Blocked diisocyanates as reactive coupling agents: Application to pine fiber-polypropylene composites

In this paper, composites from polypropylene and Kraft pulp (from Pinus radiata) were prepared. Phenyl isocyanate, unblocked and phenol blocked derivatives of 4,4`-methylenebis (phenyl isocyanate) (MDI) were used as coupling agents and the mechanical properties of the obtained composites analyzed. The results showed that the addition of such compatibilizers readily improved the tensile and flexural strengths of the composites. However, no significant variation in the mechanical properties was observed for composite formulations comprising different isocyanate compounds. Accordingly, the chemical structure of isocyanate derivatives did not affect extensively the mechanical properties of MDI-coupled pine fiber reinforced composites. These results were similar to those obtained in previous studies regarding the efficiency of organosilane coupling agents. In comparison to monoreactive isocyanates, the addition of MIDI increased considerably the mechanical properties of pine fiber-polypropylene composites. The mechanical anchoring of polymeric PP chains onto the irregular reinforcement surface supported this result. Non-isothermal DSC analysis showed a slowing effect of MDI on the crystallization kinetics of the coupled composites. This may have been the result of diminished polymer chain mobility in the matrix due to mechanical anchoring onto the fiber surface. Considering these results, the occurrence of strong bonds between the composite components was stated, rather than the unique existence of Van der Waals interactions among the non-polar structures. (c) 2008 Elsevier Ltd. All rights reserved.

Compatible Ternary Blends of Chitosan/poly(vinyl alcohol)/poly(lactic acid) Produced by Oil-in-Water Emulsion Processing

Ternary compatible blends of chitosan, poly(vinyl alcohol), and poly(lactic acid) were prepared by an oil-in-water (O/W) emulsion process. Solutions of chitosan in aqueous acetic acid, poly(vinyl alcohol) (PVA) in water, and poly(lactic acid) (PLA) in chloroform were blended with a high shear mixer. PVA was used as an emulsifier to stabilize the emulsion and to reduce the interfacial tension between the solid polymers in the blends-produced. It proved to work very well because the emulsions were stable for periods of days or weeks and compatible blends were obtained When PVA was added. This effect was attributed to a synergistic effect of PVA and chitosan because the binary blends PVA/PLA and chitosan/PLA were completely incompatible; The blends were characterized by scanning electron microscopy (SEM), differential scanning calorimetry (DSC), thermal mechanical analysis (TMA), stress strain tests, and Fourier transform infrared spectroscopy (FTIR). The results indicated that despite the fact that the system contained distinct phases some degree of molecular miscibility occurred when the three components were present in the blend.

Discoloration and fungal growth on three fiber cement formulations exposed in urban, rural and coastal zones

Three formulations of fiber cement were evaluated for fungal colonization and color change after five years of exposure in aging stations located in urban (Sao Paulo), rural (Pirassununga) and coastal (Rio Grande) zones in Brazil. The lowest color change and fungal colonization were registered in Rio Grande, which has a temperate climate, as opposed to Sao Paulo and Pirassununga, which are tropical. The highest fungal colonization was recorded in Sao Paulo, one of the most air polluted cities in Brazil. Pirassununga samples had an intermediate fungal colonization, in spite of showing the highest color change with visible dark spots on the surfaces. These spots were identified as cyanobacteria, which significantly contributed to the darkening of the specimens. The fiber cement formulation, varying in proportion of organic fibers such as poly (vinyl alcohol) and cellulose, was less significant for fungal bioreceptivity than the characteristics of the exposure site. The most frequent fungal genus found in the tropical climate, in both urban and rural zones, and the main one responsible for the higher records in Sao Paulo, was Scytalidiurn sp. which was registered for the first time on this building material in Brazil. (C) 2010 Elsevier Ltd. All rights reserved.

