Nuovi processi catalitici per la produzione di syngas

The study of the combined Steam/Dry Reforming (S/DR) process for the production of syngas (CO + H2) from clean biogas was carried out using Ni/Ir bimetallic catalysts on Mg and Al mixed-oxides, obtained by calcination of hydrotalcite-type precursors (Ht) prepared by co-precipitation. The presence of small amounts of Ir promoted the catalytic activity and limited the deactivation phenomena through the formation of a bimetallic alloy, which does the catalyst very active even at lowest temperature and in lack of steam. By integrating a High Temperature–WGS unit (HTS) after the S/DR reactor it was possible to increase the H2 yield of the process. The performance of the Zn/Al/Cu-based catalyst was improved using a templating agent during the synthesis of the catalyst, which increased the catalyst’s structural properties and activity especially at lowest temperatures and at highest contact times. Finally, starting from the laboratory data, it was possible to simulate the S/DR process on industrial scale, evaluating its scalability and environmental impact. The results showed that, using the S/DR technology instead of the current processes, it was possible to reduce the energy costs and the atmospheric emissions of the plant.

Studio del reforming combinato del biogas su nanoparticelle bimetalliche supportate

The study of the combined reforming (CR) process to produce synthesis gas (CO + H2) feeding Clean Biogas (CB, biogas in which the main pollutants have been removed) has been performed on Ni-based bimetallic catalysts promoted by small amounts of Rh or Cu, prepared by incipient wetness impregnation or coprecipitation of different precursors on mixed oxides Mg/Al/O obtained by calcination of hydrotalcite-type (Ht) coprecipitates. It has been observed as the formation of bimetallic particles promoted the catalytic activity and limited the deactivation phenomena, allowing to operate at lower temperature and feeding lower amounts of steam. By this way, it was possible to define the best promoter, to tune its amount and the formation of the bimetallic nanoparticles. Finally, it has been simulated the scale-up of the CR process to industrial level, evaluating the feasibility and economic degree by comparison with the industrially exploited Autothermal reforming (ATR) process, evidencing the possible scalability and the advantages at environmental and energetic level in comparison to the current reforming processes.

Local atomic structure in tetragonal pure ZrO(2) nanopowders

The local atomic structures around the Zr atom of pure (undoped) ZrO(2) nanopowders with different average crystallite sizes, ranging from 7 to 40 nm, have been investigated. The nanopowders were synthesized by different wet-chemical routes, but all exhibit the high-temperature tetragonal phase stabilized at room temperature, as established by synchrotron radiation X-ray diffraction. The extended X-ray absorption fine structure (EXAFS) technique was applied to analyze the local structure around the Zr atoms. Several authors have studied this system using the EXAFS technique without obtaining a good agreement between crystallographic and EXAFS data. In this work, it is shown that the local structure of ZrO(2) nanopowders can be described by a model consisting of two oxygen subshells (4 + 4 atoms) with different Zr-O distances, in agreement with those independently determined by X-ray diffraction. However, the EXAFS study shows that the second oxygen subshell exhibits a Debye-Waller (DW) parameter much higher than that of the first oxygen subshell, a result that cannot be explained by the crystallographic model accepted for the tetragonal phase of zirconia-based materials. However, as proposed by other authors, the difference in the DW parameters between the two oxygen subshells around the Zr atoms can be explained by the existence of oxygen displacements perpendicular to the z direction; these mainly affect the second oxygen subshell because of the directional character of the EXAFS DW parameter, in contradiction to the crystallographic value. It is also established that this model is similar to another model having three oxygen subshells, with a 4 + 2 + 2 distribution of atoms, with only one DW parameter for all oxygen subshells. Both models are in good agreement with the crystal structure determined by X-ray diffraction experiments.

Synchrotron X-ray powder diffraction and extended X-ray absorption fine structure spectroscopy studies on nanocrystalline ZrO(2)-CaO solid solutions

The crystal structure and the local atomic order of a series of nanocrystalline ZrO(2)-CaO solid solutions with varying CaO content were studied by synchrotron radiation X-ray powder diffraction and extended X-ray absorption fine structure (EXAFS) spectroscopy. These samples were synthesized by a pH-controlled nitrate-glycine gel-combustion process. For CaO contents up to 8 mol%, the t' form of the tetragonal phase (c/a > 1) was identified, whereas for 10 and 12 mol% CaO, the t '' form (c/a=1; oxygen anions displaced from their ideal positions in the cubic phase) was detected. Finally, the cubic phase was observed for solid solutions with CaO content of 14 mol% CaO or higher. The t'/t '' and t ''/cubic compositional boundaries were determined to be at 9 (1) and 13 (1) mol% CaO, respectively. The EXAFS study demonstrated that this transition is related to a tetragonal-to-cubic symmetry change of the first oxygen coordination shell around the Zr atoms.

