Fabrication of Novel Superhydrophobic Surfaces and Water Droplet Bouncing Behavior - Part 1: Stable ZnO-PDMS Superhydrophobic Surface with Low Hysteresis Constructed Using ZnO Nanoparticles

A superhydrophobic surface has many advantages in micro/nanomechanical applications, such as low adhesion, low friction and high restitution coefficient, etc. In this paper, we introduce a novel and simple route to fabricate superhydrophobic surfaces using ZnO nanocrystals. First, tetrapod-like ZnO nanocrystals were prepared via a one-step, direct chemical vapor deposition (CVD) approach. The nanostructured ZnO material was characterized by scanning electron microscope (SEM) and X-ray diffraction (XRD) and the surface functionalized by aminopropyltriethoxysilane (APS) was found to be hydrophobic. Then the superhydrophobic surface was constructed by depositing uniformly ZnO hydrophobic nanoparticles (HNPs) on the Poly(dimethylsiloxane) (PDMS) film substrate. Water wettability study revealed a contact angle of 155.4 +/- 2 degrees for the superhydrophobic surface while about 110 degrees for pure smooth PDMS films. The hysteresis was quite low, only 3.1 +/- 0.3 degrees. Microscopic observations showed that the surface was covered by micro- and nano-scale ZnO particles. Compared to other approaches, this method is rather convenient and can be used to obtain a large area superhydrophobic surface. The high contact angle and low hysteresis could be attributed to the micro/nano structures of ZnO material; besides, the superhydrophobic property of the as-constructed ZnO-PDMS surface could be maintained for at least 6 months. (C) Koninklijke Brill NV, Leiden, 2010

Fabrication of nano-sized grains by pulsed laser surface melting

In this work, the formation and characterization of nano-sized grains on the modified surfaces of GCr15 and H13 steels have been investigated. The material was processed by pulsed laser surface melting (LSM) under different depths of de-ionized water. The microstructures and phases of the melted zones were examined by x-ray diffraction, environmental field emission scanning electron microscopy and high resolution transmission electron microscopy. The results indicate that LSM under water can successfully fabricate nano-scaled grains on the surfaces of steel, due to the rapid solidification and crystallization by heterogeneous nucleation. The elemental segregation of chromium and activated heterogeneous nucleation mechanism of austenite in liquid metal play a key role in the formation of nano-sized grains at high cooling rates. This one-step technique provides us a new way to prepare uniform nano-scaled grains, and is of great importance for further understanding the growth of nano-materials under extreme conditions.

Experimental Investigation of Performance of a Miniature Direct Methanol Fuel Cell in Short-Term Microgravity

Experimental study of a liquid fed direct methanol fuel cell has been conducted in different gravity environments. A small single cell with 5 cm x 5 cm active area has single serpentine channel on the graphite cathode polar plate and 11 parallel straight channels on the graphite anode flow bed. Cell voltage and current have been measured and two-phase flow in anode channels has been in situ visually observed. The experimental results indicate that the effect of gravity on power performance of the direct methanol fuel cell is large when the concentration polarization governs fuel cells operation. Gravitational effect becomes larger at higher current density. Increasing methanol feeding molarity is conducive to weaken the influence of gravity on performance of liquid fed direct methanol fuel cells. Increasing feeding flow rate of methanol solution from 6 to 15 ml/min could reduce the size of carbon dioxide bubbles, while the influence of gravity still exist. Transport phenomena inside direct methanol fuel cells in microgravity is also analyzed and discussed.

Electrochemical fabrication of single-crystalline and polycrystalline Au nanowires: the influence of deposition parameters

We report the electrochemical growth of gold nanowires with controlled dimensions and crystallinity. By systematically varying the deposition conditions, both polycrystalline and single-crystalline wires with diameters between 20 and 100 nm are successfully synthesized in etched ion-track membranes. The nanowires are characterized using scanning electron microscopy, high resolution transmission electron microscopy, scanning tunnelling microscopy and x-ray diffraction. The influence of the deposition parameters, especially those of the electrolyte, on the nanowire structure is investigated. Gold sulfite electrolytes lead to polycrystalline structure at the temperatures and voltages employed. In contrast, gold cyanide solution favours the growth of single crystals at temperatures between 50 and 65 degrees C under both direct current and reverse pulse current deposition conditions. The single-crystalline wires possess a [110] preferred orientation.

