Fretting fatigue in overhead conductors: Rig design and failure analysis of a Grosbeak aluminium cable steel reinforced conductor

The performance optimisation of overhead conductors depends on the systematic investigation of the fretting fatigue mechanisms in the conductor/clamping system. As a consequence, a fretting fatigue rig was designed and a limited range of fatigue tests was carried out at the middle high cycle fatigue regime in order to access an exploratory S-N curve for a Grosbeak conductor, which was mounted on a mono-articulated aluminium clamping system. Subsequent to these preliminary fatigue tests, the components of the conductor/clamping system, such as ACSR conductor, upper and lower clamps, bolt and nuts, were subjected to a failure analysis procedure in order to investigate the metallurgical free variables interfering on the fatigue test results, aiming at the optimisation of the testing reproducibility. The results indicated that the rupture of the planar fracture surfaces observed in the external At strands of the conductor tested under lower bending amplitude (0.9 mm) occurred by fatigue cracking (I mm deep), followed by shear overload. The V-type fracture surfaces observed in some At strands of the conductor tested under higher bending amplitude (1.3 mm) were also produced by fatigue cracking (approximately 400 mu m deep), followed by shear overload. Shear overload fracture (45 degrees fracture surface) was also observed on the remaining At wires of the conductor tested under higher bending amplitude (1.3 mm). Additionally, the upper and lower Al-cast clamps presented microstructure-sensitive cracking, which was folowed by particle detachment and formation of abrasive debris on the clamp/conductor tribo-interface, promoting even further the fretting mechanism. The detrimental formation of abrasive debris might be inhibited by the selection of a more suitable class of as-cast At alloy for the production of clamps. Finally, the bolt/nut system showed intense degradation of the carbon steel nut (fabricated in ferritic-pearlitic carbon steel, featuring machined threads with 190 HV), with intense plastic deformation and loss of material. Proper selection of both the bolt and nut materials and the finishing processing might prevent the loss in the clamping pressure during the fretting testing. It is important to control the specification of these components (clamps, bolt and nuts) prior to the start of large scale fretting fatigue testing of the overhead conductors in order to increase the reproducibility of this assessment. (c) 2008 Elsevier Ltd. All rights reserved.

Cracking of 2.25Cr-1.0Mo steel tube/stationary tube-sheet weldment of a heat-exchanger

The premature failure of a horizontal heat-exchanger, which occurred after service exposure at 580 degrees C for 50,000 h, revealed the occurrence of extensive through-thickness cracking in approximately 40% of the tube/stationary tube-sheet welds. Additionally, the internal surface of the welded joint featured intensive secondary intergranular cracking (up to 250 mu m deep), preferential formation of a 150 mu m thick layer of (Fe, Cr)(3)O-4 and internal intergranular oxidation (40 mu m deep). The welded region also showed intense carbon pick-up and, as consequence, severe precipitation of intergranular M7C3 and M23C6 carbides. The fracture surface was composed of two distinct regions: a ""planar"" region of 250 mu m, formed due to the stable crack growth along by the intergranular oxidation; and a slant region with radial marks, formed by the fast crack growth along the network of intergranular carbides. The association of intergranular oxidation pre-cracks with microstructural embrittlement promoted the premature failure, which took place by an overload mechanism, probably due to the jamming of the floating tube-sheet during the maintenance halt (cooling operation). (C) 2007 Elsevier Ltd. All rights reserved.

