Structural and ferroelectric properties of Pb1-xSrxTiO3 thin films

Strontium-modified lead titanate (PST) thin films with composition Pb1-xSrxTiO3 (0.10 < x &LE; 0.60) were grown on Pt/Ti/SiO2/Si substrates using a soft chemical process. The crystallization of the PST thin films was achieved by heat treatment at 600&DEG;C. The structural and microstructural modifications in the films were studied using X-ray diffraction (XRD) and atomic force microscopy, respectively. The XRD study shows that the lattice parameters of polycrystalline PST thin films calculated from X-ray data indicate a decrease in lattice tetragonality with the increase in strontium content in these films. This indicates a gradual change from tetragonal to cubic structure. By atomic force microscopy analysis, the average grain size of the thin films was systematically reduced with the increase in Sr content. The dielectric property of the thin films was found to be strongly dependent on the Sr concentration. With 60 at.% Sr content, a ferroelectric to paraelectric phase transition was observed at room temperature.

Preparation and characterization of nanosized SrBi2Nb2O9 powder by the combustion synthesis

This work presents the preparation of SrBi2Nb2O9 (SBN) directly by the combustion synthesis. Strontium nitrate, niobium ammonium oxalate (NH4H2[NbO-(C2O4)(3)].3H(2)O) and bismuth oxide were used as oxidant reactants and urea as fuel. The influence of the fuel was evaluated by the addition of different fuel amounts (50%, 100%, 200% and 300%), 100% being the stoichiometric proportion. The XRD patterns showed that the SBN perovskite crystallized as the majority phase. The as-synthesized stoichiometric powder presented a specific surface area of around 13 m(2)/g and a mean grain size of around 16 nm. Dilatometric measurements showed that the maximum sintering rate occurs at 1275degreesC. The determination of the ferroparaelectric transition showed a Curie temperature (T-c) of 429degreesC. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Temperature dependence on the electrical properties of Ba(Ti0.90Zr0.10)O-3:2V ceramics

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Synthesis, structural refinement and optical behavior of CaTiO3 powders: A comparative study of processing in different furnaces

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Preparation and characterizations of Ba0.8Ca0.2TiO3 by complex polymerization method (CPM)

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Synthesis, ferroelectric and optical properties of (Pb,Ca)TiO3 thin films by soft solution processing

Calcium modified lead titanate sol was synthesized using a soft solution processing, the so-called polymeric precursor method. In soft chemistry method, soluble precursors such as lead acetate trihydrate, calcium carbonate and titanium isopropoxide, as starting materials, were mixed in aqueous solution. Pb0.7Ca0.3TiO3 thin films were deposited on platinum-coated silicon and quartz substrates by means of the spinning technique. The surface morphology and crystal structure, dielectric and optical properties of the thin films were investigated. The electrical measurements were conducted on metal-ferroelectric-metal (MFM) capacitors. The typical measured small signal dielectric constant and dissipation factor at a frequency of 100 kHz were 299 and 0.065, respectively, for a thin film with 230 nm thickness annealed at 600degreesC for 2 h. The remanent polarization (2P(r)) and coercive field (E-c) were 32 muC/cm(2) and 100 kV/cm, respectively. Transmission spectra were recorded and from them, refractive index, extinction coefficient, and band gap energy were calculated. Thin films exhibited good optical transmissivity, and had optical direct transitions. The present study confirms the validity of the DiDomenico model for the interband transition, with a single electronic oscillator at 6.858 eV. The optical dispersion behavior of PCT thin film was found to fit well the Sellmeir dispersion equation. The band gap energy of the thin film, annealed at 600degreesC, was 3.56 eV. The results confirmed that soft solution processing provides an inexpensive and environmentally friendly route for the preparation of PCT thin films.

Crystallographic, dielectric and optical properties of SrBi2Ta2O9 thin films prepared by the polymeric precursor method

Strontium bismuth tantalate thin films were prepared on several substrates (platinized silicon (PvTi/SiO2/Si), n-type (100)-oriented and p-type (111)-oriented silicon wafers, and fused silica) by the solution deposition method. The resin was obtained by the polymeric precursor method, based on the Pechini process, using strontium carbonate, bismuth oxide, and tantalum ethoxide as starting reagents. Characterizations by XRD and SEM were performed for structural and microstructural evaluations. The electrical measurements, carried on the MFM configuration, showed P-r values of 6.24 muC/cm(2) and 31.5 kV/cm for the film annealed at 800 degreesC. The film deposited onto fused silica and treated at 700 degreesC presented around 80 % of transmittance.

CaTiO3:Eu3+ obtained by microwave assisted hydrothermal method: A photoluminescent approach

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Structural refinement and photoluminescence properties of irregular cube-like (Ca-1_Cu-x(x))TiO3 microcrystals synthesized by the microwave-hydrothermal method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Disorder-dependent photoluminescence in Ba0.8Ca0.2TiO3 at room temperature

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structure, microstructure, ferroelectric/electromechanical properties and retention characteristics of [Bi1-x Nb (x) ]FeO3 thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Phase Transformation in Titania Nanocrystals by the Oriented Attachment Mechanism: The Role of the pH Value

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Sol-gel synthesis of mesoporous CaCu3Ti4O12 thin films and their gas sensing response

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Evaluation of different rhodium modifiers and coatings on the simultaneous determination of As, Bi, Pb, Sb, Se and of Co, Cr, Cu, Fe, Mn in milk by electrothermal atomic absorption spectrometry

Different kinds of modifiers and coatings on the integrated platform of transversely heated graphite atomizer (THGA) have been tested for the simultaneous determination of two group of elements: the first, the more volatile, formed by arsenic, bismuth, lead, antimony and selenium; the second, the less volatile, formed by cobalt, chromium, cupper, iron and manganese in milk by electrothermal atomic absorption spectrometry. Different Rh-modifiers were studied, such as Rh-coated platforms (Rh), carbide plus rhodium coated platforms (W-Rh, Zr-Rh), carbide-coated platforms (W and Zr) with co-injection of RhCl3, solutions and uncoated platforms with injection of solutions of Pd(NO3)(2), Mg(NO3)(2), and RhCl3. Milk samples were diluted 1:10 in 1.0% HNO3 and injected into the tube. The mass of modifier deposited and co-injected in the tube and the use of end capped tubes were also evaluated in order to improve the electrothermal behavior of analytes. Integrated platform pretreated with W plus co-injection RhCl3 for first group and pretreated with W-Rh for second group were elected. For 20 mu L injected samples the analytical curves in the 5.0-20.0 mu g L-1 concentration range have good linear correlation coefficients (r > 0.998). Relative standard deviations (n = 12) are < 6% and the calculated characteristic masses are between 5 pg and 62 pg.

Investigation on the structural properties in Er-doped PbTiO3 compounds: A correlation between experimental and theoretical results

The aim of this work is to investigate the structural properties of the (Pb1-xErx)TiO3 (PET) powders, with x varying from 0.01 to 0.08, prepared by the polymeric precursor method. Combined X-ray diffraction, Raman spectroscopy and ab initio calculation reveal a diffuse phase-transition of a tetragonal to a cubic phase. The crystalline models built allowed to calculate electronic properties and to analyze the behavior of the doping element in the structure of the material, which are consistent with the experimental results that indicate the beginning of phase-transition from tetragonal to cubic. (C) 2007 Elsevier B.V. All rights reserved.