High-temperature X-ray powder diffraction study of the tetragonal-cubic phase transition in nanocrystalline, compositionally homogeneous ZrO2-CeO2 solid solutions

Crystal structure of compositionally homogeneous, nanocrystalline ZrO2-CeO2 solutions was investigated by X-ray powder diffraction as a function of temperature for compositions between 50 and 65 mol % CeO2 center dot ZrO2-50 and 60 mol % CeO2 solid solutions, which exhibit the t'-form of the tetragonal phase at room temperature, transform into the cubic phase in two steps: t'-to-t '' followed by t ''-to-cubic. But the ZrO2-65 mol % CeO2, which exhibits the t ''-form, transforms directly to the cubic phase. The results suggest that t'-to-t '' transition is of first order, but t ''-to-cubic seems to be of second order. (C) 2008 International Centre for Diffraction Data.

Preparation, characterization and catalytic studies of V2O5-SiO2 xerogel composite

In this work, we report the synthesis, characterization and catalytic properties of a vanadium oxide-silicon oxide composite xerogel prepared by a soft chemistry approach. In order to obtain such material, we submitted a vanadium pentoxide gel previously synthesized via protonation of metavanadate species to an ""in situ"" progressive polycondensation into silica gel. The material has been characterized by X-ray diffraction, infrared spectroscopy, thermogravimetric analysis and scanning electron microscopy. Further, the catalytic activity of this material was evaluated for the epoxidation of styrene and cyclooctene using iodosylbenzene, hydrogen peroxide and m-chloroperbenzoic acid as the oxidizing agent.

Effect of mesoporosity of vanadium oxide prepared by sol-gel process as cathodic material evaluated by cyclability during Li(+) insertion/deinsertion

The effect of pore structure on the behavior of lithium intercalation into an electrode containing porous V(2)O(5) film has been investigated and compared with the electrode containing a non-porous V(2)O(5) film. X-ray diffraction patterns indicate a lamellar structure for both materials. Nitrogen adsorption isotherms, t-plot method, and Scanning Electronic Microscopy show that the route employed for the preparation of mesoporous V(2)O(5) was successful. The electrochemical performance of these matrices as lithium intercalation cathode materials was evaluated. The porous material reaches stability after several cycles more easily compared with the V(2)O(5) xerogel. Lithium intercalation into the porous V(2)O(5) film electrode is crucially influenced by pore surface and film surface irregularity, in contrast with the non-porous surface of the V(2)O(5) xerogel.

Analysis in vitro of the cytotoxicity of potential implant materials. I: Zirconia-titania sintered ceramics

Zirconia (ZrO(2)) is a bioinert, strong, and tough ceramic, while titania (TiO(2)) is bioactive but has poor mechanical properties. It is expected that ZrO(2)-TiO(2) mixed ceramics incorporate the individual properties of both ceramics, so that this material would exhibit better biological properties. Thus, the objective of this study was to compare the biocompatibility properties of ZrO(2)-TiO(2) mixed ceramics. Sintered ceramics pellets, obtained from powders of TiO(2), ZrO(2), and three different ZrO(2)-TiO(2) mixed oxides were used. Roughnesses, X-ray diffraction, microstructure through SEM, hardness, and DRIFT characterizations were performed. For biocompatibility analysis cultured FMM1 fibroblasts were plated on the top of disks and counted in SEM micrographs 1 and 2 days later. Data were compared by ANOVA complemented by Tukey`s test. All samples presented high densities and similar microstructure. The H(2)O content in the mixed ceramics was more evident than in pure ceramics. The number of fibroblasts attached to the disks increased significantly independently of the experimental group. The cell growth on the top of the ZrO(2)-TiO(2) samples was similar and significantly higher than those of TiO(2) and ZrO(2) samples. Our in vitro experiments showed that the ZrO(2)-TiO(2) sintered ceramics are biocompatible allowing faster cell growth than pure oxides ceramics. The improvement of hardness is proportional to the ZrO(2) content. Thus, the ZrO(2)-TiO(2) sintered ceramics could be considered as potential implant material. (C) 2010 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 94B: 305-311, 2010.

