LC-MS/MS quantitation of plasma progesterone in cattle

Quantitation of progesterone (P(4)) in biological fluids is often performed by radioimmunoassay (RIA), whereas liquid chromatography coupled to tandem mass spectrometry (LC-MS/MS) has been used much less often. Due to its autoconfirmatory nature, LC-MS/MS greatly minimizes false positives and interference. Herein we report and compare with RIA an optimized LC-MS/MS method for rapid, efficient, and cost-effective quantitation of P(4) in plasma of cattle with no sample derivatization. The quantitation of plasma P(4) released from three nonbiodegradable, commercial, intravaginal P(4)-releasing devices (IPRD) over 192 h in six ovariectomized cows was compared in a pairwise study as a test case. Both techniques showed similar P(4) kinetics (P > 0.05) whereas results of P(4) quantitation by RIA were consistently higher compared with LC-MS/MS (P < 0.05) due to interference and matrix effects. The LC-MS/MS method was validated according to the recommended analytical standards and displayed P(4) limits of detection (LOD) and quantitation (LOQ) of 0.08 and a 0.25 ng/mL, respectively. The high selective LC-MS/MS method proposed herein for P(4) quantitation eliminates the risks associated with radioactive handling; it also requires no sample derivatization, which is a common requirement for LC-MS/MS quantitation of steroid hormones. Its application to multisteroid assays is also viable, and it is envisaged that it may provide a gold standard technique for hormone quantitation in animal reproductive science studies. (C) 2011 Elsevier Inc. All rights reserved.

Effect of Recombinant Bovine Somatotropin on Plasma Concentrations of Insulin-like Growth Factor I, Insulin and Membrane Integrity of Bull Spermatozoa

Contents This study aimed to evaluate the effect of the exogenous recombinant bovine somatotropin (rbST) on plasma concentrations of insulin-like growth factor I (IGF-I), insulin and semen quality of bulls. Twenty bulls (Aberdeen Angus and Brangus) were divided by breed into two groups. Placebo group was injected with NaCl 0.9% (s.c.) and treatment group with rbST (s.c., 500 mg) at days 0 and 14 of the experiment. Immediately after semen collection, blood samples were taken on days 0, 14, 28, 42 and 56 of the experiment. Semen was also collected on day 70 of the experiment. Evaluation of sperm motility was performed at pre-freezing and post-thawing stage, whereas assessment of sperm membrane integrity was performed after freezing and thawing. Analysis of data revealed that the effect of treatment and treatment-by-collection day on plasma concentrations of IGF-I and insulin was not significant. However, mean plasma concentrations of IGF-I and insulin were affected (p < 0.0001) by days of blood sampling. Effect of treatment and treatment-by-collection day on motility of spermatozoa was similar (p > 0.05) at pre-freezing and post-thawing stage. Intactness of plasmalemma and tail membrane of spermatozoa at post-thawing stage was higher (p < 0.05) in rbST-treated group than in control. In conclusion, rbST did not affect plasma concentrations of IGF-I and insulin, however, it did improve post-thaw sperm membrane integrity.

Validation of non-fluorescent methods to reliably detect acrosomal and plasma membrane integrity of common marmoset (Callithrix jacchus) sperm

Simple, rapid and stable sperm evaluation methods which have been optimized for common marmoset (Callithrix jacchus) are critical for studies involving collection and evaluation of sperm in the field. This is particularly important for new species groups such as Callitrichidae where the sperm have been little studied. Of this family, C jacchus is the best known, and has been chosen as a model species for other members of the genus Callithrix. The fundamental evaluation parameters for sperm of any species are viability and acrosomal status. Semen samples were collected by penile vibratory stimulation. To evaluate sperm plasma membrane integrity, Eosin-Nigrosin was tested here for the common marmoset sperm to be used under field conditions. Further, a non-fluorescent stain for acrosome, the ""Simple"" stain, developed for domestic and wild cats, was tested on common marmoset sperm. This was compared with a fluorescent staining, Fluorescein isothiocyanate-Pisum sativum agglutinin (FITC-PSA), routinely used and validated for common marmoset at the German Primate Centre to evaluate acrosomal integrity. Results obtained with the ""Simple"" stain showed a marked differentiation between sperm with intact and non-intact acrosome both with and without ionophore treatment and closely correlated with results obtained with FITC-PSA. Temperature had no effect on the results with the ""Simple"" stain and the complete processing is simple enough to be carried out under field conditions. These findings indicated that the ""Simple"" stain and Eosin-Nigrosin provide rapid and accurate results for C. jacchus sperm and that those methods can be reliably used as field tools for sperm evaluation for this species. (c) 2008 Elsevier Inc. All rights reserved.