Performance comparison of low-temperature direct alcohol fuel cells with different anode catalysts

Low-temperature polymer electrolyte membrane fuel cells directly fed by methanol and ethanol were investigated employing carbon supported Pt, PtSn and PtRu as anode catalysts, respectively. Employing Pt/C as anode catalyst, both direct methanol fuel cell (DMFC) and direct ethanol fuel cell (DEFC) showed poor performances even in presence of high Pt loading on anode. It was found that the addition of Ru or Sn to the Pt dramatically enhances the electro-oxidation of both methanol and ethanol. It was also found that the single cell adopting PtRu/C as anode shows better DMFC performance, while PtSn/C catalyst shows better DEFC performance. The single fuel cell using PtSn/C as anode catalyst at 90degreesC shows similar power densities whenever fueled by methanol or ethanol. The cyclic voltammetry (CV) and single fuel cell tests indicated that PtRu is more suitable for DMFC while PtSn is more suitable for DEFC. (C) 2003 Elsevier B.V. All rights reserved.

CO selective oxidation in a microchannel reactor for PEM fuel cell

It is indispensable to remove CO at the level of less than 50ppm in H-2-rich feed gas for the proton exchange membrane (PEM) fuel cells. In this paper, catalyst with high activity and selectivity, and a microchannel reactor for CO preferential oxidation (PROX) have been developed. The results indicated that potassium on supported Rh metal catalysts had a promoting effect in the CO selective catalytic oxidation under H-2-rich stream, and microchannel reactor has an excellent ability to use in on-board hydrogen generation system. CO conversion keeps at high levels even at a very high GHSV as 500 000 h(-1), so, miniaturization of hydrogen generation system can be achieved by using the microchannel reactor. (C) 2004 Elsevier B.V. All rights reserved.

Preparation and characterization of PtSn/C anode electrocatalysts for direct ethanol fuel cell

Highly active PtSn/C catalyst was prepared by a polyol method. The catalyst was reduced in H-2/Ar atmosphere at 600 degreesC for 2 h in order to obtain different metallic phase. TEM images show uniform dispersion of spherical metal nanoparticles with average diameters of 1.8 and 3.9 nm for the as-prepared and treated catalysts, respectively. UV-vis spectrophotometry is employed to monitor the preparation process and the results indicate that Pt-Sn complex formed once the precursors of Pt and Sn were mixed together. The structure properties of the samples were characterized using X-ray diffraction. The results show that after reduction, the catalyst tends to form PtSn alloy. TPR experiment results show that Sn exists in multivalent state in the as-prepared sample while only zero-valence Sn was detected in the treated sample, while it could not be excluded that the multivalent tin existed in the treated sample. Cyclic voltammetry (CV) technique and single direct ethanol fuel cell (DEFC) tests indicate that the as-prepared catalyst possesses superior catalytic activity for ethanol oxidation to the treated sample. The results suggest that Pt and multivalent Sn are the active species for ethanol oxidation. (C) 2004 Elsevier B.V. All rights reserved.

Synthesis and characterization of carbon black supported Pt-Ru alloy as a model catalyst for fuel cells

A set of bimetallic Pt-Ru catalysts prepared by co-impregnation of carbon black with ruthenium(III) chloride hydrate and hydrogen hexachloroplatinate(IV) hydrate were investigated by temperature-programmed reduction (TPR), chemisorption of hydrogen, transmission electron microscopy (TEM), microcalorimetry of adsorbed CO and a structure-sensitive reaction (n-hexane conversion). The results showed that the volumetric capacities for CO and H-2 adsorption is influenced in the bimetallic Pt-Ru catalysts by the formation of a Pt-Ru alloy. The n-hexane reaction revealed that the reaction mechanism for the pure Pt catalyst mainly occurs via cyclic isomerization and aromatization due to the presence of bigger Pt surface ensembles, whereas the Pt-Ru catalysts exhibited predominantly bond-shift isomerization by the diluting effect of Ru metal addition. The differential heats of CO chemisorption on Pt-Ru catalysts fell between the two monometallic Pt and Ru catalysts extremes. (C) 2004 Elsevier B.V. All rights reserved.