Nanosized precipitates in H13 tool steel low temperature plasma nitriding

A comprehensive study of pulsed nitriding in AISI H13 tool steel at low temperature (400 degrees C) is reported for several durations. X-ray diffraction results reveal that a nitrogen enriched compound (epsilon-Fe2-3N, iron nitride) builds up on the surface within the first process hour despite the low process temperature. Beneath the surface, X-ray Wavelength Dispersive Spectroscopy (WDS) in a Scanning Electron Microscope (SEM) indicates relatively higher nitrogen concentrations (up to 12 at.%) within the diffusion layer while microscopic nitrides are not formed and existing carbides are not dissolved. Moreover, in the diffusion layer, nitrogen is found to be dispersed in the matrix and forming nanosized precipitates. The small coherent precipitates are observed by High-Resolution Transmission Electron Microscopy (HR-TEM) while the presence of nitrogen is confirmed by electron energy loss spectroscopy (EELS). Hardness tests show that the material hardness increases linearly with the nitrogen concentration, reaching up to 14.5 GPa in the surface while the Young Modulus remains essentially unaffected. Indeed, the original steel microstructure is well preserved even in the nitrogen diffusion layer. Nitrogen profiles show a case depth of about similar to 43 mu m after nine hours of nitriding process. These results indicate that pulsed plasma nitriding is highly efficient even at such low temperatures and that at this process temperature it is possible to form thick and hard nitrided layers with satisfactory mechanical properties. This process can be particularly interesting to enhance the surface hardness of tool steels without exposing the workpiece to high temperatures and altering its bulk microstructure. (c) 2012 Elsevier B.V. All rights reserved.

Efeitos de altas temperaturas na germinação de sementes de capim-dourado (Syngonanthus nitens (Bong.) Ruhland, Eriocaulaceae): implicações para o manejo

Este estudo teve por objetivo investigar potenciais efeitos do fogo na germinação de sementes de capim-dourado (Syngonanthus nitens) (Bong.) Ruhland (Eriocaulaceae). Sementes coletadas na região do Jalapão, Tocantins, foram submetidas a choques de temperaturas de 60º, 100 ºC, 150 ºC e 200 ºC durante 1, 3 e 5 minutos. Foram feitas 5 réplicas, com 20 sementes para cada tratamento, e controle. As sementes foram dispostas em placas de Petri e em câmaras de germinação a 28 ºC, fotoperíodo 12h/12h, por 40 dias. As taxas de germinação das sementes foram analisadas por meio de ANOVA com teste de aleatorização. A maioria dos tratamentos resultou em altas taxas de germinação (>85%), exceto 200ºC/3' (50%) e 200ºC/5', que apresentou uma queda significativa (4,5%, P<0,05). Os resultados obtidos indicam que as sementes de S. nitens não são estimuladas nem mortas por altas temperaturas, exceto quando combinados temperatura e tempos de exposição extremos (200ºC/5'). A passagem do fogo é muito rápida durante queimadas nos campos úmidos, onde S. nitens ocorre e as temperaturas frequentemente não atingem os 150 ºC. Nessas condições, estes resultados indicam que as sementes de S. nitens potencialmente sobrevivem à passagem do fogo na maioria das queimadas. Esta informação é de utilidade imediata para o manejo desta espécie de alto valor comercial.

Conduction mechanisms in p-type Pb1-xEuxTe alloys in the insulator regime

Electrical resistivity measurements were performed on p-type Pb1-xEuxTe films with Eu content x = 4%, 5%, 6%, 8%, and 9%. The well-known metal-insulator transition that occurs around 5% at room temperature due to the introduction of Eu is observed, and we used the differential activation energy method to study the conduction mechanisms present in these samples. In the insulator regime (x>6%), we found that band conduction is the dominating conduction mechanism for high temperatures with carriers excitation between the valence band and the 4f levels originated from the Eu atoms. We also verified that mix conduction dominates the low temperatures region. Samples with x = 4% and 5% present a temperature dependent metal insulator transition and we found that this dependence can be related to the relation between the thermal energy k(B)T and the activation energy Delta epsilon(a). The physical description obtained through the activation energy analysis gives a new insight about the conduction mechanisms in insulating p-type Pb1-xEuxTe films and also shed some light over the influence of the 4f levels on the transport process in the insulator region. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4729813]

Comparison of the n-Alkanes and Polycyclic Aromatic Hydrocarbons Concentrations in the Atmosphere during the Preparation of Warm and Hot Mixtures Asphalt for Pavements

