Tailoring of physical properties in highly filled experimental nanohybrid resin composites

Objectives. To assess the elastic modulus (EM), volumetric shrinkage (VS), and polymerization shrinkage stress (PSS) of experimental highly filled nanohybrid composites as a function of matrix composition, filler distribution, and density. Methods. One regular viscosity nanohybrid composite (Grandio, VOCO, Germany) and one flowable nanohybrid composite (Grandio Flow, VOCO) were tested as references along with six highly filled experimental nanohybrid composites (four Bis-GMA-based, one UDMA-based, and one Ormocer (R) -based). The experimental composites varied in filler size and density. EM values were obtained from the ""three-point bending"" load-displacement curve. VS was calculated with Archimedes` buoyancy principle. PSS was determined in 1-mm thick specimens placed between two (poly) methyl methacrylate rods (empty set = 6 mm) attached to an universal testing machine. Data were analyzed using oneway ANOVA, Tukey`s test (alpha = 0.05), and linear regression analyses. Results. The flowable composite exhibited the highest VS and PSS but lowest EM. The PSS was significantly lower with Ormocer. The EM was significantly higher among experimental composites with highest filler levels. No significant differences were found between all other experimental composites regarding VS and PSS. Filler density and size did not influence EM, VS, or PSS. Significance. Neither the filler configuration nor matrix composition in the investigated materials significantly influenced composite shrinkage and mechanical properties. The highest filled experimental composite seemed to increase EM by keeping VS and PSS low; however, matrix composition seemed to be the determinant factor for shrinkage and stress development. The Ormocer, with reduced PSS, deserves further investigation. Filler size and density did not influence the tested parameters. (C) 2011 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Polymerization stress of resin composites as a function of system compliance

Objectives. Evaluate the effect of testing system compliance on polymerization stress and stress distribution of composites. Methods. Composites tested were Filtek Z250 (FZ), Herculite (HL), Tetric Ceram (TC), Helio Fill-AP (HF) and Heliomolar (HM). Stress was determined in 1-mm thick specimens, inserted between two rods of either poly(methyl methacrylate), PMMA, or glass. Experimental nominal stress (sigma(exp)) was calculated by dividing the maximum force recorded 5 min after photoactivation by the cross-sectional area of the rod. Composites` elastic modulus (E) was obtained by three-point bending. Data were submitted to one-way ANOVA/Tukey`s test (alpha = 0.05). Stress distribution on longitudinal (sigma(y)) and transverse (sigma(x)) axes of models representing the composites with the highest and lowest E (FZ and HM, respectively) were evaluated by finite element analysis (FEA). Results. sigma(exp) ranged from 5.5 to 8.8 MPa in glass and from 2.6 to 3.4 MPa in PMMA. Composite ranking was not identical in both substrates, since FZ showed or sigma(exp) statistically higher than HM in glass, while in PMMA FZ showed values similar to the other composites. A strong correlation was found between stress reduction (%) from glass to PMMA and composite`s E (r(2) = 0.946). FEA revealed that system compliance was influenced by the composite (FZ led to higher compliance than HM). sigma(x) distribution was similar in both substrates, while cry distribution showed larger areas of compressive stresses in specimens built on PMMA. Significance. sigma(exp) determined in PMMA was 53-68% lower than in glass. Composite ranking varied slightly due to differences in substrates` longitudinal and transverse deformation. (c) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Substance P and NK-1R expression in oral precancerous epithelium

The objectives of this study were to investigate the presence and distribution of substance P and neurokinin 1 receptor in oral premalignant epithelium and their relation with the presence of dysplasia, and to analyze whether the expression of substance P can be considered an early oncogenic event in oral carcinogenesis. Substance P and neurokinin I receptor expression was immunohistochemically studied in 83 oral carcinomas and adjacent nontumor epithelia. The presence and degree of epithelial dysplasia was assessed according to WHO criteria. The nuclear, cytoplasmic, and membrane expression of substance P and the cytoplasmic and membrane expression of neurokinin 1 receptor were assessed in tumor and adjacent non-tumor epithelium. Nuclear and cytoplasmic expression of substance P in non-tumor epithelium was significantly associated with the presence of epithelial dysplasia (p<0.001) and carcinoma in. situ (p=0.021). Nuclear, cytoplasmic, and membrane expressions of substance P in non-tumor epithelium were significantly (p<0.001) associated with its expression in the corresponding tumor. These findings suggest that substance P plays a role in early oral carcinogenesis by promoting the proliferation and growth of premalignant fields.

