Interface formation of nanostructured heterojunction SnO 2:Eu/GaAs and electronic transport properties

Thin films of tin dioxide (SnO2) are deposited by the sol-gel-dip-coating technique, along with GaAs layers, deposited by the resistive evaporation technique. The as-built heterojunction has potential application in optoelectronic devices, combining the emission from the rare-earth doped transparent oxide (Eu3+-doped SnO2 presents very efficient red emission) with a high mobility semiconductor. The advantage of this structure is the possibility of separation of the rare-earth emission centers from the electron scattering, leading to a strongly indicated combination for electroluminescence. Electrical characterization of the heterojunction SnO2:Eu/GaAs shows a significant conductivity increase when compared to the conductivity of the individual films, and the monochromatic light irradiation (266 nm) at low temperature of the heterojunction GaAs/SnO2:Eu leads to intense conductivity increase. Scanning electron microscopy (SEM) of the heterojunction cross section shows high adherence and good morphological quality of the interfaces substrate/SnO2 and SnO2/GaAs, even though the atomic force microscopy (AFM) image of the GaAs surface shows disordered particles, which increases with sample thickness. On the other hand, the good morphology of the SnO2:Eu surface, shown by AFM, assures the good electrical performance of the heterojunction. The observed improvement on the electrical transport properties is probably related to the formation of short conduction channels at the semiconductors interface, which may exhibit two-dimensional electron gas (2DEG) behavior. © 2012 Elsevier B.V. All rights reserved.

Prediction of dopant atom distribution on nanocrystals using thermodynamic arguments

A theoretical approach aiming at the prediction of segregation of dopant atoms on nanocrystalline systems is discussed here. It considers the free energy minimization argument in order to provide the most likely dopant distribution as a function of the total doping level. For this, it requires as input (i) a fixed polyhedral geometry with defined facets, and (ii) a set of functions that describe the surface energy as a function of dopant content for different crystallographic planes. Two Sb-doped SnO2 nanocrystalline systems with different morphology and dopant content were selected as a case study, and the calculation of the dopant distributions expected for them is presented in detail. The obtained results were compared to previously reported characterization of this system by a combination of HRTEM and surface energy calculations, and both methods are shown to be equivalent. Considering its application pre-requisites, the present theoretical approach can provide a first estimation of doping atom distribution for a wide range of nanocrystalline systems. We expect that its use will support the reduction of experimental effort for the characterization of doped nanocrystals, and also provide a solution to the characterization of systems where even state-of-art analytical techniques are limited.

Single precursor route to efficient cobalt sulphide counter electrodes for dye sensitized solar cells

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Characterization of metallic electrical contacts to SnO2 thin films lightly doped with Eu3+ ions, and photo-induced resistivity

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effects of synthesis and processing on supersaturated rare earth-doped nanometric SnO2 powders

This paper presents and discusses some of the results of the effects of processing on rare earth-doped nanosize SnO2. Several relevant factors that may influence the characteristics of the final product are studied. The influence of two preparation routes and two heat-treatment conditions on the incorporation of dopants is investigated. The route whereby a soluble salt is used as the dopant source is found to provide the highest degree of dopant incorporation, even under the least favorable heat-treatment conditions.

Structural and microstructural behaviour of SnO2 dense ceramics doped with ZnO and WO3

SnO2-based varistors doped with ZnO and WO3 were prepared by mixed oxide method. Experimental evidence shows that the increase in ZnO amount increases the volume and microstrain of unit cell while the WO3 promotes a decrease. The effect of ZnO and WO3 additives could be explained by the substitution of Sn4+ by Zn2+ and W6+. The addition of WO3 inhibits the grain growth due to the segregation in the grain boundary without influence in the densification of the samples. Besides that, an increase in the electrical resistance of the SnO2-ZnO-WO3 system was observed independent of the WO3 concentration. (c) 2005 Elsevier B.V. All rights reserved.

Physical properties of silicate glasses doped with SnO2

The presence of tin in the network of silicate glasses produces changes in several of their physico-chemical properties. Glasses with the composition (mol%) 22Na(2)O (.) 8CaO (.) 70SiO(2) containing up to 5 wt% of SnO2 were analyzed under several experimental techniques. Dilatometric measurements showed an increase of the glass transition temperature with increasing tin content, while the average thermal expansion coefficient is reduced. Vickers microhardness, density, and refractive index also increase with the tin content. Diffuse reflectance spectra in the infrared (DRIFT) showed that the presence of tin, even at low concentrations, is responsible for some structural changes since there is an increase of the bridging oxygen concentration. The doped glasses present a brown color and optical absorption spectra measurements are interpreted as being due to precipitation of tin in the form of colloidal particles during cooling of the melted glass. In the Na+ <-> K+ ion exchange process the presence of tin in the glass network hinders the diffusion of these ions. The diffusion coefficients of those ions were calculated by the Boltzmann-Matano technique, after concentration profiles obtained by EDS measurements. All results obtained present evidences that Sn4+ cation acts as a glass network former. (c) 2005 Elsevier B.V. All rights reserved.