Asphalt binder is used in the production of hot mixes asphalt (HMA) for paving and, due to the high temperatures used, generates fumes thatcontainn-alkanes and polycyclic aromatic hydrocarbons (PAH). Asphalt mixes prepared at lower temperatures, such as warm mixes asphalt (WMA), may contribute to reduce the emissions of those compounds and save energy. This paper investigatesn-alkanes and PAH in the total suspended particles during the preparation of WMA, in comparison with HMA, in laboratory. The results showed that the n-alkanes of the WMA and HMA presented C-max at n-C-26 and n-C-28, respectively; also, the total content of n-alkanes was higher for the HMA than forthe WMA. Besides, benzo[b]fluoranthene and benzo[a]anthracene were the major PAH in the WMA, while the higher temperatures of the HMA were observed to volatilize all larger PAH, demonstrating higher potential of inhalation exposure.

Cellulolytic bacteria from soils in harsh environments

It is believed that the exposure of organisms to harsh climate conditions may select for differential enzymatic activities, making the surviving organisms a very promising source for bioprospecting. Soil bacteria play an important role in degradation of organic matter, which is mostly due to their ability to decompose cellulose-based materials. This work focuses on the isolation and identification of cellulolytic bacteria from soil found in two environments with stressful climate conditions (Antarctica and the Brazilian semi-arid caatinga). Cellulolytic bacteria were selected using enrichments at high and low temperatures (4 or 60A degrees C) in liquid media (trypic soy broth-TSB and minimum salt medium-MM) supplemented with cellulose (1%). Many of the isolates (119 out of 254-46.9%) displayed the ability to degrade carboxymethyl-cellulose, indicating the presence of endoglucolytic activity, while only a minority of these isolates (23 out of 254-9.1%) showed exoglucolytic activity (degradation of avicel). The obtained isolates revealed a preferential endoglucolytic activity according to the temperature of enrichments. Also, the identification of some isolates by partial sequencing of the 16S rRNA gene indicated that the Bacteroidetes (e.g., Pedobacter, Chryseobacterium and Flavobacterium) were the main phylum of cellulolytic bacteria isolated from soil in Antarctica; the Firmicutes (e.g., Bacillus) were more commonly isolated from samples from the caatinga; and Actinobacteria were found in both types of soil (e.g., Microbacterium and Arthrobacter). In conclusion, this work reports the isolation of bacteria able to degrade cellulose-based material from soil at very low or very high temperatures, a finding that should be further explored in the search for cellulolytic enzymes to be used in the bioenergy industry.

Propuesta de medidas de mejora de la eficiencia energética y del bienestar térmico de los edificios de viviendas en los campamentos de refugiados saharauis en Tinduf

Máster Universitario en Eficiencia Energética (SIANI)

Caratterizzazione di membrane metalliche e ionomeriche per applicazioni energetiche

