Serrated Plastic Flow in a Zr-Based Bulk Metallic Glass During Nanoindentation

We investigate plastic deformation of Zr41.2Ti13.8Cu12.5Ni10Be22.5 bulk metallic glass using depth sensing nanoindentation. Numerous serrations in the load-displacement curves during indentation, shear bands and pile-ups around the indent were observed. The results revealed that the serrated plastic flow behaviour in this alloy depends strongly on the indentation strain rate.

Behavior of Multiple Shear Bands in Zr-Based Bulk Metallic Glass

The deformation behavior of Zr41.2Ti13.8Cu12.5Ni10Be22.5 bulk metallic glass was studied by in situ scanning electron microscopy (SEM) quasi-static uniaxial compression tests at room temperature. Multiple shear bands were observed with a large plasticity. Microscopic examination demonstrates that slipping, branching and intersecting of multiple shear bands are the main mechanisms for enhancing the plasticity of this metallic glass. Additionally, nano/micro-scale voids and cracks at the intersecting sites of shear bands and preferential etching of shear bands were observed as well. These observations demonstrated that the formation of shear bands in bulk metallic glasses is resulted mainly from local free volume coalescence.

Characterization of Plastic Flow in Two Zr-Based Bulk Metallic Glasses

Plastic deformation behaviors of Zr65Al10Ni10CU15 and Zr52.5Al10Ni10Cu15Be12.5 bulk metallic glasses (BMGs) are studied by using the depth-sensing nanoindentation, microindentation and uniaxial compression. The Be-containing BMG exhibits a significantly improved overall plastic strain compared with the Be-free alloy during compressive tests. Both BMGs show a loading-rate-dependent serrated flow during nanoindentation measurements, but the Be-containing alloy exhibits a much lower critical loading rate for the disappearance of the serration than the Be-free BMG. The shear band patterns developed during plastic deformation are investigated by microindentation technique, wherein much higher shear band density is found in the Be-containing alloy than in the Be-free alloy, indicating an easier nucleation of shear bands in the former BMG. The difference in the plastic deformation behavior of the two BMGs can be explained by a free volume model.

Microstructure and mechanical properties of a novel Zr-based bulk metallic glass composite

Zr48.5Cu46.5Al5 bulk metallic glass (BMG) composites with diameters of 3 and,4 mm were prepared through suction casting in an arc melting furnace by modulating the alloy composition around the monothetic BMG composition of the high glass forming ability. Microstructural characterization reveals that the composites contain micron-sized CuZr phase with martensite structure, as well as nano-sized Zr2Cu crystalline particles and Cu10Zr7 plate-like phase embedded in an amorphous matrix. Room temperature compression tests showed that the composites exhibited significant strain hardening and obvious plastic strain of 7.7% for 3 nun and 6.4% for 4 nun diameter samples, respectively.

Microstructure and mechanical properties of Zr-Cu-Al bulk metallic glasses

Zr49Cu46Al5 and Zr48.5Cu46.5Al5 bulk metallic glasses(BMGs) with diameter of 5 mm were prepared through water-cooled copper mold casting. The phase structures of the two alloys were identified by X-ray diffractometry(XRD). The thermal stability was examined by differential scanning calorimetry(DSC). Zr49Cu46Al5 alloy shows a glass transition temperature, T, of about 689 K, an crystallization temperature, T-x, of about 736 K. The Zr48.5Cu46.5Al5 alloy shows no obvious exothermic peak. The microstructure of the as-cast alloys was analyzed by transmission electron microscopy(TEM). The aggregations of CuZr and CuZr2 nanocrystals with grain size of about 20 nm are observed in Zr49Cu46Al5 nanocrystalline composite, while the Zr48.5Cu46.5Al5 alloy containing many CuZr martensite plates is crystallized seriously. Mechanical properties of bulk Zr49Cu46Al5 nanocrystalline composite and Zr48.5Cu46.5Al5 alloy measured by compression tests at room temperature show that the work hardening ability of Zr48.5Cu46.5Al5 alloy is larger than that of Zr48.5Cu46.5Al5 alloy.

一种新型Zr基块状非晶复合材料的显微组织与力学性能

通过在块状Zr-Cu—Al非晶合金形成能力较大的成分范围附近设计成分，利用电弧炉吸铸的方法制备了直径分别为3和4mm的Zr48.5Cu46.5Al5块状非晶复合材料．显微组织分析表明，复合材料中含有微米尺度的具有马氏体结构的CuZr相，同时还生成了在非晶基体上均匀分布的Zr2Cu纳米颗粒和Cu10Zr7片状相．室温压缩实验表明，直径为3和4mm块状非晶复合材料分别达到7．7％和6．4％的塑性变形，同时有显著的应变硬化现象．

Synthesis Of Plastic Zr-Based Bulk Metallic Glass Matrix Composites By The Copper-Mould Suction Casting And The Bridgman Solidification

Zr-based bulk metallic glass matrix composites with the composition of Zr56.2Ti13.8Nb5.0Cu6.9Ni5.6Be12.(5) were synthesized by the copper-mould suction casting and the Bridgman solidification. The composite, containing a well-developed flowery beta-Zr dendritic phase, was obtained by the Bridgman solidification with the withdrawal velocity of 0.8 mm/s and the temperature gradient of 45 K/mm, and the ultimate strength of 2050 MPa and fracture plastic strain of 14.6% of the composite were achieved, which was mainly interpreted by the homogeneous dispersion of bcc beta-Zr phase in the glass matrix. Crown Copyright (C) 2008 Published by Elsevier B.V. All rights reserved.

Measurement of Residual Stresses in Ferroelectric Pb(Zr

The residual stresses in Pb(Zr0.3Ti0.7)O3thin films were measured by the \sin^{2}\Psi method using the normal X-ray incidence. The spacing of different planes (hkl) parallel to the film surface were converted to the spacing of a set of inclined planes (100). The angles between (100) and (hkl) were equivalent to the tilting angles of (100) from the normal of film surface. The residual stresses were extracted from the linear slope of the strain difference between the equivalent inclined direction and normal direction with respect to the \sin^{2}\Psi. The results were in consistency with that derived from the conventional \sin^{2}\Psi method.

Measurement of residual stresses in ferroelectric Pb(Zr 0.3Ti0.7)O3 thin films by X-ray diffraction

The residual stresses in Pb(Zr0.3Ti0.7)O3 thin films were measured by the sin2 Ψ method using the normal X-ray incidence. The spacing of different planes (hkl) parallel to the film surface were converted to the spacing of a set of inclined planes (100). The angles between (100) and (hkl) were equivalent to the tilting angles of (100) from the normal of film surface. The residual stresses were extracted from the linear slope of the strain difference between the equivalent inclined direction and normal direction with respect to the sin2 Ψ. The results were in consistency with that derived from the conventional sin2 Ψ method. © 2013 The Japan Society of Applied Physics.

Theoretical investigation on the phase stability of Nd2Fe14B and site preference of V, Cr, Mn, Zr and Nb

The stability of the excellent permanent magnetic compound Nd2Fe14B and substitution of Fe in the compound by V, Cr, Mn, Zr and Nb are investigated by using interatomic pair potentials which are converted from lattice-inversion method. Calculation shows that the substitution always makes the cell volume larger, and the increase of the volume is almost linear with substituent concentration. The calculated cohesive energy shows that the preferential order of substitution of Fe is Nb, V, Cr, Mn, Zr. Nevertheless, all the five substituting elements should most preferentially replace Fe in the j(2)' site, which has the greatest space among all six Fe sites. (C) 2005 Elsevier B.V. All rights reserved.