Influence of rare earth doping on the structural and catalytic properties of nanostructured tin oxide

Nanoparticles of tin oxide, doped with Ce and Y, were prepared using the polymeric precursor method. The structural variations of the tin oxide nanoparticles were characterized by means of nitrogen physisorption, carbon dioxide chemisorption, X-ray diffraction, and X-ray photoelectron spectroscopy. The synthesized samples, undoped and doped with the rare earths, were used to promote the ethanol steam reforming reaction. The SnO2-based nanoparticles were shown to be active catalysts for the ethanol steam reforming. The surface properties, such as surface area, basicity/base strength distribution, and catalytic activity/selectivity, were influenced by the rare earth doping of SnO2 and also by the annealing temperatures. Doping led to chemical and micro-structural variations at the surface of the SnO2 particles. Changes in the catalytic properties of the samples, such as selectivity toward ethylene, may be ascribed to different dopings and annealing temperatures.

Estudo da segregação de dopantes no contorno de grão e sua influência nas propriedades elétricas de cerâmicas à base de 'SN''O IND.2'

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Translucent tin dioxide ceramics obtained by natural sintering

Dense SnO2-based ceramics (relative density >95%) have been obtained by natural sintering at a moderate temperature (less than or equal to 1300 degrees C) with the help of a small amount of manganese, Further thermal treatments above 1500 degrees C result in grain growth and transport of manganese toward the sample surface. If the ceramic is embedded inside alumina powder, the diffusion of Mn out of the sample and into alumina during such heat treatments leads to a manganese-free body (<40 ppm) which is translucent. The transmission in the visible region depends on sample thickness; 61% was achieved for a 0.05 mm thick sample.

Engineering thin films of magnetic alloys and semiconductor oxides at the nanoscale

The thesis aims to exploit properties of thin films for applications such as spintronics, UV detection and gas sensing. Nanoscale thin films devices have myriad advantages and compatibility with Si-based integrated circuits processes. Two distinct classes of material systems are investigated, namely ferromagnetic thin films and semiconductor oxides. To aid the designing of devices, the surface properties of the thin films were investigated by using electron and photon characterization techniques including Auger electron spectroscopy (AES), X-ray photoelectron spectroscopy (XPS), grazing incidence X-ray diffraction (GIXRD), and energy-dispersive X-ray spectroscopy (EDS). These are complemented by nanometer resolved local proximal probes such as atomic force microscopy (AFM), magnetic force microscopy (MFM), electric force microscopy (EFM), and scanning tunneling microscopy to elucidate the interplay between stoichiometry, morphology, chemical states, crystallization, magnetism, optical transparency, and electronic properties. Specifically, I studied the effect of annealing on the surface stoichiometry of the CoFeB/Cu system by in-situ AES and discovered that magnetic nanoparticles with controllable areal density can be produced. This is a good alternative for producing nanoparticles using a maskless process. Additionally, I studied the behavior of magnetic domain walls of the low coercivity alloy CoFeB patterned nanowires. MFM measurement with the in-plane magnetic field showed that, compared to their permalloy counterparts, CoFeB nanowires require a much smaller magnetization switching field , making them promising for low-power-consumption domain wall motion based devices. With oxides, I studied CuO nanoparticles on SnO2 based UV photodetectors (PDs), and discovered that they promote the responsivity by facilitating charge transfer with the formed nanoheterojunctions. I also demonstrated UV PDs with spectrally tunable photoresponse with the bandgap engineered ZnMgO. The bandgap of the alloyed ZnMgO thin films was tailored by varying the Mg contents and AES was demonstrated as a surface scientific approach to assess the alloying of ZnMgO. With gas sensors, I discovered the rf-sputtered anatase-TiO2 thin films for a selective and sensitive NO2 detection at room temperature, under UV illumination. The implementation of UV enhances the responsivity, response and recovery rate of the TiO2 sensor towards NO2 significantly. Evident from the high resolution XPS and AFM studies, the surface contamination and morphology of the thin films degrade the gas sensing response. I also demonstrated that surface additive metal nanoparticles on thin films can improve the response and the selectivity of oxide based sensors. I employed nanometer-scale scanning probe microscopy to study a novel gas senor scheme consisting of gallium nitride (GaN) nanowires with functionalizing oxides layer. The results suggested that AFM together with EFM is capable of discriminating low-conductive materials at the nanoscale, providing a nondestructive method to quantitatively relate sensing response to the surface morphology.

