Effect of Carbamide Peroxide Bleaching Gel Concentration on the Bond Strength of Dental Substrates and Resin Composite

Purpose: This study evaluated the effect of bleaching gel containing 10%, 15% and 20% carbamide peroxide (CP) on the bond strength of dental enamel or dentin and resin composite restorations.Methods: The buccal surfaces of 12 bovine tooth crowns were conditioned with 37% phosphoric acid, and the adhesive resin Single Bond 2 and the resin composite Filtek Z350 were used to perform the restorations. The blocks were sectioned to obtain bar specimens. Each specimen group (enamel-E, dentin-D) was divided into four subgroups (n=15): S-artificial saliva; 10-10% CP bleaching; 15-15% CP bleaching; 20-20% CP bleaching. CP was applied for six hours daily for two weeks. The specimens were submitted to the a test in a universal testing machine. The data were analyzed by one-way ANOVA and the Tukey post-hoc test and a correlation analysis (r) was performed.Results: For Group E, the mean value (+/- standard-deviation) was 21.86 (+/- 6.03)a, 18.91 (+/- 8.31)ab, 15.43 (+/- 7.44)b and 10.6 (+/- 4.94)c for ES, E10, E15 and E20, respectively. For Group D, the alpha values were 34.73 (+/- 4.68)a, 35.12 (+/- 13.43)a, 29.67 (+/- 6.84)ab and 24.56 (+/- 6.54)b for DS, D10, D15 and D20, respectively. A negative correlation between the CP concentration and mean values was observed for both the enamel (r=-0.95) and dentin (r=-0.85) groups.Conclusion: In the current study, the bond strength of the restoration to enamel and the restoration to dentin were influenced by the application of CP and was dependent on the CP concentration in the bleaching gel.

Effects of cement thickness and bonding on the failure loads of CAD/CAM ceramic crowns: Multi-physics FEA modeling and monotonic testing

Objective. To determine the influence of cement thickness and ceramic/cement bonding on stresses and failure of CAD/CAM crowns, using both multi-physics finite element analysis and monotonic testing.Methods. Axially symmetric FEA models were created for stress analysis of a stylized monolithic crown having resin cement thicknesses from 50 to 500 mu m under occlusal loading. Ceramic-cement interface was modeled as bonded or not-bonded (cement-dentin as bonded). Cement polymerization shrinkage was simulated as a thermal contraction. Loads necessary to reach stresses for radial cracking from the intaglio surface were calculated by FEA. Experimentally, feldspathic CAD/CAM crowns based on the FEA model were machined having different occlusal cementation spaces, etched and cemented to dentin analogs. Non-bonding of etched ceramic was achieved using a thin layer of poly(dimethylsiloxane). Crowns were loaded to failure at 5 N/s, with radial cracks detected acoustically.Results. Failure loads depended on the bonding condition and the cement thickness for both FEA and physical testing. Average fracture loads for bonded crowns were: 673.5 N at 50 mu m cement and 300.6 N at 500 mu m. FEA stresses due to polymerization shrinkage increased with the cement thickness overwhelming the protective effect of bonding, as was also seen experimentally. At 50 mu m cement thickness, bonded crowns withstood at least twice the load before failure than non-bonded crowns.Significance. Occlusal "fit" can have structural implications for CAD/CAM crowns; pre-cementation spaces around 50-100 mu m being recommended from this study. Bonding benefits were lost at thickness approaching 450-500 mu m due to polymerization shrinkage stresses. (C) 2012 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Marginal and Internal Discrepancies Related to Margin Design of Ceramic Crowns Fabricated by a CAD/CAM System

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

In Vitro Assessment of Chemical Activation Efficiency During In-office Dental Bleaching

Purpose: This study compared five types of chemical catalyzing agents added to 35% hydrogen peroxide gel, with regard to their capacity of intensifying in-office dental bleaching results.Methods: One-hundred and twenty bovine incisors were used, of which the crowns and roots were cut in the incisor-apical direction, to acquire the dimensions of a human central incisor. The specimens were sectioned in the mesiodistal direction by means of two longitudinal cuts, the lingual halves being discarded. The vestibular halves received prophylaxis with a bicarbonate jet, ultrasound cleaning and acid etching on the dentinal portion. Next, the specimens were stored in receptacles containing a 25% instant coffee solution for two weeks. After the darkening period, initial measurement of the shade obtained was taken with the Easy Shade appliance, which allowed it to be quantified by the CIELab* method. The samples were divided into six groups, corresponding to the chemical activator used: a) none (CON); b) ferric chloride (CF); c) ferrous sulphate (SF); d) manganese gluconate (GM); e) manganese chloride (CM); f) mulberry root extract (RA). Each group received three 10-minute applications of the gels containing the respective activating agents. Next, a new shade measurement was made.Results: The Analysis of Variance and Tukey tests (alpha=5%) showed statistically significant differences for the shade perception values (p=0.002). Groups GM, CM and RA showed significantly higher means than the control group.Conclusion: The presence of some chemical activators is capable of resulting in a significant increase in tooth shade variation.

Characterization of ceramic powders used in the inCeram systems to fixed dental Prosthesis

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)