The work of this thesis has been focused on the characterization of metallic membranes for the hydrogen purification from steam reforming process and also of perfluorosulphonic acid ionomeric (PFSI) membranes suitable as electrolytes in fuel cell applications. The experimental study of metallic membranes was divided in three sections: synthesis of palladium and silver palladium coatings on porous ceramic support via electroless deposition (ELD), solubility and diffusivity analysis of hydrogen in palladium based alloys (temperature range between 200 and 400 °C up to 12 bar of pressure) and permeation experiments of pure hydrogen and mixtures containing, besides hydrogen, also nitrogen and methane at high temperatures (up to 600 °C) and pressures (up to 10 bar). Sequential deposition of palladium and silver on to porous alumina tubes by ELD technique was carried out using two different procedures: a stirred batch and a continuous flux method. Pure palladium as well as Pd-Ag membranes were produced: the Pd-Ag membranes’ composition is calculated to be close to 77% Pd and 23% Ag by weight which was the target value that correspond to the best performance of the palladium-based alloys. One of the membranes produced showed an infinite selectivity through hydrogen and relatively high permeability value and is suitable for the potential use as a hydrogen separator. The hydrogen sorption in silver palladium alloys was carried out in a gravimetric system on films produced by ELD technique. In the temperature range inspected, up to 400°C, there is still a lack in literature. The experimental data were analyzed with rigorous equations allowing to calculate the enthalpy and entropy values of the Sieverts’ constant; the results were in very good agreement with the extrapolation made with literature data obtained a lower temperature (up to 150 °C). The information obtained in this study would be directly usable in the modeling of hydrogen permeation in Pd-based systems. Pure and mixed gas permeation tests were performed on Pd-based hydrogen selective membranes at operative conditions close to steam-reforming ones. Two membranes (one produced in this work and another produced by NGK Insulators Japan) showed a virtually infinite selectivity and good permeability. Mixture data revealed the existence of non negligible resistances to hydrogen transport in the gas phase. Even if the decrease of the driving force due to polarization concentration phenomena occurs, in principle, in all membrane-based separation systems endowed with high perm-selectivity, an extensive experimental analysis lack, at the moment, in the palladium-based membrane process in literature. Moreover a new procedure has been introduced for the proper comparison of the mass transport resistance in the gas phase and in the membrane. Another object of study was the water vapor sorption and permeation in PFSI membranes with short and long side chains was also studied; moreover the permeation of gases (i.e. He, N2 and O2) in dry and humid conditions was considered. The water vapor sorption showed strong interactions between the hydrophilic groups and the water as revealed from the hysteresis in the sorption-desorption isotherms and thermo gravimetric analysis. The data obtained were used in the modeling of water vapor permeation, that was described as diffusion-reaction of water molecules, and in the humid gases permeation experiments. In the dry gas experiments the permeability and diffusivity was found to increase with temperature and with the equivalent weight (EW) of the membrane. A linear correlation was drawn between the dry gas permeability and the opposite of the equivalent weight of PFSI membranes, based on which the permeability of pure PTFE is retrieved in the limit of high EW. In the other hand O2 ,N2 and He permeability values was found to increase significantly, and in a similar fashion, with water activity. A model that considers the PFSI membrane as a composite matrix with a hydrophilic and a hydrophobic phase was considered allowing to estimate the variation of gas permeability with relative humidity on the basis of the permeability in the dry PFSI membrane and in pure liquid water.

Structural changes and dynamic behaviour of vanadium oxide-based catalysts for gas-phase selective oxidations