A Role for the Substance P/NK-1 Receptor Complex in Cell Proliferation in Oral Squamous Cell Carcinoma

Objective: To investigate the presence and distribution of substance P (SP) and neurokinin I receptor (NK-IR) in oral squamous cell carcinoma (OSCC) and their relationship with proliferation. Patients and Methods: Ninety OSCCs from 73 patients were immunohistochemically analyzed using monoclonal antibodies against SP, NK-IR and Ki-67 in a case and control study. Results: Seventy-one percent (n=49) of cases expressed SP on tumour cell membrane, 81.3% (n=69) in cytoplasm, 39.4% (n=28) in nucleus, 81.6% (n=71) in infiltrating lymphocytes, and 58.1% (n=43) in peritumoural or intratumoural blood vessels; 14% (n=12) of cases expressed NK-1R on tumour cell membrane, 50% (n=43) in cytoplasm, 48.3% (n=42) in infiltrating lymphocytes and 22.5% (n=18) in tumour blood vessels. All cases expressed Ki-67, which was expressed in >25% of tumour cells in 79.8% of cases (n=63). Direct significant associations were observed in SP expression between different tissue levels (p<0.01), between SP and NK-IR tumour cell membrane expression (p<0.01), and between joint,SP and NK-IR expression in tumour cell cytoplasm and a higher expression of Ki-67 (p<0.05). Conclusion: The ubiquitous presence of SP strongly suggests a role for SP/NK-1R complex in tumour development and progression and possibly for NK-IR antagonists, such as L-773060, in the management of patients with oral cancer.

Differential Production of Macrophage Inflammatory Protein-1 alpha, Stromal-Derived Factor-1, and IL-6 by Human Cultured Periodontal Ligament and Gingival Fibroblasts Challenged With Lipopolysaccharide From P. gingivalis

Background: Fibroblasts are considered important cells in periodontitis. When challenged by different agents, they respond through the release of cytokines that participate in the inflammatory process. The aim of this study is to evaluate and compare the expression and production of macrophage inflammatory protein (MIP)-1 alpha, stromal-derived factor (SDF)-1, and interleukin (IL)-6 by human cultured periodontal ligament and gingival fibroblasts challenged with lipopolysaccharide (LPS) from Porphyromonas gingivalis. Methods: Fibroblasts were cultured from biopsies of gingival tissue and periodontal ligament of the same donors and used on the fourth passage. After confluence in 24-well plates, the culture medium alone (control) or with 0.1 to 10 mu g/ml of LPS from P. gingivalis was added to the wells, and after 1, 6, and 24 hours, the supernatant and the cells were collected and analyzed by enzyme-linked immunosorbent assay and real-time polymerase chain reaction, respectively. Results: MIP-1 alpha, SDF-1, and IL-6 protein production was significantly greater in gingival fibroblasts compared to periodontal ligament fibroblasts. IL-6 was upregulated in a time-dependent manner, mainly in gingival fibroblasts (P<0.05), which secreted more MIP-1 alpha in the lowest concentration of LPS used (0.1 mu g/ml). In contrast, a basal production of SDF-1 that was inhibited with the increase of LPS concentration was detected, especially after 24 hours (P<0.05). Conclusion: The distinct ability of the gingival and periodontal ligament fibroblasts to secrete MIP-1 alpha, SDF-1, and IL-6 emphasizes that these cells may differently contribute to the balance of cytokines in the LPS-challenged periodontium. J Periodontol 2010;81:310-317.

Human osteoblastic cell response to a Ca- and P-enriched titanium surface obtained by anodization

The aim of the present study was to evaluate the in vitro osteogenic potential of subcultured human osteoblastic cells derived from alveolar bone on a titanium (Ti) surface produced by an anodized alkali treatment (BSP-AK). Primary osteoblastic cells were subcultured on BSP-AK and machined Ti discs (control) and grown for periods of up to 21 days under osteogenic conditions. Morphologic and biochemical methods were used to assess important parameters of in vitro bone-like tissue formation. Although no major differences were observed between the BSP-AK and the control Ti surface in terms of cell attachment and mineralized matrix formation, a significant increase in cell population, ALP activity, and collagen content was detected in cultures on BSP-AK surface. Our results demonstrate that human osteoblastic cells are sensitive to the BSP-AK-modified Ti surface during the transitional stage between the end of the proliferative phase and the onset of the differentiation /matrix maturation ones. Together with the good mechanical properties exhibited by the Ca- and P- coating, our findings suggest that BSP-AK treatment could be useful for the development of a new surface for dental and orthopedic implants. (c) 2008 Wiley Periodicals, Inc.J Biomed Mater Res 88A: 841-848, 2009

Thermal characterization of copolymers obtained by radiation grafting of styrene onto poly(tetrafluoroethyleneperfluoropropylvinylether) substrates: thermal decomposition, melting behavior and low-temperature transitions