Electronic ceramics based on polycrystalline SnO2, TiO2 and (Sn xTi1-x)O2 solid solution

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Propriedades elétricas e modelagem da barreira de potencial do sistema varistor à base de SnO2-TiO2

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Grain-boundary segregation and precipitates in La2O3 and Pr2O3 doped SnO2 center dot CoO-based varistors

Structural heterogeneities in SnO2.CoO-based varistors were analyzed by transmission electron microscopy. In SnO2.CoO-based system doped with La2O3 and Pr2O3 two kinds of precipitate phases at grain boundary region were found. Using energy dispersive spectrometry they were found to be Co2SnO4 and Pr2Sn2O7, presenting a defined crystalline structure. It was also identified that such precipitate phases are mainly located in triple-junctions of the microstructure. HRTEM analysis revealed the existence of other two types of junctions, one as being homo-junctions of SnO2 grains and other due to twin grain boundaries inside the SnO2.CoO grain. The role of these types of junction in the overall nonlinear electrical features is also discussed. (C) 2003 Elsevier B.V. Ltd. All rights reserved.

The influence of yttrium on a typical SnO2 varistor system: Microstructural and electrical features

The influence of yttrium oxide, Y2O3, on the microstructure development of the SnO(2)center dot Co(3)O(4)center dot Nb2O5 typical varistor system was studied with scanning (SEM) and transmission (TEM) electron microscopies. The different phases present in the studied samples were characterized through XRD, EDS and selected area diffraction patterns (SAD). Particles of Co2SnO4 were observed with TEM in every sample, whereas clusters of the pyrochlore phase T2Sn2O7 were observed with SEM in samples with 0.05, 0.10 and 0.25 mol% of Y2O3. The higher non-linearity (a = 16) was achieved with the addition of 0.05 mol% of Y2O3. The influence of the secondary phases on the electrical properties is also addressed in this work. (c) 2005 Published by Elsevier B.V.

Planar waveguides based on nanocrystalline and Er3+ doped SnO2

Luminescent SnO2: x%mol Er3+ (x=0.1-2.0) thin films have been spin coated on borosilicate and silica substrates from water colloidal suspensions that could be prepared containing up to 40% in weight SnO2 nanocrystalline powders. High Resolution Transmission Electron Microscopy results show the well known SnO2 cassiterite structure and nanocrystallites around 10 nm in diameter, corroborating results from X-ray diffraction. Mono and multi layers have been prepared from the stable colloidal suspensions and films thickness was observed to increase linearly, up to 200 nm, with the colloidal suspensions nanoparticles amount. Excitation and emission spectra have been measured and Er3+ ions were found to be essentially incorporated into the cassiterite structure, substituting for Sn4+, for doping concentration lower than 0.05 mol%. Er3+ ions also appear segregated at the grains surface for higher doping concentration. The optical parameters (refractive index, thickness and propagating modes) of a waveguide sample were measured at 632.8 and 543.4 nm by the prism coupling technique. A monomodal waveguide was obtained with attenuation loss of 3.5 dB/cm along a 2.5 cm optical path.

Investigation of the electrical properties of SnO2 varistor system using impedance spectroscopy

The electrical properties of tin oxide varistors doped with CoO, Nb2O5 and Cr2O3, were investigated using the impedance spectroscopy technique with the temperature ranging from 25 to 400 degrees C. The impedance data, represented by means of Nyquist diagrams, show two time constants with different activation energies, one at low frequencies and the other at high frequencies. These activation energies were associated with the adsorption and reaction of O-2 species at the grain boundary interface. The Arrhenius plots show two slopes with a turnover at 200 degrees C for both the higher and lower frequency time constants. This behavior can be related with the decrease of minor charge carrier density. The barrier formation mechanism was associated with the presence of Cr-Sn at the surface, which promotes the adsorption of the O' and O species which are in turn proposed as being responsible for the barrier formation. (C) 1998 American Institute of Physics. [S0021-8979(98)04719-7]

