Thermal analysis of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) irradiated under vacuum

Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) was irradiated by Co-60 gamma-rays (doses of 50, 100 and 200kGy) under vacuum. The thermal analysis of control and irradiated PHBV, under vacuum was carried out by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC). The tensile properties of control and irradiated PHBV were examined by using an Instron tensile testing machine. In the thermal degradation of control and irradiated PHBV, a one-step weight loss was observed. The derivative thermogravimetric curves of control and irradiated PHBV confirmed only one weight-loss step change. The onset degradation temperature (T-o) and the temperature of maximum weight-loss rate (T-p) of control and irradiated PHBV were in line with the heating rate (degreesC min(-1)). T-o and T-p of PHBV decreased with increasing radiation dose at the same heating rate. The DSC results showed that Co-60 gamma-radiation significantly affected the thermal properties of PHBV. With increasing radiation dose, the melting temperature (T-m) of PHBV shifted to a lower value, due to the decrease in crystal size. The tensile strength and fracture strain of the irradiated PHBV decreased, hence indicating an increased brittleness.

A novel laser light-scattering study of enzymatic biodegradation of poly(epsilon-caprolactone) nanoparticles

A successful micronization of water-insoluble poly(epsilon-caprolactone) (PCL) into narrowly distributed nanoparticles stable in water has not only enabled us to study the enzymatic biodegradation of PCL in water at 25 degrees C by a combination of static and dynamic laser light scattering (LLS), but also to shorten the biodegradation time by a factor of more than 10(3) compared with using a thin PCL film, i.e. a 1 week conventional experiment becomes a 4 min one. The time-average scattering intensity decreased linearly. It was interesting to find that the decrease of the scattering intensity was not accompanied by a decrease of the average size of the PCL nanoparticles, indicating that the enzyme, Lipase Pseudomonas (PS), ''eats'' the PCL nanoparticles one-by-one, so that the biodegradation rate is determined mainly by the: enzyme concentration. Moreover, we found that using anionic sodium lauryl sulphate instead of cationic hexadecyltrimethylammonium bromide as surfactant in the micronization can prevent the biodegradation, suggesting that the biodegradation involves two essential steps: the adsorption of slightly negatively charged Lipase PS onto the PCL nanoparticles and the interaction between Lipase PS and PCL. (C) 1999 Elsevier Science Ltd. All rights reserved.

Thermal analysis of ethylene propylene copolymer-grafted-acrylic acid

The thermal properties of ethylene propylene copolymer-grafted-acrylic acid (EP-g-AA) were investigated by using differential scanning calorimetry (DSC). Compared with the ethylene propylene copolymer (EP), the peak values of the melting temperature (T-m) of the propylene sequences in the grafted EP changed a little, the crystallization temperature (T-c) increased about 8-12 degrees C, and the melting enthalpy (Delta H-m) increased about 4-6 J/g. The isothermal crystallization kinetics of grafted and ungrafted samples was carried out by DSC. Within the scope of the researched crystallization temperature, the Avrami exponent (n) of the ungrafted sample was 1.6-1.8, and that of grafted samples were all above 2, which indicated that the grafted monomer could become the crystal nuclei for the crystallization of propylene sequence. With increasing grafted monomer content, the crystallization rate of propylene sequence in grafted EP increased; it might be the result of rapid nucleation rate and crystal growth rate.

Thermal analysis of ethylene-propylene copolymer-grafted-glycidyl methacrylate

The thermal properties of ethylene-propylene copolymer grafted with glycidyl methacrylate (EP-g-GMA) were investigated by using differential scanning calorimetry (DSC). Compared to the plain ethylene-propylene copolymer (EP), peak values of melting temperature (T-m) of the propylene sequences in the grafted EP changed a little, crystallization temperature (T-c) increased about 8-12 degrees C, and melting enthalpy (Delta H-m) increased about 4-6 J/g. The isothermal and nonisothermal crystallization kinetics of grafted and ungrafted samples was carried out by DSC. Within the scope of the researched crystallization temperature, the Avrami exponent (n) of ungrafted sample is 1.6-1.8, and those of grafted samples are all above 2. The crystallization rates of propylene sequence in EP-g-GMA were faster than that in the plain EP and increased with increasing of grafted monomer content. It might be attributed to the results of rapid nucleation rate. (C) 1996 John Wiley & Sons, Inc.

