Toxic effects of brake wear particles on epithelial lung cells in vitro

ABSTRACT: BACKGROUND: Fine particulate matter originating from traffic correlates with increased morbidity and mortality. An important source of traffic particles is brake wear of cars which contributes up to 20% of the total traffic emissions. The aim of this study was to evaluate potential toxicological effects of human epithelial lung cells exposed to freshly generated brake wear particles. RESULTS: An exposure box was mounted around a car's braking system. Lung cells cultured at the air-liquid interface were then exposed to particles emitted from two typical braking behaviours ("full stop" and "normal deceleration"). The particle size distribution as well as the brake emission components like metals and carbons was measured on-line, and the particles deposited on grids for transmission electron microscopy were counted. The tight junction arrangement was observed by laser scanning microscopy. Cellular responses were assessed by measurement of lactate dehydrogenase (cytotoxicity), by investigating the production of reactive oxidative species and the release of the pro-inflammatory mediator interleukin-8. The tight junction protein occludin density decreased significantly (p < 0.05) with increasing concentrations of metals on the particles (iron, copper and manganese, which were all strongly correlated with each other). Occludin was also negatively correlated with the intensity of reactive oxidative species. The concentrations of interleukin-8 were significantly correlated with increasing organic carbon concentrations. No correlation was observed between occludin and interleukin-8, nor between reactive oxidative species and interleukin-8. CONCLUSION: These findings suggest that the metals on brake wear particles damage tight junctions with a mechanism involving oxidative stress. Brake wear particles also increase pro-inflammatory responses. However, this might be due to another mechanism than via oxidative stress.

The boundary lubricated friction and wear of low alloy steel

Pin on disc wear machines were used to study the boundary lubricated friction and wear of AISI 52100 steel sliding partners. Boundary conditions were obtained by using speed and load combinations which resulted in friction coefficients in excess of 0.1. Lubrication was achieved using zero, 15 and 1000 ppm concentrations of an organic dimeric acid additive in a hydrocarbon base stock. Experiments were performed for sliding speeds of 0.2, 0.35 and 0.5 m/s for a range of loads up to 220 N. Wear rate, frictional force and pin temperature were continually monitored throughout tests and where possible complementary methods of measurement were used to improve accuracy. A number of analytical techniques were used to examine wear surfaces, debris and lubricants, namely: Scanning Electron Microscopy (SEM), Auger Electron Spectroscopy (AES), Powder X-ray Diffraction (XRD), X-ray Photoelectron Spectroscopy (XPS), optical microscopy, Back scattered Electron Detection (BSED) and several metallographic techniques. Friction forces and wear rates were found to vary linearly with load for any given combination of speed and additive concentration. The additive itself was found to act as a surface oxidation inhibitor and as a lubricity enhancer, particularly in the case of the higher (1000 ppm) concentration. Wear was found to be due to a mild oxidational mechanism at low additive concentrations and a more severe metallic mechanism at higher concentrations with evidence of metallic delamination in the latter case. Scuffing loads were found to increase with increasing additive concentration and decrease with increasing speed as would be predicted by classical models of additive behaviour as an organo-metallic soap film. Heat flow considerations tended to suggest that surface temperature was not the overriding controlling factor in oxidational wear and a model is proposed which suggests oxygen concentration in the lubricant is the controlling factor in oxide growth and wear.

The Mechanisms of wear of the video head

      This thesis examines the mechanism of wear occuring to the video head and their effect on signal reproduction. in particular it examines the wear occuring to manganese-zinc ferrite heads in sliding contact with iron oxide media.       A literature survey is presented, which covers magnetic recording technologies, focussing on video recording. Existing work on wear of magnetic heads is also examined, and gaps in the theoretical account of wear mechanisms presented in the literature are identified.       Pilot research was carrried out on the signal degradation and wear associated witha number of commercial video tapes, containing a range of head cleaning agents. From this research, the main body of the research was identified. A number of methods of wear measurement were examined for use in this project. Knoop diamond indentation was chosen because experimentation showed it to be capable of measuring wear occuring in situ. This technique was then used to examine the wear associated with different levels of A12O3 and Cr2O3 head cleaning agents.      The results of the research indicated that, whilst wear of the video head increases linearly with increasing HCA content, signal degradation does not vary significantly. The most significant differences in wear and signal reproduction were observed between the two HCAs. The signal degradation of heads worn with tape samples containing A12O3 HCA was found to be lower than heads worn with tapes containing Cr2O3 HCA.      The results also indicate that the wear to the head is an abrasive process characterised by ploughing of the ferrite surface and chipping of the edges of the head gap. Both phenomena appear to be caused by poor iron oxide and head cleaning particles, which create isolated asperities on the tape surface.   

The transition from severe to mild wear in law alloy steel

The wear rates of sliding surfaces are significantly reduced if mild oxidational wear can be encouraged. It is hence of prime importance in the interest of component life and material conservation to understand the factors necessary to promote mild, oxidational wear, The present work investigates the fundamental mechanism of the running-in wear of BS EN 31!EN 8 steel couples. under various conditions of load. speed and test duration. Unidirectional sliding experiments were carried out on a pin-on~disc wear machine where frictional force, wear rate, temperature and contact resistance were continuously monitored during each test. Physical methods of analysis (x-ray, scanning electron microscopy etc.) were used to examine the wear debris and worn samples. The wear rate versus load curves revealed mild wear transitions, which under long duration of running, categorized mild wear into four distinct regions.α-Fe20s. Fe304, FeO and an oxide mixture were the predominant oxides in four regions of oxidational wear which were identified above the Welsh T2 transition. The wear curves were strongly effected by the speed and test duration. A surface model was used to calculate the surface parameters, and the results were found to be comparable with the experimentally observed parameters. Oxidation was responsible for the transition from severe to mild wear at a load corresponding to the Welsh T2 transition. In the running-in period sufficient energy input and surface hardness enabled oxide growth rate to increase and eventually exceeded the rate of removal, where mild wear ensued. A model was developed to predict the wear volume up to the transition. Remarkable agreement was found between the theoretical prediction and the experimentally-measured values. The oxidational mechanjsm responsible for transitjon to mild wear under equilibrium conditions was related to the formation of thick homogenous oxide plateaux on subsurface hardened layers, FeO was the oxide formed initially at the onset of mild wear but oxide type changed.during the total running period to give an equilibrium oxide whose nature depended on the loads applied.