Nanostructured GdxZn1-xO thin films by nebulizer spray pyrolysis technique: Role of doping concentration on the structural and optical properties

Nanostructured GdxZn1-xO thin films with different Gd concentration from 0% to 10% deposited at 400 degrees C using the NSF technique. The films were characterized by structural, surface and optical properties, respectively. X-ray diffraction analysis shows that the Gd doped ZnO films have lattice parameters a = 3.2497 angstrom and c = 5.2018 angstrom with hexagonal structure and preferential orientation along (002) plane. The estimated values compare well with the standard values. When film thickness increases from 222 to 240 nm a high visible region transmittance (>70%) is observed. The optical band gap energy, optical constants (n and k), complex dielectric constants (epsilon(r), and epsilon(i)) and optical conductivities (sigma(r), and sigma(i)) were calculated from optical transmittance data. The optical band gap energy is 3.2 eV for pure ZnO film and 3.6 eV for Gd0.1Zn0.9-O film. The PL studies confirm the presence of a strong UV emission peak at 399 nm. Besides, the UV emission of ZnO films decreases with the increase of Gd doping concentration correspondingly the ultra-violet emission is replaced by blue and green emissions.

Synthesis, structural and optical properties of nanocrystalline Ba2NaNb5O15

Fine powders comprising nanocrystallites of barium sodium niobate, Ba2NaNb5O15 (BNN) were obtained via a citrate assisted sol-gel route at a much lower temperature than that of the conventional solid-state reaction route. The phase evolution of BNN as a function of temperature was investigated by thermogravimetric analysis (TGA), differential thermal analysis (DTA), Fourier transform infrared spectroscopy (FTIR) and X-ray powder diffraction (XRD). DTA data followed by XRD studies confirmed the BNN formation temperature to be around 923 K. The as-synthesized powders heat-treated at 923 K/10 h attained an orthorhombic structure akin to that of the parent BNN phase. Transmission electron microscopy revealed that the nanocrystallites are associated with dislocations. The optical band gap was calculated using the Kubelka-Munk function. These nanocrystallites exhibited strong visible photoluminescence (PL) at room temperature. The PL mechanism was explained by invoking the dielectric confinement effect, defect states and generation of self-trapped excitons.

Pr6O11 micro-spherical nano-assemblies: microwave-assisted synthesis, characterization and optical properties

We report the synthesis of Pr6O11 microspheres self-assembled from ultra-small nanocrystals formed by the microwave irradiation of a solution of a salt of Pr in ethylene glycol (EG). The as-prepared product consists of microspheres measuring 200 to 500 nm in diameter and made of <5 nm nano-crystallites. The surface of these microspheres/nanocrystals is covered/capped with an organic layer of ethylene glycol as shown by TEM analysis and confirmed by IR spectroscopy measurements. The as-prepared product shows blue-green emission under excitation, which changes to orange-red when the product is annealed in air at 600 degrees C for 2 h. This change in luminescence behaviour can be attributed to presence of ethylene glycol layer in the as-prepared product. The samples were characterized by X-ray powder diffraction (XRD), field emission scanning electron microscopy (FE-SEM), IR Spectroscopy (IR), transmission electron microscopy (TEM), and thermogravimetric analysis (TGA). (C) 2013 Elsevier B.V. All rights reserved.

Novel spherical hierarchical structures of GdOOH and Eu:GdOOH: rapid microwave-assisted synthesis through self-assembly, thermal conversion to oxides, and optical studies

We report a novel, rapid, and low-temperature method for the synthesis of undoped and Eu-doped GdOOH spherical hierarchical structures, without using any structure-directing agents, through the microwave irradiation route. The as-prepared product consists of nearly monodisperse microspheres measuring about 1.3 mu m in diameter. Electron microscopy reveals that each microsphere is an assembly of two-dimensional nanoflakes (about 30 nm thin) which, in turn, result from the assembly of crystallites measuring about 9 nm in diameter. Thus, a three-level hierarchy can be seen in the formation of the GdOOH microspheres: from nanoparticles to 2D nanoflakes to 3D spherical structures. When doped with Eu3+ ions, the GdOOH microspheres show a strong red emission, making them promising candidates as phosphors. Finally, thermal conversion at modest temperatures leads to the formation of corresponding oxide structures with enhanced luminescence, while retaining the spherical morphology of their oxyhydroxide precursor.

Ferroelectric and optical properties of Ba5Li2Ti2Nb8O30 ceramics potential for memory applications

Giant grained (42 mu m) translucent Ba5Li2Ti2Nb8O30 ceramic was fabricated by conventional sintering technique using the powders obtained via solid state reaction route. These samples were confirmed to possess tetragonal tungsten bronze structure (P4bm) at room temperature. The scanning electron microscopy established the average grain size to be close to 20 mu m. The photoluminescence studies carried out on these ceramics indicated sharp emission bands around 433 and 578 nm at an excitation wavelength of 350 nm which were attributed to band-edge emission as the band gap was 2.76 eV determined by Kubelka-Munk function. The dielectric properties of these ceramics were studied over wide frequency range (100-1 MHz) at room temperature. The decrease in dielectric constant with frequency could be explained on the basis of Koops theory. The dielectric constant and the loss were found to decrease with increasing frequency. The Curie temperature was confirmed to be similar to 370 A degrees C based on the dielectric anomaly observed when these measurements were carried out over a temperature range of 30-500 A degrees C. This shows a deviation from Curie-Weiss behaviour and hence an indicator of the occurrence of disordering in the system, the gamma = 1.23 which confirms the diffuse ferroelectric transition. These ceramics at room temperature exhibited P-E hysteresis loops, though not well saturated akin to that of their single crystalline counterparts. These are the suitable properties for ferroelectric random access memory applications.

