Transdentinal diffusion and cytotoxicity of self-etching adhesive systems

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Microleakage in primary teeth restored by conventional or bonded amalgam technique.

The aim of this in vitro study was to evaluate marginal leakage in class V restorations in primary teeth restored with amalgam, using three different techniques. Thirty maxillary anterior primary teeth, clinically sound and naturally exfoliated, were used. In group 1 (n = 10), two thin layers of a copal varnish (Cavitine) were applied. In group 2 (n = 10), Scotchbond Multi-Purpose Plus, a dual adhesive system, was used according to manufacturer instructions. In group 3 (n = 10), One-Step adhesive system in combination with a low-viscosity resin (Resinomer) were used according to manufacturer instructions. All samples were restored with a high-copper dental amalgam alloy (GS 80, SDI). After restoration, the samples were stored in normal saline at 37 degrees C for 72 h. The specimens were polished, thermocycled (500 cycles, 5 degrees and 55 degrees C, 30-s dwell time) and impermeabilized with fingernail polish to within 1.0 mm of the restoration margins. The teeth were then placed in 0.5% methylene blue for 4 h. Finally, the samples were sectioned and evaluated for marginal leakage. The Kruskal-Wallis test showed that the filled adhesive resin (group 3) had the least microleakage. There was no significant difference between groups 1 and 2.

Resistance to maxillary premolar fractures after restoration of class II preparations with resin composite or ceromer.

OBJECTIVE: The aim of this study was to evaluate the resistance to fracture of intact and restored human maxillary premolars. METHOD AND MATERIALS: Thirty noncarious human maxillary premolars, divided into three groups of 10, were submitted to mechanical tests to evaluate their resistance to fracture. Group 1 consisted of intact teeth. Teeth in group 2 received mesio-occlusodistal cavity preparations and were restored with direct resin composite restorations. Teeth in group 3 received mesio-occlusodistal cavity preparations and were restored with ceromer inlays placed with the indirect technique. After restoration, teeth were stored at 37 degrees C for 24 hours and then thermocycled for 500 cycles at temperatures of 5 degrees C and 55 degrees C. RESULTS: Statistical analysis revealed that group 3 (178.765 kgf) had a significantly greater maximum rupture load than did group 1 (120.040 kgf). There was no statistically significant difference between groups 1 and 2 or between groups 2 and 3. CONCLUSION: Class II cavity preparations restored with indirect ceromer inlays offered greater resistance to fracture than did intact teeth. The fracture resistance of teeth restored with resin composite was not significantly different from that of either the ceromer or intact teeth.

Polymerization shrinkage evaluation of three packable composite resins using a gas pycnometer.

Modern restorative dentistry has been playing an outstanding role lately since composite resins, allied to adhesive systems, have been widely applied on anterior and posterior teeth restorations. The evolution of composite resins has mostly been verified due to the improvement of their aesthetic behavior and the increase in their compressive and abrasive strengths. In spite of these developments, the polymerization shrinkage inherent to the material has been a major deficiency that, so far, has been impossible to avoid. Using a gas pycnometry, this research investigated the polymerization shrinkage of three packable composite resins: Filtek P60 (3M), Prodigy Condensable (Kerr), and SureFil (Dentsply/Caulk), varying the distance from the light source to the surface of the resins (2 mm or 10 mm). The pycnometer Accupyc 1330 (Micromeritics, USA) precisely records helium displacement, allowing fast and reliable measurements of the volume of composite resin immediately before and after polymerization, without interference of temperature or humidity. Results were not found to be statistically different for the three tested resins, either for 2 mm or 10 mm-distance from the light source to the composite surface.

Treatment options for the occlusal surface of first permanent molars

Restorative dentistry has been increasingly concerned with preservation of the dental structure. For that reason, ultraconservative cavity preparations have been performed with air abrasion systems. The aim of this study was to present treatment options for the occlusal surface of first permanent molars with employment of the conventional method and the air abrasion system for accomplishment of the cavity preparation and a composite occlusal matrix for an accurate reproduction of the tooth surface.

The effect of adhesive and flowable composite on postoperative sensitivity: 2-Week results

