Influência do número de refundições da liga Ni-Cr-Mo-Ti sobre as propriedades de próteses metalocerâmicas

A frequently encountered difficulty in oral prosthetics is associated with the loss of metallic alloys during the melting stage of the production of metal-ceramic replacement systems. Remelting such materials could impar their use in oral rehabilitation due to loss in esthetics, as well as in the chemical, physical, electrochemical and mechanical properties. Nowadays, the Ni-Cr-Mo-Ti alloy is widely used in metal-ceramic systems. Manufacturers state that this material can be remelted without significant alterations in its behavior, however little has been established as to the changes in the performance of this alloy after successive remelting, which is common practice in oral prosthetics. Therefore, the objective of this study was to evaluate possible changes in the esthetics and associated properties of metalceramic samples consisting of Ni-Cr-Mo-Ti and dental porcelain. Three to five remelting steps were carried out. The results revealed that Ni-Cr-Mo-Ti can be safely used even after three remelting steps. Further remelting significantly affect the characteristics of the alloys and should not be recommended for the manufacture of metal-ceramic systems

Formulação de massas cerâmicas para porcelanas elétricas utilizando resíduos oriundos de corpos de fusíveis

The power industry generates as waste ceramic bodies of electrical fuses that are discarded after use. The formulation of ceramic bodies for porcelain electrical insulators using waste from the bodies fuse allocation promotes environmentally appropriate, through the reuse of the material. This work evaluated the technical feasibility of using waste for use in electrical porcelains with formulations containing the residue, feldspar and kaolinite. The raw materials were processed through grinding and sieving to 200 mesh. The ceramic material obtained from the proposed formulations with 25%, 30%, 34% and 40% of the residue went through a vibratory mill for grinding and homogenization, and then were sieved at 325 mesh. The samples were shaped in a uniaxial press, with the application of 25 MPa and sintered at 1100° C, 1150°C, 1200°C, 1225°C and 1250°C, at levels of 20 and 45 minutes. Were also developed bodies of evidence with reference formulations obtained without residue, to establish a comparison on physical, mechanical and electrical. The tests were conducted and technology: linear shrinkage, porosity, water absorption, resistance to bending to three points, measuring insulation resistance electrical resistivity of the material, X-ray diffraction and X-ray fluorescence Waste characterizations pointed to the existence of two phases: mullite and quartz phases are of great importance in the microstructure of the ceramic and this fact reveals a possibility for reuse in electrical porcelains. The mullite is an important constituent because it is a phase that makes it possible to increase the mechanical strength in addition to the body allows the use at high temperatures. The use of ceramic bodies residue fuses, proved feasible for application in electrical porcelain and the most significant results were obtained by the formulations with 25% waste and sintering at 1200°C

Estudo da oxidação superficial de ligas odontológicas de Ni-Cr em plasma pulsado para uso em restaurações metalocerâmicas

Metal ceramic restorations matches aesthetic and strength, and in your making occurs an interface oxide layer, wetting resulting and atomic and ionic interactions resulting between metal, oxide and porcelain. However, frequent clinical fails occurs in this restoration type, because lost homogeneous deposition oxide layer and lost interface bond. Thus, in this study, thought depositate homogeneous oxide films above Ni-Cr samples surfaces polite previously, at plasma oxide environment. Six samples was oxided at 300 and 400ºC at one hour, and two samples was oxided in a comum chamber at 900ºC, and then were characterized: optical microscopic, electronic microscopic, micro hardness, and X ray difratometry. Colors stripes were observed at six samples plasma oxided and a grey surface those comum oxided, thus like: hardness increase, and several oxides from basic metals (Ni-Cr)

Avaliação do desgaste abrasivo causado pelas cerâmicas Duceram e Vita em resinas compostas pelo método do disco retificado

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Análise da influência dos diferentes tempos de polimerização por luz incandescente sobre a resistência ao desgaste abrasivo de resinas compostas

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Avaliação clínica e radiográfica das complicações técnicas em próteses sobre implantes