Exercise training accelerates the removal from plasma of LDL-like nanoemulsion in moderately hypercholesterolemic subjects

Objective: Exercise training improves plasma lipid profile and diminishes risk of coronary heart disease. Previously, we showed that training increases LDL plasma clearance, as tested by an artificial LDL-like nanoemulsion method, presumably by increasing LDL receptor activity. In this study, we investigated whether training could also improve LDL clearance in hypercholesterolemic subjects (HCh) that are exposed to increased risk of cardiovascular events. Methods: Twenty sedentary HCh and 20 normolipidemic (NL) sedentary volunteers were divided into four groups: 12 HCh submitted to 4-month training program, 8 HCh with no exercise program, 12 NL submitted to 4-month training and 8 NL with no exercise program. An LDL-like nanoemulsion labeled with 14C-cholesteryl ester was injected intravenously into all subjects and plasma samples were collected during 24h after injection to determine the fractional clearance rate (FCR, in h-1) by compartmental analysis. The study was performed on the first and on the last day of the 4-month study period. Results: In both, trained HCh and NL groups, training increased nanoemulsion FCR by 36% (0.0443 +/- 0.0126; 0.0602 +/- 0.0187, p=0.0187 and 0.0503 +/- 0.0203; 0.0686 +/- 0.0216, p=0.0827, respectively). After training, LDL cholesterol diminished in both HCh and NL groups. In HCh, but not in NL group, LDL susceptibility to oxidation decreased, but oxidized LDL was unchanged. In both non-trained groups FCR was the same for the last and the 4-month previous evaluation. Conclusion: In HCh, exercise training increased the removal of LDL as tested by the nanoemulsion, and this probably accounted for decreased LDL cholesterol and diminished LDL susceptibility to oxidation. (C) 2010 Elsevier Ireland Ltd. All rights reserved.

Proving Temporal Properties of Z Specifications Using Abstraction

This paper presents a systematic approach to proving temporal properties of arbitrary Z specifications. The approach involves (i) transforming the Z specification to an abstract temporal structure (or state transition system), (ii) applying a model checker to the temporal structure, (iii) determining whether the temporal structure is too abstract based on the model checking result and (iv) refining the temporal structure where necessary. The approach is based on existing work from the model checking literature, adapting it to Z.

Effects of sperm concentration and straw volume on motion characteristics and plasma, acrosomal, and mitochondrial membranes of equine cryopreserved spermatozoa

The advantages of using cryopreserved semen in equine reproduction are well known. During cryopreservationl spermatozoa undergo many changes that lead to a decrease in fertility. There is no agreement on the ideal sperm dose and concentration to maximize fertility rates. Thus, the objectives of this experiment were to evaluate sperm motion by computer-assisted analysis (CASA), sperm membrane integrity and function with fluorescence probes of cryopreserved sperm at three concentrations: 100 (C100), 200 (C200) and 400 x 10(6) sperm/mL (C400), and two straw volumes (0.50 and 0.25 mL). There was no interaction between sperm concentration and storage volume (P > .05). Sperm motion characteristics were influenced by concentration (C100 > C200 > C400; P < .05). Curvilinear velocity (VCL) in 0.25-mL straws had higher average values (P < .05). Membrane integrity and function were not changed by straw volume (P > .05). However, sperm concentration changed the percentage of cells with intact plasma membrane (C100 > C200 > C400; P < .05) and the percentage of cells with high mitochondrial membrane potential (C100 = C200; P > .05 and C400 < C100 and C200; P < .05). According to this experiment, the best freeing method was that involving 100 x 10(6) sperm/mL, regardless of straw volume.

Physical-mechanical properties of glass ionomer cements indicated for atraumatic restorative treatment

Background: This study evaluated mechanical properties of glass ionomer cements (GICs) used for atraumatic restorative treatment. Wear resistance, Knoop hardness (Kh), flexural (F(s)) and compressive strength (C(s)) were evaluated. The GICs used were Riva Self Cure (RVA), Fuji IX (FIX), Hi Dense (HD), Vitro Molar (VM), Maxxion R (MXR) and Ketac Molar Easymix (KME). Methods: Wear was evaluated after 1, 4, 63 and 365 days. Two-way ANOVA and Tukey post hoc tests (P = 0.05) analysed differences in wear of the GICs and the time effect. F(s), C(s), and Kh were analysed with one-way ANOVA. Results: The type of cement (p < 0.001) and the time (p < 0.001) had a significant effect on wear. In early-term wear and Kh, KME and FIX presented the best performance. In long-term wear, F(s) and C(s), KME, FIX and HD had the best performance. Strong explanatory power between F(s) and the Kh (r(2) = 0.85), C(s) and the Kh (r(2) = 0.82), long-term wear and F(s) of 24 h (r(2) = 0.79) were observed. Conclusions: The data suggested that KME and FIX presented the best in vitro performance. HD showed good results except for early-term wear.

