolinites using different excitation wavelengths

The Raman spectra of both low- and high-defect kaolinites in the hydroxyl stretching and low-wavenumber region were obtained with excitation at three visible wavelengths of 633, 514 and 442 nm and a UV wavelength of 325 nm. The UV-excited spectra were comparable to those excited by the visible wavelengths. The Raman spectra show hydroxyl stretching bands at 3621 cm-1 attributed to the inner hydroxyl, at 3692 and 3684 cm-1 attributed to the longitudinal and transverse optic modes of the inner surface hydroxyls and at 3668 and 3653 cm-1 assigned to the out-of phase vibrations of the inner surface hydroxyls. Two bands were observed in the spectral profile at 3695 cm-1 for the high-defect kaolinite at 3698 and 3691 cm-1 and were assigned to TO/LO splitting. An increase in relative intensity of the transverse optic mode is observed with decrease in laser wavelength. The intensity of the out-of-phase vibrations at 3668 and 3653 cm-1 of the inner surface hydroxyls shows a linear relationship with the longitudinal and transverse optic modes. In the low-wavenumber region excellent correlation was found between the experimentally determined and the calculated band positions.

Guidelines on building design and operation to minimize air quality impacts from major roads in transit oriented development

Poor air quality has a huge detrimental effect, both economic and on the quality of life, in Australia. Transit oriented design (TOD), which aims to minimise urban sprawl and lower dependency on vehicles, leads to an increasing number of buildings close to transport corridors. This project aims at providing guidelines that are appropriate to include within City Plan to inform future planning along road corridors, and provide recommendations on when mitigation measures should be utilised.