Metallurgical evaluation of a copper-based alloy for dental castings.

The present study was designed to evaluate the metallurgical properties of an experimental, low-cost copper-zinc-aluminum-nickel alloy for dental castings. Some specimens were subjected to heat treatment after induction casting. The extent of corrosion was determined by measuring weight loss of specimens stored in a sodium sulfite solution. In the as-cast specimens, tests demonstrated the presence of three phases: the first consisted of copper-zinc-aluminum, the second was similar but lower in copper and aluminum, and the third consisted of an intermetallic compound of manganese-nickel-phosphorus. After heat treatment, the first phase remained relatively constant, the second was converted to Cu3Al, and the third increased in volume. The weight loss from the as-cast specimens was eight times that of the heat-treated specimens. It was concluded that the heat treatment substantially changed the microstructure and improved the corrosion resistance of the experimental alloy.

Unrestricted linear dimensional changes of two hard chairside reline resins and one heat-curing acrylic resin

The selection and use of hard chairside reline resins must be made with regard to dimensional stability, which will influence the accuracy of fit of the denture base. This study compared the dimensional change of two hard chairside reline resins (Duraliner II and Kooliner) and one heat-curing denture base resin (Lucitone 550). A stainless steel mold with reference dimensions (AB, CD) was used to obtain the samples. The materials were processed according to the manufacturer's recommendations. Measurements of the dimensions were made after processing and after the samples had been stored in distilled water at 37° C for eight different periods of time. The data were recorded and then analyzed with analysis of variance. All materials showed shrinkage immediately after processing (p < 0.05). The only resin that exhibited shrinkage after 60 days of storage in water was Duraliner II; these changes could be clinically significant in regard of tissue fit.

A study of different calcification areas in newly formed bone 8 weeks after insertion of dental implants in rabbit tibias

In orofacial implantology there are many types of implants for the different systems. Among these is the implant surface type, e.g., a screw type, cylindrical and laminar. Furthermore, the implants are different in their dimensions, their metal composition, their surface condition, such as smooth, grit or layered surfaces and in their methods of application. Two different self-tapping implants, one smooth and the other grit-blasted, are screwed into the bone, and another one with a plasma of titanium coating, which is also in a screw form but with greater spaces between the screw threads are compared. The greatest amount of bone deposition in the bone/implant interface was encountered in the latter one, the smooth surfaced implant being in second place. All of these systems can alter the implant healing process and to demonstrate this, we injected bone markers in the rabbits over different periods of time so as to observe the different areas of bone deposition in the tibias where the implants had been inserted. The bone tracers used were Alizarin, Calcein and Xylenol-orange. The amount of deposition was calculated by using the method of surface morphometry.

Loss of space and dental arch length after the loss of the lower first primary molar: A longitudinal study

The premature loss of primary teeth may harm the normal occlusal development, although there are debates relating to the necessity of using space maintainer appliances. The aim of the study is to evaluate the changes in the dental arch perimeter and the space reduction after the premature loss of the lower first primary molar in the mixed dentition stage. The sample consists of 4 lower arch plaster models of 31 patients, within the period of pre-extraction, 6, 12 and 18 months after the lower first primary molar extraction. A reduction of space was noted with the cuspid dislocation and the permanent incisors moving toward the space of the extraction site. It was concluded that the lower first molar primary premature loss, during the mixed dentition, implicates an immediate placement of a space maintainer.

Biocompatibility of an adhesive system applied to exposed human dental pulp

Human pulp tissue was directly capped with All Bond 2, or calcium hydroxide and evaluated 7, 30, or 60 days after the procedures. Histological analysis was performed to assess the inflammatory cell response, tissue disorganization, dentin bridging, and the presence of bacteria. At 7 days, with All Bond 2 capping, there was a large area of neutrophilic infiltrate underlying the pulp capping material, and the death of adjacent odontoblasts, was observed. However, with time, the neutrophilic reaction was replaced by fibroblastic proliferation with macrophages and giant cells surrounding globules of resin scattered in the coronal pulp tissue. The persistent inflammatory reaction and hyaline alteration of extracellular matrix inhibited complete pulp repair or dentin bridging. In contrast, at 7 days, the pulp tissue capped with calcium hydroxide exhibited odontoblast-like cells organized underneath coagulation necrosis. Pulp repair evolved into apparent complete dentin bridge formation at 60 days. All Bond 2 did not appear to allow any pulp repair and does not appear to be indicated for direct pulp capping of human teeth. Copyright © 1999 by The American Association of Endodontists.

