A new method to fabricate InGaN quantum dots by metalorganic chemical vapor deposition

A new method to form nanoscale InGaN quantum dots using MOCVD is reported, This method is much different from a method. which uses surfactant or the Stranski-Krastannow growth mode. The dots were formed by increasing the energy barrier for adatoms, which are hopping by surface passivation, and by decreasing the growth temperature. Thus, the new method can be called as a passivation-low-temperature method. Regular high-temperature GaN films were grown first and were passivated. A low-temperature thin layer of GaN dot was then deposited on the surface that acted as the adjusting layer. At last the high-density InGaN dots could be fabricated on the adjusting layer. Atomic force microscopy measurement revealed that InGaN dots were small enough to expect zero-dimensional quantum effects: The islands were typically 80 nm wide and 5 nm high. Their density was about 6 x 10(10) cm(-2). Strong photoluminescence emission from the dots is observed at room temperature, which is much stronger than that of the homogeneous InGaN film with the same growth time. Furthermore, the PL emission of the GaN adjusting layer shows 21 meV blueshift compared with the band edge emission of the GaN due to quantum confine effect. (C) 2002 Elsevier Science B.V. All rights reserved.

Structural and photoelectric studies on double barrier quantum well infrared detectors

GaAs/AlAs/GaAlAs double barrier quantum well (DBQW) structures are employed for making 3-5 um photovoltaic infrared (IR) detectors with a peak detectivity of 5 x 10(11) cm Hz(1/2)/W at 80 K. Double crystal X-ray diffraction is combined with synchrotron radiation X-ray analysis to determine successfully the exact thickness of GaAs, AlAs and GaAlAs sublayers. The interband photovoltaic (PV) spectra of the linear array of the detectors are measured directly by edge excitation method, providing the information about spatial separation processes of photogenerated carriers in the multiquantum wells and the distribution of built-in field in the active region. The spectral response of the IR photocurrent of the devices is also measured and compared with the temperature dependent IR absorption of the DBQW samples in order to get a better understanding of the bias-controlled optical and transport behavior of the detector photoresponse and thus to optimize the detector performance. (C) 1999 Elsevier Science Ltd. All rights reserved.

Tunneling transmission in two quantum wires coupled by a magnetically defined barrier

A numerical analysis of an electron waveguide coupler based on two quantum wires coupled by a magnetically defined barrier is presented with the use of the scattering-matrix method. For different geometry parameters and magnetic fields, tunneling transmission spectrum is obtained as a function of the electron energy. Different from that of conventional electron waveguide couplers, the transmission spectrum of the magnetically coupled quantum wires does not have the symmetry with regard to those geometrically symmetrical ports, It was found that the magnetic field in the coupling region drastically enhances the coupling between the two quantum wires for one specific input port while it weakens the coupling for the other input port. The results can be well understood by the formation of the edge states in the magnetically defined barrier region. Thus, whether these edge states couple or decouple to the electronic propagation modes in the two quantum wires, strongly depend on the relative moving directions of electrons in the propagating mode in the input port and the edge states in the magnetic region. This leads to a big difference in transmission coefficients between two quantum wires when injecting electrons via different input ports. Two important coupler specifications, the directivity and uniformity, are calculated which show that the system we considered behaves as a good quantum directional coupler. (C) 1997 American Institute of Physics.

Leakage current analysis in AlGaInP/GaInP multi-quantum well lasers by the electrical derivative method - art. no. 60202F

In AlGaInP/GaInP multi-quantum well (MQW) lasers, the electron leakage current is a much more serious problem than that in laser diodes with longer wavelength. To further improve the output performance, the leakage current should be analyzed. In this letter, the temperature dependence of electrical derivative characteristics in AlGaInP/GaInP multi-quantum well lasers was measured, and the potential barrier for electron leakage was obtained. With the help of secondary ion mass spectroscopy (SIMS) measurement, theoretical analysis of the potential barrier was presented and compared with the measurement result. The influence of p-cladding doping level and doping profile on the potential barrier was discussed, and this can be helpful in metalorganic chemical vapor deposition (MOCVD) growth.

