Magnetic properties of nanostructured ferrimagnetic zinc ferrite

Nanostructured ZnFe2O4 ferrites with different grain sizes were prepared by high energy ball milling for various milling times. Both the average grain size and the root mean square strain were estimated from the x-ray diffraction line broadening. The lattice parameter initially decreases slightly with milling and it increases with further milling. The magnetization is found to increase as the grain size decreases and its large value is attributed to the cation inversion associated with grain size reduction. The Fe-57 Mossbauer spectra were recorded at 300 K and 77 K for the samples with grain sizes of 22 and 11 nm. There is no evidence for the presence of the Fe2+ charge state. At 77 K the Mossbauer spectra consist of a magnetically ordered component along with a doublet due to the superparamagnetic behaviour of small crystalline grains with the superparamagnetic component decreasing with grain size reduction. At 4.2 K the sample with 11 nm grain size displays a magnetically blocked state as revealed by the Mossbauer spectrum. The Mossbauer spectrum of this sample recorded at 10 K in an external magnetic field of 6 T applied parallel to the direction of gamma rays clearly shows ferrimagnetic ordering of the sample. Also, the sample exhibits spin canting with a large canting angle, maybe due to a spin-glass-like surface layer or grain boundary anisotropies in the material.

Structural and magnetic properties of Sr2Fe1+xMo1-xO6 (-1 <= x <= 0.25)

We have synthesized the solid solution Sr2Fe1+xMo1-xO6 with -1 <= x <= 0.25, the composition x=0 corresponding to the well-known double-perovskite system Sr2FeMoO6. We report structural and magnetic properties of the above system, exhibiting systematic variations across the series. These results restrict the range of models that can explain magnetism in this family of compounds, providing an understanding of the magnetic structure.

Synthesis, structure and magnetic properties of the polyoxovanadate cluster Zn-2(NH2(CH2)(2)NH2)(5)]{Zn(NH2(CH2)(2)NH2)(2)}(2){V18O42(H2O)\ ]center dot xH(2)O (x similar to 12), possessing a layered structure

A hydrothermal reaction of a mixture of ZnCl2, V2O5, ethylenediamine and water gave rise to a layered poly oxovanadate material. clusters. These clusters, with all the vanadium ions in the +4 state, are connected together through Zn(NH2(CH2)(2)NH2)(2) linkers forming a two-dimensional structure. The layers are also separated by distorted trigonal bipyramidal [Zn-2(NH2(CH2)(2)NH2)(5)] complexes. The Structure, thus, presents a dual role for the Zn-ethylenediamine complex. The magnetic susceptibility studies indicate that the interactions between the V centres in I are predominantly antiferromagnetic in nature and the compound shows highly frustrated behaviour. The magnetic properties are compared to the theoretical calculations based oil the Heisenberg model, in addition to correlating to the structure. Crystal data for the complexes are presented.

Studies on high‐density nickel zinc ferrite and its magnetic properties using novel hydrazine precursors

Nickel zinc ferrites have been very widely used in the high‐frequency applications. In our present study we have prepared Ni1−x Znx Fe2O4 (0≤x≤1) using novel hydrazinium metal hydrazinecarboxylate precursors. High densities (∼99%) have been obtained for all the ferrites sintered at relatively low temperatures, 1100 °C, in comparison with the conventional method (≥1200 °C). The variation of magnetic properties like magnetic moment, Curie temperature, and permeability with zinc concentration have been studied.

Optical and magnetic properties of the exact PPP states of biphenyl

The low-lying singlets and triplets of biphenyl are obtained exactly within the PPP model using the diagrammatic valence bond method. The energy gaps within the singlet manifold as well as the lowest singlet-triplet gap are found to be in good agreement with experimental results. The two weak absorptions between 4·1 and 4·2 eV reported experimentally are attributed to the two states lying below the optical gap that become weakly allowed on breaking electron-hole and inversion symmetries. The observed blue shift of the spectral lines, attributed to a change in dihedral angle, on going from crystalline to solution to vapour phase is also well reproduced within the PPP model. The bond orders show that the ground singlet state is benzenoidal while the dipole excited state as well as the lowest triplet state are quinonoidal and planar. Comparison with the experimental spin densities and the fine structure constants D and E in the triplet state point to slightly weaker correlations than assumed by the PPP model. The introduction of a 1-8 bond to mimic poly(paraphenylene)s gives an optical gap that is in good agreement with experiment.

