Pyrene appended bile acid conjugates: Synthesis and a structure-gelation property study

A wide variety of novel compounds obtained by combining two types of known organogelators, viz., bile acid alkyl amides and pyrene alkanoic acids, were synthesized and screened for their gelation ability. The 3 alpha esters of 1-pyrene butyric acid (PBA) of alkylamides of deoxycholic acid (DCA) turned out to be effective in the gel formation with many organic solvents although the gelation has to be triggered by the addition of a charge transfer (CT) agent 2,4,7-trinitrofluorenone (TNF). The special feature of these molecules is that the organogelation is achieved only after derivatizing the acid moiety of the 1-pyrenealkanoic acids. Additionally, the gelation properties can be fine-tuned by inserting different functional groups at the bile acid side chain. The gels obtained are deep red in colour and optically transparent up to 2% w/v. The SEM studies of the obtained xerogels revealed bundled rod-like morphology without specialized branching.

CO adsorption on ionic Pt, Pd and Cu sites in Ce(1-x)M(x)O(2-delta) (M = Pt(2+), Pd(2+), Cu(2+))

Noble metal ion substituted CeO(2) in the form of Ce(0.98)M(0.02)O(2-delta) solid solution (where M = Pt, Pd, Cu) are the new generation catalysts with applications in three-way exhaust catalysis. While adsorption of CO on noble metals ions is well-known, adsorption of CO on noble metal ions has not been studied because creating exclusive ionic sites has been difficult. Using first-principles density functional theory (DFT) we have shown that CO gets adsorbed on the noble metal Pt(2+), Pd(2+), Cu(2+) ionic sites in the respective compounds, and the net energy of the overall system decreases. Adsorption of CO on metal ions is also confirmed by Fourier transform infrared spectroscopy (FTIR).

Photocatalytic properties of KBiO(3) and LiBiO(3) with tunnel structures

In the present study, KBiO(3) is synthesized by a standard oxidation technique while LiBiO(3) is prepared by hydrothermal method. The synthesized catalysts are characterized by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), BET surface area analysis and Diffuse Reflectance Spectroscopy (DRS). The XRD patterns suggest that KBiO(3) crystallizes in the cubic structure while LiBiO(3) crystallizes in orthorhombic structure and both of these adopt the tunnel structure. The SEM images reveal micron size polyhedral shaped KBiO(3) particles and rod-like or prismatic shape particles for LiBiO(3). The band gap is calculated from the diffuse reflectance spectrum and is found to be 2.1 eV and 1.8 eV for KBiO(3) and LiBiO(3), respectively. The band gap and the crystal structure data suggest that these materials can be used as photocatalysts. The photocatalytic activity of KBiO(3) and LiBiO(3) are evaluated for the degradation of anionic and cationic dyes, respectively, under UV and solar radiations.

Stress-Strain Prediction of Jointed Rocks using Artificial Neural Networks

The applicability of Artificial Neural Networks for predicting the stress-strain response of jointed rocks at varied confining pressures, strength properties and joint properties (frequency, orientation and strength of joints) has been studied in the present paper. The database is formed from the triaxial compression tests on different jointed rocks with different confining pressures and different joint properties reported by various researchers. This input data covers a wide range of rock strengths, varying from very soft to very hard. The network was trained using a 3 layered network with feed forward back propagation algorithm. About 85% of the data was used for training and remaining15% for testing the predicting capabilities of the network. Results from the analyses were very encouraging and demonstrated that the neural network approach is efficient in capturing the complex stress-strain behaviour of jointed rocks. A single neural network is demonstrated to be capable of predicting the stress-strain response of different rocks, whose intact strength vary from 11.32 MPa to 123 MPa and spacing of joints vary from 10 cm to 100 cm for confining pressures ranging from 0 to 13.8 MPa.