Cytotoxic effects of current dental adhesive systems on immortalized odontoblast cell line MDPC-23

Objectives: Evaluate the cytotoxic effect of the three dental adhesive systems. Methods: The immortalized mouse odontoblast cell line (MDPC-23) was plated (30,000 cell/cm 2) in 24 well dishes, allowed to grow for 72 h, and counted under inverted light microscopy. Uncured fresh adhesives were added to culture medium to simulate effects of unset adhesive. Three adhesives systems were applied for 120 min to cells in six wells for each group: Group 1) Single Bond (3M), Group 2) Prime & Bond 2.1 (Dentsply), and Group 3) Syntac Sprint (Vivadent). In the control group, PBS was added to fresh medium. The cell number was counted again and the cell morphology was assessed under SEM. In addition, the adhesive systems were applied to circles of filter paper, light-cured for 20 s, and placed in the bottom of 24 wells (six wells for each experimental materials and control group). MDPC-23 cells were plated (30,000 cell/cm 2) in the wells and allowed to incubate for 72 h. The zone of inhibition around the filter papers was measured under inverted light microscopy; cell morphology was evaluated under SEM; and the MTT assay was performed for mitochondrial respiration. Results: The fresh adhesives exhibited more toxic (cytopathic effects) to MDPC-23 cells than polymerized adhesives on filter papers, and as compared to the control group. The cytopathic effect of the adhesive systems occurred in the inhibition zone around the filter papers, which was confirmed by the MTT assay and statistical analysis (ANOVA) combined with Fisher's PLSD test. In the control group, MDPC-23 cells were dense on the plastic substrate and were in contact with the filter paper. In the experimental groups, when acid in the adhesive systems was removed by changing the culture medium, or when the adhesives were light-cured, some cells grew in the wells in spite of the persistent cytotoxic effect. Significance: All dentin adhesive systems were cytotoxic odontoblast-like cells. Both acidity and non-acidic components of these systems were responsible for the high cytopathic effect of those dental materials. © 1999 Academy of Dental Materials. Published by Elsevier Science Ltd. All rights reserved.

Use of one-bottle adhesive as an intermediate bonding layer to reduce sealant microleakage on saliva-contaminated enamel

Purpose: To evaluate the influence of three different adhesives, each used as an intermediary layer, on microleakage of sealants applied under condition of salivary contamination. Materials and Methods: Six different experimental conditions were compared, 3 with adhesives and 3 without. After prophylaxis and acid etching of enamel, salivary contamination was placed for 10 s. In Group SC the sealant was applied after saliva without bonding agent and then light-cured. In Group SCA, after saliva, the surface was air dried, and then the sealant was applied and cured. In Groups ScB, SB and PB, a bonding agent (Scotchbond Dual Cure/3M, Single Bond/3M and Prime & Bond 2.1/Dentsply, respectively) was applied after the saliva and prior to the sealant application and curing. After storage in distilled water at 37°C for 24 hrs, the teeth were submitted to 500 thermal cycles (5°C and 55°C), and silver nitrate was used as a leakage tracer. Leakage data were collected on cross sections as percentage of total enamel-sealant interface length. Representative samples were evaluated under SEM. Results: Sealants placed on contaminated enamel with no bonding agent showed extensive microleakage (94.27% in SC; 42.65% in SCA). The SEM revealed gaps as wide as 20 μm in areas where silver nitrate leakage could be visualized. In contrast, all bonding agent groups showed leakage less than 6.9%. Placement of sealant with a dentin-bonding agent on contaminated enamel significantly reduced microleakage (P< 0.0001). The use of a bonding agent as an intermediary layer between enamel and sealant significantly reduced saliva's effect on sealant microleakage.

Use of dental implants in children: A literature review

The aim of this literature review is to discuss the use of dental implants in growing patients and the influence of maxillary and mandibular skeletal and dental growth on the stability of those implants. It is recommended to wait for the completion of dental and skeletal growth, except for severe cases of ectodermal dysplasia.

Healing process of dog dental pulp after pulpotomy and pulp covering with mineral trioxide aggregate or Portland cement.

Considering several reports about the similarity between the chemical compositions of the mineral trioxide aggregate (MTA) and Portland cement (PC), the subject of this investigation was to analyze the behavior of dog dental pulp after pulpotomy and direct pulp protection with these materials. After pulpotomy, the pulp stumps of 26 roots of dog teeth were protected with MTA or PC. Sixty days after treatment, the animal was sacrificed and the specimens removed and prepared for histomorphological analysis. There was a complete tubular hard tissue bridge in almost all specimens. In conclusion, MTA and PC show similar comparative results when used in direct pulp protection after pulpotomy.

Changes in occlusal vertical dimension in microwave processing of complete dentures.

This study investigated the effect of different microwave curing cycles on the changes in occlusal vertical dimension of complete dentures. Four test groups with 12 maxillary dentures each were evaluated. Groups 1, 2 and 3 were polymerized with different cycles by microwave radiation and Group 4 was the control and cured by water bath. The average pin opening for all groups was less than 0.5 mm. There was no significant difference between the groups polymerized by the microwave method and the control group. However, analyses of the vertical dimension changes showed statistically significant differences between groups 2 (0.276 +/- 0.141 mm) and 3 (0.496 +/- 0.220 mm).