THERMAL-ANALYSIS OF Y1-XCAXBA2CU3O7-Y

TG and DTA analysis of Y1-xCaxBa2Cu3O7-y suggests that the stability of the 123 phase increases with increasing Ca contents. The O(1) in the Cu(1)-O chain is unstable but O(2) and O(3) in Cu(2)-O planes are very stable. There are hardly any oxygen vacanci

CRYSTAL STRUCTURE AND THERMAL ANALYSIS OF ERBIUM COMPLEX WITH BENZENE ACETIC ACID

The crystal structure of erbium (III) complex of benzene acetic acid is reported. The complex crystallizes in the monoclinic space group P2(1)/a with a = 0,9008(3)nm, b=1.4242(5) nm, c=1.8437(7) nm, beta=98.80(3)degrees, V = 2.337(1) nm(3), Z = 4. The mechanism of thermal decomposition of complex has been studied by TG-DTG-DTA. The activation energy for dehydration reaction has been calculated by Freeman Carroll method. The enthalpy change for dehydration and phase change process has been determined.

THERMAL ANALYSIS AND INFRARED SPECTRA OF DIALKYLAMMONIUM TETRAC HLOROCUPRATE

The thermal stability and the solid solid phase transitions in Ills compounds with n = 7-12 have been studied by DSC and TG methods. Comparision with CnZn compounds want made. The nature of three phases of CnCu has been discussed in terms of infrared spectroscopy and the assignment of the phase transitions has been given. The thermal stability of CnCu is lower than that of CnZn and presents an obvious odd even effect. All of these compounds exhibit two solid solid phase transitions in the temperature range of 248-337 K. The peak tempe nature of phase transitions changes regularly. The peak temperature or the main phase transition increases with the chain length. The total transition enthalpies and entropies increase with increasing chain length. When n <= 9, the high temperature phase exists in a partial disorder state. When n >= 10, the high temperature phase exists in a conformational disorder state. The main phase transition and the phase transition at 307.7 K of CnCu may mainly are from the change of the packing structure and the change of the partial conformational order-disorder of alkyl chain, respectively.

THERMAL-ANALYSIS OF POLYARYLENE ETHER SULFONES AND POLYIMIDES

Some results on the thermal analysis of polyimides and polyaryl ether sulfones, some reactions and the purity determination of the monomers, and the thermal stability and kinetic analysis of the thermo-oxidative degradation of these polymers are described.

Solder life prediction in a thermal analysis software environment

This paper describes recent developments made to the stress analysis module within FLOTHERM, extending its capability to handle viscoplastic behavior. It also presents the validation of this approach and results obtained for an SMT resistor as an illustrative example. Lifetime predictions are made using the creep strain energy based models of Darveaux. Comment is made about the applicability of the damage model to the geometry of the joint under study.

Thermal analysis of LEDS for liquid crystal display's backlighting

This paper investigated the thermal design of the light emitting diode (LED)onto the board and its packaging. The LED was a 6-lead MultiLED with three chips designed for LCD backlighting and other lighting purposes. A 3D finite element model of this LED was built up and thermal analysis was carried out using the multi physics software package PHYSICA. The modeling results were presented as temperature distributions in each LED, and the predicted junction temperature was used for thermal resistance calculation. The results for the board structure indicated that (1) removing the foil attach decreased the thermal resistance, (2) Increasing the copper foil thickness reduced the thermal resistance. package design indicated that the SMT designed LED with integrated slug gave lower thermal resistance. Pb-free solder material gave lower thermal resistance and junction temperature when compared with conductive adhesive