SELF-CONSISTENT TREATMENT OF 3-DIMENSIONAL - 2-DIMENSIONAL AND 2-DIMENSIONAL - 2-DIMENSIONAL RESONANT-TUNNELING IN DOUBLE-BARRIER STRUCTURES

By using a transfer-matrix method on the basis of two-dimensional (2D) Bloch sums in accordance with a tight-binding scheme, a self-consistent calculation on the resonant tunneling in asymmetric double-barrier structures is presented, in which contributions to resonant tunneling from both three-dimensional (3D) electrons in the contacts and 2D electrons in the spacer or accumulation layers are considered simultaneously. The charge buildup effect on the current versus voltage (I-V) curves is evaluated systematically, showing quantitatively how it results in the I-V bistability and enhanced differences between I-V curves for positive and negative bias in an asymmetric double-barrier structure. Special attention is focused on the interaction between 3D-2D and 2D-2D resonant-tunneling processes, including the suppression of 2D-2D resonant tunneling by the charge buildup in the well accompanying the 3D-2D resonant tunneling. The effects of the emitter doping condition (doping concentration, spacer thickness) on the presence of two types of quasi-2D levels in the emitter accumulation layers, and on the formation of a potential bulge in the emitter region, are discussed in detail in relation to the tunneling process.

TUNNELING ESCAPE TIME OF ELECTRONS THROUGH DOUBLE-BARRIER RESONANT-TUNNELING STRUCTURES

Tunneling escape of electrons from quantum wells (QWs) has systematically been studied in an arbitrarily multilayered heterostructures, both theoretically and experimentally. A wave packet method is developed to calculate the bias dependence of tunneling escape time (TET) in a three-barrier, two-well structure. Moreover, by considering the time variation of the band-edge profile in the escape transient, arising from the decay of injected electrons in QWs, we demonstrate that the actual escape time of certain amount of charge from QWs, instead of single electron, could be much longer than that for a single electron, say, by two orders of magnitude at resonance. The broadening of resonance may also be expected from the same mechanism before invoking various inhomogeneous and homogeneous broadening. To perform a close comparison between theory and experiment, we have developed a new method to measure TET by monitoring transient current response (TCR), stemming from tunneling escape of electrons out of QWs in a similar heterostructure. The time resolution achieved by this new method reaches to several tens ns, nearly three orders of magnitude faster than that by previous transient-capacitance spectroscopy (TCS). The measured TET shows an U-shaped, nonmonotonic dependence on bias, unambiguously indicating resonant tunneling escape of electrons from an emitter well through the DBRTS in the down-stream direction. The minimum value of TET obtained at resonance is accordance with charging effect and its time variation of injected electrons. A close comparison with the theory has been made to imply that the dynamic build-up of electrons in DBRTS might play an important role for a greatly suppressed tunneling escape rate in the vicinity of resonance.

A Numerical Method for Calculating Transmission Coefficients Across Arbitrary Potential Barriers with High Accuracy

We report a new method for calculating transmission coefficients across arbitrary potential barriers based on the Runge-Kutta method. A numerical solution of the Schrodinger equation is calculated using the Runge-Kutta method,and a new model is established to analyze the numerical results to find the transmission coefficient. This technique is applied to various cases, such as parabolic potential barrier and double-barrier structures. Transmission probability with high precision is obtained and discussed. The tunnelling current density through a MOS structure is also explored and the result coincides with the Fowler-Nordheim model,which indicates the applicability of our method.

Resonant tunneling of holes in GaMnAs-related double- barrier structures

Using the multiband quantum transmitting boundary method (MQTBM), hole resonant tunneling through AlGaAs/GaMnAs junctions is investigated theoretically. Because of band-edge splitting in the DMS layer, the current for holes with different spins are tuned in resonance at different biases. The bound levels of the "light" hole in the quantum well region turned out to be dominant in the tunneling channel for both "heavy" and "light" holes. The resonant tunneling structure can be used as a spin filter for holes for adjusting the Fermi energy and the thickness of the junctions.