Doping effect of Ag+, Mn2+ ions on Structural and Optical Properties of ZnO nanoparticles

Pure ZnO and co-doped (Mn, Ag) ZnO nanoparticles have been successfully prepared by chemical co-precipitation method without using a capping agent. X-ray diffraction (XRD) studies confirms the presence of wurtzite (hexagonal) crystal structure similar to undoped ZnO, suggesting that doped Mn, Ag ions are substituted to the regular Zn sites. The morphology of the samples were studied by scanning electron microscopy (SEM). The chemical composition of pure and co-doped ZnO nanoparticles were characterized by energy dispersive X-ray analysis spectroscopy (EDAX). Optical absorption properties were determined by UV-vis Diffuse Reflectance Spectrophotometer. The incorporation of Ag+, Mn2+ in the place of Zn2+ provoked to decrease the size of nanocrystals as compared to pure ZnO. Optical absorption measurements indicates blue shift in the absorption band edge upon Ag, Mn ions doped ZnO nanoparticles.

Structural and optical characterization of nonpolar (10-10) m-InN/m-GaN epilayers grown by PAMBE

Plasma-assisted molecular beam epitaxy growth of (10-10) m-InN/(10-10) m-GaN was carried out on bare (10-10) m-sapphire substrate. The high resolution X-ray diffraction studies confirmed the orientation of the as-grown films. Nonpolar InN layer was grown at different growth temperatures ranging from 390 degrees C to 440 degrees C and the FWHM of rocking curve revealed good quality film at low temperatures. An in-plane relationship was established for the hetrostructures using phi-scan and a perfect alignment was found for the epilayers. Change of morphology of the films grown at different temperatures was observed using an atomic force microscopy technique showing the smoothest film grown at 400 degrees C. InN optical band gap was found to be vary from 0.79-0.83 eV from absorption spectra. The blue-shift of absorption edge was found to be induced by excess background electron concentration. (C) 2015 Elsevier B.V. All rights reserved.

Evaporation-Condensation Synthesis and Optical Property of In(2)O(3)Octahedrons

Synthesis of In2O3 octahedrons is carried out successfully by heating Indium metal pieces in air ambient. The sample is characterized by scanning electron microscopy (SEM), Energy dispersive X-ray spectroscope (EDS), X-ray diffraction (XRD) and Raman spectroscopy. The as-prepared In2O3 octahedrons are highly crystalline and exhibit body centered cubic structure. Room temperature and temperature (293-453K) dependence photoluminescence reveals a deep levelbroad emission of yellowish-orange spectra centered around 605 nm. The emission is due to the presence of defect levels in the band gap of materials.

Growth and optical properties of peculiar ZnO tetrapods

Regular ZnO tetrapods with different morphologies have been obtained on Si(100) substrate via the chemical vapour deposition approach. Varying the growth temperature and gas rate, we have obtained different structured ZnO materials: tetrapods with a large hexagonal crown, a flat top and a small hexagonal crown. The results suggest that these tetrapods are all single crystals with a wurtzite structure that grow along the (0001) direction. However, photoluminescence spectra shows that their optical properties are quite different: for those with large hexagonal crown, the green emission overwhelms that of the near band-edge (NBE) ultraviolet (UV) peak, while others have only a strong NBE UV peak at ~386 nm.

Thermal, structural and optical properties of NiOx thin films deposited by reactive dc-magnetron sputtering

The NiOx thin films were deposited by reactive dc-magnetron sputtering from a nickel metal target in Ar + O-2 with the relative O-2 content 5%. The as-deposited NiOx, thin films could represent a two-component system comprising crystalline NiO particles dispersed in an amorphous Ni2O3. Decomposition temperature of the as-deposited NiO, thin films was at about 263 degrees C. After annealed at 400 degrees C for 30 min in air, the surface morphology of the films became very rough due to the decomposition of the Ni2O3, leading to the changes of the optical properties of the NiO, thin films. The reflectivity of the films annealed at 400 degrees C was lower than that of the as-deposited one and the optical contrast was 52% at 405 nm. (c) 2006 Elsevier B.V. All rights reserved.

Growth, characterization and optical quality of CaF2 single crystals grown by the temperature gradient technique

The CaF2 single crystals with diameters up to 200 mm were successfully grown by modified temperature gradient technique (TGT), which are suitable for application as optical elements in the ultraviolet range. The optimizations of various growth parameters were systematically studied. Properties of as-grown CaF2 crystals were characterized by the nature of inclusions, dislocations, crystallinity, and impurities contents. The results showed that the dislocations and multinucleation were mostly constrained in the conical part of the crystals with the cylindrical parts having the best crystalline quality and lowest impurity contents. The high optical quality of TGT-grown CaF2 single crystals was also confirmed to have excellent optical transmission in 190-2500 nm and refractive index homogeneity. (c) 2005 Elsevier Ltd. All rights reserved.

Crystal growth and optical properties of Gd1.99-xYxCe.0.01SiO5 single crystals

Gd1.99-xYxCe0.01SiO5 (Ce:GYSO) crystals (x = 0, 0.0995, 0.199) have been grown by the Czochralski (Cz) method. Crystal structure and the distribution coefficients of Ce have been determined for all three crystals. Spectroscopic measurements indicate that optical transmittance and luminescence intensity of Gd1.99-xYxCe0.01SiO5 (x = 0.0995, 0.199) crystals are Substantially higher than those of Ce:Gd2SiO5 (Ce:GSO), especially at x = 0.0995, which makes them good candidate materials for scintillation applications. The particularly important result is that the alloyed Ce:GYSO crystals can be grown easily by the Cz method and, unlike Ce:GSO, they do not undergo cleavage during the growth process or subsequent mechanical treatment. (c) 2005 Elsevier B.V. All rights reserved.