Ru(4+) ion in CeO(2) (Ce(0.95)Ru(0.05)O(2-delta)): A non-deactivating, non-platinum catalyst for water gas shift reaction

Hydrogen is a clean energy carrier and highest energy density fuel. Water gas shift (WGS) reaction is an important reaction to generate hydrogen from steam reforming of CO. A new WGS catalyst, Ce(1-x)Ru(x)O(2-delta) (0 <= x <= 0.1) was prepared by hydrothermal method using melamine as a complexing agent. The Catalyst does not require any pre-treatment. Among the several compositions prepared and tested, Ce(0.95)Ru(0.05)O(2-delta) (5% Ru(4+) ion substituted in CeO(2)) showed very high WGS activity in terms of high conversion rate (20.5 mu mol.g(-1).s(-1) at 275 degrees C) and low activation energy (12.1 kcal/mol). Over 99% conversion of CO to CO(2) by H(2)O is observed with 100% H(2) selectivity at >= 275 degrees C. In presence of externally fed CO(2) and H(2) also, complete conversion of CO to CO(2) was observed with 100% H(2) selectivity in the temperature range of 305-385 degrees C. Catalyst does not deactivate in long duration on/off WGS reaction cycle due to absence of surface carbon and carbonate formation and sintering of Ru. Due to highly acidic nature of Ru(4+) ion, surface carbonate formation is also inhibited. Sintering of noble metal (Ru) is avoided in this catalyst because Ru remains in Ru(4+) ionic state in the Ce(1-x)Ru(x)O(2-delta) catalyst.

Imidazole Functionalized Polyaniline: Synthesis, Characterization, and Cu (II) Coordination Studies

Polyaniline functionalized with imidazole as strategically designed receptor group in its backbone was synthesized for copper binding. The synthesized polymer has been characterized using FTIR, NMR, and UV-Vis spectroscopic techniques. The addition of copper (II) to the polymer distinctly changes the properties such as crystallinity, molecular weight, aggregation, and electronic properties. XRD, DLS, SEM, and four-point probe techniques have been used for study of these changes. It is observed that the secondary ion generated as a result of copper coordination results in the doping of the polyaniline backbone, which enhances the conductivity by one order of magnitude. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci 123: 526-534, 2012

Thermodynamic properties of Fe3O4 FeV2O4 and Fe3O4 FeCr2O4 spinel solid solutions

Solid solutions of Fe304-FeV204 and Fe304-FeCr204 were prepared and equilibrated with Pt under controlled streams of CO/CO, gas mixtures at 1673 K. The concentration of Fe in Pt was used to determine the activity of Fe304 in the solid solutions. The activity of the second component was calculated by Gibbshhem integration. From these data, the Gibbs energy of mixing was derived for both systems. The experimental results and theoretical values which are determined from calculated cation distribution compare favorably in the case of vanadite solid solutions but not in the case of chromite solid solutions. The difference is attributed to a heat term arising from lattice distortion due to cation size difference. The positive heat of mixing will give rise to a miscibility gap in the system Fe304-FeCr204 at lower temperatures.

Low oxygen potential boundary for the stability of YBA2Cu3O7−δ

On lowering the oxygen potential, the tetragonal phase of YBa2Cu3O7−δ was found to decompose into a mixture of Y2BaCuO5, BaCuO2 and BaCu2O2 in the temperature range 773–1173 K. The 123 compound was contained in a closed crucible of yttria-stabilized zirconia in the temperature range 773–1073 K. Oxygen was removed in small increments by coulometric titration through the solid electrolyte crucible at constant temperature. The oxygen potential was calculated from the open circuit e.m.f. of the solid state cell after successive titrations. Pure oxygen at a pressure of 1.01 × 105 Pa was used as the reference electrode. The decomposition of the 123 compound manifested as a plateau in oxygen potential. The decomposition products were identified by X-ray diffraction. At temperatures above 1073 K there was some evidence of reaction between the 123 compound, solid electrolyte crucible and platinum. For measurements above 1073 K, the 123 compound was contained in a magnesia crucible placed in a closed outer silica tube. The oxygen potential in the gas phase above the 123 compound was controlled and measured by a solid state cell based on yttria-stabilized zirconia which served both as a pump and sensor. The lower oxygen potential limit for the stability of the 123 compound is given by View the MathML source The oxygen non-stoichiometric parameter δ for the 123 compound has a value of 0.98 (View the MathML source) at dissociation.

Gibbs’ energy of formation of YBa2Cu3O7-x (tetragonal)

The high temperature ceramic oxide superconductor YBa2Cu3O7-x (1–2–3 compound) is generally synthesized in an oxygen-rich environment. Hence any method for determining its thermodynamic stability should operate at a high oxygen partial pressure. A solid-state cell incorporating CaF2 as the electrolyte and functioning under pure oxygen at a pressure of 1·01 × 105 Pa has been employed for the determination of the Gibbs’ energy of formation of the 1–2–3 compound. The configuration of the galvanic cell can be represented by: Pt, O2, YBa2Cu3O7−x , Y2BaCuO5, CuO, BaF2/CaF2/BaF2, BaZrO3, ZrO2, O2, Pt. Using the values of the standard Gibbs’ energy of formation of the compounds BaZrO3 and Y2BaCuO5 from the literature, the Gibbs’ energy of formation of the 1–2–3 compound from the constituent binary oxides has been computed at different temperatures. The value ofx at each temperature is determined by the oxygen partial pressure. At 1023 K for O content of 6·5 the Gibbs’ energy of formation of the 1–2–3 compound is −261·7 kJ mol−1.

