Reliability of a method for evaluating porosity in denture base resins

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Location of the mandibular foramen according to the amount of dental alveoli

The aim of this study was to analyze the anatomotopographic location of the mandibular foramen in the right and left ramus, and to verify the influence of the amount of dental alveoli on the foramen position. Thirty-five adult dry human mandibles of Araraquara Dental School, UNESP - São Paulo State University were assessed, with or without dental alveoli. Measurements were obtained, using a ruler and a digital caliper. The following distances were measured: Fl - distance between the lowest point of the mandibular incisure and the mandibular foramen (F point); FB - distance between the mandibular base and F point; FP - distance between the posterior margin of the ramus and F point; FA - distance between the anterior margin of the ramus and F point; FT - distance between the apex of the retromolar trigone and F point. The Mann-Whitney test was used to compare each measurement according to hemi-arch, and the Kruskal-Wallis test was used to analyze the influence of the presence of alveoli on the measures. For multiple comparison, Dunn's method was used. There was no statistically significant difference in the location of the mandibular foramen when compared to the right and left hemi-arches. The amount of dental alveoli influenced, significantly, only on FA and FP distances. Thus, it was concluded that the right and left mandibular ramus showed symmetry in the location of the mandibular foramen, and the amount of alveoli influenced on the distances of the anterior and posterior margins of the mandibular rams, in relation to the mandibular foramen.

Cloning and Identification of a Complete cDNA Coding for a Bactericidal and Antitumoral Acidic Phospholipase A(2) from Bothrops jararacussu Venom

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

A proposta biomecânica para a avaliação de sobrecarga na coluna lombar: efeito de diferentes variáveis demográficas na fadiga muscular

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Healing process after surgical treatment with scalpel, electrocautery and laser radiation: histomorphologic and histomorphometric analysis

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of recycled tiles and OSB ceiling materials in closed broiler house prototypes

This study aimed at evaluating the thermal performance of a modular ceiling system for poultry houses. The reduced- and distorted-scale prototypes used ceiling modules made of reforested wood and were covered with recycled long-life package tiles. The following parameters were measured for 21 days: tile internal surface temperature (ST), globe temperature and humidity index (WBGT), and radiant heat load (RHL). Measurements were made at times of highest heat load (11:00 am, 13:00 pm, and 03:00 pm). Collected data were analyzed by R statistics software. Means were compared by multiple comparison test (Tukey) and linear regression was performed, both at 5% significance level. The results showed that the prototype with the ceiling was more efficient to reduce internal tile surface temperature; however, this was not sufficient to provide a comfortable environment for broilers during the growout. Therefore, other techniques to provide proper cooling are required in addition to the ceiling.

Pulpal temperature increases with Er : YAG laser and high-speed handpieces

Statement of problem. During tooth preparation, both high-speed handpieces and lasers generate heat, which, if not controlled, can cause pulpal necrosis.Purpose. The aim of this study was to compare temperature increases produced by a high-speed dental handpiece with those produced by a relatively new instrument, the Er:YAG (erbium: yttrium-aluminum-garnet) laser.Material and methods. Thirty bovine mandibular incisors were reduced to an enamel/dentin thickness of 2.5 mm. Class V preparations were completed to a depth of 2.0 mm, measured with a caliper or by a mark oil the burs. A thermocouple was placed inside the pulp chamber to determine temperature increases (degreesC). Analysis was performed on the following groups (n = 10): Group 1, high-speed handpiece without water cooling, Group 11, high-speed handpiece with water cooling (30 mL/min), and Group III, the noncontact Er:YAG laser (2.94 mum at 350 mJ/10 Hz) with water cooling (4.5 mL/min). The temperature increases were recorded by a computer linked to the thermocouples. The data were analyzed using the Kruskal-Wallis test. The Dunn multiple comparison test was used as post hoc test (alpha = .05).Results. The average temperature rises were: 11.64degreesC (+/-4.35) for Group 1, 0.96degreesC (+/-0.71) for Group 11, and 2.69degreesC (+/-1.12) for Group III. There were no statistical differences between Groups 11 and III, both 11 and III differed from Group I significantly (P = .000 and P = .002, respectively).Conclusion. The preparations made with the high-speed and the laser instrument generated similar heat increases under water cooling. Water cooling was essential to avoid destructive temperature increases when using both the high-speed handpiece and laser.