Open-circuit voltages: Theoretical and experimental optimizations of rear passivated silicon solar cells using Fz and Cz wafers

The theoretical and experimental open-circuit voltage optimizations of a simple fabrication process of silicon solar cells n(+)p with rear passivation are presented. The theoretical results were obtained by using an in-house developed program, including the light trapping effect and metal-grid optimization. On the other hand, the experimental steps were monitored by the photoconductive decay technique. The starting materials presented thickness of about 300 pm and resistivities: FZ (0.5 Omega cm), Cz-type 1 (2.5 Omega cm) and Cz-type 2 (3.3 Omega cm). The Gaussian profile emitters were optimized with sheet resistance between 55 Omega/sq and 100 Omega/sq, and approximately 2.0 mu m thickness in accordance to the theoretical results. Excellent implied open-circuit voltages of 670.8 mV, 652.5 mV and 662.6 mV, for FZ, Cz-type 1 and Cz-type 2 silicon wafers, respectively, could be associated to the measured lifetimes that represents solar cell efficiency up to 20% if a low cost anti-reflection coating system, composed by random pyramids and SiO(2) layer, is considered even for typical Cz silicon. (C) 2009 Elsevier Ltd. All rights reserved.

Corrosion resistant and adsorbent plasma polymerized thin film

Adsorbent and corrosion resistant films are useful for sensor development. Therefore, the aim of this work is the production and characterization of plasma polymerized fluorinated organic ether thin films for sensor development. The polymerized reactant was methyl nonafluoro(iso)butyl ether. Infrared Spectroscopy showed fluorinated species and eventually CO but CH(n) is a minor species. Contact angle measurements indicated that the film is hydrophobic and organophilic but oleophobic. Optical microscopy reveals not only a good adherence on metals and acrylic but also resistance for organic solvents, acid and basic aqueous solution exposure. Double layer and intermixing are possible and might lead to island formation. Quartz Crystal Microbalance showed that 2-propanol permeates the film but there is no sensitivity to n-hexane. The microreactor manufactured using a 73 cm long microchannel can retain approximately 9 X 10(-4) g/cm(2) of 2-propanol in vapor phase. Therefore, the film is a good candidate for preconcentration of volatile organic compounds even in corrosive environment. (C) 2009 Elsevier B.V. All rights reserved.

TL and OSL properties of KAlSi(3)O(8):Mn, obtained by sol-gel process

Thermoluminescence (TL) and Optically Stimulated Luminescence (OSL) properties of KAlSi(3)O(8):Mn glasses obtained through the sol gel technique were investigated. Samples were obtained with five different molar concentrations of 0.25, 0.5, 1, 2 and 5 mol% of manganese. Transmission Electronic Microscopy (TEM) indicated the occurrence of nanoparticles composed by glass matrix elements with Mn. Best results for TL response were obtained with 0.5 mol% Mn doped sample, which exhibits a TL peak at 180 degrees C. The TL spectrum of this sample presents a broad emission band from 450 to 700 nm with a peak at 575 nm approximately. The emission band fits very well with the characteristic lines of the Mn(2+) emission features. According to this fact, the band at 410 nm can be ascribed to (6)A(1)(S) -> (4)A(1)(G), (4)E(G) transition, while the 545 nm band can be attributed to the superposition of the transitions (6)A(1)(S) -> (4)T(2)(G) and (6)A(1)(S) -> (4)T(1)(G). The dependence of the TL response with the energy of X-rays (27-41 keV) showed a small decrease of the TL intensity in the high energy region. Excitation with blue LEDs showed OSL in the UV region with a fast decay component. (C) 2011 Elsevier Ltd. All rights reserved.

