Development of a new epoxy resin for superconducting magnet impregnation

A novel epoxy resin system based on a low viscosity Bisphenol-A (DGEBA)/Bisphenol-F (DGEBF) blend has been investigated for use in tight-wound superconducting magnet impregnation. The principle is to decrease the Bisphenol-A resin system viscosity by adding the low viscosity Bisphenol-F resin. The rheological and mechanical properties of the blend system are compared to the pure Bisphenol-A resin and also to the Bisphenol-F resin both cured with acid anhydride. For the vacuum/pressure impregnation, both the pure Bisphenol-F resin system and DGEBA/DGEBF blend system can be applied without S-glass fabric between coil layers due to its higher rigidity at low temperature and good resistance to thermal shock. This resin system have been tested for impregnation of copper and NbTi wire wound coils whilst Bisphenol-A resin system have been used for testing Nb3Sn coil impregnation where S-glass braid is present as wire insulation.

Repair bond strength of a resin composite to alumina-reinforced feldspathic ceramic

This study compared the microtensile bond strength of a repair resin to an alumina-reinforced feldspathic ceramic (Vitadur-alpha, Vita) after 3 surface conditioning methods: Group 1, etching with 9.6% hydrofluoric acid for 1 minute plus rinsing and drying, followed by application of silane for 5 minutes; group 2, airborne particle abrasion with 110-mm aluminum oxide using a chairside air-abrasion device followed by silane application for 5 minutes; group 3, chairside tribochemical silica coating with 30-mu m SiOx followed by silane application for 5 minutes (N = 30). Group 1 presented the highest mean bond strength (19.7 +/- 3.8 MPa), which was significantly higher than those of groups 2 (10 +/- 2.6 MPa) and 3 (10.4 +/- 4 MPa) (P <.01). Scanning electron microscope analysis of the failure modes demonstrated predominantly mixed types of failures, with adhesive and/or cohesive failures in all experimental groups.

Influence of ceramic surface conditioning and resin cements on microtensile bond strength to a glass ceramic

Statement of problem. It is not clear how different glass ceramic surface pretreatments influence the bonding capacity of various luting agents to these surfaces.Purpose. The purpose of this study was to evaluate the microtensile bond strength (mu TBS) of 3 resin cements to a lithia disilicate-based ceramic submitted to 2 surface conditioning treatments.Material and methods. Eighteen 5 X 6 X 8-mm ceramic (IPS Empress 2) blocks were fabricated according to manufacturer's instructions and duplicated in composite resin (Tetric Ceram). Ceramic blocks were polished and divided into 2 groups (n=9/treatment): no conditioning (no-conditioning/control), or 5% hydrofluoric acid etching for 20 seconds and silanization for 1 minute (HF + SIL). Ceramic blocks were cemented to the composite resin blocks with I self-adhesive universal resin cement (RelyX Unicem) or 1 of 2 resin-based luting agents (Multilink or Panavia F), according to the manufacturer's instructions. The composite resin-ceramic blocks were stored in humidity at 37 degrees C for 7 days and serially sectioned to produce 25 beam specimens per group with a 1.0-mm(2) cross-sectional area. Specimens were thermal cycled (5000 cycles, 5 degrees C-55 degrees C) and tested in tension at 1 mm/min. Microtensile bond strength data (MPa) were analyzed by 2-way analysis of variance and Tukey multiple comparisons tests (alpha=.05). Fractured specimens were examined with a stereomicroscope (X40) and classified as adhesive, mixed, or cohesive.Results. The surface conditioning factor was significant (HF+SIL > no-conditioning) (P<.0001). Considering the unconditioned groups, the mu TBS of RelyX Unicem was significantly higher (9.6 +/- 1.9) than that of Multilink (6.2 +/- 1.2) and Panavia F (7.4 +/- 1.9). Previous etching and silanization yielded statistically higher mu TBS values for RelyX Unicem (18.8 +/- 3.5) and Multilink (17.4 +/- 3.0) when compared to Panavia F (15.7 +/- 3.8). Spontaneous debonding after thermal cycling was detected when luting agents were applied to untreated ceramic surfaces.Conclusion. Etching and silanization treatments appear to be crucial for resin bonding to a lithia disilicate-based ceramic, regardless of the resin cement used.

Topographical, diametral, and quantitative analysis of dentin tubules in the root canals of human and bovine teeth

The aim of this study was to evaluate the number and the diameter of dentin tubules in root canals, in the cervical, middle, and apical thirds, of human and bovine teeth. Twenty-four single-rooted, human premolars were divided into four groups (n = 6): GH1, 10 to 15 years; GH2, 16 to 30 years; GH3, 31 to 45 years; and GH4, 46 to 80 years; and 24 bovine incisors were divided into four groups (n = 6): GB1, central; GB2, lateral first; GB3, lateral second; and GB4, lateral third. The crowns were removed from the specimens, which were then debrided, sectioned longitudinally in the vestibular-lingual direction, and submitted to ultrasonic cleaning. Scanning electron microscopic evaluations were made with 1,000x and 5,000x magnification. According to the root thirds, statistically significant differences were found both for the number and the diameter of dentin tubules, with the cervical third presenting the highest mean values for both specimen types. As regards the number of dentin tubules, it was observed that the bovine specimens presented a significantly higher mean value than the human specimens; this difference was not observed when the diameters of the two types were compared.

EPR investigation of the influence of side chain protecting groups on peptide-resin solvation of the Asx and Glx model containing peptides

In spite of all progressive efforts aiming to optimize SPPS, serious problems mainly affecting the assembly of aggregating sequences have persisted. Following the study intended to unravel the complex solvation phenomenon of peptide-resin beads, the XING and XAAAA model aggregating segments were labeled with a paramagnetic probe and studied via EPR spectroscopy. Low and high substituted resins were also comparatively used, with the X residue being Asx or Glx containing the main protecting groups used in the SPPS. Notably, the cyclo-hexyl group used for Asp and Glu residues in Boc-chemistry induced greater chain immobilization than its tert-butyl partner-protecting group of the Fmoc strategy. Otherwise, the most impressive peptide chain immobilization occurred when the large trytil group was used for Asn and Gln protection in Fmoc-chemistry. These surprising results thus seem to stress the possibility of the relevant influence of the amino-acid side chain protecting groups in the overall peptide synthesis yield. (C) 2007 Elsevier Ltd. All rights reserved.