In vitro evaluation of root canal preparation using oscillatory and rotary systems in flattened root canals

Objective: the aim of this study was to evaluate the biomechanical preparation of flattened root canals using the following systems: Endo-Eze AET stainless steel oscillatory instruments (Ultradent) and RaCe rotary NiTi instruments (FKG Dentaire). Materials and Methods: Twenty extracted human mandibular incisors were randomly assigned to two groups: Group I Instrumentation with oscillatory Endo-Eze AET files (oscillatory technique); Group 2 - Instrumentation with rotary NiTi RaCe files (rotary technique). The teeth were decoronated, had their apices and coronal openings sealed with sticky wax and were embedded in crystal-clear orthophtalic polyester resin. The roots were sectioned transversally with diamond discs at 10 mm (middle third) and 5 mm (apical third) from the apex and the segments were reassembled for instrumentation. The sections were photographed before and after root canal instrumentation and evaluated with respect to whether the original root canal shape was modified by instrumentation. To evaluate the differences in the root canal shape before and after biomechanical preparation, scores were given regarding the instruments touch on the intracanal walls. Results: In middle third of the root canals instrumented with the rotary system, there was a change in the original canal anatomy (p < 0.05), with formation of a protuberance in the mesiodistal direction. This protuberance did not occur when the oscillatory instrumentation was used. The oscillatory system had better results in the middle and apical thirds as evaluated by Dunn's multiple-comparison test (p > 0.05). Conclusion: Under the tested conditions, Endo-Eze oscillatory system yielded the instrumentation of all flattened oot canal walls, maintaining the canal original shape throughout the biomechanical preparation, and was more effective than RaCe rotary system.

Microleakage of hydrophilic adhesive systems in Class V composite restorations

Purpose: To investigate the microleakage of four hydrophilic adhesive systems: one multiple-bottles (Scotchbond Multi-Purpose Plus); two one-bottle (Single Bond, Stae); and one self-etching (Etch & Prime 3.0). Materials and Methods: 120 bovine incisor teeth were divided into four groups (n = 30) and Class V cavities were prepared at the cemento-enamel junction. The cavities were restored with the adhesive systems and with Z100 composite. The teeth were thermocycled 1,000 times between 5 +/- 2 degreesC and 55 +/- 2 degreesC with a dwell time of 1 min, and then placed in a 2% methylene blue dye (pH 7.0) for 4 hrs, washed and sectioned vertically through the center of the restorations. The qualitative evaluation was made by three examiners who distributed pre-established scores (0-4) for each tooth using a stereomicroscope at x30 magnification. Results: In enamel margins little microleakage was observed and the Kruskal-Wallis analysis did not show differences. In dentin margins the KruskaI-Wallis and multiple comparison analyses were applied: microleakage was significantly greater with Stae (median 3) and Scotchbond MP Plus (median 4). Single Bond (median 1) and Etch & Prime 3.0 (median 2) showed the best results in dentin margins, and the statistical analysis did not demonstrate differences in microleakage among these groups.

The effect of mold temperature on castability of CPTi and Ti-6Al-4V castings into phosphate bonded investment materials

Objective. The aim of this study was to evaluate the castability of CP titanium and Ti-6Al-4V alloy castings into Rematitan Plus investment at three different mold temperatures.Methods. A nylon mesh pattern (20 mm with 64 squares and wire of 0.7 mm in diameter) was used for the castability testing. Initially, an image of the wax pattern was obtained by means of a digital camera and the total extension of filaments (mm) was then measured, using the Leica Qwin image analysis system. The mesh sprued was placed in the Rematitan Plus investment material and the castings were made in a Discovery Plasma machine at three different mold temperatures: 430 degrees C (control group), 480 degrees C or 530'C. Ten castings were made for each temperature. The images of the castings were analyzed (Leica Qwin) and the castability index determined by the number of the completely cast segments as a percentage of the wax pattern. Data were analyzed by two-way ANOVA and Tukey's multiple comparison test (a = 0.05) using materials and temperatures as discriminating variables.Results. The Ti-6Al-4V alloy (60.86%) presented a better castability index than CP Ti (48.44%) (p < 0.000001). For CP Ti, the temperature of 530 degrees C (23.96%) presented better castability than at other temperatures, 480 degrees C (14.66%) and 430 degrees C (12.54%), with no difference between them (p < 0.001). For Ti-6Al-4V alloy, there was a statistically significant difference among the three temperatures: 530 degrees C (28.36%) > 480 degrees C (19.66%) > 430 degrees C (15.97%) (p < 0.002).Significance. Within the limitations of this study, the increase in the mold temperature of the Rematitan Plus investment resulted in a better castability index for both materials, and Ti-6Al-4V presented a better castability index than CP Ti. (c) 2005 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Avaliacao da necessidade da dosagem rotineira de hematocrito, hemoglobina, ureia e creatinina sericos durante a avaliacao pre-anestesica