In Vitro and In Vivo Evaluation of Lyophilized Bioprosthetic Valve

Freeze-drying of biological tissues allows for dry storage and gamma ray sterilization, which may improve their use as a medical prosthesis. The objective of this study was to evaluate the rehydration characteristics and hydrodynamic performance of prosthetic valves before and after lyophilization. Two size 23 bovine pericardium aortic valve prostheses from different manufacturers were evaluated in a Shelhigh (Union, NJ, USA) pulse duplicator (80 ppm, 5 L/min) before and after lyophilization. Flow and transvalvular pressure gradient were registered in vitro and in vivo, and images of opening and closing of the prosthesis were obtained in the pulse duplicator in a digital camera. Rehydration was evaluated by comparison of dry valve weight with valve weight after 15 min, and 1, 24, 48, and 72 h in saline solution, inside the pulse duplicator. In vivo performance was assessed by surgical implantation in Santa Ines young male sheep in the pulmonary position after 30 min rehydration with 0.9% saline. Transvalvular pressure gradient and flow measurements were obtained immediately after implantation and 3 months after surgery when valves were explanted. Captured images showed a change in the profile opening and closing of valve prosthesis after lyophilization. The gradient measured (in vitro) in two valves was 17.08 +/- 0.57 and 18.76 +/- 0.70 mm Hg before lyophilization, and 34.24 +/- 0.59 and 30.40 +/- 0.97 mm Hg after lyophilization. Rehydration of both lyophilized valves was approximately 82%. Drying changed the profile of the opening and closing of valve prostheses, and increased on average by 83% the gradient in vitro tests. The result of the in vivo tests suggests maintaining pressure levels of the animal with the lyophilized prostheses within acceptable levels.

Tax Cost of Investment Projects: the case of ICMS credits

This article discusses the impact on the profitability of firms under Complementary Law 102/2000 (which abrogated the Law 89/96 - Kandir Law) allowing the appropriation of ICMS credits, due to investment in fixed assets goods, at a ratio of 1/48 per month. The paper seeks to demonstrate how this new system - which resulted in the transformation of the ICMS as a value added tax (VAT) consumption-type to an income-type - leads to a loss of approximately 30% of the value of credits to be recovered and the effect it generates on the cost of investment and the profits for small, medium and large firms. From the methodological point of view, it is a descriptive and quantitative research, which proceeded in three stages. Initially, we have obtained estimated value of net sales and volume of investments, based on report Painel de Competitividade prepared by the Federacao das Indtustrias do Estado de Sao Paulo (Fiesp/Serasa). Based on this information, it was possible to obtain estimates of the factors of generation of debits and credits for ICMS, using the model Credit Control of Fixed Assets (CIAP). Finally, we have calculated three indicators: (i) present value of debt recovery/value of credits, (ii) present value of debt recovery / investment value, (iii) present value of debt recovery / sales profitability. We have conclude that the system introduced by Complementary Law 102/2000 implicates great opportunity cost for firms and that legislation should be reviewed from this perspective, aiming to ensure lower costs associated with investment projects.

Determining the effect of grain size and maximum induction upon coercive field of electrical steels

Although theoretical models have already been proposed, experimental data is still lacking to quantify the influence of grain size upon coercivity of electrical steels. Some authors consider a linear inverse proportionality, while others suggest a square root inverse proportionality. Results also differ with regard to the slope of the reciprocal of grain size-coercive field relation for a given material. This paper discusses two aspects of the problem: the maximum induction used for determining coercive force and the possible effect of lurking variables such as the grain size distribution breadth and crystallographic texture. Electrical steel sheets containing 0.7% Si, 0.3% Al and 24 ppm C were cold-rolled and annealed in order to produce different grain sizes (ranging from 20 to 150 mu m). Coercive field was measured along the rolling direction and found to depend linearly on reciprocal of grain size with a slope of approximately 0.9 (A/m)mm at 1.0 T induction. A general relation for coercive field as a function of grain size and maximum induction was established, yielding an average absolute error below 4%. Through measurement of B(50) and image analysis of micrographs, the effects of crystallographic texture and grain size distribution breadth were qualitatively discussed. (C) 2011 Elsevier B.V. All rights reserved.

Measuring the eco-efficiency of cement use

At present, the cement industry generates approximately 5% of the world`s anthropogenic CO(2) emissions. This share is expected to increase since demand for cement based products is forecast to multiply by a factor of 2.5 within the next 40 years and the traditional strategies to mitigate emissions, focused on the production of cement, will not be capable of compensating such growth. Therefore, additional mitigation strategies are needed, including an increase in the efficiency of cement use. This paper proposes indicators for measuring cement use efficiency, presents a benchmark based on literature data and discusses potential gains in efficiency. The binder intensity (bi) index measures the amount of binder (kg m(-3)) necessary to deliver 1 MPa of mechanical strength, and consequently express the efficiency of using binder materials. The CO(2) intensity index (ci) allows estimating the global warming potential of concrete formulations. Research benchmarks show that bi similar to 5 kg m(-3) MPa(-1) are feasible and have already been achieved for concretes >50 MPa. However, concretes with lower compressive strengths have binder intensities varying between 10 and 20 kg m(-3) MPa(-1). These values can be a result of the minimum cement content established in many standards and reveal a significant potential for performance gains. In addition, combinations of low bi and ci are shown to be feasible. (c) 2010 Elsevier Ltd. All rights reserved.

