Resumo:
研究了Cr^3+,Yb^3+,Er^3+共掺磷酸盐铒玻璃转镜调Q激光性质.三种Er2O3掺杂浓度的激光实验结果表明,在Er2O3名义掺杂浓度为0.5wt%时,玻璃的综合激光性质最好,重复频率为0.1Hz时,它的激光阈值功率为14.5mJ,最大输出能量为9.6mJ,斜率效率为0.55%.在同种实验条件下,比较了Cr14和Kigre公司生产的QE-7S激光性质参数,实验表明,前者激光阈值功率稍低,而后者的斜率效率和最大输出功率略高.
Resumo:
制备了不同含水量的掺铒磷酸盐玻璃,研究了各种工艺参数对反应气氛法除水效果的影响。结果表明由鼓泡气体带入的除水剂是玻璃除水的主要动力;在通气最初阶段的除水速率最快,并且提高除水温度、增大通气流量均有助于提高除水效率;结合实验从反应热力学角度讨论了除水机理,并指出在玻璃熔体中除水反应受熔体“笼效应”影响,反应速率大小取决于OH与CCl4形成偶遇对概率的大小。
Resumo:
研究了Al2O3 ,B2O3对P2O5-Al2O3-B2O3-ZnO-Na2O-CuCl玻璃形成区的影响规律;包边玻璃的物化性质随B/(B+Al)的变化规律;以及特定组分包边玻璃的透射光谱和吸收系数。这些研究工作对高功率大尺寸钕磷酸盐激光包边玻璃的研制具有非常重要的意义。
Resumo:
研究了氙灯抽运脉宽、输出耦合镜的反射率、铒玻璃工作温度以及工作重复频率对铬镱铒共掺磷酸盐玻璃激光输出能量的影响。结果表明, 对于输出能量, 抽运脉宽为2.3 ms(10%最大幅度间)时较好; 综合考虑激光阈值和斜率效率, 输出耦合镜的反射率为85%时较好。此外, 如同大多数激光介质那样, 铬镱铒共掺磷酸盐玻璃的激光输出能量随铒玻璃工作温度的升高和工作重复频率的增加而降低。
Resumo:
The upconversion emission of Er3+/Yb3+ codoped phosphate glass with 980 nm excitation was investigated. In the glass Er3+ concentration has a great influence on the intensity and the ratio of green and red light upconversion. The slope of the green luminenscence intensity as a function of pumping power ranges from 2.52 to 3.27, is the evidence of the three photon excitation process. The three photon process can also be concluded from excitation spectra when emission wavelength is 545 nm. The effect of Er3+ concentration is also discussed.
Resumo:
Phosphate glasses 60P
Resumo:
制备了镱铒共掺的磷酸盐玻璃并研究了室温下LD泵浦的连续激光输出性质。在泵浦功率为496mW时实现了最大输出功率77mW。讨论了在不同玻璃样品厚度和谐振腔长度时的斜率效率的变化以及在不同玻璃样品厚度,泵浦功率和谐振腔长度时的不同激光模式竞争的动力学行为。结果表明:激光光谱受到光学增益和光学损耗相对大小的限制。
Resumo:
To study the effects of upconversion in Erbium, a set of rate equations that simulates the performance of the passively Q-switched Er:Yb:glass laser with a Co2+:MgAl
Resumo:
制备了化学稳定的Er^3+/Yb^3+共掺的磷酸盐玻璃,并在其中制作了用于光放大器和激光器的平面光波导.这种磷酸盐玻璃的失重速率为4.7×10^-5g·cm^-2·hr^-1,小于Kigre公司商业化的磷酸盐玻璃QX/Er的失重速率.采用Ag^+-Li^+交换技术制作了平面光波导并用m-线光谱在632.8nm测量了平面光波导的有效折射率.根据反WKB法得到折射率形貌,计算了离子交换参数如:离子交换深度、表面折射率,折射率改变和扩散系数等.
Resumo:
Er3+-doped halide modified tellurite glasses were synthesized by conventional melting and quenching method. The Judd-Ofelt analysis was performed on the absorption spectra and the transition probabilities, excited state lifetimes, and the branching ratios were calculated and discussed. The intense infrared and visible fluorescence spectra under 980 nm excitation were obtained. Strong upconversion signal was observed at pumping power as low as 30 mW in the glasses with halide ions. The upconversion mechanisms and power dependent intensities were discussed, which showed two-photon process are involved for the green and red emissions. The decay times of the emitting states and the corresponding quantum efficiency were determined and explained. (C) 2004 American Institute of Physics.
Resumo:
The physical and thermal properties Of P2O5-Al2O3-BaO-La2O3 glasses were investigated. The effects of glass compositions on the transition temperature, thermal expansion coefficient, density, hardness and refractive index of glasses were studied. The highest hardness of the glasses is 4143.891 MPa and the lowest thermal expansion coefficient of the glasses is 71.770 x 10(-7)/° C. A phosphate glass with high mechanical strength and good thermal characteristic is obtained.
Resumo:
High-uniform nanowires with diameters down to 50 nm are directly taper-drawn from bulk glasses. Typical loss of these wires goes down to 0.1 dB/mm for single-mode operation. Favorable photonic properties such as high index for tight optical confinement in tellurite glass nanowires and photoluminescence for active devices in doped fluoride and phosphate glass nanowires are observed. Supporting high-index tellurite nanowires with solid substrates (such as silica glass and MgF2 crystal) and assembling low-loss microcoupler with these wires are also demonstrated. Photonic nanowires demonstrated in this work may open up vast opportunities for making versatile building blocks for future micro- and nanoscale photonic circuits and components. (c) 2006 Optical Society of America.
Resumo:
The authors demonstrate a 1.5 mu m wavelength microfiber laser formed by tightening a doped microfiber into a knot in air. The 2-mm-diameter knot, assembled using a 3.8-mu m-diameter microfiber that is directly drawn from Er:Yb-doped phosphate glass, serves as both active medium and resonating cavity for lasing. Single-longitudinal-mode laser with threshold of about 5 mW and output power higher than 8 mu W is obtained. Their initial results suggest a simple approach to highly compact lasers based on doped microscale optical fibers. (c) 2006 American Institute of Physics.
Resumo:
研究了掺铒磷酸盐玻璃波导放大器的特性。利用重叠因子将980nm光抽运的掺铒玻璃波导放大器四能级模型的速率-传输方程进行化简,在考虑上转换效应和放大自发发射的情况下.利用数值模拟的方法,得到了掺铒玻璃波导放大器的增益与Er^3+离子浓度、抽运功率、波导长度等参量之间的关系曲线;同时模拟出放大自发发射曲线并与实验测量结果进行比较。结果表明在考虑上转换效应和放大自发发射的情况下,理论结果和实验测量结果是一致的。同时看到,选择合适的铒离子浓度是制作掺铒玻璃波导放大器的关键;并且为了全面发挥掺铒玻璃波导放大器的性能
Resumo:
研究了退火和二次离子交换对Er^3+/Yb^3+共掺的磷酸盐玻璃平面光波导传输特性的影响。在退火过程中,由于热效应和波导层Ag^+离子的浓度差使得Ag^+离子重新分布;随着退火时间的延长和温度的升高,光波导模式数目逐渐增加,波导层深度加深,且波导表面折射率与玻璃基质折射率差减小,退火扩散深度与退火时间的平方根成正比。电子探针结果显示在二次离子交换后形成了掩埋式的光波导,Ag^+离子浓度接近二次方分布,而掩埋式的光波导有助于降低光波导的传输损耗。