Structural and photoelectric studies on double barrier quantum well infrared detectors

GaAs/AlAs/GaAlAs double barrier quantum well (DBQW) structures are employed for making the 3 similar to 5 mu m photovoltaic infrared (IR) detectors with a peak detectivity of 5x10(11) cmHz(1/2)/W at 80K. The double crystal x-ray diffraction is combined with synchrotron radiation x-ray analysis to determine the exact thickness of GaAs, AlAs and GaAlAs sublayers. The interband photovoltaic (PV) spect ra of the DBQW sample and the spectral response of the IR photocurrent of the devices are measured directly by edge excitation method, providing the information about spatial separation processes of photogenerated carriers in the multiquantum wells and the distribution of built-in field in the active region.

An eigenfunction expansion-variational method in prediction of the transverse thermal conductivity of fiber reinforced composites considering interfacial characteristics

An eigenfunction expansion-variational method based on a unit cell is developed to deal with the steady-state heat conduction problem of doubly-periodic fiber reinforced composites with interfacial thermal contact resistance or coating. The numerical results show a rapid convergence of the present method. The present solution provides a unified first-order approximation formula of the effective thermal conductivity for different interfacial characteristics and fiber distributions. A comparison with the present high-order results, available experimental data and micromechanical estimations demonstrates that the first-order approximation formula is a good engineering closed-form formula. An engineering equivalent parameter reflecting the overall influence of the thermal conductivities of the matrix and fibers and the interfacial characteristic on the effective thermal conductivity, is found. The equivalent parameter can greatly simplify the complicated relation of the effective thermal conductivity to the internal structure of a composite. (c) 2010 Elsevier Ltd. All rights reserved.

Interface delamination of the thermal barrier coating subjected to local heating

To investigate the possible failure modes of the thermal barrier coating (TBC) used to protect the scramjet combustion chamber, the local heating via laser beam irradiation was utilized to simulate the service condition of high thermal flux and high temperature gradient. Firstly, the experimental method and process were described and the typical fracture morphology of the TBC under test were provided. Then, the theoretical and finite element modeling were carried out to study the temperature, deformation and stresses of the specimen when the top ceramic coat was subjected to local heating, and to demonstrate the mechanism on the failure of the TBC. It is revealed that the interface delamination shall appear and ultimately lead to the failure of the TBC under such thermal loading of local quick heating. According to the outcome of this study, the driving force of the interface delamination is influenced greatly by the key structural parameters and performance matching. Moreover, by utilizing the rules of the effects of these parameters on the fracture driving force, there is some possibility for the designer to optimize the performances of the TBC.

Roundness parameters in barrier-lagoon systems in northeastern Shandong Peninsula, China: limitations to environmental discrimination

Twenty-five samples from six subenvironments in the barrier-lagoon systems in northeastern Shandong province, China, are examined. A statistical method is used to study the roundness variation of grains of different sizes. Roundness of very fine pebble and very coarse sand varies significantly in different subenvironments. It is possible to discriminate among aqueous depositional environments using the roundness of grains of these sizes. Roundness of grains finer than 0.84 φ is not distinguishable in different subenvironments.

A SIMPLE METHOD FOR PREDICTION OF GAS-PERMEABILITY OF POLYMERS FROM THEIR MOLECULAR-STRUCTURE

A method for the prediction of gas permeabilities (P) through polymers from their chemical structure has been developed on the basis of the ratio of molar free volume to molar cohesive energy, V(f)/E(coh). The permeation of small gas molecules through polymer membranes is dependent on the chain packing density measured by V(f) and segmental motion of polymer chains measured by E(coh). But no simple relationship between P and V(f) or E(coh) alone was found. The permeability data of more than 60 polymers covering 7 orders of magnitude for six gases have been treated with linear regression analysis. All plots of log P vs. V(f)/E(coh) gave good straight lines. It is also found that a linear relationship holds when plotting both the intercepts and slopes of log P vs. V(f)/E(coh) lines against square of the diameters of gas molecules. Therefore, the permeabilities of all the non-swelling gases through a great variety of polymers can be estimated using two correlations above. Moreover, this method is more accurate than others in the literature and may found useful for the selection of gas separation or barrier membrane materials.

