Colloidal photonic crystals with a graded lattice-constant distribution

In this work, a gradient polystyrene colloidal photonic crystal was fabricated by annealing in a graded temperature field. The lattice constant of the gradient crystal gradually varied along the temperature-gradient direction. The positional bandgap wavelength as well as the attenuation of the bandgap wavelength could be tuned dependent on the position of the gradient colloidal crystal along the gradient direction because of the lattice-constant variation.

Morphology and structure of poly(di-n-butylsilane) single crystals prepared by controlling kinetic process of solvent evaporation

The silicon backbone conformation in poly(di-n-butylsilane) (PDBS) has been shown to be a 7/3 helix at ambient conditions, which is in marked contrast to the near-planar conformation of its homologous polymers with side chain lengths of one to three or six to eight carbon atoms. In this work, both the 7/3 helical and near-planar chain conformations are achieved by controlling the solvent evaporation rate around room temperature. The chain conformation and crystal structure obtained in this method have been correlated to the crystal morphology by wide-angle X-ray diffraction, transmission electron microscopy, electron diffraction, optical microscopy, atomic force microscopy, and UV absorption spectrum. The lath-shaped single crystals obtained at 12 degreesC correspond to an orthorhombic form with near-planar chain conformation whereas the lozenge-shaped single crystals obtained at 30 degreesC (in coexistence with the lath-shaped crystals) are orthohexagonal with a 7/3 helix.

Thickness-dependent molecular chain and lamellar crystal orientation in ultrathin poly(di-n-hexylsilane) films

The molecular chain and lamellar crystal orientation in ultrathin films (thickness < 100 nm) of poly(di-n-hexylsilane) (PDHS) on silicon wafer substrates have been investigated by using transmission electronic microscopy, wide-angle X-ray diffraction, atomic force microscopy, and UV absorption spectroscopy. PDHS showed a film thickness-dependent molecular chain and lamellar crystal orientation. Lamellar crystals grew preferentially in flat-on orientation in the monolayer ultrathin films of PDHS, i.e., the silicon backbones were oriented along the surface-normal direction. By contrast, the orientation of lamellar crystals was preferentially edge-on in ultrathin films thicker than ca. 13 nm, i.e., the silicon backbones were oriented parallel to the substrate surface. We interpret the different orientations of molecular chain and lamellar crystal as due to the reduction of the entropy of the polymer chain near the substrate surface and the particularity of the crystallographic (001) plane of flat-on lamellae, respectively. A remarkable influence of the orientations of the silicon backbone on the UV absorption of these PDHS ultrathin films was observed due to the one-dimensional nature of sigma-electrons delocalized along the silicon backbone.

Conducting probe atomic force microscopy investigation of anisotropic charge transport in solution cast PBD single crystals induced by an external field

2-(4-Biphenylyl)-5-(4-tert-butylphenyl)-1,3,4-oxdiazole (PBD) is a good electron-transporting material and can form single crystals from solution. In this work, solution cast PBD single crystals with different crystallographic axes (b, c) perpendicular to the Au/S substrates in large area are achieved by controlling the rate of solvent evaporation in the presence and absence of external electrostatic field, respectively. The orientation of these single crystals on Au/S substrate was characterized by transmission electron microscopy (TEM) and atomic force microscopy (AFM). Conducting probe atomic force microscopy (CP-AFM) was used to measure the charge transport characteristics of PBD single crystals grown on Au/S substrates. Transport was measured perpendicular to the substrate between the CP-AFM tip and the Au/S substrate. The electron mobility of 3 x 10(-3) cm(2)/(V s) for PBD single crystal along crystallographic b-axis is determined. And the electron mobility of PBD single crystal along the c-axis is about 2 orders of magnitude higher than that along the b-axis due to the anisotropic charge transport at the low voltage region.

Reversibly strain-tunable elastomeric photonic crystals

Reversibly strain-tunable polymeric photonic crystals made of thermoplastic polyester elastomer (TPEE) were fabricated by using the self-assembled silica opals as templates. The stop band of the polymeric photonic crystal locates at the near infrared (IR) regime in its transmission spectrum, and exhibits a blue shift with the increase of the incident angle. Because of the elasticity of the TPEE, the stop band of the TPEE photonic crystal can also be reversibly tuned at ambient temperature through to and fro uniaxially or biaxially stretching and recovering by changing the lattice spacing and the symmetry of the crystal along (1 1 1) plane.

Vaterite-type YBO3 : Eu3+ crystals: hydrothermal synthesis, morphology and photoluminescence properties

Vaterite-type YBO3:Eu3+ crystals with interesting flower and hedgehog fungus-like structures composed of nanosheets were obtained by controlled crystallization of Y2O3 and Eu2O3 in H3BO3 solutions under acidic hydrothermal (HT) conditions. Nanosheets of uniform thicknesses were formed by preferential crystal growth along the (100) crystallographic plane and specific three-dimensional structures were further developed through a homocentric growth mechanism. Optical emission measurements showed that the HT-grown nanosheet crystals exhibited a higher ratio of the emitted red-to-orange light ratio than crystals grown from solid-state reactions. The photoluminescence intensity and emission lifetimes were also studied as a function of the Eu3+ dopant concentration and the HT synthesis temperature. The effect of some additives: a chelating ligand, a surfactant and a polymer, on the YBO3:Eu3+ crystals morphology was also investigated.