Selective oxidation is one of the simplest functionalization methods and essentially all monomers used in manufacturing artificial fibers and plastics are obtained by catalytic oxidation processes. Formally, oxidation is considered as an increase in the oxidation number of the carbon atoms, then reactions such as dehydrogenation, ammoxidation, cyclization or chlorination are all oxidation reactions. In this field, most of processes for the synthesis of important chemicals used vanadium oxide-based catalysts. These catalytic systems are used either in the form of multicomponent mixed oxides and oxysalts, e.g., in the oxidation of n-butane (V/P/O) and of benzene (supported V/Mo/O) to maleic anhydride, or in the form of supported metal oxide, e.g., in the manufacture of phthalic anhydride by o-xylene oxidation, of sulphuric acid by oxidation of SO2, in the reduction of NOx with ammonia and in the ammoxidation of alkyl aromatics. In addition, supported vanadia catalysts have also been investigated for the oxidative dehydrogenation of alkanes to olefins , oxidation of pentane to maleic anhydride and the selective oxidation of methanol to formaldehyde or methyl formate [1]. During my PhD I focused my work on two gas phase selective oxidation reactions. The work was done at the Department of Industrial Chemistry and Materials (University of Bologna) in collaboration with Polynt SpA. Polynt is a leader company in the development, production and marketing of catalysts for gas-phase oxidation. In particular, I studied the catalytic system for n-butane oxidation to maleic anhydride (fluid bed technology) and for o-xylene oxidation to phthalic anhydride. Both reactions are catalyzed by systems based on vanadium, but catalysts are completely different. Part A is dedicated to the study of V/P/O catalyst for n-butane selective oxidation, while in the Part B the results of an investigation on TiO2-supported V2O5, catalyst for o-xylene oxidation are showed. In Part A, a general introduction about the importance of maleic anhydride, its uses, the industrial processes and the catalytic system are reported. The reaction is the only industrial direct oxidation of paraffins to a chemical intermediate. It is produced by n-butane oxidation either using fixed bed and fluid bed technology; in both cases the catalyst is the vanadyl pyrophosphate (VPP). Notwithstanding the good performances, the yield value didn’t exceed 60% and the system is continuously studied to improve activity and selectivity. The main open problem is the understanding of the real active phase working under reaction conditions. Several articles deal with the role of different crystalline and/or amorphous vanadium/phosphorous (VPO) compounds. In all cases, bulk VPP is assumed to constitute the core of the active phase, while two different hypotheses have been formulated concerning the catalytic surface. In one case the development of surface amorphous layers that play a direct role in the reaction is described, in the second case specific planes of crystalline VPP are assumed to contribute to the reaction pattern, and the redox process occurs reversibly between VPP and VOPO4. Both hypotheses are supported also by in-situ characterization techniques, but the experiments were performed with different catalysts and probably under slightly different working conditions. Due to complexity of the system, these differences could be the cause of the contradictions present in literature. Supposing that a key role could be played by P/V ratio, I prepared, characterized and tested two samples with different P/V ratio. Transformation occurring on catalytic surfaces under different conditions of temperature and gas-phase composition were studied by means of in-situ Raman spectroscopy, trying to investigate the changes that VPP undergoes during reaction. The goal is to understand which kind of compound constituting the catalyst surface is the most active and selective for butane oxidation reaction, and also which features the catalyst should possess to ensure the development of this surface (e.g. catalyst composition). On the basis of results from this study, it could be possible to project a new catalyst more active and selective with respect to the present ones. In fact, the second topic investigated is the possibility to reproduce the surface active layer of VPP onto a support. In general, supportation is a way to improve mechanical features of the catalysts and to overcome problems such as possible development of local hot spot temperatures, which could cause a decrease of selectivity at high conversion, and high costs of catalyst. In literature it is possible to find different works dealing with the development of supported catalysts, but in general intrinsic characteristics of VPP are worsened due to the chemical interaction between active phase and support. Moreover all these works deal with the supportation of VPP; on the contrary, my work is an attempt to build-up a V/P/O active layer on the surface of a zirconia support by thermal treatment of a precursor obtained by impregnation of a V5+ salt and of H3PO4. In-situ Raman analysis during the thermal treatment, as well as reactivity tests are used to investigate the parameters that may influence the generation of the active phase. Part B is devoted to the study of o-xylene oxidation of phthalic anhydride; industrially, the reaction is carried out in gas-phase using as catalysts a supported system formed by V2O5 on TiO2. The V/Ti/O system is quite complex; different vanadium species could be present on the titania surface, as a function of the vanadium content and of the titania surface area: (i) V species which is chemically bound to the support via oxo bridges (isolated V in octahedral or tetrahedral coordination, depending on the hydration degree), (ii) a polymeric species spread over titania, and (iii) bulk vanadium oxide, either amorphous or crystalline. The different species could have different catalytic properties therefore changing the relative amount of V species can be a way to optimize the catalytic performances of the system. For this reason, samples containing increasing amount of vanadium were prepared and tested in the oxidation of o-xylene, with the aim of find a correlations between V/Ti/O catalytic activity and the amount of the different vanadium species. The second part deals with the role of a gas-phase promoter. Catalytic surface can change under working conditions; the high temperatures and a different gas-phase composition could have an effect also on the formation of different V species. Furthermore, in the industrial practice, the vanadium oxide-based catalysts need the addition of gas-phase promoters in the feed stream, that although do not have a direct role in the reaction stoichiometry, when present leads to considerable improvement of catalytic performance. Starting point of my investigation is the possibility that steam, a component always present in oxidation reactions environment, could cause changes in the nature of catalytic surface under reaction conditions. For this reason, the dynamic phenomena occurring at the surface of a 7wt% V2O5 on TiO2 catalyst in the presence of steam is investigated by means of Raman spectroscopy. Moreover a correlation between the amount of the different vanadium species and catalytic performances have been searched. Finally, the role of dopants has been studied. The industrial V/Ti/O system contains several dopants; the nature and the relative amount of promoters may vary depending on catalyst supplier and on the technology employed for the process, either a single-bed or a multi-layer catalytic fixed-bed. Promoters have a quite remarkable effect on both activity and selectivity to phthalic anhydride. Their role is crucial, and the proper control of the relative amount of each component is fundamental for the process performance. Furthermore, it can not be excluded that the same promoter may play different role depending on reaction conditions (T, composition of gas phase..). The reaction network of phthalic anhydride formation is very complex and includes several parallel and consecutive reactions; for this reason a proper understanding of the role of each dopant cannot be separated from the analysis of the reaction scheme. One of the most important promoters at industrial level, which is always present in the catalytic formulations is Cs. It is known that Cs plays an important role on selectivity to phthalic anhydride, but the reasons of this phenomenon are not really clear. Therefore the effect of Cs on the reaction scheme has been investigated at two different temperature with the aim of evidencing in which step of the reaction network this promoter plays its role.