A formate bridged Ni(II) sheet and its 3D analogue in presence of a linear organic linker: Synthesis, crystal structure and magnetic properties

Reaction of formamide with Ni(NO3)(2)center dot 6H(2)O under hydrothermal condition in a mixture of MeOH/H2O forms a two-dimensional formate bridged sheet Ni(HCOO)(2)(MeOH)(2) (1). X-ray structure analysis reveals the conversion of formamide to formate which acts as a bridging ligand in complex 1 where the axial sites of Ni(II) are occupied by methanol used as a solvent. An analogous reaction in presence of 4,4'-bipyridyl (4,4'-bipy) yielded a three-dimensional structure Ni(HCOO)(2)(4,4'-bpy) (2). DC magnetic measurements as a function of temperature and field established the presence of spontaneous magnetization with T-c (Curie temperature) = 17 and 20.8 K in 1 and 2, respectively, which can be attributed due to spin-canting. DFT calculations were performed to corroborate the magnetic results of 1 and 2. (C) 2010 Elsevier Ltd. All rights reserved.

Structure, dielectric, and magnetic properties of Sr2TiMnO6 ceramics

Sr2TiMnO6, a double perovskite associated with high degree of B-site cation disorder was investigated in detail for its structural, magnetic, and dielectric properties. Though x-ray powder diffraction analysis confirms its cubic structure, first order Raman scattering and infrared reflectivity spectra indicate a breaking of the local cubic symmetry. The magnetization study reveals an anomaly at 14 K owing to a ferrimagnetic/canted antiferromagneticlike ordering arising from local Mn-O-Mn clusters. Saturated M-H hysteresis loops obtained at 5 K also reflect the weak ferromagnetic exchange interactions present in the system and an approximate estimation of Mn3+/Mn4+ was done using the magnetization data for the samples sintered at different temperatures. The conductivity and dielectric behavior of this system has been investigated in a broad temperature range of 10 to 300 K. Intrinsic permittivity was obtained only below 100 K whereas giant permittivity due to conductivity and Maxwell-Wagner polarization was observed at higher temperatures. X-ray photoemission studies further confirmed the presence of mixed oxidation states of Mn and the valence band spectra analysis was carried out in detail. (C) 2010 American Institute of Physics. doi: 10.1063/1.3500369]

Magnetic properties of pure, Sr- and Ca-Doped La2NiO4+δ ceramics: Onset of high-Tc superconductivity

We present the results for the temperature and field dependence of the magnetic for ceramic materials of the composition La2−xMxNiO4, with M=Sr or Ca and 0≤x≤0.4. The onset of a strong diamagnetism has been observed at temperatures between 8 and 70 K, depending on sample composition, annealing conditions. and thermal cycling procedures. The results are similar to those obtained earlier for monocrystalline samples and are likewise interpreted as due to the onset of superconductivity in a minority phase. A comparison with the results for superconducting La1.8Sr0.2Cu0.9Ni0.1O4 ceramics is also made; this illustrates some unique features of the nickelate systems, such as the high values of the critical fields Hc1 and Hc2. The differences between monocrystalline and ceramic systems are also discussed.

Crystal structures, spectral and magnetic properties of (µ-hydroxo)(µ-acetato)dicopper(II) complexes containing chelating amines

The reaction of [Cu2(O2CMe)4(H2O)2] with N, N, N′, N′-tetramethylethane- 1,2-diamine (tmen) in ethanol yielded the dicopper(II) complex [Cu2(OH)(O2CMe)(tmen)2][ClO4]21. A similar reaction with N, N- dimethylethane- 1,2-diamine (dmen) afforded a crystalline product 2 in which two dicopper(II) complexes, [Cu2(OH)(O2CMe)(dmen)2][ClO4]22a and [Cu2(OH)(O2CMe)(H2O)2(dmen)2][ClO4]22b, are cocrystallized in a 1 : 1 molar ratio along with 2NaClO4. The crystal structures of 1 and 2 have been determined. The complexes have an asymmetrically dibridged [Cu2(µ-OH)(µ-O2CMe)]2+ core. The co-ordination geometry of the metal is square planar (CuO2N2). The copper atoms in 2b have a square-pyramidal CuO3N2 co-ordination sphere. The Cu Cu distances and Cu–O–Cu angles in 1, 2a and 2b are 3.339(2), 3.368(3), 3.395(7)Å, 120.1(2), 116.4(1) and 123.6(2)°, respectively. Complex 1 exhibits an axial ESR spectrum in a methanol glass giving g∥= 2.26 (A∥= 164 × 10–4 cm–1) and g⊥= 2.04. The ESR spectra obtained from the bulk material of the dmen product are indicative of the presence of two dimers, viz. complex 2a(g∥= 2.25, A∥= 165 × 10–4 cm–1; g⊥= 2.03) and 2b(g∥= 2.19, A∥= 184 × 10–4 cm–1; g⊥= 2.0). Variable-temperature magnetic susceptibility measurements on these complexes show an intramolecular antiferromagnetic coupling in the dimeric core. The fitting parameters are J=–27.8 cm–1, g= 2.1 for complex 1 and J=–10.1 cm–1, g= 2.0 for 2. The magnetostructural properties of the complexes are discussed. There is a linear correlation of the –2J values with the Cu Cu distances among dibridged complexes having square-planar copper(II) centres.