Spectroscopic studies of SnO2 doped with Cr, Co or Nb

SnO2 ceramics doped with different amounts of Co, Cr or Nb were investigated using visible and infrared spectroscopy at room temperature. Based on the observed d-d transitions the valence states of incorporated dopants were determined. Values of the optical band-gap were calculated in all samples. The infrared spectra of the samples displayed variations in the position, relative intensity and width of the bands, which were attributed to the presence of dopants.

Photoluminescence of the Eu-doped thin film heterojunction GaAs/SnO2 and rare-earth doping distribution

Tin dioxide (SnO2) thin films doped with Eu3+, are deposited by the sol-gel-dip-coating process on top of GaAs films, which is deposited by resistive evaporation on glass substrate. This heterojunction assembly presents luminescence from the rare-earth ion, unlike the SnO2 deposition directly on a glass substrate, where emissions from the Eu3+ transitions are absent. The Eu3+ transitions are clearly identified and are similar to the observation on SnO2 pressed powder (pellets), thermally treated at much higher temperatures. However, in the form of heterojunction films, the Eu emission comes along a broad band, located at higher energy compared to Eu3+ transitions, which is blue-shifted as the thermal annealing temperature increases. The size of nanocrystallites points toward quantum confinement or electron transfer between oxygen vacancies, originated from the disorder in the material, and trivalent rare-earth ions, which present acceptor-like character in this matrix. This electron transfer may relax for higher temperatures in the case of pellets, and the broad band is eliminated.

Evidences of the evolution from solid solution to surface segregation in Ni-doped SnO(2) nanoparticles using Raman spectroscopy

Ni-doped SnO(2) nanoparticles, promising for gas-sensing applications, have been synthesized by a polymer precursor method. X-ray diffraction (XRD) and transmission electron microscopy (TEM) data analyses indicate the exclusive formation of nanosized particles with rutile-type phase (tetragonal SnO(2)) for Ni contents below 10 mol%. The mean crystallite size shows a progressive reduction with the Ni content. Room-temperature Raman spectra of Ni-doped SnO(2) nanoparticles show the presence of Raman active modes and modes activated by size effects. From the evolution of the A(1g) mode with the Ni content, a solubility limit at similar to 2 mol% was estimated. Below that content, Raman results are consistent with the occurrence of solid solution (ss) and surface segregation (seg.) of Ni ions. Above similar to 2 mol% Ni, the redshift of A(1g) mode suggests that the surface segregation of Ni ions takes place. Disorder-activated bands were determined and their integrated intensity evolution with the Ni content suggest that the solid-solution regime favors the increase of disorder; meanwhile, that disorder becomes weaker as the Ni content is increased. Copyright (C) 2010 John Wiley & Sons, Ltd.

Structural, electrical and magnetic studies of Co:SnO2 and (Co,Mo):SnO2 films prepared by pulsed laser deposition

Here we report on the structural, optical, electrical and magnetic properties of Co-doped and (Co,Mo)-codoped SnO2 thin films deposited on r-cut sapphire substrates by pulsed laser deposition. Substrate temperature during deposition was kept at 500 degrees C. X-ray diffraction analysis showed that the undoped and doped films are crystalline with predominant orientation along the [1 0 1] direction regardless of the doping concentration and doping element. Optical studies revealed that the presence of Mo reverts the blue shift trend observed for the Co-doped films. For the Co and Mo doping concentrations studied, the incorporation of Mo did not contribute to increase the conductivity of the films or to enhance the ferromagnetic order of the Co-doped films. (C) 2012 Elsevier B.V. All rights reserved.

Influence of pH of Colloidal Suspension on the Electrical Conductivity of SnO2 thin Films Deposited Via Sol-Gel-Dip-Coating

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Interface Formation and Electrical Transport in SnO2:Eu3+/GaAs Heterojunction Deposited by Sol-Gel Dip-Coating and Resistive Evaporation

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo da corrosão de cadinhos de SnO2-ZnO, na fusão de vidros contendo metais pesados

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Dependence of the nonlinear electrical behavior of SnO2-based varistors on Cr2O3 addition

Tin dioxide varistors doped with Coo, ZnO, Ta2O5 and Cr2O3 were prepared by the mixed oxide method. Temperature dependent impedance spectroscopy revealed two different activation energies, one at low frequencies and the other at high frequencies. These activation energies were associated with the adsorption and reaction of O-2 species at the grain boundary interface. We show that Cr2O3 improves the varistor properties, generating sites for the adsorption of O' and O at the grain boundary region. The O' and O defects are truly responsible for the barrier formation at the grain boundary interface. (c) 2005 Elsevier Ltd and Techna Group S.r.l. All rights reserved.