Hardware and software development of a multichannel readout board named CARLOSrx for the ALICE experiment

ALICE, that is an experiment held at CERN using the LHC, is specialized in analyzing lead-ion collisions. ALICE will study the properties of quarkgluon plasma, a state of matter where quarks and gluons, under conditions of very high temperatures and densities, are no longer confined inside hadrons. Such a state of matter probably existed just after the Big Bang, before particles such as protons and neutrons were formed. The SDD detector, one of the ALICE subdetectors, is part of the ITS that is composed by 6 cylindrical layers with the innermost one attached to the beam pipe. The ITS tracks and identifies particles near the interaction point, it also aligns the tracks of the articles detected by more external detectors. The two ITS middle layers contain the whole 260 SDD detectors. A multichannel readout board, called CARLOSrx, receives at the same time the data coming from 12 SDD detectors. In total there are 24 CARLOSrx boards needed to read data coming from all the SDD modules (detector plus front end electronics). CARLOSrx packs data coming from the front end electronics through optical link connections, it stores them in a large data FIFO and then it sends them to the DAQ system. Each CARLOSrx is composed by two boards. One is called CARLOSrx data, that reads data coming from the SDD detectors and configures the FEE; the other one is called CARLOSrx clock, that sends the clock signal to all the FEE. This thesis contains a description of the hardware design and firmware features of both CARLOSrx data and CARLOSrx clock boards, which deal with all the SDD readout chain. A description of the software tools necessary to test and configure the front end electronics will be presented at the end of the thesis.

Raman-spektroskopische Untersuchungen an Alkali- und Erdalkalisilicatgläsern bei hohen Temperaturen

In der vorliegenden Arbeit wird die Struktur von Alkali- und Erdalkalisilicatglaesern bei hohen Temperaturen (bis 1800 K) mit Hilfe der Raman-Spektroskopie untersucht. Ein wesentlicher Teil der vorliegenden Arbeit besteht in dem Aufbau einer Hochtemperatureinrichtung, die es erlaubt, Raman-Spektren von Silicatglaesern bei sehr hohen Temperaturen zu messen. Mit der Hochtemperatur-Raman-Spektroskopie an Silicatglaesern sind erhebliche experimentelle Schwierigkeiten verbunden: Die thermische Strahlung der Probe überlagert sich mit dem Raman-Spektrum.Die Temperaturbestimmung der Glasprobe, die einen Durchmesser von nur 0,8 mm hat, erfolgt durch den Vergleich der Stokes- und Anti-Stokes-Raman-Intensitaeten einer intensiven Linie einer Referenzprobe. Die Natriumsilicatglaeser werden detailliert untersucht und die Verteilung der Struktureinheiten in den Natriumsilicatglaesern wird zwischen Zimmertemperatur und 900 K bestimmt. Aus der Verteilung der Strukturelemente wird eine Gleichgewichtskonstante K berechnet, welche die Disproportionierungsreaktion zwischen den Struktureinheiten in den Glaesern beschreibt. Der Wert für die Reaktionsenthalpie liegt im untersuchten Konzentrationsbereich zwischen 0 und 28 kJ/mol und haengt systematisch von der Zusammensetzung ab. Die Reaktionsenthalpie nimmt mit zunehmendem Natriumoxid-Gehalt zu.Die quantitative Auswertung der Raman-Spektren der Kaliumsilicatglaeser und der Bariumsilicatglaeser ist auf Grund deren Kristallisation bei hohen Temperaturen mit Problemen behaftet.

Electrothermal characterization and nonlinear modelling of GaN transistors for telecommunication circuit design

This thesis starts showing the main characteristics and application fields of the AlGaN/GaN HEMT technology, focusing on reliability aspects essentially due to the presence of low frequency dispersive phenomena which limit in several ways the microwave performance of this kind of devices. Based on an equivalent voltage approach, a new low frequency device model is presented where the dynamic nonlinearity of the trapping effect is taken into account for the first time allowing considerable improvements in the prediction of very important quantities for the design of power amplifier such as power added efficiency, dissipated power and internal device temperature. An innovative and low-cost measurement setup for the characterization of the device under low-frequency large-amplitude sinusoidal excitation is also presented. This setup allows the identification of the new low frequency model through suitable procedures explained in detail. In this thesis a new non-invasive empirical method for compact electrothermal modeling and thermal resistance extraction is also described. The new contribution of the proposed approach concerns the non linear dependence of the channel temperature on the dissipated power. This is very important for GaN devices since they are capable of operating at relatively high temperatures with high power densities and the dependence of the thermal resistance on the temperature is quite relevant. Finally a novel method for the device thermal simulation is investigated: based on the analytical solution of the tree-dimensional heat equation, a Visual Basic program has been developed to estimate, in real time, the temperature distribution on the hottest surface of planar multilayer structures. The developed solver is particularly useful for peak temperature estimation at the design stage when critical decisions about circuit design and packaging have to be made. It facilitates the layout optimization and reliability improvement, allowing the correct choice of the device geometry and configuration to achieve the best possible thermal performance.