Investigation on the Magnetic Anomaly and the Role of Orbital Moment on the Magnetic Properties of LaMn0.5Co0.5O3

Two distinct ferromagnetic phases are present in LaMn0.5Co0.5O3 for which the spin-only magnetic moment calculated from the high temperature dc susceptibility is found to be unusually high. Such a high moment can only be accounted for by assigning the valence state of the cations to Mn2+-Co4+. This is unrealistic as the earlier report based on X-ray absorption spectroscopy (XAS) has suggested the valence state to be mainly Mn4+-Co2+ with traces of Co3+. Also from our studies using XAS, it is found that the valence state is mainly Mn4+-Co2+. In addition, no notable difference is observed in the minor Co3+ present in both phases. Our results based on X-ray magnetic circular dichroism studies (XMCD) reveal the presence of ``distinct'' high orbital moment associated with Co2+ for both phases. Thus it is found that the distinctness of the orbital moment also plays a vital role in determining the magnetic moment and T-c of both phases of LaMn0.5Co0.5O3. By considering the orbital moment obtained from XMCD, the anomaly in the paramagnetic susceptibility is resolved and thus we are able to assign the valence state to Mn4+-Co2+ configuration. The difference in the magnitude of orbital moment in both phases is believed to be due to the crystal field effects.

Synthesis, Crystal Structure, and Magnetic Properties of a Ferromagnetically Coupled Angular Trinuclear Copper(11) Complex [Cu3(02CMe)4(bpy)s(HzO)](PF)62

The synthesis, X-ray crystal structure, and magnetic properties of an angular trinuclear copper(II) complex [Cu3(O2CMC)4(bpy)3(H2O)](PF6)2 (1), obtained from a reaction of Cu2(O2CMe)4(H2O)2 With 2,2'-bipyridine (bpy) and NH4PF6 in ethanol, are reported. Complex 1 crystallizes in triclinic space group P1BAR with a = 11.529(1) angstrom, b = 12.121(2) angstrom, c = 17.153(2) angstrom, alpha = 82.01(1)-degrees, beta = 79.42(1)-degrees, gamma = 89.62(1)-degrees, and Z = 2. A total of 6928 data with I > 2.5sigma(I) were refined to R = 0.0441 and R(w) = 0.0557. The structure consists of a trinuclear core bridged by four acetate ligands showing different bonding modes. The coordination geometry at each copper is distorted square-pyramidal with a CuN2O2...O chromophore. The Cu...Cu distances are 3.198(1) angstrom, 4.568(1) angstrom, and 6.277(1) angstrom. There are two monoatomic acetate bridges showing Cu-O-Cu angles of 93.1(1) and 97.5(1)-degrees. Magnetic studies in the temperature range 39-297 K show the presence of a strong ferromagnetically coupled dicopper(II) unit (2J = +158 cm-1) and an essentially isolated copper(II) center (2J' = -0.4 cm-1) in 1. The EPR spectra display an axial spectrum giving g(parallel-to) = 2.28 (A(parallel-to) = 160 X 10(-4) cm-1) and g(perpendicular-to) = 2.06 (A(perpendicular-to) = 12 X 10(-4) cm-1) for the normal copper and two intense isotropic signals with g values 2.70 and 1.74 for the strongly coupled copper pair. The structural features of 1 compare well with the first generation models for ascorbate oxidase.