Objective: To measure 2-week postoperative sensitivity in Class II composite restorations placed with a self-etching adhesive (Clearfil SE Bond) or a total-etch adhesive (Prime&Bond NT) with or without a flowable composite as cervical increment. Method and materials: Upon approval by the University of Guarulhos Committee on Human Subjects, 100 restorations were inserted in 46 patients who required Class II restorations in their molars and premolars. Enamel and dentin walls were conditioned with a self-etching primer (for Clearfil SE Bond) or etched with 34% phosphoric acid (for Prime&Bond NT). A 1- to 2-mm-thick increment of a flowable composite (Filtek Flow) was used in the proximal box in 50% of the restorations of each adhesive. Preparations were restored with a packable composite (Surefil). The restorations were evaluated preoperatively and 2 weeks postoperatively for sensitivity to cold, air, and masticatory forces using a visual analog scale. Marginal integrity of the accessible margins was also evaluated. Statistical analysis used a mixed linear model with subject as a random effect. Results: Ninety-eight teeth from 44 subjects were observed at 2 weeks. The type of adhesive and use of flowable composite had no significant effects or interaction for any of the four outcomes of interest, ie, change from baseline to 2 weeks in sensitivity and response time for the cold or air stimulus. For the air stimulus, the overall average change from baseline was not significant for either sensitivity or response time. For the cold stimulus, the overall average change from baseline was significant for both sensitivity and response time. No case of sensitivity to masticatory forces was observed. Conclusion: No differences in postoperative sensitivity were observed between a self-etch adhesive and a total-etch adhesive at 2 weeks. The use of flowable composite did not decrease postoperative sensitivity.

Clinical evaluation of proximal contacts of Class II esthetic direct restorations

Objective: This study evaluated the effectiveness of proximal contacts in Class II restorations using two types of matrix bands (steel and polyester) with two different restoration techniques (incremental and with prepolymerized particles). Method and materials: Eighty-eight Class II adjacent restorations using Prodigy resin composite were performed: 44 with the incremental technique (22 with steel matrix bands, 22 with polyester matrix bands) and 44 utilizing prepolymerized resin particles (22 steel matrix, 22 polyester matrix). The restorations were clinically evaluated at baseline and at 6, 12, and 18 months. Proximal contacts obtained immediately after restoration procedure in all restorations were satisfactory. Results: No statistically significant alterations were found in 18 months of evaluation. Conclusion: Regardless of the utilized resin composite, there were no differences in the amount of proximal contact variations with respect to tested techniques and matrices.

Effect of ceramic surface treatment on the microtensile bond strength between a resin cement and an alumina-based ceramic

Purpose: The objective of this study was to test the following hypothesis: the silica coating on ceramic surface increases the bond strength of resin cement to a ceramic. Materials and Methods: In-Ceram Alumina blocks were made and the ceramic surface was treated: G1 - sandblasting with 110-μm aluminum oxide particles; G2 - Rocatec System: tribochemicai silica coating (Rocatec-Pre powder + Rocatec-Plus powder + Rocatec-Sil); G3 - CoJet System: silica coating (CoJet-Sand) + ESPE-Sil. The ceramic blocks were cemented to composite blocks with Panavia F resin cement (under a load of 750 g/1 min). The cemented blocks were stored in distilled water at 37°C for 7 days and sectioned along the x and y axes with a diamond disk. Samples with an adhesive area of ca 0.8 mm 2 (n = 45) were obtained. The samples were attached to an adapted device for the microtensile test, which was performed in a universal testing machine (EMIC) at a crosshead speed of 1 mm/min. Results: The obtained results were submitted to ANOVA and Tukey's test. Mean values of tensile strength (MPa) and standard deviation values were: (G1) 16.8 ± 3.2; (G2) 30.6 ± 4.5; (G3) 33.0 ± 5.0. G2 and 63 presented greater tensile strength than G1. There was no significant difference between G2 and G3. All the failures took place at the ceramic/resin cement interface. Conclusion: The silica coating (Rocatec or CoJet systems) of the ceramic surface increased the bond strength between the Panavia F resin cement and alumina-based ceramic.

SEM analysis of internal adaptation of adhesive restorations after contamination with saliva

Purpose: This study tested the null hypothesis that different treatments of saliva-contaminated substrate would not affect microgap formation at the dentin walls of bonded restorations. Materials and Methods: Forty freshly extracted human molars received standardized Class V preparations on buccal and lingual surfaces. The specimens were assigned to four experimental groups (n = 20): [G1] no contamination (control group), [G2] saliva contamination (10 s) after etching followed by 5 s air stream; [G3] saliva contamination after etching and rinsed for 10 s; and [G4] re-etching for 10 s after saliva contamination. All specimens were restored with a one-bottle adhesive (Single Bond, 3M ESPE) and microhybrid composite resin (Filtek Z250, 3M ESPE) according to the manufacturer's instructions. The specimens were thermocycled, sectioned through the center of the restoration, and then processed for SEM. Microgaps were measured at the axial wall at 1500X magnification. The data were submitted to Kruskal-Wallis nonparametric statistical analysis at p < 0.05. Results: The data revealed that different groups resulted in a statistically significant difference (p < 0.01) in gap formation. Air drying [G2] and rinsing [G3] the saliva-contaminated dentin resulted in similar microgap values (p > 0.05). However, re-etching the dentin after saliva contamination [G4] increased microgap formation (p < 0.05) when compared with the groups G1 and G2. Although air drying and rinsing produced results comparable to noncontaminated dentin, the presence of microgaps was not completely eliminated. Conclusion: Contaminated saliva did not prevent hybrid layer formation; however, it did reduce the adaptation of the restorative material to bonded surfaces.