The evaluation criteria of the cases treated with dental implants are based on clinical and radiographic tests. In this context it is important to conduct research to determine prognosis of different types of prosthetic rehabilitation and determination of the main problems affecting this type of treatment. Thus, the objective of this study was to assess the prosthetic conditions of individuals rehabilitated with implant-supported prosthesis. In this cross-sectional study 153 patients were treated, accounting for a sample of 509 implants. The failures were observed by clinical and radiographic examination. The results showed that the fracture (0.2%) loss (0.4%) and loosening of the screws (3.3%) were failures are less frequent. The fracture structures as the resin (12.4%), porcelain (5.5%) and metallic (1.5%), loss of resin that covers the screw (23.8%) and loss of retention overdentures on implants (18.6%) had a higher occurrence. The failure of adaptation between the abutment and the implant (6.9%) and especially between the prosthesis and the abutment (25.4%) had a high prevalence and, when related to other parameters showed a significant association, particularly with the cemented prosthesis (OR = 6.79). It can be concluded that to minimize the appearance of failures, protocols must be observed from diagnosis to the settlement and control of prostheses on implants, particularly with respect to technical steps of the making of the prosthesis and care in radiographic evaluating the fit between their components

Efeito alelopático de plantas daninhas e concentrações de capim-braquiária (Brachiaria decumbens) no desenvolvimento inicial de eucalipto (Eucalyptus grandis)

Com o objetivo de verificar possível efeito alelopático de 18 espécies de plantas daninhas sobre o crescimento inicial de Eucalyptus grandis, realizaram-se dois experimentos em casa de vegetação. No primeiro experimento, dentre 18 espécies de plantas daninhas testadas, Brachiaria decumbens (BRADC) demonstrou acentuada capacidade de reduzir o crescimento de Eucalyptus grandis, quando incorporada ao solo. No segundo experimento avaliou-se o efeito da adição no substrato de concentrações de matéria seca de BRADC sobre o crescimento inicial de mudas de E. grandis. A matéria seca triturada de BRADC foi incorporada ao solo nas concentrações de 0% (testemunha), 0,5%, 1,0%, 2,0% e 3,0% (p/p). Instalou-se também uma réplica do experimento, com adição de idênticas quantidades totais de carbono entre os tratamentos. O ajuste da quantidade de carbono foi feito através da adição de Sphagnum. Extraiu-se a solução do solo por meio de cápsulas de porcelana introduzidas nos vasos quando do transplante das mudas de eucalipto. As soluções foram coletadas ao final do experimento (39 dias após o transplante das mudas), sendo utilizadas para a determinação de pH, condutividade elétrica, potencial osmótico e para análise de teores de nutrientes. As mínimas proporções de BRADC, com efeito inibitório, foram de 0,5 e 1,0%, com e sem Sphagnum, respectivamente. Nestas duas condições, a área foliar média do eucalipto foi reduzida em 24 e 23%, respectivamente. As análises de solução do solo dos tratamentos permitiram concluir que os teores de nutrientes e as características químicas destes foram pouco alterados pelos tratamentos, sendo pouco provável que a redução do crescimento do E. grandis se deva às restrições nas quantidades de nutrientes disponíveis.

Avaliação da resistência de união metalocerâmica em função de diferentes tempos de oxidação prévia

Avaliou-se a resistência de união metal/porcelana utilizando-se uma liga de Ni-Cr, submetida a diferentes tempos de oxidação prévia com o sistema cerâmico Vita-VMK, através do teste preconizado por CHIODI NETTO3. A análise dos resultados permitiu as seguintes conclusões: a ausência da oxidação prévia possibilitou os melhores resultados, sendo que a diferença foi estatisticamente significante; diferentes tempos de oxidação prévia provocaram redução acentuada nos valores obtidos e foram semelhantes entre si; o grupo submetido ao processo de jateamento após a oxidação prévia por cinco minutos mostrou resultados similares aos grupos que também passaram pelo processo de oxidação e não sofreram jateamento posterior.

Desgaste abrasivo e dureza de seis resinas compostas expostas a diferentes tempos de fotopolimerização com aparelhos de LED e lâmpada incandescente

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Uma contribuição para o estudo do efeito causado pela névoa salina em isoladores cerâmicos de chaves fusíveis

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Avaliação da influência de diferentes materiais oclusais na confecção de próteses fixas implantossuportadas unitárias com diferentes diâmetros dos implantes osseointegrados: estudo pelo método dos elementos finitos tridimensionais

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Caracterização de materiais descartados de redes de distribuição de eletricidade para fins de reciclagem

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Efeito de tratamentos de superfície sobre a adesão de reparo com resina composta em restarações cerâmicas á base de zircônia Y-TPZ envelhecida hidrotermicamente

Pós-graduação em Reabilitação Oral - FOAR

Avaliação pelo método dos elementos finitos de cargas axiais aplicadas sobre implantes e componentes protéticos com diversas inclinações

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Avaliação da resistência ao cisalhamento de sistemas para reparo em metalocerâmicas

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)