Magnetic properties of rare earth nickelates of the Ln(2)BaNiO(5) family

Rare-earth nickelates Ln(2)BaNi(1-x)Cu(2)O(5), Ln = Nd and Dy, and Dy2-xYxBaNiO5 have been synthesized in order to investigate the effect of substitution of Ni by Cu and Dy by nonmagnetic Y on the magnetic properties of the nickelates. In Ln(2)BaNi(1-x)Cu(x)O(5), the nickelate structure (x=0.0) changes to the cuprate structure (x=1.0) at a specific composition (x=0.3). The Neel temperature of Nd2BaNi1-xCuxO5 decreases continuously with increase in x upto x=0.3 (T-N = 18K); when x > 0.3, the materials are paramagnetic down to 20K. The mu(eff) in Nd2BaNi1-xCxO5 essentially corresponds to the contribution of the Nd ions. In Dy2-xYxBaNiO5, the Neel temperature decreases from 40K when x=0.0 to 24K when x=1.5. The compositions with 1.5 less than or equal to x less than or equal to 2 (including the x=1.95 composition) are paramagnetic down to 20K, unlike Y2BaNiO5 (x=2.0) which exhibits a T-N of 370K. Even the smallest concentration of paramagnetic Dy seems to destroy the antiferromagnetic Ni-O-Ni chains in Y2BaNiO5.

Magnetic properties of mechanically alloyed nanocrystalline Ni3Fe

Disordered nanocrystalline Ni3Fe alloy was prepared by mechanical alloying of elemental powders. X-ray diffractograms show the formation of Ni3Fe single phase. The chemical composition and morphology of the powder have been obtained by using EDAX and SEM analysis respectively. While the saturation magnetisation decreases with milling time, the coercivity increases. The width of the hyperfine field distributions obtained from Mossbauer studies shows that the alloy is highly disordered Atomic ordering is found to take place at a faster rate compared to that in the bulk alloy. (C) 1999 Acta Metallurgica Inc.

Magneto-structural correlation in (mu-alkoxo/hydroxo)(mu-carboxylato)dicopper(II) systems: Synthesis, X-ray structure and magnetic properties of aquo(mu-hydroxo) (mu-arylcarboxylato)bis(N,N,N ',N '-tetramethylethane-1,2-diamine)dicopper(II) diperchlorate

Asymmetrically dibridged dicopper(II) complexes, [Cu-2(OH)(O2CC6H4-p-Me)(tmen)(2)(H2O)](ClO4)(2) (1) and [Cu-2(OH)(O2CC6H4-p-OMe)(tmen)(2)(H2O)](ClO4)(2) (2) (tmen = N,N,N',N'-tetramethylethane-1,2-diamine), were prepared and structurally characterized. Complex 1 crystallizes in the monoclinic space group P2(1)/a with a = 17.718(2), b = 9.869(1), c = 19.677(2) Angstrom, beta = 115.16(1)degrees, V = 3114.3(6) Angstrom(3) and Z = 4. The structure was refined to R(wR(2)) = 0.067(0.178). Complex 2 crystallizes in the monoclinic space group P2(1)/a with a = 17.695(3), b = 9.574(4), c = 20.104(2) Angstrom, beta = 114.18(1)degrees, V = 3107(1) Angstrom(3) and Z = 4. The final residuals are R(wR(2)) = 0.067(0.182). The complexes have a [Cu-2(mu-OH)(mu-OH)(mu-O2CAr)](2+) core with tmen Ligands occupying the terminal sites of the core. In addition, one copper is axially bound to a water molecule. The Cu ... Cu distances and the Cu-OH Cu angles in the core are 3.394(1) Angstrom, 124.4(2)degrees for 1 and 3.374(1) Angstrom, 123.3(3)degrees for 2. The complexes show axial X-band EPR spectral features in methanol glass at 77 K giving g(perpendicular to) = 2.02, g(parallel to) = 2.3 (A(parallel to) = 165 x 10(-4) cm(-1)) and a visible band near similar to 630 nm in methanol. The complexes are weakly antiferromagnetic. A theoretical fit of the magnetic susceptibility data in the temperature range 40-295 K gives -J = 10 cm(-1), g = 2.05 for 1 and -J = 10 cm(-1), g = 2.0 for 2. Plots of -2J versus the Cu-OH-Cu angle (phi) in this class of asymmetrically dibridged dicopper(II) complexes having d(x2-y2)-d(x2-y2) magnetic orbitals show a linear magneto-structural correlation: -2J(cm(-1)) = 11.48 phi(deg) - 1373.

Studies on magnetic properties of MnTi1-xNbxO3 system

Synthesis and characterization of electrical and magnetic properties of ilmenite phases of the type MnTi1-xNbxO3 have been carried out. Single phase materials could be obtained for 0.0 less than or equal to x less than or equal to 0.25. The electrical conductivity increases with increasing Nb content. Magnetic susceptibility studies show that the phases exhibit 2D antiferromagnetic behavior. The magnetic susceptibility data has been analyzed using Fisher's specific heat to determine the long range ordering temperature, (C) 1998 Academic Press.