Effects of the high-temperature plasma immersion ion-implantation treatment on corrosion behavior of Ti-6Al1-4V

Nitrogen implantation into Ti alloys at higher temperatures improves their mechanical and corrosion resistance properties by forming a thicker nitride layer. In this paper, two different sets of Ti-6Al-4V samples were plasma immersion ion implantation (PIII)-treated using nitrogen plasma, varying the treatment time from 30 to 150 min (800 degrees C) and the process temperature from 400 degrees C to 800 degrees C (t = 60 min). Nanoindentation measurements of the PIII-treated samples at 800 C during 150 min showed the highest hardness value, 24 GPa, which is about four times bigger than untreated sample hardness. The N penetration at these conditions reached approximately 150 nm as analyzed by Auger spectroscopy. on the other hand, the lowest passive current density (3 x 10(-7) A. cm(-2)) was obtained for a PIII-treated sample during 30 min at higher temperature (800 degrees C). The corrosion resistance of this sample is almost the same as for the untreated specimen. Corrosion behavior evidenced that in strong oxidizing media, all PIII-treated samples are more corrosion resistant than the untreated one. PIII processing at higher temperatures promotes smoothing of the sample surface as observed by scanning electron microscopy (SEM). Grazing incidence X-ray diffraction analyses of the untreated samples identified the two typical Ti phases, Ti alpha and Ti beta. After the implantation, Ti2N and TiO2 phases were also detected.

Influência da dopagem com oxigênio nas propriedades anelásticas e biocompatibilidade de ligas Ti-5%pNb e Ti-10%pNb

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Efeito de elementos substitucionais e intersticiais na microestrutura, dureza e módulo de elasticidade de ligas Ti-Nb

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of heat treatment and mechanical cycling on hardness and fracture analysis of Ti35Nb5Zr casting alloy

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Chemical And Structural Analyses Of Titanium Plates Retrieved From Patients.

The aim of this study was to evaluate the microscopic structure and chemical composition of titanium bone plates and screws retrieved from patients with a clinical indication and to relate the results to the clinical conditions associated with the removal of these devices. Osteosynthesis plates and screws retrieved from 30 patients between January 2010 and September 2013 were studied by metallographic, gas, and energy dispersive X-ray (EDX) analyses and the medical records of these patients were reviewed. Forty-eight plates and 238 screws were retrieved. The time elapsed between plate and screw insertion and removal ranged between 11 days and 10 years. Metallographic analysis revealed that all the plates were manufactured from commercially pure titanium (CP-Ti). The screw samples analyzed consisted of Ti-6Al-4V alloy, except four samples, which consisted of CP-Ti. Titanium plates studied by EDX analysis presented greater than 99.7% titanium by mass. On gas analysis of Ti-6Al-4V screws, three samples were outside the standard values. One CP-Ti screw sample and one plate sample also presented an oxygen analysis value above the standard. The results indicated that the physical properties and chemical compositions of the plates and screws did not correspond with the need to remove these devices or the time of retention.

Corrosion resistance improvement of titanium base alloys

The corrosion resistance of the new Ti-6Al-4V-1Zr alloy in comparison with ternary Ti-6Al-4V alloy in Ringer-Brown solution and artificial Carter-Brugirard saliva of different pH values was studied. In Ringer-Brown solution, the new alloy presented an improvement of all electrochemical parameters due to the alloying with Zr; also, impedance spectra revealed better protective properties of its passive layer. In Carter-Brugirard artificial saliva, an increase of the passive film thickness was proved. Fluoride ions had a slight negative influence on the corrosion and ion release rates, without to affect the very good stability of the new Ti-6Al-4V-1Zr alloy.

An investigation on sliding wear behavior of PVD coatings

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Caracterizacion metalografica de aleaciones metalicas utilizadas como biomateriales en implantes quirurgicos

In this work, the chemical structure, the microstructure and the surface morphology of two non-ferrous materials used in dental implants (Ti-6Al-4V and Co-Cr-Mo) were studied. This was done by chemical analysis, scanning electron microscopy (SEM), energy disperse spectroscopy (EDS), and strength measurements (HV). Metallographic studies reveal that titanium alloy surface present a fine granular binary phase structure, while cobalt alloy present cast dendrite structures with an intense precipitation of carbides. To correlate the macro and microstructure with the mechanical behavior of the material, microhardness measurements were performed. Using the Vickers hardening method, the Ti-6Al-4V alloy yielded strength mean values smaller than the Co-Cr-Mo alloy. Their values are associated to the chemical composition and to the microstructural distribution of these materials. The Ti-6Al-4V alloy presents hardness similar to dental enamel, which suggests better performance as dental implant.

Materialografia quantitativa de micro estruturas complexas baseada na segmentação por texturas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Desenvolvimento, comportamento mecânico e microestrutural de uma prótese mandibular em liga de titânio produzida por sinterização direta a laser de metal (DMLS)

Pós-graduação em Engenharia Mecânica - FEIS

Fadiga em titânio aeronaútico revestido por PVD

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Desenvolvimento de pastilhas cerâmicas à bases de Si3N4 para aplicações tribológicas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliações biomecânicas e biológicas relacionadas às próteses implanto-suportadas e aos implantes osseointegrados

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Comparação in vivo da biocompatilidade de amostras com superfície porosa confeccionadas com diferentes ligas de titânio

Pós-graduação em Biopatologia Bucal - ICT

Cimentação de coroas com fosfato de zinco sobre munhões de liga de titânio, irradiados ou não por laser

By means of tensile strength, NiCr total crowns were removed from machine-made conical abutments composed by an Ti-6Al-4V alloy. In a total of 20 abutments, 10 were used with it surface presenting high smoothness and 10 abutments had its surfaces modifi ed by laser both cemented with zinc phosphate. The mechanical test was performed at a MTS 810 universal machine adjusted to a speed of 0.5 mm/m. The statistical analysis was done by Levene’s test, which showed homogeneity of variances among groups (F =2.21; p < 0.1). “Student t test” showed that signifi cant differences were found between groups. The modifi cation of the abutment surface through laser caused an increase in pull-out resistance of crowns cemented with zinc phosphate from 430.66 N to 1.514,87 N.