Comparative study of MTA and other materials in retrofilling of pulpless dogs' teeth

This in vivo study compared the effect of mineral trioxide aggregate (MTA), IRM, Super EBA and ZOE in a puttylike consistency, used as retrofilling materials, in the healing process of periapical tissue of pulpless dogs' teeth submitted to a conventional retrofilling technique. Twenty-four premolars obtained from three dogs were used. At the first intervention, the animals were anesthetized, coronal access was obtained and pulpectomy was done. Root canals were kept open to the oral environment for 180 days to induce the formation of apical lesions. After surgical removal of the lesions with curettes, 2 mm of the apical root was cut out perpendicular to the long axis of the teeth, and root-end cavities were shaped with a low-speed round bur. The bone cavities were irrigated and dried, and the root-end cavities were filled with MTA, IRM, Super EBA and ZOE in a puttylike consistency. The bone cavities were passively filled with blood and flaps were sutured. The coronal access openings were cleaned and double-sealed with ZOE and amalgam. After 180 days, the animals were killed by anesthetic overdose, maxilla and mandible were removed and the pieces were processed for histomorphologic analysis. Data were evaluated blindly on the basis of several histopathologic events and the scores obtained were analyzed statistically using the Kruskal Wallis test. No significant differences were observed among MTA, Super EBA and IRM (p>0.05). However, ZOE had a significantly more negative influence on the apical healing (p<0.05). In conclusion, MTA, Super EBA and IRM had similar histopathologic effects among each other and better performance than ZOE used in a puttylike consistency. Furthermore, only MTA stimulated hard tissue deposition in direct contact with the retrofilling material, even when it was inserted under critical conditions.

Aplicação da técnica de condicionamento total ou de primers autocondicionantes em dentes decíduos após abrasão a ar

Since the use of air abrasion has grown in pediatric dentistry, the aim of this study was to evaluate, by means of shear bond strength testing, the need to use the total etching technique or self-etching primers on dentin of primary teeth after air abrasion. Twenty-five exfoliated primary molars had their occlusal dentin exposed by trimming and polishing. Specimens were treated by: Air abrasion + Scotchbond MultiPurpose adhesive (G1); 37% phosphoric acid + Scotchbond MP adhesive (G2); Clearfil SE (G3); Air abrasion ( 37% phosphoric acid + Scotchbond MP adhesive (G4); Air abrasion + Clearfil SE (G5). On the treated surface, a cylinder of 2 mm by 6 mm was made using a composite resin (Z100). Duncan's test showed that: (G2 = G3 = G5) > (G1 = G4). The use of a selfetching primer on air abraded dentin is recommended to obtain higher bond strengths.

Influence of activation modes on diametral tensile strength of dual-curing resin cements.

In metallic restorations, the polymerization of dual-curing resin cements depends exclusively on chemical activation. The effect of the lack of photoactivation on the strength of these cements has been rarely studied. This study evaluated the influence of activation modes on the diametral tensile strength (DTS) of dual-curing resin cements. Base and catalyst pastes of Panavia F, Variolink II, Scotchbond Resin Cement, Rely X and Enforce were mixed and inserted into cylindrical metal moulds (4 x 2 mm). Cements were either: 1) not exposed to light (chemical activation = self-cured groups) or 2) photoactivated through mylar strips (chemical and photo-activation = dual-cured groups) (n = 10). After a 24 h storage in 37 masculineC distilled water, specimens were subjected to compressive load in a testing machine. A self-curing resin cement (Cement-It) and a zinc phosphate cement served as controls. Comparative analyses were performed: 1) between the activation modes for each dual-curing resin cement, using Students t test; 2) among the self-cured groups of the dual-curing resin cements and the control groups, using one-way ANOVA and Tukeys test (alpha = 0.05). The dual-cured groups of Scotchbond Resin Cement (53.3 MPa), Variolink II (48.4 MPa) and Rely X (51.6 MPa) showed higher DTS than that of self-cured groups (44.6, 40.4 and 44.5 MPa respectively) (p < 0.05). For Enforce (48.5 and 47.8 MPa) and Panavia F (44.0 and 43.3 MPa), no significant difference was found between the activation modes (p > 0.05). The self-cured groups of all the dual-curing resin cements presented statistically the same DTS as that of Cement-It (44.1 MPa) (p > 0.05), and higher DTS than that of zinc phosphate (4.2 MPa). Scotchbond Resin Cement, Variolink II and Rely X depended on photoactivation to achieve maximum DTS. In the absence of light, all the dual-curing resin cements presented higher DTS than that of zinc phosphate and statistically the same as that of Cement-It (p > 0.05).

