Upconversion luminescence and mechanisms in Yb3+-sensitized Tm3+-doped oxyhalide tellurite glasses

Effect of Yb2O3 content on upconversion luminescence and mechanisms in Yb3+-sensitized Tm3+-doped oxyhalide tellurite glasses were investigated under 980 nm excitation. Intense blue and relatively weak red upconversion emission centered at 476 and 649nm corresponding to the transitions (1)G(4) -> H-3(6) and (1)G(4) -> H-3(4) of Tm3+, respectively, are simultaneously observed at room temperature. The results show that upconversion blue and red emission intensities of Tm3+ first increase, reach its maximum at Yb2O3% = 3 mol%, and then decrease with increasing Yb2O3 content. The effect of Yb2O3 content on upconversion intensity is discussed, and possible effect mechanisms are evaluated. The investigated results were conducing to increase upconversion luminescence efficiency of Tm3+. (c) 2005 Elsevier B.V. All rights reserved.

Upconversion luminescence of TM3+/Yb3+ codoped oxyfluoride glasses

Novel oxyfluoride glasses are developed with the composition of 30SiO(2)-15Al(2)O(3)-28PbF(2)-22CdF(2)-0.1TmF(3)-xYbF(3) -(4.9-x) AlF3(x = 0, 0.5, 1.0, 1.5, 2.0) in mol fraction. Furthermore, the upconversion luminescence characteristics under a 970nm excitation are investigated. Intense blue, red and bear infrared luminescences peaked at 453nm, 476nm, 647nm and 789nm, which correspond to the transitions of Tm3+: D-1(2) -> F-3(4), (1)G(4) -> H-3(6), (1)G(4) -> F-3(4), and H-3(4) -> H-3(6), respectively, are observed. Due to the sensitization of Yb3+ ions, all the upconversion luminescence intensities are enhanced considerably with Yb3+ concentration increasing. The upconversion mechanisms are discussed based on the energy matching rule and quadratic dependence on excitation power. The results indicate that the dominant mechanism is the excited state absorption for those upconversion emissions.

Upconversion properties of TM3+/Yb3+ codoped fluorophosphate glasses with low phonon density of states

Fluorophosphate glasses codoped with Tm3+ and Yb3+ were prepared and their thermal stability, phonon states, and upconversion properties were studied. It is found that the increment of phosphate content is good for the thermal stability but increases the phonon density of states. However, the phonon density of states of these fluorophosphate glasses is very low due to the low phosphate content in their composition. The upconversion luminescence spectra were measured under excitation of 970 nm laser diode, and the intense blue (476 nm) and near infrared (794 nm) emission were simultaneous obtained at room temperature. The sensitizing mechanisms of Yb3+ to Tm3+ for blue and red emission contain both sequential and cooperative sensitization. The near infrared emission is a two-photon upconversion process. These researches suggest that when the phosphate content in the composition is low enough, fluorophosphate glass can be suitable host material of Tm3+ codoped with Yb3+ for blue and near infrared upconversion luminescence. (c) 2005 Elsevier B.V All rights reserved.

Spectroscopic properties and thermal stability of Er3+/Yb3+-codoped fluorophosphate glasses

A comprehensive study on the thermal stability and spectroscopic properties of Er3+/Yb3+-codoped Al(PO3)(3)-based fluorophosphate glasses is reported of the 1.5μ m fibre amplifiers in this paper. From optical absorption spectra, the Judd-Ofelt parameters of Er3+ in the glasses and several important optical properties, such as the radiative transition probability, the branching ratio and the spontaneous emission probability, have been calculated by using Judd-Ofelt theory. The fluorophosphate glass exhibits broadband near-infrared emission at 1.53μ m with a full width at half-maximum over 63nm, and a large calculated stimulated-emission cross-section of 6.85 x 10(-21)cm(2).

Effect of CdF2 addition on thermal stability and upconversion luminescence properties in Tm3+-Yb3+ codoped oxyfluoride silicate glasses

Tm3+-Yb3+ codoped oxyfluoride silicate glasses suitable for upconversion laser has been fabricated. In this paper, effect of CdF2 addition on thermal stability and upconversion luminescence properties in Tm3+-Yb3+ codoped oxyfluoride silicate glasses have been systematically investigated. The experimental results indicate that, with the substitution CdF2 for PbF2, the glass thermal stability increases and the UV cutoff edge moves to short-wave band slightly. With increasing CdF2 content, the blue and red upconversion luminescence intensity increases slightly at first, and then increases rapidly. While the near infrared (NIR) upconversion emission intensity increases notably at first and then increases slightly. However, the blue and NIR luminescence intensity are much stronger than that of red, indicating these oxyfluoride silicate glasses are more preferable for blue and NIR emissions than red emission. The possible upconversion mechanisms for the blue, red and NIR fluorescence are also estimated and evaluated. (c) 2006 Elsevier B.V. All rights reserved.

Comparative investigation of up-conversion luminescence in Tm3+/Yb3+-codoped germanate-niobic and germanium-bismuth glasses: effect of phonon density on up-conversion emission

Tm3+/Yb3+-codoped gernianate-niobic (GN) and germanium-bismuth (GB) glasses have been synthesized by conventional ruching and quenching method. Intense blue and weak red emissions centered at 477 and 650 nm, corresponding to the transitions (1)G(4)->H-3(6) and (1)G(4)->H-3(4), respectively, were observed at room temperature. The possible Up-conversion mechanisms are discussed and estimated. GN glass showed a weaker up-conversion emission than GB glass, which is inconsistent with the prediction from the difference of maximum phonon energy between GN and GB glasses. In this paper, Raman spectroscopy was employed to investigate the origin of the difference in up-conversion luminescence in the two glasses. Compared with phonon side-band spectroscopy, Raman spectroscopy extracts more information including both phonon energy and phonon density. For the first time, our results reveal that, besides the maximum phonon energy, the phonon density of host glasses is also an important factor in determining the up-conversion efficiency. (c) 2005 Elsevier Ltd. All rights reserved.