Partitioning sets of triples into small planes

We study partitions of the set of all ((v)(3)) triples chosen from a v-set into pairwise disjoint planes with three points per line. Our partitions may contain copies of PG(2, 2) only (Fano partitions) or copies of AG(2, 3) only (affine partitions) or copies of some planes of each type (mixed partitions). We find necessary conditions for Fano or affine partitions to exist. Such partitions are already known in several cases: Fano partitions for v = 8 and affine partitions for v = 9 or 10. We construct such partitions for several sporadic orders, namely, Fano partitions for v = 14, 16, 22, 23, 28, and an affine partition for v = 18. Using these as starter partitions, we prove that Fano partitions exist for v = 7(n) + 1, 13(n) + 1, 27(n) + 1, and affine partitions for v = 8(n) + 1, 9(n) + 1, 17(n) + 1. In particular, both Fano and affine partitions exist for v = 3(6n) + 1. Using properties of 3-wise balanced designs, we extend these results to show that affine partitions also exist for v = 3(2n). Similarly, mixed partitions are shown to exist for v = 8(n), 9(n), 11(n) + 1.

Efeito da composição das correntes do conversor das unidades de FCC no desempenho catalítico de aditivos DESOx

Hydrotalcite-like compounds having Mg partially replaced by Cu or Mn were prepared and used as precursors for two mixed oxides (Cu-OM50 and Mn-OM50) that were evaluated for SOx removal in the presence of O2, NO and CO. Under SO2/O2 reaction system, SOx removal was slightly higher over Cu-OM50. The addition of CO and NO to the feed markedly hindered the SO2 oxidation over Cu-OM50 while no significant effect was observed for Mn-OM50. For the regeneration step, the use of propane instead of H2 reduces regeneration capacity, mainly for Cu-OM50. Mn-OM50 was less affected by the feed composition, suggesting that it was a promising additive for SOx removal.

Fases estacionárias modernas para cromatografia líquida de alta eficiência em fase reversa

This review first discusses the limitations of many of the supports and stationary phases used in reversed phase high performance liquid chromatography and then describes those, developed more recently, that present better stabilities and more versatile selectivities. Emphases will be given to stationary phases that use higher purity silicas, hybrid silicas, monolithic silicas, metallic oxides and mixed oxides as supports and those that have embedded polar groups or contain phenyl or fluoro groups as the stationary phase as well as the phases used for mixed mode or hydrophilic interaction separations. These modern stationary phases facilitate the analysis of complex mixtures.

Síntese da perovsquita do tipo LaNiO3 através do método dos precursores quelantes usando EDTA: otimização do teor de agente quelante

The perovskites are strategic materials due their catalytic, electronic and magnetic properties. These properties are influenced by the calcination and synthesis conditions. In this work was carried out the synthesis of LaNiO3 perovskite-type by chelating precursor method using EDTA and also was studied the optimization of the EDTA content in the synthesis. The synthesized materials were characterized by X-ray diffraction (XRD), thermal gravimetric analysis (TG) and Infrared Spectroscopy (FTIR). In the optimization of the EDTA content the lowest ratio of metal / EDTA used was 1.0 / 0.1, where it was possible to obtain monophasic perovskite.

O efeito da desativação térmica nas propriedades oxirredutoras e na atividade catalítica de catalisadores CZ e Pd-CZ

Automotive catalyst, using in Brazil since 1992, is a essential technology for vehicular emissions control. Noble metals are the active phase of these catalysts, and cerium zirconium mixed oxides (CZ), responsibles for the oxygen storage capacity (OSC), one of the most important aspect for the operational performance of the catalyst. In this context, the oxireduction properties analysis of CZ and Pd/CZ (palladium supported in CZ) system are the objective of this study, as well as, the impact of the thermal aging in the OSC. Aging consisted of treatments at 900 or 1200 °C, for 12 or 36 h, in oxidizing condition.

Theoretical investigations of the bulk modulus in the tetra-cubic transition of PbTiO3 material

Resulting from ion displacement in a solid under pressure, piezoelectricity is an electrical polarization that can be observed in perovskite-type electronic ceramics, such as PbTiO3, which present cubic and tetragonal symmetries at different pressures. The transition between these crystalline phases is determined theoretically through the bulk modulus from the relationship between material energy and volume. However, the change in the material molecular structure is responsible for the piezoelectric effect. In this study, density functional theory calculations using the Becke 3-Parameter-Lee-Yang-Parr hybrid functional were employed to investigate the structure and properties associated with the transition state of the tetragonal-cubic phase change in PbTiO3 material.

Synthesis, structural and morphological characterization of CeO2-ZnO nanosized powder systems from Pechini's method

This work reports on the investigation of nanosized CeO2-ZnO systems prepared by Pechini's method. The structural and morphological characterization of CeO2-ZnO systems as well as the characterization of CeO2 and ZnO separately, showed that the employed method result in powders with spheroidal particles whose size are in the range 30 - 200 nm, which is appropriate to provide homogeneous suspensions. The ZnO present in the prepared mixed oxides seems to increase particle size distribution and to influence the arrangement of the particles after powder dispersion.