Fractal effects on the measurement of the specific surface areas of single-walled carbon nanotubes

The specific surface area (SSA) of single-walled carbon nanotubes (SWNTs) has been measured by different groups. Fujiwara et al. measured the SSA of SWNT bundles by using nitrogen and oxygen as adsorbates, and found that the SSA from O2-adsorption was 6.6% larger than that from N2-adsorption for the same SWNT sample [1]. Also Wei et al. [2] measured the SSA of HiPco SWNTs by using O2, N2 and Ar, and found that, for the same samples, Vm(Ar) > Vm(O2) > Vm(N2), here Vm is the monolayer adsorption capacity at the standard conditions of temperature and pressure (STP). Those research results indicate that, for the same SWNT sample, its measured surface area depends on the employed adsorbate.

Adsorption of argon on homogeneous graphitized thermal carbon black and heterogeneous carbon surface

In this paper we investigate the effects of surface mediation on the adsorption behavior of argon at different temperatures on homogeneous graphitized thermal carbon black and on heterogeneous nongraphitized carbon black surface. The grand canonical Monte Carlo (GCMC) simulation is used to study the adsorption, and its performance is tested against a number of experimental data on graphitized thermal carbon black (which is known to be highly homogeneous) that are available in the literature. The surface-mediation effect is shown to be essential in the correct description of the adsorption isotherm because without accounting for that effect the GCMC simulation results are always greater than the experimental data in the region where the monolayer is being completed. This is due to the overestimation of the fluid–fluid interaction between particles in the first layer close to the solid surface. It is the surface mediation that reduces this fluid–fluid interaction in the adsorbed layers, and therefore the GCMC simulation results accounting for this surface mediation that are presented in this paper result in a better description of the data. This surface mediation having been determined, the surface excess of argon on heterogeneous carbon surfaces having solid–fluid interaction energies different from the graphite can be readily obtained. Since the real heterogeneous carbon surface is not the same as the homogeneous graphite surface, it can be described by an area distribution in terms of the well depth of the solid–fluid energy. Assuming a patchwise topology of the surface with patches of uniform well depth of solid–fluid interaction, the adsorption on a real carbon surface can be determined as an integral of the local surface excess of each patch with respect to the differential area. When this is matched against the experimental data of a carbon surface, we can derive the area distribution versus energy and hence the geometrical surface area. This new approach will be illustrated with the adsorption of argon on a nongraphitized carbon at 87.3 and 77 K, and it is found that the GCMC surface area is different from the BET surface area by about 7%. Furthermore, the description of the isotherm in the region of BET validity of 0.06 to 0.2 is much better with our method than with the BET equation.

Thermal stability of porous sol-gel phosphosilicates and their surface area stabilisation by lanthanum addition

The thermal stability of porous sol-gel phosphosilicates was studied by comparing the textural features upon calcination between 400 and 550 °C. A significant loss of surface area and pore volume were observed; the first is due to thermal coarsening of the nanoparticles, and the pore volume reduction was ascribed to sintering of the most external nanoparticles producing less void volume. Lanthanum addition was investigated as thermal stabilizer. For the mesoporous phosphosilicate composition, lanthanum addition enhanced the surface area, showing a 45% and 50% improvement with respect to the La-free counterpart; the effect was much less visible for the macroporous composition.

Condensation-enhanced self-assembly as a route to high surface area α-aluminas

High surface area nanosized α-alumina has been obtained by thermally treating a sol-gel-derived mesophase at 1200 C; the mesophase was synthesized by a sol-gel route involving evaporation induced self-assembly (EISA) of a hydrolyzed gel from Al-tri-sec-butoxide in s-BuOH in the presence of a nonionic surfactant (EO20PO70EO20), HCl as catalyst, and water (H2O/Al = 6). The activated material renders moderate surface areas of about 8.4-10 m2 g-1, associated with significant crystallite coarsening. The key aspect to produce smaller crystallites is making the mesophase more resistant to coarsening. This was achieved by enhancing the condensation step by treating the hydrolyzed gel with tetrabutyl ammonium hydroxide (TBAOH) before evaporation. The characteristics of the mesophase indicate condensation of the primary particles with less AlO5 unsaturated sites, at the expense of a lower solid yield due to small crystallites dissolution. The activated TBAOH condensed EISA material is composed of α-alumina aggregated crystallites of about 60-100 nm, and the material possesses surface areas ranging from 16 to 24 m2 g -1 due to the improved resistance to coarsening. At least two aspects are suggested to play a role in this. The worm-hole morphology of the mesophase aggregates yields high particle coordination, which favors densification rather than coarsening. Furthermore, the decrease of the AlO5 defect sites by the TBAOH condensation makes the mesophase less reactive and consequently more resistant to coarsening. © 2013 American Chemical Society.