Exploring the potential of functionally graded materials concept for the development of fiber cement

In this study we establish the concept of functionally graded fiber cement. We discuss the use of statistical mixture designs to choose formulations and present ideas for the production of functionally graded fiber cement components for Hatschek machines. The feasibility of producing functionally graded fiber cement by grading PVA fiber content has been experimentally evaluated. Thermogravimetric analysis (TG) was employed to assess fiber distribution profiles and four-point bending tests were applied to evaluate the mechanical performance of both conventional and graded composites. The results show that grading PVA fiber content is an effective way to produce functionally graded fiber cement, which allows for a reduction of the total fiber volume without a significant reduction on modulus of rupture of composite. TG tests were found adequate to assess the fiber content at different points in functionally graded fiber cements. (C) 2009 Elsevier Ltd. All rights reserved.

Experimental investigation on the dynamic behaviour of a railway vehicle travelling through a turnout

Track critical locations with respect to the railway vehicle safety are the passages through the turnouts. The purpose of this investigation is to evaluate the safety of a railway vehicle crossing a turnout. In this study, the topography of a track turnout lay-out has been experimentally measured, and its geometric properties were synthesised. Results show that a constant wavelength vehicle oscillation occurs on the switches in the turnout and that the maximum lateral force at 65 km/h is almost 65% greater than those at low speeds (under 30 km/h).

Numerical solution of the two-phase expansion of a metastable flashing liquid jet using the dispersion-controlled dissipative scheme

This paper presents a study of the stationary phenomenon of superheated or metastable liquid jets, flashing into a two-dimensional axisymmetric domain, while in the two-phase region. In general, the phenomenon starts off when a high-pressure, high-temperature liquid jet emerges from a small nozzle or orifice expanding into a low-pressure chamber, below its saturation pressure taken at the injection temperature. As the process evolves, crossing the saturation curve, one observes that the fluid remains in the liquid phase reaching a superheated condition. Then, the liquid undergoes an abrupt phase change by means of an oblique evaporation wave. Across this phase change the superheated liquid becomes a two-phase high-speed mixture in various directions, expanding to supersonic velocities. In order to reach the downstream pressure, the supersonic fluid continues to expand, crossing a complex bow shock wave. The balance equations that govern the phenomenon are mass conservation, momentum conservation, and energy conservation, plus an equation-of-state for the substance. A false-transient model is implemented using the shock capturing scheme: dispersion-controlled dissipative (DCD), which was used to calculate the flow conditions as the steady-state condition is reached. Numerical results with computational code DCD-2D vI have been analyzed. Copyright (C) 2009 John Wiley & Sons, Ltd.

Failure analysis of belt/roll tribological pair used for the production of eucalypt fiber panels

The premature failure of a large agglomeration machine used for the annual production of 360,000 m(3) of eucalypt fiber panels was investigated to identify the nucleation and growth mechanisms of cracking in PH stainless steel belts (126 m x 2.9 m x 3.0 mm). These belts are used to compress a cushion composed of eucalyptus fibers and glue, being the pressure transmitted from the pistons by the action of numerous case-hardening steel rolls. Examination of the belt working interfaces (belt/rolls and belt/eucalypt fibers) indicated that the main cracking was nucleated on the belt/roll interface and that there is a clear relationship between the crack nucleation and the presence of superficial irregularities, which were observed on the belt/roll working surface. Used rolls showed the presence of perimetric wear marks and 2 mu m silicon-rich encrusted particles (identified as silicon carbide). Lubricant residues contained the presence of helicoidal wires, which were originated by the release of the stainless steel cleaning brush bristles, and 15 mu m diameter metallic particles, which were generated by material detachment of the belt. The presence of foreign particles on the tribological interface contributed to an increase of the shear stresses at the surfaces and, consequently, the number of the contact fatigue crack nucleation sites in the belt/roll tribo-interface. The cracking was originated on the belt/roll interface of the stainless steel belt by a mixed rolling/slip contact fatigue mechanism, which promoted spalling and further nucleation and growth of conventional fatigue cracks. Finally, the system lubrication efficiency and the cleaning procedure should be optimised in order to increase the life expectancy of the belt. (c) 2006 Elsevier Ltd. All rights reserved.