Background and Objectives - There are many questions and opinions about the value of routine preoperative tests as an integral part of the preanesthetic evaluation. Current trends suggest that such tests should be based on detailed clinical and physical evaluation. Since such tests are still routinely performed and questions about their real value still persist, the aim of this study was to assess the value of routine hematocrit (Ht), hemoglobin concentration (Hb), blood urea nitrogen (BUN) and serum creatinine results in patients undergoing elective surgery, to establish when they are needed and aiming at answering such questions. Methods - 1065 patients aged 12 years and above, physical status ASA I, II and III, scheduled for elective surgery were studied. Patients were divided into 7 different age groups with randomized distribution of gender. Ht, Hb, BUN and serum creatinine results, routinely asked by our surgical departments, were observed and analyzed. Variance Analysis was used for each variable, and the Bonferroni Multiple Comparison Test was used to compare group to group. Differences were considered significant when p < 0.05 (5%). Results - For all patients, 4025 laboratory tests were obtained. The number of tests was the same for each group. There were no differences in Ht and Hb values which remained within normal ranges. Considering BUN and serum creatinine, there was a difference between younger and older patients, but the results were normal in all groups. Conclusions - We concluded that mean Ht, Hb, BUN and serum creatinine values in all age groups were all acceptable for surgical patients in general. However, they are barely useful if performed regardless of clinical evaluation. Thus, such preoperative routine tests should be abandoned and the good clinical practice with common sense should prevail in indicating them.

Effect of a heat-treatment on the linear dimensional change of a hard chairside reline resin

Statement of problem. Little data are available regarding the effect of heat-treatments on the dimensional stability of hard chairside reline resins. Purpose. The objective of this in vitro study was to evaluate whether a heat-treatment improves the dimensional stability of the reline resin Duraliner II and to compare the linear dimensional changes of this material with the heat-polymerized acrylic resin Lucitone 550. Material and methods. The materials were mixed according to the manufacturer's instructions and packed into a stainless steel split mold (50.0 mm diameter and 0.5 mm thickness) with reference points (A, B, C, and D). Duraliner II specimens were polymerized for 12 minutes in water at 37°C and bench cooled to room temperature before being removed from the mold. Twelve specimens were made and divided into 2 groups: group 1 specimens (n=6) were left untreated, and group 2 specimens (n=6) were submitted to a heat-treatment in a water bath at 55°C for 10 minutes and then bench cooled to room temperature. The 6 Lucitone specimens (control group) were polymerized in a water bath for 9 hours at 71°C. The specimens were removed after the mold reached the room temperature. A Nikon optical comparator was used to measure the distances between the reference points (AB and CD) on the stainless steel mold (baseline readings) and on the specimens to the nearest 0.001 mm. Measurements were made after processing and after the specimens had been stored in distilled water at 37°C for 8 different periods of time. Data were subjected to analysis of variance with repeated measures, followed by Tukey's multiple comparison test (P<.05). Results. All specimens exhibited shrinkage after processing (control, -0.41%; group 1, -0.26%; and group 2, -0.51%). Group 1 specimens showed greater shrinkage (-1.23%) than the control (-0.23%) and group 2 (-0.81%) specimens after 60 days of storage in water (P<.05). Conclusion. Within the limitations of this study, a significant improvement of the long-term dimensional stability of the Duraliner II reline resin was observed when the specimens were heat-treated. However, the shrinkage remained considerably higher than the denture base resin Lucitone 550. Copyright © 2002 by The Editorial Council of The Journal of Prosthetic Dentistry.