Dental implants: Surface modification of cp-Ti using plasma spraying and the deposition of hydroxyapatite

The commercial pure titanium (cp-Ti) is currently being used with great success in dental implants. In this work we investigate how the cp-Ti implants can be improved by modifying the metal surface morphology, on which a synthetic material with properties similar to that of the inorganic part of the bone, is deposited to facilitate the bone/implant bonding. This synthetic material is the hydroxyapatite, HA, a calcium-phosphate ceramic. The surface modification consists in the application of a titanium oxide (TiO2) layer, using the thermal aspersion - plasma spray technique, with posterior deposition of HA, using the biomimetic method. The X-ray diffraction (XRD), Scanning Electron Microscopy (SEM) with Energy Dispersive X-ray (EDX) and Diffuse Reflectance Infrared Fourier Transform (DRIFT) techniques have been used for characterizing phases, microstructures and morphologies of the coatings. The TiO2 deposit shows a mixture of anatase, rutilo and TiO2-x phases, and a porous and laminar morphology, which facilitate the HA deposition. After the thermal treatment, the previously amorphous structured HA coating, shows a porous homogeneous morphology with particle size of about 2-2.5 μm, with crystallinity and composition similar to that of the biological HA.

Behavioral evaluation during dental care in children ages 0 to 3 years

Purpose: Many studies concluded that the behavior of babies complicated dental care because of child immaturity or the difficulty of establishing acceptable communication and comprehension. Methods: The records of 696 babies were randomly selected from the baby clinic of Araçatuba in Brazil. Patient age ranged from 0 to 36 months. They were divided into 6 groups according to age: Group I-0 to 6 months; Group II-7 to 12 months; Group III-13 to 18 months; Group IV-19 to 24 months; Group V-25 to 30 months; Group VI-31 to 36 months. The behavior of the child was evaluated upon entrance in the dental office and during the first 4 clinical appointments with a clinical exam and oral physiotherapy. The baby was classified as collaborator (C) or noncollaborator (NC). Statistical analysis was performed using Pearson's chi-square method (P< .05). Results: The percentage of NC for Groups II, III, IV, and V (66%), was significantly higher than for groups I (30%) and VI (50%). Conclusions: Babies from 0 to 6 months showed a collaborative behavior; babies from 7 to 30 months showed noncollaborative behavior; and babies from 31 to 36 months showed no statistically significant difference between the percentage of C and NC.

Influence of dental care for infants on caries prevalence: A comparative study

Purpose: The influence of early dental care on the prevalence of dental caries was determined in children ages 35 to 40 months divided into 2 groups of 160 children each, with 1 group participating in a dental care program from the first year of life to the time of the study, while the other group did not receive any dental care. Methods: The clinical conditions considered for the evaluation were: sound teeth, enamel caries without cavitation, enamel caries with cavitation, and dentinal caries. The proportion and chi-square tests were used for statistical analysis with the level of significance set at 5%. Results: A significant difference regarding the presence of dental caries, especially in the number of children presenting enamel caries with cavitation (P<.0001), was observed between the 2 groups. The number of children with enamel caries without cavitation and dentinal caries was similar for the 2 groups. Conclusions: Considering the aspect of dental caries prevention, the authors concluded that children in the age range of 3 to 4 years who received early dental care showed better oral conditions.

Microbiologic and radiographic analysis of ligature-induced peri-implantitis with different dental implant surfaces

Purpose: The goal of this study was to evaluate microbiota and radiographic peri-implant bone loss associated with ligature-induced peri-implantitis. Materials and Methods: Thirty-six dental implants with 4 different surfaces (9 commercially pure titanium, 9 titanium plasma-sprayed, 9 hydroxyapatite, and 9 acid-etched) were placed in the edentulous mandibles of 6 dogs. After 3 months with optimal plaque control, abutment connection was performed. On days 0, 20, 40, and 60 after placement of cotton ligatures, both microbiologic samples and periapical radiographs were obtained. The presence of Actinobacillus actinomycetemcomitans, Porphyromonas gingivalis, Prevotella intermedia/nigrescens, Campylobacter spp, Capnocytophaga spp, Fusobacterium spp, beta-hemolytic Streptococcus, and Candida spp were evaluated culturally. Results: P intermedia/nigrescens was detected in 13.89% of implants at baseline and 100% of implants at other periods. P gingivalis was not detected at baseline, but after 20 and 40 days it was detected in 33.34% of implants and at 60 days it was detected in 29.03% of dental implants. Fusobacterium spp was detected in all periods. Streptococci were detected in 16.67% of implants at baseline and in 83.34%, 72.22%, and 77.42% of implants at 20, 40, and 60 days, respectively. Campylobacter spp and Candida spp were detected in low proportions. The total viable count analysis showed no significant differences among surfaces (P = .831), although a significant difference was observed after ligature placement (P < .0014). However, there was no significant qualitative difference, in spite of the difference among the periods. The peri-implant bone loss was not significantly different between all the dental implant surfaces (P = .908). Discussion and Conclusions: These data suggest that with ligature-induced peri-implantitis, both time and periodontal pathogens affect all surfaces equally after 60 days.