Molekulardynamiksimulationen zur Untersuchung des Mischalkali-Effektes in silikatischen Gläsern

In der vorliegenden Arbeit wird mittels Molekulardynamik(MD)-Computersimulationen die Dynamik von verschiedenen Alkalisilikaten in der Schmelze und im Glas untersucht. Es ist bekannt, daß diese Systeme ionenleitend sind, was auf eine hohe Mobilität der Alkaliionen im Vergleich zu den glasbildenden Komponenten Si und O zurückzuführen ist. Im Mittelpunkt des Interesses steht der sog. Mischalkalieffekt (MAE), der in ternären Mischungen aus Siliziumdioxid mit zwei Alkalioxiden auftritt. Gegenüber Mischungen mit nur einer Alkaliionensorte weisen letztere Systeme eine signifikante Verlangsamung der Alkaliionendiffusion auf. Zunächst werden zwei binäre Alkalisilikate simuliert, nämlich Lithiumdisilikat (LS2) und Kaliumdisilikat (KS2). Die Simulationen zeigen, daß der Ursprung der hohen Mobilität der Alkaliionen in der Struktur begründet ist. KS2 und LS2 weisen auf intermediären Längenskalen Ordnung auf, die in partiellen statischen Strukturfaktoren durch Prepeaks reflektiert ist. Die den Prepeaks zugrundeliegende Struktur erklärt sich durch perkolierende Netzwerke aus alkalioxidreichen Kanälen, die als Diffusionskanäle für die mobilen Alkaliionen fungieren. In diesen Kanälen bewegen sich die Ionen mittels Sprüngen (Hopping) zwischen ausgezeichneten Plätzen. In der Simulation beobachtet man für die hohen Temperaturen (4000K>=1500K) eine ähnliche Aktivierungsenergie wie im Experiment. Im Experiment findet allerdings unterhalb von ca.1200K ein Crossover in ein Arrheniusverhalten mit höherer Aktivierungsenergie statt, welches von der Simulation nicht nachvollzogen wird. Das kann mit der in der Simulation nicht im Gleichgewicht befindlichen Si-O-Matrix erklärt werden, bei der Alterungseffekte beobachtet werden. Am stärksten ist der MAE für eine Alkalikomponente, wenn deren Konzentrationsanteil in einem ternären Mischalkalisystem gegen 0 geht. Daher wird ein LS2-System untersucht, in dem ein Li-Ion gegen ein K-Ion getauscht wird. Der Einfluß des K-Ions ist sowohl lokal in den charakteristischen Abständen zu den ersten nächsten Nachbarn (NN) zu sehen, als auch in der ortsaufgelösten Koordinationszahlverteilung bis zu Längenskalen von ca. 8,5 Angstrom. Die Untersuchung der Dynamik des eingesetzten K-Ions zeigt, daß die Sprungwahrscheinlichkeit nicht mit der Lokalisierung, einem Maß für die Bewegung eines Teilchens um seine Ruheposition, korreliert ist, aber daß eine chemische Umgebung mit wenig Li- und vielen O-NN oder vielen Li- und wenig O-NN ein Sprungereignis begünstigt. Zuletzt wird ein ternäres Alkalisilikat (LKS2) untersucht, dessen Struktur alle charakteristischen Längenskalen von LS2 und KS2 aufweist. Es stellt sich also eine komplexe Struktur mit zwei perkolierenden Subnetzwerken für Alkaliionen ein. Die Untersuchung der Dynamik zeigt eine geringe Wahrscheinlichkeit dafür auf, daß Ionen in ein Subnetzwerk andersnamiger Ionen springen. Auch kann gezeigt werden, daß das Modellpotential den MAE reproduzieren kann, daß also die Diffusionskonstanten in LKS2 bei bis zu einer Größenordnung langsamer sind als in KS2 bzw. LS2. Der beobachtete Effekt stellt sich zudem vom funktionalen Verlauf her so dar, wie er beim MAE erwartet wird. Es wurde auch festgestellt, daß trotz der zeitlichen Verzögerung in den dynamischen Größen die Anzahl der Sprünge pro Zeit nicht geringer ist und daß für niedrige Temperaturen (d.h.im Glas) Sprünge auf den Nachbarplatz mit anschließendem Rücksprung auf die vorherige Position deutlich wahrscheinlicher sind als bei hohen Temperaturen (also in der Schmelze). Die vorliegenden Resultate geben Aufschluß über die Details der Mechanismen mikroskopischer Ionenleitung in binären und ternären Alkalisilikaten sowie dem MAE.