Composite pre-heating: Effects on marginal adaptation, degree of conversion and mechanical properties

Objectives. This study evaluated the effect of composite pre-polymerization temperature and energy density on the marginal adaptation (MA), degree of conversion (DC), flexural strength (FS), and polymer cross-linking (PCL) of a resin composite (Filtek Z350, 3M/ESPE). Methods. For MA, class V cavities (4mmx2mmx2mm) were prepared in 40 bovine incisors. The adhesive system Adper Single Bond 2 (3M/ESPE) was applied. Before being placed in the cavities, the resin composite was either kept at room-temperature (25 degrees C) or previously pre-heated to 68 degrees C in the Calset (TM) device (AdDent Inc., Danbury, CT, USA). The composite was then light polymerized for 20 or 40s at 600mW/cm(2) (12 or 24 J/cm(2), respectively). The percentage of gaps was analyzed by scanning electron microscopy, after sectioning the restorations and preparing epoxy resin replicas. DC (n = 3) was obtained by FT-Raman spectroscopy on irradiated and non-irradiated composite surfaces. FS (n = 10) was measured by the three-point-bending test. KHN (n = 6) was measured after 24h dry storage and again after immersion in 100% ethanol solution for 24 h, to calculate PCL density. Data were analyzed by appropriate statistical analyses. Results. The pre-heated composite showed better MA than the room-temperature groups. A higher number of gaps were observed in the room-temperature groups, irrespective of the energy density, mainly in the axial wall (p < 0.05). Composite pre-heating and energy density did not affect the DC, FS and PCL (p > 0.05). Significance. Pre-heating the composite prior to light polymerization similar in a clinical situation did not alter the mechanical properties and monomer conversion of the composite, but provided enhanced composite adaptation to cavity walls. (C) 2010 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Effect of ion-exchange temperature on mechanical properties of a dental porcelain

The objective of this study was to determine the influence of different ion-exchange temperatures on the biaxial flexural strength (sigma(f)), hardness (HV) and indentation fracture resistance (K(IF)) of a dental porcelain. Disk-shaped specimens were divided into five groups (n = 10) and submitted to an ion-exchange procedure using KNO(3) paste for 15 min in the following temperatures (degrees C); (I) 430; (II) 450; (III) 470; (IV) 490; (V) 510; and control (no ion exchange). The value of sigma(f) was determined in artificial saliva at 37 degrees C. The values of HV and K(IF) were obtained using 3 Vickers indentations in each specimen (19.6 N). Results showed that ion exchange increases significantly the properties of the material as compared to the control and no significant differences were found among the temperatures tested for any of the properties studied. (C) 2010 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Effect of argon purity on mechanical properties, microstructure and fracture mode of commercially pure (cp) Ti and Ti-6Al-4V alloys for ceramometal dental prostheses

Provision of an inert gas atmosphere with high-purity argon gas is recommended for preventing titanium castings from contamination although the effects of the level of argon purity on the mechanical properties and the clinical performance of Ti castings have not yet been investigated. The purpose of this study was to evaluate the effect of argon purity on the mechanical properties and microstructure of commercially pure (cp) Ti and Ti-6Al-4V alloys. The castings were made using either high-purity and/or industrial argon gas. The ultimate tensile strength (UTS), proportional limit (PL), elongation (EL) and microhardness (VHN) at different depths were evaluated. The microstructure of the alloys was also revealed and the fracture mode was analyzed by scanning electron microscopy. The data from the mechanical tests and hardness were subjected to a two-and three-way ANOVA and Tukey`s test (alpha = 0.05). The mean values of mechanical properties were not affected by the argon gas purity. Higher UTS, PL and VHN, and lower EL were observed for Ti-6Al-4V. The microhardness was not influenced by the argon gas purity. The industrial argon gas can be used to cast cp Ti and Ti-6Al-4V.

Bis-GMA co-polymerizations: Influence on conversion, flexural properties, fracture toughness and susceptibility to ethanol degradation of experimental composites