Effect of lithium-sodium mixed-alkali on phase transformation kinetics in Er3+/Yb3+ co-doped aluminophosphate glasses

Er3+ doped aluminophosphate glasses with various Na2O/Li2O ratios were prepared at 1250 degrees C using a silica crucible to study mixed alkali effect (MAE). The effect of relative alkali content on glass transition temperature, crystallization temperature and thermal stability were investigated using differential scanning calorimetry (DSC). In addition, apparent activation energies for crystallization, E, were determined employing the Kissinger equation. The effect of Al2O3 content on the magnitude of MAE was also discussed. No mixed-alkali effect is observed on crystallization temperature. (c) 2006 Elsevier B.V. All rights reserved.

Planar waveguides formed in a new chemically stable Er3+/Yb3+ co-doped phosphate glass

A new Er(3+)/Yb(3+) co-doped phosphate glass has been prepared, which exhibits good chemical durability and spectralproperties. Planar graded index waveguides have been fabricated in the glass by (Ag+)-Na(+) ion exchange in a mixed melt of silver nitrate and potassium nitrate. Ion exchange is carried out by varying the process parameters such as temperature, diffusion time, and molten salt compositions. The diffusion parameters, diffusion coefficients, and activation energy are determined by the guidelines of fabricated waveguides, which are determined by the input prism coupling technique.

Influence of TeO2, PbF2, ZnF2 on the spectroscopic and lasing properties of Yb3+ doped fluorophosphate glass

The influence of TeO2 on the crystallization stability, thermal stability, spectroscopic and lasing properties of Yb3+ doped fluorophosphate (FP) glass was studied. It is shown that 2 mol% TeO2 is the optimum doping amount which results in better spectroscopic and lasing properties as well as improve the crystallization and thermal stabilities of the glass. In order to enhance the physical and optical properties further, the effect of PbF2 and ZnF2 to the TeO2 contained FP glasses is also investigated, which shows that PbF2 has advantages in improving the crystallization properties while ZnF2 is preferable in enhancing spectroscopic and lasing properties. Results indicate that the co-existence of TeO2, PbF2 or ZnF2 is an effective way to enhance the spectroscopic, lasing and physical properties of Yb3+ doped FP glasses. (c) 2004 Published by Elsevier B.V.

Spectroscopic and fluorescence decay behaviors of Yb3+ -doped SiO2-PbO-Na2O-K2O glass

The spectroscopic and fluorescent decay behaviors of Yb3+-doped SiO2-PbO-Na2O-K2O glass is reported in this work. Yb2O3 contents of 1, 1.5 and 2mol% are added into the glass. Through the measurement of absorption and fluorescence spectra, and fluorescent decay rate at room temperature and at low temperature (18 K), it is found that the nonradiative decay rate of Yb3+ ions is mainly determined by the interaction between residual hydroxyl groups and Yb3+ ions. Concentration quenching effect can be omitted in this glass up to the Yb3+ ion concentration of 8.98 x 10(20)/cm(3). Multiphonon decay rate is also very small because of the large energy gap between F-2(5/2) and F-2(7/2) levels of Yb3+ ions. (c) 2004 Elsevier B.V. All rights reserved.

Effect of F- ions on spectroscopic properties of Yb3+-doped zinc-tellurite glasses

this paper is retracted

Enhanced broadband near-infrared luminescence in transparent silicate glass ceramics containing Yb3+ ions and Ni2+-doped Li Ga5 O8 nanocrystals

Spectral properties of Yb3+/Ni2+ codoped transparent silicate glass ceramics containing LiGa5O8 nanocrystals were investigated. The near-infrared emission intensity of Ni2+ was largely increased with Yb3+ codoping due to Yb3+-> Ni2+ energy transfer. The qualitative calculation of the energy transfer constant Cs-a and rate Ps-a showed that the Yb3+-> Ni2+ energy transfer was much greater than in the opposite direction. Yb3+/Ni2+ codoped glass ceramics with 0.75 mol % Yb2O3 exhibited a near-infrared emission with full width at half maximum of 290 nm and fluorescent lifetime of 920 mu s. The glass ceramics are promising for broadband optical amplification.

Upconversion Luminescence of Er3+-Yb3+ Codoped NaYF4-PVP Electrospun Nanofibers

NaYF4: 0.02Er center dot xYb-PVP composite nanofibers with the diameter of similar to 400 nm have been prepared by electrospinning. Field emission scanning electron microscope and X-ray diffraction have been utilized to characterize morphology and structure of the as-prepared electrospun nanofibers. Their up-conversion luminescence is investigated under a 980-nm excitation. Green (538 and 520 nm), red (6-55 nm), and blue (405 nm) emissions are observed in the up-conversion luminescence spectra, and the intensity of these three emissions changes differently with the variety of Yb content, which has been interpreted successfully in this letter. The color of NaYF4: 0.02Er center dot xYb-PVP nanolibers under a 980-nm excitation can be changed from green --> white --> yellow gradually via changing the Yb content.