Investigation of electrical properties of tantalum doped SnO2 varistor system

Ta2O5 doped SnO2 varistor systems containing 0.5 mol% ZnO and 0.5 mol% Coo were prepared by mixed oxide method. Considering that ZnO and Coo oxides are densification additives only the SnO(2)center dot ZnO center dot CoO ceramics cannot exhibit electrical nonlinearity. A small amount of Ta2O5 improves the nonlinear properties of the samples greatly. The height and width of the defect barriers were calculated. It was found that samples doped with 0.05 mol% Ta2O5 exhibit the highest density (98.5%), the lowest electric breakdown field (E-b = 1100 V/cm) and the highest coefficient of nonlinearity (alpha = 11.5). The effect of Ta2O5 dopant could be explained by the substitution of Ta5+ by Sn4+. A grain-boundary defect barrier model for the SnO(2)center dot ZnO center dot CoO center dot Ta2O5 varistor system was also introduced. (c) 2004 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

The effect of TiO(2) on the microstructural and electrical properties of low voltage varistor based on (Sn,Ti)O(2) ceramics

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Self-assembled SnO2 micro- and nanosphere-based gas sensor thick films from an alkoxide-derived high purity aqueous colloid precursor

Tin oxide is considered to be one of the most promising semiconductor oxide materials for use as a gas sensor. However, a simple route for the controllable build-up of nanostructured, sufficiently pure and hierarchical SnO2 structures for gas sensor applications is still a challenge. In the current work, an aqueous SnO2 nanoparticulate precursor sol, which is free of organic contaminants and sorbed ions and is fully stable over time, was prepared in a highly reproducible manner from an alkoxide Sn(OR)4 just by mixing it with a large excess of pure neutral water. The precursor is formed as a separate liquid phase. The structure and purity of the precursor is revealed using XRD, SAXS, EXAFS, HRTEM imaging, FTIR, and XRF analysis. An unconventional approach for the estimation of the particle size based on the quantification of the Sn-Sn contacts in the structure was developed using EXAFS spectroscopy and verified using HRTEM. To construct sensors with a hierarchical 3D structure, we employed an unusual emulsification technique not involving any additives or surfactants, using simply the extraction of the liquid phase, water, with the help of dry butanol under ambient conditions. The originally generated crystalline but yet highly reactive nanoparticles form relatively uniform spheres through self-assembly and solidify instantly. The spheres floating in butanol were left to deposit on the surface of quartz plates bearing sputtered gold electrodes, producing ready-for-use gas sensors in the form of ca. 50 μm thick sphere-based-films. The films were dried for 24 h and calcined at 300°C in air before use. The gas sensitivity of the structures was tested in the temperature range of 150-400°C. The materials showed a very quickly emerging and reversible (20-30 times) increase in electrical conductivity as a response to exposure to air containing 100 ppm of H2 or CO and short (10 s) recovery times when the gas flow was stopped.

Nanocrystalline SnO2 by liquid pyrolisis

Liquid pyrolysis is presented as a new production method of SnO2 nanocrystalline powders suitable for gas sensor devices. The method is based on a pyrolytic reaction of high tensioned stressed drops of an organic solution of SnCl4·5(H2O). The main advantages of the method are its capability to produce SnO2 nanopowders with high stability, its accurate control over the grain size and other structural characteristics, its high level of repeatability and its low industrialization implementation cost. The characterization of samples of SnO2 nanoparticles obtained by liquid pyrolysis in the range between 200ºC and 900ºC processing temperature is carried out by X-ray diffraction, transmission electron microscopy, Raman and X-ray photoelectron spectroscopy. Results are analyzed and discussed so as to validate the advantages of the liquid pyrolysis method.

Defect study of SnO2 nanostructures by cathodoluminescence analysis: Application to nanowires

Defects in SnO2 nanowires have been studied by cathodoluminescence, and the obtained spectra have been compared with those measured on SnO2 nanocrystals of different sizes in order to reveal information about point defects not determined by other characterization techniques. Dependence of the luminescence bands on the thermal treatment temperatures and pre-treatment conditions have been determined pointing out their possible relation, due to the used treatment conditions, with the oxygen vacancy concentration. To explain these cathodoluminescence spectra and their behavior, a model based on first-principles calculations of the surface oxygen vacancies in the different crystallographic directions is proposed for corroborating the existence of surface state bands localized at energy values compatible with the found cathodoluminescence bands and with the gas sensing mechanisms. CL bands centered at 1.90 and 2.20 eV are attributed to the surface oxygen vacancies 100° coordinated with tin atoms, whereas CL bands centered at 2.37 and 2.75 eV are related to the surface oxygen vacancies 130° coordinated. This combined process of cathodoluminescence and ab initio calculations is shown to be a powerful tool for nanowire defect analysis.