Objectives. The aim of this study was to evaluate the influence of monomer content on fracture toughness (K(Ic)) before and after ethanol solution storage, flexural properties and degree of conversion (DC) of bisphenol A glycidyl methacrylate (Bis-GMA) co-polymers. Methods. Five formulations were tested, containing Bis-GMA (B) combined with TEGDMA (T), UDMA (U) or Bis-EMA (E), as follows (in mol%): 30B:70T; 30B:35T:35U; 30B:70U; 30B:35T:35E; 30B:70E. Bimodal filler was introduced at 80 wt%. Single-edge notched beams for fracture toughness (FT, 25 mm x 5 mm x 2.5 mm, a/w = 0.5, n = 20) and 10 mm x 2 mm x 1 mm beams for flexural strength (FS) and modulus (FM) determination (10 mm x 2 mm x 1 mm, n = 10) were built and then stored in distilled water for 24 h at 37 degrees C. All FS/FM beams and half of the FT specimens were immediately submitted to three-point bending test. The remaining FT specimens were stored in a 75%ethanol/25%water (v/v) solution for 3 months prior to testing. DC was determined with FT-Raman spectroscopy in fragments of both FT and FS/FM specimens at 24 h. Data were submitted to one-way ANOVA/Tukey test (alpha = 5%). Results. The 30B:70T composite presented the highest K(Ic) value (in MPa m(1/2)) at 24 h (1.3 +/- 0.4), statistically similar to 30B:35T:35U and 30B:70U, while 30B:70E presented the lowest value (0.5 +/- 0.1). After ethanol storage, reductions in K(Ic) ranged from 33 to 72%. The 30B:70E material presented the lowest reduction in FT and 30B:70U, the highest. DC was similar among groups (69-73%), except for 30B:70U (52 +/- 4%, p < 0.001). 30B:70U and 30B:35T:35U presented the highest FS (125 +/- 21 and 122 +/- 14 MPa, respectively), statistically different from 30B:70T or 30B:70E (92 +/- 20 and 94 +/- 16 MPa, respectively). Composites containing UDMA or Bis-EMA associated with Bis-GMA presented similar FM, statistically lower than 30B:35T:35U. Significance. Composites formulated with Bis-GMA:TEGDMA:UDMA presented the best compromise between conversion and mechanical properties. (C) 2009 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Shrinkage stress and mechanical properties of photoactivated composite resin using the argon ion laser

The objective of this study was to verify the influence of photoactivation with the argon ion laser on shrinkage stress (SS), followed by evaluation of Vickers microhardness (VM), percentage of maximum hardness (PMH), flexural strength (FS), and flexural modulus (FM) of a composite resin. The study groups were: L1-laser at 200 mW for 10 seconds; L2-laser at 200 mW for 20 seconds; L3-laser at 250 mW for 10 seconds; L4-laser at 250 mW for 20 seconds; H-halogen light at 275 mW for 20 seconds. Data were analyzed by ANOVA/Tukey`s test (alpha=5%). The values of SS (MPa) were statistically lower for the group L3 (1.3)c, followed by groups L1 (2.7)b, L4 (3.4)a, b, L2 (3.7)a, and H (4.5)a. There was no difference in the values of VM when the same time of photoactivation was used, with respective values being L1=70.1a, L2=78.1b, L3=69.9a, L4=78.1b and H=79.9b. All groups showed a PMH of at least 80%. Only the group L1 showed differences in FS (MPa) and FM (GPa), the respective values of 86.2 and 5.4 being lower. Therefore, the use of argon ion laser had influenced the composite resin polymerization. The L3 group presented adequate mechanical properties and minimum SS, reducing the clinical working time for photoactivation of restorations with the tested resin by 50%.

Tailoring of physical properties in highly filled experimental nanohybrid resin composites

Objectives. To assess the elastic modulus (EM), volumetric shrinkage (VS), and polymerization shrinkage stress (PSS) of experimental highly filled nanohybrid composites as a function of matrix composition, filler distribution, and density. Methods. One regular viscosity nanohybrid composite (Grandio, VOCO, Germany) and one flowable nanohybrid composite (Grandio Flow, VOCO) were tested as references along with six highly filled experimental nanohybrid composites (four Bis-GMA-based, one UDMA-based, and one Ormocer (R) -based). The experimental composites varied in filler size and density. EM values were obtained from the ""three-point bending"" load-displacement curve. VS was calculated with Archimedes` buoyancy principle. PSS was determined in 1-mm thick specimens placed between two (poly) methyl methacrylate rods (empty set = 6 mm) attached to an universal testing machine. Data were analyzed using oneway ANOVA, Tukey`s test (alpha = 0.05), and linear regression analyses. Results. The flowable composite exhibited the highest VS and PSS but lowest EM. The PSS was significantly lower with Ormocer. The EM was significantly higher among experimental composites with highest filler levels. No significant differences were found between all other experimental composites regarding VS and PSS. Filler density and size did not influence EM, VS, or PSS. Significance. Neither the filler configuration nor matrix composition in the investigated materials significantly influenced composite shrinkage and mechanical properties. The highest filled experimental composite seemed to increase EM by keeping VS and PSS low; however, matrix composition seemed to be the determinant factor for shrinkage and stress development. The Ormocer, with reduced PSS, deserves further investigation. Filler size and density did not influence the tested parameters. (C) 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.