Impact of sample preparation on mineralogical analysis of iron reactive barrier materials

Permeable reactive barriers (PRBs) of zero-valent iron (Fe0) are increasingly being used to remediate contaminated ground water. Corrosion of Fe0 filings and the formation of precipitates can occur when the PRB material comes in contact with ground water and may reduce the lifespan and effectiveness of the barrier. At present, there are no routine procedures for preparing and analyzing the mineral precipitates from Fe0 PRB material. These procedures are needed because mineralogical composition of corrosion products used to interpret the barrier processes can change with iron oxidation and sample preparation. The objectives of this study were (i) to investigate a method of preparing Fe0 reactive barrier material for mineralogical analysis by X-ray diffraction (XRD), and (ii) to identify Fe mineral phases and rates of transformations induced by different mineralogical preparation techniques. Materials from an in situ Fe0 PRB were collected by undisturbed coring and processed for XRD analysis after different times since sampling for three size fractions and by various drying treatments. We found that whole-sample preparation for analysis was necessary because mineral precipitates occurred within the PRB material in different size fractions of the samples. Green rusts quickly disappeared from acetone-dried samples and were not present in air-dried and oven-dried samples. Maghemite/magnetite content increased over time and in oven-dried samples, especially after heating to 105°C. We conclude that care must be taken during sample preparation of Fe0 PRB material, especially for detection of green rusts, to ensure accurate identification of minerals present within the barrier system.

Self-potential signatures associated with an injection experiment at an in situ biological permeable reactive barrier

Strategies available to evaluate the performance of in situ permeable reactive barriers are currently not well developed and often rely on fluid and media sampling directly from the permeable reactive barrier (PRB). Here, we investigate the utility of the self-potential (SP) method as a technique to monitor in situ PRB performance. Our field study was conducted at in situ biological PRB in Portadown, Northern Ireland, UK, which was emplaced to assist in the remediation of groundwater contamination (e.g., hydrocarbons, ammonia) that resulted from the operations and waste disposal practices of a former gasworks. Borehole SP measurements were collected during the injection of contaminant groundwater slugs in an attempt to monitor/detect the response of the microbial activity associated with the breakdown of the added contaminants into the PRB. In addition, an uncontaminated groundwater slug was injected into a different portion of the PRB as a ‘control’ and SP measurements were collected for comparison to the SP response of the contaminant slugs. The results of the SP signals due to the contaminant injections show that the magnitude of the response was relatively small (<10 mV) yet showed a consistent decrease during both contaminant injections. The net decrease in SP recorded during the contaminant injections slowly rebounded to near background values through ~44 hours post-injection. The SP response during the uncontaminated injection showed a slight, albeit negligible (within the margin of error), 1 mV increase in the measured SP signals, in contrast to the contaminant injections. The results of the SP signals recorded from the uncontaminated groundwater injection also persisted through a period of ~47 hours after injection but show a net increase in SP relative to pre-injection values. Based on the difference in SP response between the contaminated and uncontaminated injections, we suggest that the responses are likely to be the result of differences in the chemistry of the injection types (contaminated versus uncontaminated) and in situ groundwater. We argue that the SP signals associated with the contaminated injections are dominated by diffusion (electrochemical) potential, possibly enhanced by a microbial effect. While the results of our investigation show a consistent SP response associated with the contaminant injections that is dominated by diffusional effects, further studies are required in order to better understand the effect of microbial activity on SP signals and the potential utility for the SP method to detect/monitor changes that may be indicative of biological PRB performance.