Variation of the partial thermodynamic properties of oxygen with composition in YBa2Cu3O7−δ

The variation of equilibrium oxygen potential with oxygen concentration inYBa 2Cu3O7-δhas been measured in the temperature range of 773 to 1223 K. For temperatures up to 1073 K, the oxygen content of theYBa 2Cu3O7-δsample, held in a stabilized-zirconia crucible, was altered by coulometric titration. The compound was in contact with the electrolyte, permitting direct exchange of oxygen ions. For measurements above 1073 K, the oxide was contained in a magnesia crucible placed inside a closed silica tube. The oxygen potential in the gas phase above the 123 compound was controlled and measured by a solid-state cell based on yttria-stabilized zirconia, which served both as a pump and sensor. Pure oxygen at a pressure of 1.01 × 105 Pa was used as the reference electrode. The oxygen pressure over the sample was varied from 10-1 to 105 Pa. The oxygen concentrations of the sample equilibrated with pure oxygen at 1.01 × 105 Pa at different temperatures were determined after quenching in liquid nitrogen by hydrogen reduction at 1223 K. The plot of chemical potential of oxygen as a function of oxygen non-stoichiometry shows an inflexion at δ ∼ 0.375 at 873 K. Data at 773 K indicate tendency for phase separation at lower temperatures. The partial enthalpy and entropy of oxygen derived from the temperature dependence of electromotive force (emf ) exhibit variation with composition. The partial enthalpy for °= 0.3, 0.4, and 0.5 also appears to be temperature dependent. The results are discussed in comparison with the data reported in the literature. An expression for the integral free energy of formation of YBa2Cu3O6.5 is evaluated based on measurements reported in the literature. By integration of the partial Gibbs’ energy of oxygen obtained in this study, the variation of integral property with oxygen concentration is obtained at 873 K.

Growth and ferroelectric properties of Bi2VO5.5 thin films with metallic LaNiO3 electrodes

Novel ferroelectric bismuth vanadate, Bi2VO5.5 (BVO), thin films have been grown between lattice matched metallic LaNiO3 (LNO) layers deposited on SrTiO3 (STO) by the pulsed laser deposition technique. LNO/BVO/LNO/STO and Au/BVO/LNO/STO trilayer structures exhibited c‐oriented (001) growth of BVO. LNO has been found to be a good metallic electrode with sheet resistance ∼20 Ω in addition to aiding c‐axis oriented BVO growth. The dielectric constant, ϵr of LNO/BVO/LNO/STO, at 300 K was about 12. However, when an Au electrode was used on top of BVO/LNO/STO film, it showed a significant improvement in the dielectric constant (ϵr=123). The ferroelectric properties of BVO thin films have been confirmed by hysteresis behavior with a remnant polarization, Pr=4.6×10−8 C/cm2 and coercive field, Ec=23 kV/cm at 300 K.

Sparking potentials and ionisation coefficients in SF6

Steady-state ionisation currents under uniform field conditions have been measured in SF6 over the range 110 ÿE/pÿ1000V cmÿ1torrÿ1 with gas pressures varying from 1 to 10 torr, at 20ðC. Sparking potentials Vs were also measured for a range 1ÿpdÿ20 torr-cm. Townsend's primary ionisation (ÿ/p) and electron-attachment (ÿ/p) coefficients were found to depend on E/p only. The values of secondary-ionisation coefficient (ÿ) were also determined over the range 140ÿE/pÿ600 V cmÿ1 torrÿ1. Measurements of Vs of SF6 have shown that the deviations from Paschen's law rise up to ñ3.5% at values of pd near the Paschen minimum.

Prebreakdown current measurements in vacuum gaps stressed by alternating voltages

A method has been suggested for the measurement of prebreakdown currents under a.c. conditions. Measurements were made using hemispherical stainless steel electrodes and currents from 10~3 A down to 10~7 A have been measured.