Thermal and mechanical characteristics of polyurethane/curaua fiber composites

Polyurethane composites reinforced with curaua fiber at 5, 10 and 20% mass/mass proportions were prepared by using the conventional melt-mixing method. The influence of curaua fibers on the thermal behavior and polymer cohesiveness in polyurethane matrix was evaluated by dynamic mechanical thermal analysis (DMTA) and by differential scanning calorimetry (DSC). This specific interaction between the fibers and the hard segment domain was influenced by the behavior of the storage modulus E` and the loss modulus EaEuro(3) curves. The polyurethane PU80 is much stiffer and resistant than the other composites at low temperatures up to 70A degrees C. All samples were thermoplastic and presented a rubbery plateau over a wide temperature range above the glass transition temperature and a thermoplastic flow around 170A degrees C.

Effect of rolling on the residual stresses and magnetic properties of a 0.5% Si electrical steel

Cold-rolled (0-19% of reduction) 0.5% Si electrical steel sheets were studied in detail, including macro and micro residual stress measurements, crystallographic texture, dc-hysteresis curves and iron losses. Even for the smallest deformation, losses increase significantly, with large increase of the hysteresis losses, whereas the anomalous losses reduce slightly. The residual microstresses are similar to 150-350 MPa, whereas residual macrostresses are compressive, similar to 50 MPa. The large increase of the hysteresis losses is attributed to the residual microstresses. The dislocation density estimated by X-ray diffraction is in reasonable agreement with that predicted from the Sablik et al. model for effect of plastic deformation on hysteresis. The intensity of the texture fibers {1 1 1}< u v w > and < 110 >//RD (RD = rolling direction) increases with the reduction. (C) 2008 Elsevier B.V. All rights reserved.

Morphological alterations in leave of micropropagated pineapple plants cv. IAC Gomo-de-mel acclimatizated in different conditions of luminosity

(Morphological alterations in leave of micropropagated pineapple plants cv. IAC Gomo-de-mel acclimatizated in different conditions of luminosity). Microprapagated plants usually show difficulties to adapt to ex vitro conditions, and many times are submitted to the rustication process to aim the reduction of all the impacts resulting from the environmental changes. Once the leaf and its annexes are important indicators of adaptability strategies of the plants to adverse environmental conditions, the objective of this work was to compare the leaf anatomy of pineapple cv. IAC Gomo-de-mel in vitro cultivated plants with microplants acclimatized in different conditions of luminosity, under mesh, with 50% of shading and directly exposed to sunlight, to verify the needed of rustication process on this cultivar. Evaluations of the leaf epidermis using light and electronic scanning microscopy showed an increase on scale density in both leaves surfaces of the ex vitro microplants, mainly related to the ones directly exposed to sunlight. Subsequent observations showed an increase on cuticle thickness, on wavy contours of epidermal cells, and on the distribution and quantity of mesophyll fibers, evidencing the light conditions interference in morphological characteristics of these microplants. These alterations had not harmed microplant development, showing that are not need of rustication stages on the acclimatization process of this cultivar.

Formulating Mixed Models for Experiments, Including Longitudinal Experiments

Mixed models have become important in analyzing the results of experiments, particularly those that require more complicated models (e.g., those that involve longitudinal data). This article describes a method for deriving the terms in a mixed model. Our approach extends an earlier method by Brien and Bailey to explicitly identify terms for which autocorrelation and smooth trend arising from longitudinal observations need to be incorporated in the model. At the same time we retain the principle that the model used should include, at least, all the terms that are justified by the randomization. This is done by dividing the factors into sets, called tiers, based on the randomization and determining the crossing and nesting relationships between factors. The method is applied to formulate mixed models for a wide range of examples. We also describe the mixed model analysis of data from a three-phase experiment to investigate the effect of time of refinement on Eucalyptus pulp from four different sources. Cubic smoothing splines are used to describe differences in the trend over time and unstructured covariance matrices between times are found to be necessary.