Klassische und ab initio Molekulardynamik-Untersuchungen zu Germaniumdioxidschmelzen

Germaniumdioxid (GeO2) ist ein Glasbildner, der wie das homologe SiO2 ein ungeordnetes tetraedrisches Netzwerk ausbildet. In dieser Arbeit werden mit Hilfe von Molekulardynamik-Computersimulationen die Struktur und Dynamik von GeO2 in Abhängigkeit von der Temperatur untersucht. Dazu werden sowohl Simulationen mit einem klassischen Paarpotentialmodell von Oeffner und Elliott als auch ab initio-Simulationen gemäß der Car-Parrinello-Molekulardynamik (CPMD), bei der elektronische Freiheitsgrade mittels Dichtefunktionaltheorie beschrieben werden, durchgeführt. In der klassischen Simulation werden dazu ein Temperaturen zwischen 6100 K und 2530 K betrachtet. Darüberhinaus ermöglichen Abkühlläufe auf T=300 K das Studium der Struktur des Glases. Zum Vergleich werden CPMD-Simulationen für kleinere Systeme mit 60 bzw. 120 Teilchen bei den Temperaturen 3760 K und 3000 K durchgeführt. In den klassischen Simulationen kann die im Experiment bis 1700 K nachgewiesene, im Vergleich zu SiO2 starke, Temperaturabhängigkeit der Dichte auch bei höheren Temperaturen beobachtet werden. Gute Übereinstimmungen der Simulationen mit experimentellen Daten zeigen sich bei der Untersuchung verschiedener struktureller Größen, wie z.B. Paarkorrelationsfunktionen, Winkelverteilungen, Koordinationszahlen und Strukturfaktoren. Es können leichte strukturelle Abweichungen der CPMD-Simulationen von den klassischen Simulationen aufgezeigt werden: 1. Die Paarabstände in CPMD sind durchweg etwas kleiner. 2. Es zeigt sich, daß die Bindungen in den ab initio-Simulationen weicher sind, was sich auch in einer etwas stärkeren Temperaturabhängigkeit der strukturellen Größen im Vergleich zu den klassischen Simulationen niederschlägt. 3. Für CPMD kann ein vermehrtes Auftreten von Dreierringstrukturen gezeigt werden. 4. In der CPMD werden temperaturabhängige Defektstrukturen in Form von Sauerstoffpaaren beobachtet, die vor allem bei 3760 K, kaum jedoch bei 3000 K auftreten. Alle strukturellen Unterschiede zwischen klassischer und CPMD-Simulation sind eindeutig nicht auf Finite-Size-Effekte aufgrund der kleinen Systemgrößen in den CPMD-Simulationen zurückzuführen, d.h. sie sind tatsächlich methodisch bedingt. Bei der Dynamik von GeO2 wird in den klassischen Simulationen ebenfalls eine gute Übereinstimmung mit experimentellen Daten beobachtet, was ein Vergleich der Diffusionskonstanten mit Viskositätsmessungen bei hohen Temperaturen belegt. Die Diffusionskonstanten zeigen teilweise ein verschiedenes Verhalten zum homologen SiO2. Sie folgen in GeO2 bei Temperaturen unter 3000 K einem Arrheniusgesetz mit einer deutlich niedrigeren Aktivierungsenergie. Darüberhinaus werden die Möglichkeiten der Parametrisierung eines neuen klassischen Paarpotentials mittels der Kräfte entlang der CPMD-Trajektorien untersucht. Es zeigt sich, daß derartige Parametrisierungen sehr stark von den gewählten Startparametern abhängen. Ferner führen sämtliche an die Schmelze parametrisierten Potentiale zu zu hohen Dichten im Vergleich zum Experiment. Zum einen liegt dies sehr wahrscheinlich daran,daß für das System GeO2 Kraftdaten allein nicht ausreichen, um grundlegende strukturelle Größen, wie z.B. Paarkorrelationen und Winkelverteilungen, der CPMD-Simulationen gut reproduzieren zu können. Zum anderen ist wohl die Beschreibung mittels Paarpotentialen nicht ausreichend und es ist erforderlich, Merkörperwechselwirkungen in Betracht zu ziehen.