Scanning electron microscope analysis of internal adaptation of materials used for pulp protection under composite resin restorations

Purpose: The aim of this study was to evaluate the interfacial microgap with different materials used for pulp protection. The null hypothesis tested was that the combination of calcium hydroxide, resin-modified glass ionomer, and dentin adhesive used as pulp protection in composite restorations would not result in a greater axial gap than that obtained with hybridization only. Materials and Methods: Standardized Class V preparations were performed in buccal and lingual surfaces of 60 caries-free, extracted human third molars. The prepared teeth were randomly assessed in six groups: (1) Single Bond (SB) (3M ESPE, St. Paul, MN, USA); (2) Life (LF) (Kerr Co., Romulus, MI, USA) + SB; (3) LF + Vitrebond (VT) (3M ESPE) + SB; (4) VT + SB; (5) SB + VT; (6) SB + VT + SB. They were restored with microhybrid composite resin Filtek Z250 (3M ESPE), according to the manufacturer's instructions. However, to groups 5 and 6, the dentin bonding adhesive was applied prior to the resin-modified glass ionomer. The specimens were then thermocycled, cross-sectioned through the center of the restoration, fixed, and processed for scanning electron microscopy. The specimens were mounted on stubs and sputter coated. The internal adaptation of the materials to the axial wall was analyzed under SEM with × 1,000 magnification. Results: The data obtained were analyzed with nonparametric tests (Kruskal-Wallis, p ≤ .05). The null hypothesis was rejected. Calcium hydroxide and resin-modified glass ionomer applied alone or in conjunction with each other (p < .001) resulted in statistically wider microgaps than occurred when the dentin was only hybridized prior to the restoration. ©2005 BC Decker Inc.

The effect of adhesive systems on the pullout strength of a fiberglass-reinforced composite post system in bovine teeth

Purpose: To evaluate the pullout strength of a glass fiber-reinforced composite post (glass FRC) cemented with three different adhesive systems and one resin cement. The null hypothesis was that pullout strengths yielded by the adhesive systems are similar. Materials and Methods: Thirty bovine teeth were selected. The size of the specimens was standardized at 16 mm by sectioning off the coronal portion and part of the root. The specimens were divided into three groups, according to the adhesive system, which were applied following the manufacturers' instructions: G1, ScotchBond Multi-Purpose Plus; G2, Single Bond; G3, Tyrian SPE/One-Step Plus. The glass FRCs (Reforpost) were etched with 37% H3PO4 for 1 min and silanized (Porcelain Primer). Thereafter, they were cemented with the dual resin cement En-Force. The specimens were stored for 24 h, attached to an adapted device, and submitted to the pullout test in a universal testing machine (1 mm/min). The data were submitted to the one-way ANOVA and Tukey's test (α = 0.05). Results: G1 (30.2 ± 5.8 Kgf) displayed the highest pullout strength (p < 0.001) when compared to G2 (18.6 ± 5.8 Kgf) and G3 (14.3 ± 5.8 Kgf), which were statistically similar. Analysis of the specimens revealed that all failures occurred between the adhesive system and the root dentin (pullout of the post cement), regardless of group. Conclusion: The multiple-bottle, total-etch adhesive system provided higher pullout strength of the glass FRC when compared to the single-bottle, total-etch, and single-step self-etching adhesive systems. The null hypothesis was rejected (p < 0.001).

Effect of dentinal surface preparation on bond strength of self-etching adhesive systems

The aim of this study was to evaluate the effects of dentin surface treatments on the tensile bond strength (TBS) of the self-etching primer Clearfil SE Bond (CSE) and the one-step self-etching One-Up Bond F (OUB). The exposed flat dentin surfaces of twenty-four sound third molars were prepared with diamond bur at high-speed, carbide bur at low-speed or wet ground with #600 grit SiC paper. The adhesive systems were applied to the dentin surfaces and light-cured according to the manufacturers' instructions. A 6-mm high composite crown was incrementally built-up and each increment was light-cured for 40 seconds. After being stored in water (37°C/24 h), the samples were serially sectioned parallel to the long axis, forming beams (n = 20) with a cross-sectional area of approximately 0.8 mm 2. The specimens were tested in a Universal Testing Machine at 0.5 mm/min. The cross-sectional area was measured and the results (MPa) were analyzed by two-way ANOVA and Tukey Test (p < 0.05). Overall, the groups treated with CSE exhibited the highest TBS for all surface treatments. Dentin surfaces prepared with carbide bur at low speed reduced TBS in the CSE group; however, OUB was not affected by surface treatments. The effect of surface abrasive methods on TBS was material-dependent.