Radial variation of the wood anatomical structure of Gmelina arborea trees from different climatic and management conditions in Costa Rica

The evaluations of the effect of the climatic conditions and of the intensity of forest management in the trunk of the Gmelina arborea Linn. Roxb. trees are restricted to its physical-mechanical properties and use. The present work has as objective to study the radial variations of the wood anatomy of the gmelina trees sampled in plantations of 30 sites in Costa Rica, characterized by two climatic conditions (tropical dry and humid) and three intensities of forest management (intensive, moderate and without management). The results of the analyses demonstrated the existence of radial variation of the different anatomical parameters, except for the fiber lumen diameter and multiple vessels in the wood of the gmelina trees. For the wood anatomical elements, fibers (width, lumen diameter, and length), vessels (multiple vessels, diameter and frequency) and radial parenchyma (height) relationships were observed with the climate (tropical humid and dry). The radial variations of the wood anatomical elements were, also, influenced by the management regimes of the gmelina trees.

X ray densitometry applied to technological evaluation of MDF panels of eucalyptus

MDF panels from eucalyptus wood fibers were manufactured in laboratory and industrial production and had their apparent density profile determined by X-ray densitometry. The MDF panels apparent density parameters (maximum density of the superior and inferior faces; medium and minimum density) were determined and compared. The results indicated that the density values of the MDF panels made in the laboratory and in industrial line did not show significant statistical differences, indicating the similarities in the pressing phase of the fibers of both kinds. However, for MDF panels of laboratory and production line, the values of maximum, mean and minimum densities showed statistically significant correlations. The determination of the density profile for MDF panels by X-ray densitometry is important for the evaluation of pressing phase and other variables of the industrial process of production, as well for the determination of the technological properties.

RECK-Mediated Inhibition of Glioma Migration and Invasion

RECK is an anti-tumoral gene whose activity has been associated with its inhibitory effects regulating MMP-2, MMP-9, and MT1-MMP. RECK level decreases as gliobastoma progresses, varying from less invasive grade II gliomas to very invasive human glioblastoma multiforme (GBM). Since RECK expression and glioma invasiveness show an inverse correlation, the aim of the present study is to investigate whether RECK expression would inhibit glioma invasive behavior. We conducted this study to explore forced RECK expression in the highly invasive T98G human GBM cell line. Expression levels as well as protein levels of RECK, MMP-2, MMP-9, and MT1-MMP were assessed by qPCR and immunoblotting in T98G/RECK+ cells. The invasion and migration capacity of RECK+ cells was inhibited in transwell and wound assays. Dramatic cytoskeleton modifications were observed in the T98G/RECK+ cells, when compared to control cells, such as the abundance of stress fibers (contractile actin-myosin II bundles) and alteration of lamellipodia. T98G/RECK+ cells also displayed phosphorylatecl focal adhesion kinase (P-FAK) in mature focal adhesions associated with stress fibers; whereas P-FAK in control cells was mostly associated with immature focal complexes. Interestingly, the RECK protein was predominantly localized at the leading edge of migrating cells, associated with membrane ruffles. Unexpectedly, introduced expression of RECK effectively inhibited the invasive process through rearrangement of actin filaments, promoting a decrease in migratory ability. This work has associated RECK tumor-suppressing activity with the inhibition of motility and invasion in this GBM model, which are two glioma characteristics responsible for the inefficiency of current available treatments. J. Cell. Biochem. 110: 52-61, 2010. (C) 2010 Wiley-Liss. Inc.

Prospective ultramorphological characterization of human hair by optical coherence tomography

Background/purpose The continuous advancement in cosmetic science has led to an increasing demand for the development of non-invasive, reliable scientific techniques directed toward claim substantiation, which is of utmost relevance, to obtain data regarding the efficacy and safety of cosmetic products. Methods In this work, we used the optical coherence tomography (OCT) technique to produce in vitro transversal section-images of human hair. We also compared the OCT signal before and after chemical treatment with an 18% w/w ammonium thioglycolate solution. Results The mean diameter of the medulla was 29 +/- 7 mu m and the hair diameter was 122 +/- 16 mu m in our samples of standard Afro-ethnic hair. A three-dimensional (3D) image was constructed starting from 601 cross-sectional images (slices). Each slice was taken in steps of 6.0 mu m at eight frames per second, and the entire 3D image was constructed in 60 s. Conclusion It was possible to identify, using the A-scan protocol, the principal structures: the cuticle, cortex and medulla. After chemical treatment, it was not possible to identify the main structures of hair fiber due to index matching promoted by deleterious action of the chemical agent.