Grafting polymerization of L-lactide on the surface of hydroxyapatite nano-crystals

A novel method of grafting ring-opening polymerization of L-lactide (LLA) onto the surface of hydroxyapatite nano-particles (n-HAP) was developed. PLLA was directly connected onto the HAP surface through a chemical linkage. The PLLA-g-HAP particles could be stably dispersed in organic solvent such as chloroform for several weeks. The n-HAP particles still retained the original dimension and shape after the grafting of PLLA. Compared with the P-31 MAS-NMR spectrum of pure HAP powders, there appeared a downfield displacement of 1.2 ppm in the spectrum of PLLA-g-HAP. Fourier transformation infrared (FT-IR) spectra further confirmed the existence of PLLA on the surface of PLLA-g-HAP. The amount of grafted polymer determined by thermal gravimetric analysis (TGA) was about 6% in weight. The tensile strength and elongation at break of the PLLA/PLLA-g-HAP composite containing 8 wt% of PLLA-g-HAP were 55 MPa and about 10-13%, respectively, while those of the PLLA/n-HAP composites were 40 MPa and 3-5%, respectively.

Barycenter of energy of lanthanide 4f(N)-(1)5d configuration in inorganic crystals

A semiempirical method for the evaluation of the barycenter of energy of 4f(N-1)5d configurations is presented. The environmental factors affecting the barycenter are given to be the bond volume polarization, fractional covalence of the chemical bond between the central ion and the nearest anion, and presented charge of the nearest anion in the chemical bonds. The barycenter energies of 4f(N-1)5d configurations of Eu2+ and Ce3+ are calculated in various crystals, and the results are in good agreement with the experimental values. A relationship is found between the barycenter of energy of the 4f(N-1)5d configuration on Eu2+ method offers the advantage of applicability to a broad class of luminescence materials and initiates a link between macroscopic properties and microscopic structure.

Solvent-induced crystallization of spherical micelles formed by copolymer blends

We have followed the morphological evolution and crystallization process of spherical micelles formed by the mixture of polystyrene-b-poly(acrylic acid) (PS-b-PAA) and polystyrene-b-poly(2-vinylpyridine)b-poly(ethylene oxide) (PS-b-P2VP-b-PEO) (the core of the spherical micelles was made of P2VP and PAA blocks through hydrogen bonding in neutral solvent N,N-dimethylformamide, DMF) via DMF vapor treatment. Different phenomena, such as rupture of the film, formation of cylinder aggregates and regular square lamellae, were observed when the micelle film was treated in DMF for different times. At the early stage of annealing in DMF vapor, the micelle film became unstable and ruptured. Cylinder aggregates, within which the PEO blocks achieved the association and primary chain folding, formed as the mesophases before the nucleation of the PEO single crystals at this stage. Further treatment in DMF vapor resulted in the nucleation of the PEO blocks at the corners of quasi-square lamellae. Then a quite regular "sandwich" lamellar structure, constructed by a PEO single-crystal layer covered by two tethered layers of other amorphous blocks on the top and bottom crystal basal surfaces, formed when the film of micelles was annealed in DMF vapor for sufficient times.

Optical intensity gradient by colloidal photonic crystals with a graded thickness distribution

Gradient colloidal crystals with a thickness gradient were prepared by the vertical deposition technique with vertically graded concentration suspensions. The thickness of the gradient colloidal crystal gradually changes at different positions along the specific gradient direction of the crystal. The thickness gradient was determined by the concentration gradient, depending on the initial colloidal concentration and the settling time. The optical transmission intensity at the dip wavelength can be tuned by changing the thickness of the colloidal crystals. The gradient colloidal crystals lead to a gradient of optical intensity at the dip in transmission light. The gradient of optical intensity at the dip increases as the thickness gradient of the colloidal crystal increases.

Large-scale synthesis of Berlin green Fe[Fe(CN)(6)] microcubic crystals

Berlin green FeFe(CN)(6) microcubic crystals have been successfully prepared by a simple hydrothermal process between K-3[Fe(CN)(6)] with Na2S2O3 aqueous solution, free of any surfactant or template. The experimental results clearly show that the molar ratio of K-3[Fe(CN)(6)] to Na2S2O3 and their concentrations are the dominant processing factors in controlling the size, morphology, and composition of the resulting products.

Tunable photonic crystals by mixed liquids

Tunable photonic crystals were prepared by infiltrating mixed liquids into the voids of silica opals. The stop bands of the tunable photonic crystals were continuously tuned by changing the relative refraction index contrast n(mix)/ns(pheres) of the spheres and the mixed liquids by varying the volume fraction of the component of the mixed liquids. The peak wavelengths of the stop band have a red shift as the refractive index of the mixed liquids increases. The transmittance at the stop band decreases with the increase of the refractive index contrast n(mix)/n(spheres). The larger the diameter of silica opals is, the wider the tunable range of the stop band is. The position and transmittance of the peak wavelength obtained by the photonic band calculations agreed very well with the experimental data.

Estimation thermal expansion coefficient from lattice energy for inorganic crystals

By using the study of the lattice energy and the structural parameters of binary inorganic crystals, a new parameter reflecting the thermal expansion property has been found, the relation between the linear expansion coefficient and new parameter has been established. A semiempirical method for evaluation of linear expansion coefficient from the lattice energy is presented, and developed to the complex crystals. The estimated values of the linear expansion coefficients of both simple and complex crystals are in good agreement with the experimental values.

Lattice energy estimation for inorganic ionic crystals

An empirical method based on chemical bond theory for the estimation of the lattice energy for ionic crystals has been proposed. The lattice energy contributions have been partitioned into bond dependent terms. For an individual bond, the lattice energy contribution made by it has been separated into ionic and covalent parts. Our calculated values of lattice energies agree well with available experimental and theoretical values for diverse ionic crystals. This method, which requires detailed crystallographic information and elaborate computation, might be extended and possibly yield further insights with respect to bond properties of materials.