Point defects in carbon nanostructures studied by in-situ electron microscopy

In the present work, the formation and migration of point defects induced by electron irradiation in carbon nanostructures, including carbon onions, nanotubes and graphene layers, were investigated by in-situ TEM. The mobility of carbon atoms normal to the layers in graphitic nanoparticles, the mobility of carbon interstitials inside SWCNTs, and the migration of foreign atoms in graphene layers or in layers of carbon nanotubes were studied. The diffusion of carbon atoms in carbon onions was investigated by annealing carbon onions and observing the relaxation of the compressed clusters in the temperature range of 1200 – 2000oC. An activation energy of 5.0±0.3 eV was obtained. This rather high activation energy for atom exchange between the layers not only prevents the exchange of carbon atoms between the layers at lower temperature but also explains the high morphological and mechanical stability of graphite nanostructures. The migration of carbon atoms in SWCNTs was investigated quantitatively by cutting SWCNT bundles repeatedly with a focused electron beam at different temperatures. A migration barrier of about 0.25 eV was obtained for the diffusion of carbon atoms inside SWCNTs. This is an experimental confirmation of the high mobility of interstitial atoms inside carbon nanotubes, which corroborates previously developed theoretical models of interstitial diffusivity. Individual Au and Pt atoms in one- or two-layered graphene planes and MWCNTs were monitored in real time at high temperatures by high-resolution TEM. The direct observation of the behavior of Au and Pt atoms in graphenic structures in a temperature range of 600 – 700°C allows us to determine the sites occupied by the metal atoms in the graphene layer and the diffusivities of the metal atoms. It was found that metal atoms were located in single or multiple carbon vacancies, not in off-plane positions, and diffused by site exchange with carbon atoms. Metal atoms showed a tendency to form clusters those were stable for a few seconds. An activation energy of around 2.5 eV was obtained for the in-plane migration of both Au and Pt atoms in graphene (two-dimensional diffusion). The rather high activation energy indicates covalent bonding between metal and carbon atoms. Metal atoms were also observed to diffuse along the open edge of graphene layers (one-dimensional diffusion) with a slightly lower activation energy of about 2.3 eV. It is also found that the diffusion of metal atoms in curved graphenic layers of MWCNTs is slightly faster than in planar graphene.

Effects of Global Warming on Berry Composition of cv. Sangiovese: Biochemical and Molecular Aspects and Agronomical Adaptation Approaches

Wine grape must deal with serious problems due to the unfavorable climatic conditions resulted from global warming. High temperatures result in oxidative damages to grape vines. The excessive elevated temperatures are critical for grapevine productivity and survival and contribute to degradation of grape and wine quality and yield. Elevated temperature can negatively affect anthocyanin accumulation in red grape. Particularly, cv. Sangiovese was identified to be very sensitive to such condition. The quantitative real-time PCR analysis showed that flavonoid biosynthetic genes were slightly repressed by high temperature. Also, the heat stress repressed the expression of the transcription factor “VvMYBA1” that activates the expression of UFGT. Moreover, high temperatures had repressing effects on the activity of the flavonoids biosynthetic enzymes “PAL” and “UFGT”.Anthocyanin accumulation in berry skin is due to the balance between its synthesis and oxidation. In grape cv. Sangiovese, the gene transcription and activity of peroxidases enzyme was elevated by heat stress as a defensive mechanism of ROS-scavenging. Among many isoforms of peroxidases genes, one gene (POD 1) was induced in Sangiovese under thermal stress condition. This gene was isolated and evaluated via the technique of genes transformation from grape to Petunia. Reduction in anthocyanins concentration and higher enzymatic activity of peroxidase was observed in POD 1 transformed Petunia after heat shock compared to untrasformed control. Moreover, in wine producing regions, it is inevitable for the grape growers to adopt some adaptive strategies to alleviate grape damages to abiotic stresses. Therefore, in this thesis, the technique of post veraison trimming was done to improve the coupling of phenolic and sugar ripening in Vitis vinifera L. cultivar Sangiovese. Trimming after veraison showed to be executable to slow down the rate of sugar accumulation in grape (to decrease the alcohol potential in wines) without evolution of the main berry flavonoids compounds.