Time-series of snow spectral albedo and superficial snow specific surface area at Dome C in Antarctica, 2012-2015

Spectral albedo has been measured at Dome C since December 2012 in the visible and near infrared (400 - 1050 nm) at sub-hourly resolution using a home-made spectral radiometer. Superficial specific surface area (SSA) has been estimated by fitting the observed albedo spectra to the analytical Asymptotic Approximation Radiative Transfer theory (AART). The dataset includes fully-calibrated albedo and SSA that pass several quality checks as described in the companion article. Only data for solar zenith angles less than 75° have been included, which theoretically spans the period October-March. In addition, to correct for residual errors still affecting data after the calibration, especially at the solar zenith angles higher than 60°, we produced a higher quality albedo time-series as follows: In the SSA estimation process described in the companion paper, a scaling coefficient A between the observed albedo and the theoretical model predictions was introduced to cope with these errors. This coefficient thus provides a first order estimate of the residual error. By dividing the albedo by this coefficient, we produced the "scaled fully-calibrated albedo". We strongly recommend to use the latter for most applications because it generally remains in the physical range 0-1. The former albedo is provided for reference to the companion paper and because it does not depend on the SSA estimation process and its underlying assumptions.

Synthesis of Nb(2)O(5)center dot nH(2)O nanoparticles by water-in-oil microemulsion

Hydrous niobium oxide (Nb(2)O(5)center dot nH(2)O) nanoparticles had been Successfully prepared by water-in-oil microemulsion. They were characterized by X-ray diffraction (XRD), thermal analysis (TG/DTG), Fourier transform infrared spectroscopy (FTIR), BET surface area measurement, transmission electron microscopy (TEM), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS). The results showed that the nanoparticle was exactly Nb(2)O(5)center dot nH(2)O with spherical shape. Their BET surface area was 60 m(2) g(-1). XRD results showed that Nb(2)O(5)center dot nH(2)O nanoparticles with crystallite size in nanometer scale were formed. The crystallinity and crystallity size increased with increasing annealing temperature. TT-phase of Nb(2)O(5) was obtained when the sample is annealed at 550 degrees C. (C) 2009 Elsevier B.V. All rights reserved.

Carbide lime and industrial hydrated lime characterization

This paper focuses on the characterization of carbide lime (CL) - a by-product of acetylene production, composed mainly of calcium hydroxide with minor parts of carbonate - and compares its features to those of ""dry"" hydrated lime (HL) commonly used as a building material. Chemical, thermogravimetric and X-ray diffraction analyses indicated that the limes are similar in chemical and mineralogical compositions. except for the presence of carbon in the waste. Morphological and elemental chemical analyses by SEM and EDS revealed that CL particles differ from HL ones in their morphology and by the presence of carbon formations, Physical characterization included density and BET surface area of the materials. as well as, their particle size distributions in deionized water at diverse time periods. CL underwent agglomeration after approximately 60 min in water, whereas HL progressively became finer with time as determined by laser diffraction. In addition, water retention and squeeze flow tests were used to assess the pastes` fresh properties. (c) 2009 Elsevier B.V. All rights reserved.

gamma-alumina nanofibers prepared from aluminum hydrate with poly(ethylene oxide) surfactant

Introducing poly(ethylene oxide) surfactant to aluminum hydrate colloids can effectively direct the crystal growth of boehmite and the crystal morphology of final gamma-alumina crystallites. Fibrous crystallites of gamma-alumina about 3-4 nm thick and 30-60 nm long are obtained. They stack randomly, resulting in a structure with a low contact area between the fibers but with a very large porosity. Such a structure exhibits strong resistance to sintering when heated to high temperatures. A sample retains a BET surface area of 68 m(2)/g, after being heated to 1473 K. The surfactant molecules form micelles that interact with the colloid particles of aluminum hydroxide through hydrogen bonding. This interaction is not sufficient to change the intrinsic crystal structure of boehmite, but induces profound changes in the morphology of boehmite crystallites and their growth. The surfactant-induced fiber formation (SIFF) process has distinct features from templated synthesis but shows similarities in some respects to biomineralization processes in which inorganic crystals with complex morphological shapes can be formed in biological systems. SIFF offers an effective approach to create new nanostructures of inorganic oxide from aqueous media.

Preparação e caracterização de carvão ativado quimicamente a partir da casca de arroz

This work consists in a study about the chemical activation of charred rice hulls using NaOH as the activation agent. The influence of the naturally-occurring silica was particularly evidenced. X-ray diffraction patterns showed the formation of sodium carbonate and silicates in the activated samples, whereas thermogravimetric curves revealed a strong reduction in the ash content of these samples after washing with water. Nitrogen adsorption data indicated a microporosity development only in the washed samples, with BET surface area values of 450 and 1380 m2/g achieved for the samples activated at 800 °C starting from the precursor with or without silica, respectively.

Estudi per la selecció de CAG pel procés de potabilització de l'ETAP Ter

El present document representa l’estudi per la selecció de CAG pel procés de potabilització de l’ETAP Ter a partir d’un disseny experimental de planta pilot de menor escala. Es determina l'adequació de carbó en base a les característiques físiques (superfície BET, índex de iode...) i la capacitat d’eliminació de COT i UV respecte la mostra a tractar.

Síntese e propriedades catalíticas em reações de oxidação de goethitas contendo nióbio

Nb-substituted goethites have been prepared and characterized by Mössbauer spectroscopy, XRD, SEM and BET surface area measurements. Mössbauer and XRD analyses suggested that Nb replaces Fe3+ in the structure with duplet formation. The insertion of Nb into the goethite structure caused a significant increase in the BET surface area of the material. The prepared alpha-Fe1-xNb xOOH was investigated for the H2O2 decomposition to O2 and for the Fenton reaction to oxidize the dye methylene blue. It was observed that the introduction of Nb in to goethite produced a strong increase in the activity of oxidation of the dye contaminant by H2O2.