Water Treatment Plant Sludge Discharge to Wastewater Treatment Works: Effects on the Operation of Upflow Anaerobic Sludge Blanket Reactor and Activated Sludge Systems

This experiment examined the effects of the discharge of water treatment plant (WTP) sludge into the following three types of wastewater treatment systems: a pilot-scale upflow anaerobic sludge blanket (UASB) reactor, a pilot-scale activated sludge system, and a full-scale activated sludge sequencing batch reactor (SBR). The UASB reactor received 50 mg of suspended solids ( SS) of WTP sludge per liter of wastewater in the first phase, and, in the second phase, it received 75 mg SS/L. The pilot-scale activated sludge system received 25 and 50 mg SS/L in the first and second phases, respectively. The full-scale WWTP ( SBR) received approximately 74 mg SS/L. The results of the experiments showed that, despite some negative effects on nitrification, there were positive effects on phosphorus removal, and, furthermore, there was the addition of solids in all systems. Water Environ. Res., 82, 392 ( 2010).

Carbide lime and industrial hydrated lime characterization

This paper focuses on the characterization of carbide lime (CL) - a by-product of acetylene production, composed mainly of calcium hydroxide with minor parts of carbonate - and compares its features to those of ""dry"" hydrated lime (HL) commonly used as a building material. Chemical, thermogravimetric and X-ray diffraction analyses indicated that the limes are similar in chemical and mineralogical compositions. except for the presence of carbon in the waste. Morphological and elemental chemical analyses by SEM and EDS revealed that CL particles differ from HL ones in their morphology and by the presence of carbon formations, Physical characterization included density and BET surface area of the materials. as well as, their particle size distributions in deionized water at diverse time periods. CL underwent agglomeration after approximately 60 min in water, whereas HL progressively became finer with time as determined by laser diffraction. In addition, water retention and squeeze flow tests were used to assess the pastes` fresh properties. (c) 2009 Elsevier B.V. All rights reserved.

Antiproliferative Effect of Benzophenones and their Influence on Cathepsin Activity

The antiproliferative activity of two prenylated benzophenones isolated from Rheedia brasiliensis. the tri-prenylated garciniaphenone and the tetraprenylated benzophenone 7-epiclusianone, was investigated against human cancer cell lines. The antiproliferative activity on melanoma (UACC-62), breast (MCF-7), drug-resistant breast (NCI-ADR), lung/non-small cells (NCI460), ovarian (OVCAR 03), prostate (PC03), kidney (786-0), lung (NCI-460) and tongue (CRL-1624 and CRL-1623) cancer cells was determined using spectrophotometric quantification of the cellular protein content. The effect of these benzophenones on the activity of cathepsins B and G was also investigated. Garciniaphenone displayed cytostatic activity in all cell lines, whereas 7-epiclusianone showed a dose-dependent cytotoxic effect. The IC(50) values for cell proliferation revealed that 7-epiclusianone is more active than garciniaphenone against most of the cell lines. Furthermore, the antiproliferative effects demonstrated by garciniaphenone and 7-epiclusianone were related to their cathepsin inhibiting properties. In conclusion, 7-epiclusianone is a promising naturally occurring agent which displays multiple inhibitory effects which may be working in concert to inhibit cancer cell proliferation in vitro. The putative pathway by which 7-epiclusianone affects cancer cell development may involve cathepsin inhibition. Copyright (C) 2009 John Wiley & Sons, Ltd.