Effects of dentin collagen removal on microleakage of bonded restorations

Purpose: To evaluate the effects of removing dentin collagen exposed by acid etching on the microleakage of bonded restorations with and without flowable composite application and submitted to thermocycling and long-term water storage. Materials and Methods: Standardized Class V cavities were prepared in 180 bovine incisors. They were randomly assigned to three groups according to the adhesive technique used. Conventional group (C): Single Bond was applied according to the manufacturer's instructions and Z250 composite was placed. Hypochlorite group (H): After acid etching a 10% NaOCl aqueous solution was applied for 1 min, then Single Bond and Z250 were applied. Hypochlorite and Flowable group (HF): Similar to group H, but following adhesive application, a thin layer of Natural Flow flowable composite was applied before the Z250. Each group was divided into three subgroups (0, 6, 12), which remained immersed in distilled water for 24 h or 6 or 12 months and underwent 500, 1500 or 2500 thermal cycles, respectively. At the end of each storage time, the specimes were stained with silver nitrate, decalcified, immersed in methyl salicylate for clearing and observed under a stereomicroscope to determine microleakage (scores 0 to 4). The data were analyzed using the Kruskal-Wallis and the Multiple Comparison Tests (α = 0.05). Results: After 12 months, every group showed significant increases in microleakage. There was no significant difference between Groups H and HF for the three different periods of time, but they showed statistically less microleakage than Group C. Conclusion: The removal of dentinal collagen reduced the marginal microleakage when compared to the conventional technique. The use of the flowable composite did not produce significant effects. No technique was completely effective in preventing microleakage.

Cytotoxicity of hard chairside reline resins: Effect of microwave irradiation and water bath postpolymerization treatments

Purpose: To evaluate the influence of water bath and microwave postpolymerization treatments on the cytotoxicity of 6 hard reline acrylic resins. Materials and Methods: The materials tested were Tokuso Rebase Fast (TR), Ufi Gel Hard (UGH), Duraliner II (D), Kooliner (K), New Truliner (NT), and Light Liner (LL). LL resin was additionally tested with an air-barrier coating (LLABC). Nine disks of each material (10 × 1 mm) were made and divided into 3 groups: group 1 (no postpolymerization treatment); group 2 (postpolymerization in microwave oven); group 3 (postpolymerization in water bath at 55°C for 10 minutes). L929 cells were cultured in 96-well plates and incubated for 24 hours in Eagle's medium. Eluates prepared from the disks or medium without disks (control) replaced the medium. Cytotoxicity was assessed by both dehydrogenase succinic activity (MTT) assay and incorporation of radioactive 3H-thymidine assay. Tests were carried out in quadruplicate and repeated twice. Differences between groups were determined by analysis of variance with Tukey multiple-comparison intervals (α = .05). Results: For MTT assay, the postpolymerization treatments had no effect on the cytotoxicity of all materials (P > .05). For 3H-thymidine assay, the postpolymerization treatments significantly decreased the cytotoxicity of UGH (P < .05). The cytotoxicity of K, NT, LL, and LLABC increased after microwave irradiation (P < .05). TR, NT, and LLABC showed an increase in cytotoxicity after water bath (P < .05). Conclusion: When assessed by MTT assay, the cytotoxicity of the materials was not affected by postpolymerization treatments. 3H-Thymidine assay showed that the cytotoxicity of the resins was not improved by the postpolymerization treatments, with the exception of UGH.

Influência da fotopolimerização e da cor da resina composta na microdureza

Objective: To study the influence of color opacity and light-curing systems (halogen light vs blue LED) on the microhardness of a composite resin. Methods: Esthet-X composite resin (Dentsply), shades A2 and A2-O, was inserted in a stainless steel matrix (5 mm diameter and 2 mm deep) and was light cured for 40 seconds with a halogen light source (XL 3000; 3M/ESPE) or a blue LED (Optilight LD II; Gnatus). Eight groups of 15 specimens each were formed, and were further divided according to the light-curing systems, the exposed area (base and surface), and the opacity of the composite resin, producing 120 specimens. The specimens were next stored in distilled water for 24 hours, embedded in a chemically activated acrylic resin, then subjected to finishing and polishing with sandpaper and felt discs. Microhardness was measured with a Vickers Digital Microhardness meter, with a 50 g load for 30 seconds. The obtained microhardness means were analyzed by ANOVA and Tukey's multiple-comparison test at 5% significance level. Results: The surface microhardness was always greater than the base microhardness, regardless of the light-curing source. The halogen light lamp produced significantly higher composite resin microhardness means than the blue LED (57.61 vs. 42.53 HV) (p<0.05). Statistically significant differences (p<0.05) were obtained between the microhardness means for the different composite opacities; lowest microhardness in depth was produced by the A2-O shade. Conclusion: Composite resin opacity as well as the light-curing system influenced the microhardness of the material.