Annealing effects on electron-beam evaporated Al2O3 films

The effects of post-deposited annealing on structure and optical properties of electron-beam evaporated Al2O3 single layers were investigated. The films were annealed in air for 1.5 h at different temperatures from 250 to 400 degrees C. The optical constants and cut-off wavelength were deduced. Microstructure of the samples was characterized by X-ray diffraction (XRD). Profile and surface roughness measurement instrument was used to determine the rms surface roughness. It was found that the cut-off wavelength shifted to short wavelength as the annealing temperature increased and the total optical loss decreased. The film structure remained amorphous even after annealing at 400 degrees C temperature and the samples annealed at higher temperature had the higher rms surface roughness. The decreasing total optical loss with annealing temperature was attributed to the reduction of absorption owing to oxidation of the film by annealing. Guidance to reduce the optical loss of excimer laser mirrors was given. (c) 2004 Elsevier B.V. All rights reserved.

高反射率193nm Al2O3／MgF2反射膜的实验研究

用电子束热蒸发方法在熔融石英基底上沉积了Al2O3和MgF2两种材料的单层膜，研究了两种材料的光学特性，采用光度法计算并给出了薄膜材料在180～230nm的折射率n／和消光系数k的色散曲线。以两种材料作为高低折射率材料组合，采用1／4波长规整膜系设计并镀制了193nm的高反射膜，反射膜在退火后的反射率在193nm达到96％以上。结果表明在一定工艺条件下Al2O3和MgF2两种材料能够在193nm获得较好的光学性能，适用于高反射膜的制备。

退火对电子束热蒸发Al2O3薄膜性能影响的实验研究

用电子束热蒸发方法镀制了Al2O3材料的单层膜，对它们在空气中进行了250～400℃的高温退火。对样品的透射率光谱曲线进行了测量，计算了样品的消光系数、折射率和截止波长。通过X射线衍射仪(XRD)测量分析了薄膜的微观结构，采用表面轮廓仪测量了样品的表面均方根粗糙度。结果发现随着退火温度的提高光学损耗下降，薄膜结构在退火温度为400℃时仍然为无定形态，样品的表面粗糙度随退火温度的升高而增加。引起光学损耗下降起主导作用的是吸收而不是散射，吸收损耗的下降主要是由于退火使材料吸收空气中的氧而进一步氧化，从而使薄膜

Optimization of thin-film design for multi-layer dielectric grating

Thin-film design used to fabricate multi-layer dielectric (MLD) gratings should provide high transmittance during holography exposure, high reflectance at use wavelength and sufficient manufacturing latitude of the grating design making the MLD grating achieve both high diffraction efficiency and low electric field enhancement. Based on a (HLL)H-9 design comprising of quarter-waves of high-index material and half-waves of low-index material, we obtain an optimum MLD coating meeting these requirements by inserting a matching layer being half a quarter-wave of Al2O3 between the initial design and an optimized HfO2 top layer. The optimized MLD coatings exhibits a low reflectance of 0.017% under photoresist at the exposure angle of 17.8 degrees for 413 nm light and a high reflectance of 99.61% under air at the use angle of 51.2 degrees for 1053 nm light. Numerical calculation of intensity distribution in the photoresist coated on the MLD film during exposure shows that standing-wave patterns are greatly minimized and thus simulation profile of photoresist gratings after development demonstrates smoother shapes with lower roughness. Furthermore, a MLD gratings with grooves etched into the top layer of this MLD coating provides a high diffraction efficiency of 99.5% and a low electric field enhancement ratio of 1.53. This thin-film design shows perfect performances and can be easily fabricated by e-beam evaporation. (c) 2006 Elsevier B.V. All rights reserved.

Al2O3和Cr过渡层对Ag膜光学性质及其附着力的影响

研究了在玻璃基底上镀制Al2O3和Cr过渡层对Ag膜反射率及附着力的影响.分光光度计测试了Ag膜的反射率,结果表明,与Cr过渡层相比,Al2O3过渡层对Ag膜反射率的降低相对较小;而且,随着Al2O3厚度的增加,Ag膜的反射率先增大后减小.XRD与AES测试表明,引入Al2O3或Cr可明显细化Ag晶粒,减弱Ag膜（111）织构;Al2O3作过渡层时,Al原子向Ag层中扩散显著;而Cr作过渡层时,只有少量Cr原子扩散进入Ag层.因此,Al2O3作过渡层能显著增强薄膜与玻璃基体之间的附着力.

Working pressure dependence of properties of Al2O3 thin films prepared by electron beam evaporation

The effects of working pressure on properties of Al2O3 thin films are investigated. Transmittance of the Al2O3 thin film is measured by a Lambda 900 spectrometer. Laser-induced damage threshold (LIDT) is measured by a Nd:YAG laser at 355nm with a pulse width of 7ns. Microdefects were observed under a Nomarski microscope. The samples are characterized by optical properties and defect, as well as LIDT under the 355 nm Nd: YAG laser radiation. It is found that the working pressure has fundamental effect on the LIDT. It is the absorption rather than the microdefect that plays an important role on the LID T of Al2O3 thin film.

Design of high-efficiency diffraction gratings based on rigorous coupled-wave analysis for 800nm wavelength

We report on the design of a high diffraction efficiency multi-layer dielectric grating with wide incident angle and broad bandwidth for 800 nm. The optimized grating can achieve > 95% diffraction efficiency in the first order at an incident angle of 5 degrees from Littrow and a wavelength from 770nm to 830 nm, with peak diffraction efficiency of > 99.5% at 800 nm. The electric field distribution of the optimized multi-layer dielectric grating within the gratings ridge is 1.3 times enhancement of the incidence light, which presents potential high laser resistance ability. Because of its high-efficiency, wide incident, broad bandwidth and potential high resistance ability, the multi-layer dielectric grating should have practical application in Ti:sapphire laser systems.