Emerging Threats and Opportunities for Large-Scale Ecological Restoration in the Atlantic Forest of Brazil

Over the past 150 years, Brazil has played a pioneering role in developing environmental policies and pursuing forest conservation and ecological restoration of degraded ecosystems. In particular, the Brazilian Forest Act, first drafted in 1934, has been fundamental in reducing deforestation and engaging private land owners in forest restoration initiatives. At the time of writing (December 2010), however, a proposal for major revision of the Brazilian Forest Act is under intense debate in the National Assembly, and we are deeply concerned about the outcome. On the basis of the analysis of detailed vegetation and hydrographic maps, we estimate that the proposed changes may reduce the total amount of potential areas for restoration in the Atlantic Forest by approximately 6 million hectares. As a radically different policy model, we present the Atlantic Forest Restoration Pact (AFRP), which is a group of more than 160 members that represents one of the most important and ambitious ecological restoration programs in the world. The AFRP aims to restore 15 million hectares of degraded lands in the Brazilian Atlantic Forest biome by 2050 and increase the current forest cover of the biome from 17% to at least 30%. We argue that not only should Brazilian lawmakers refrain from revising the existing Forest Law, but also greatly step up investments in the science, business, and practice of ecological restoration throughout the country, including the Atlantic Forest. The AFRP provides a template that could be adapted to other forest biomes in Brazil and to other megadiversity countries around the world.

Ectopic expression of soybean leghemoglobin in chloroplasts impairs gibberellin biosynthesis and induces dwarfism in transgenic potato plants

We have characterized potato (Solanum tuberosum L.) plants expressing a soybean leghemoglobin that is targeted to plastids. Transgenic plants displayed a dwarf phenotype caused by short internode length, and exhibited increased tuberization in vitro. Under in vivo conditions that do not promote tuberization, plants showed smaller parenchymal cells than control plants. Analysis of gibberellin (GA) concentrations indicated that the transgenic plants have a substantial reduction (approximately 10-fold) of bioactive GA(1) concentration in shoots. Application of GA(3) to the shoot apex of the transformed plants completely restored the wild type phenotype suggesting that GA-biosynthesis rather than signal transduction was limiting. Since the first stage of the GA-biosynthetic pathway is located in the plastid, these results suggest that an early step in the pathway may be affected by the presence of the leghemoglobin.

Impacts of land-use pattern on soil water-content variability on the Loess Plateau of China

Long-term vegetation restoration carried out on the slopes of the Loess Plateau of China employed different spatial and temporal land-use patterns but very little is known about the effects of these patterns on soil water-content variability. For this study the small Donggou catchment was selected to investigate soil water-content distributions for three spatial scales, including the entire catchment area, sampling transects, and land-use systems. Gravimetric soil water contents were determined incrementally to a soil depth of 1.20 m, on 10 occasions from April to October, 2007, at approximately 20-day intervals. Results indicated that soil water contents were affected by the six land-use types, resulting in four distinct patterns of vertical distribution of soil moisture (uniform, increasing, decreasing, and fluctuating with soil depth). The soil water content and its variation were also influenced in a complex manner by five land-use patterns distributed along transects following the gradients of five similar slopes. These patterns with contrasting hydrological responses in different components, such as forage land (alfalfa)-cropland-shrubland or shrubland-grassland (bunge needlegrass)-cropland-grassland, showed the highest soil water-content variability. Soil water at the catchment scale exhibited a moderate variability for each measurement date, and the variability of soil water content decreased exponentially with increasing soil water content. The minimum sample size for accurate data for use in a hydrological model for the catchment, for example, required many more samples for drier (69) than for wet (10) conditions. To enhance erosion and runoff control, this study suggested two strategies for land management: (i) to create a mosaic pattern by land-use arrangement that located units with higher infiltration capacities downslope from those with lower soil infiltrabilities; and (ii) raising the soil-infiltration capacity of units within the spatial mosaic pattern where possible.