SiO2 对Bi2O3-B2O3 玻璃体系光学、热学及结构的 影响

Glasses with compositions 50Bi2O3-xB2O3- (50-x)SiO2(x=0, 10, 20, 30, 40, 50) in mol% have been prepared by using a normal melt-quench technique. The effect of SiO2 addition on thermal stability, optical properties and structural characteristic on Bi2O3-B2O3 glass were systematically investigated by using XRD, DTA, ultraviolet-visible transmittance spectra, midinfrared transmittance spectra and Raman spectra. The experimental results demonstrate that, with the addition of SiO2, thermal stability of glass samples has been obviously improved. Once the amount of SiO2 is too much, the glass samples tend to be phase seperation which results in the decrease of thermal stability. With increasing SiO2 content, the UV cutoff edge firstly shifts to short-wave band and then shifts to long-wave band, and the transmittance of mid-infrared has been greatly improved. With substitution of SiO2 for B2O3, the [BO3] triangles and [BO4] tetrahedral groups are gradually replaced by [SiO4]. [BiO6] octahedral and [SiO4] tetrahedral units are connected forming a vibrational mode of Bi-O-Si. The physical chemistry and optical performance of Bi2O3-B2O3 glass were greatly improved by addition of SiO2.

Solid-state NMR study of bioactive binary borosilicate glasses

A series of binary borosilicate glasses prepared by the sol-gel method are shown to be bioactive. Tetraethyl orthosilicate (TEOS) and trimethylborate (TMB) in acidic medium are used to prepare xB(2)O(3)center dot(1-x)SiO2 glass systems for x = 0.045-0.167. The formation of a layer of apatite-like mineral on the glass surface becomes apparent after soaking in simulated body fluid for 48 h. We have measured the B-11-B-11 homonuclear second moments of the borosilicate glasses and inferred that no macroscopic phase separation occurred in our glasses. The B-11 chemical shift data also show that the formation of clustered boroxol rings is negligible in our glass system. Although the bioactivity of our borosilicate glasses is less than that of CaO-SiO2 sol-gel glasses, these simple binary systems could be taken as reference glass systems for the search of new bioactive borosilicate glasses. (C) 2008 Elsevier Ltd. All rights reserved.

Phi 140 mm sapphire crystal growth by temperature gradient techniques and its color centers

Sapphire crystals, 140 mm in diameter and 90 turn in height, have been grown by temperature gradient techniques (TGT). The growth direction of the boule was fixed by means of Lane X-ray diffraction. A prominent 204 nm absorption band in TGT-Al2O3. which does not appear in single crystals grown by Czochralski method has been studied. Analysis further substantiates the F-center model of this band. Two relatively weaker bands absorbing at 232 nm and 254 nm were ascribed to F+ centers. F-type centers concentration was determined using Smakula's equation. (c) 2005 Elsevier B.V. All rights reserved.

Color centers and charge state change in Ce : YAG crystals grown by temperature gradient techniques

Color centers and impurity defects of Ce:YAG crystals grown in reduction atmosphere by temperature gradient techniques have been investigated by means of gamma irradiation and thermal treatments. Four absorption bands associated with color centers or impurity defects at 235, 255, 294 and 370 nm were observed in as-grown crystals. Changes in optical intensity of the 235 and 370 nm bands after gamma irradiation indicate that they are associated with F+-type color center. Charge state change processes of Fe3+ impurity and Ce3+ ions take place in the irradiation process. The variations of Ce3+ ions concentration clearly indicate that Ce4+ ions exist in Ce:YAG crystals and gamma irradiations could increase the concentration of Ce3+ ions. Annealing treatments and the changes in optical density suggest that a heterovalent impurity ion associated with the 294 nm band seems to be present in the crystals. (c) 2005 Elsevier B.V. All rights reserved.