Differential scanning calorimetric (DSC) and thermogravimetric analysis (TGA) have been used to study the thermal decomposition, the melting behavior and low-temperature transitions of copolymers obtained by radiation-induced grafting of styrene onto poly (tetrafluoroethylene- perfluoropropylvinylether) (PFA) substrates. PFA with different contents of perfluoropropylvinylether (PPVE) as a comonomer have been investigated. A two step degradation pattern was observed from TGA thermograms of all the grafted copolymers, which was attributed to degradation of PSTY followed by the degradation of the PFA backbone at higher temperature. One broad melting peak can be identified for all copolymers, which has two components in the samples with higher PPVE content. The melting peak, crystal-crystal transition and the degree of crystallinity of the grafted copolymers increases with radiation grafting up to 50 kGy, followed by a decrease at higher doses. No such decrease was observed in the ungrafted PFA samples after irradiation. This indicated that the changes in the heats of transitions and crystallinity at low doses are due to the radiation effects on the microstructure of PFA (chain scission), whereas at higher doses the grafted PSTY is the driving force behind these changes. (C) 2001 Elsevier Science Ltd. All rights reserved.

An ESR study on gamma-irradiated poly(vinyl alcohol)

The formation of radicals in poly(vinyl alcohol), PVA, powder irradiated at 77 K by gamma -rays and the transformations of these radicals during photolysis with visible wavelengths and on thermal annealing have been studied. After irradiation a four-line ESR spectrum was observed. It was assigned to a triplet of the C-alpha-radical (38%), with a splitting of 3.27 mT, superimposed on a doublet (62%) with a splitting of 2.7 mT. The doublet appears to be composed of two radicals, one of which is photo-bleachable (58%) and the other which is not photo-bleachable (42%). This suggests that the latter radical is a neutral radical. The photo-bleachable component of the doublet has been assigned to a carbonyl anion radical. but the second doublet due to a neutral radical is unassigned. The total G-value for formation of radicals at 77 K was found to be 2.41 +/- 0.03. Upon illumination with visible light, the anion radicals were removed and the doublet components or the spectrum diminished in intensity, while the three-line spectrum of the C-alpha-radical became more clearly visible. This transition was due to the photo-detachment of electrons from traps which were proposed to be located on carbonyl groups in the polymer resulting from incomplete hydrolysis of the vinyl acetate. The photo-decay of the anion radicals could be satisfactorily described by a two-stage process. The first stage comprised the decay of approximately 80% of the anion radicals present, while the second stage was associated with the decay of the remaining 20%. Subsequent thermal annealing of a photolysed sample to 290 K led to a change in the shape of the spectrum to form a more clearly defined triplet, As the doublet of the neutral radical decays on thermal annealing between 150 and 250K, the C-alpha-radical is formed. (C) 2001 Elsevier Science Ltd. All rights reserved.

An ESR study of irradiated poly(tetrafluoroethylene-co-perfluoropropyl vinyl ether) (PFA)

Poly(tetrafluoroethylene-co-perfluoropropyl vinyl ether) (PFA) with 2 mol% perfluoropropyl vinyl ether (PPVE) was exposed to gamma -irradiation in vacuum at both 77 K and room temperature and the ESR spectra recorded. Both the main chain, similar to CF2-(CF)-F-.-CF(2)similar to, and end chain, similar to (CF2CF2)-F-. radicals were identified at both temperatures and their thermal stabilities measured, No radicals unique to the radiolytic cleavage at the PPVE units were observed at room temperature, either due to the low concentration of the comonomer or beta -scission to form a chain end radical and a nonradical species. G-values for radical formation at room temperature and 77 K were found to be 0.93 and 0.16, respectively. (C) 2001 Elsevier Science Ltd. All rights reserved.

Molecular weight changes and scission and crosslinking in poly(dimethyl siloxane) on gamma radiolysis

The molecular weight changes which occur on the gamma -radiolysis of poly(dimethyl siloxane) under vacuum between 77 and 373 K and in air at 303 K have been investigated using triple detection GPC to obtain the complete molecular weight distributions for the irradiated samples and to determine the number and weight average molecular weights. The results have been interpreted in terms of the relative yields of scission and crosslinking. The total yields for crosslinking predominate over those for scission at all the temperatures investigated for radiolysis under vacuum. Based on a solid-state Si-29 NMR analysis of PDMS irradiated under vacuum at 303 K, which yielded a value of G(Y) of 1.70, the values of G(S) = 1.15 +/-0.2 and G(H) = 1.45 +/-0.2 were obtained for radiolysis under vacuum at 303 K. For radiolysis in air at 303 K, crosslinking was also predominant, but the nett yield of crosslinking was much less than that observed for radiolysis under vacuum. Under the conditions of the radiolysis in air at 303 K, because of the low solubility of oxygen in PDMS, it is likely that the radiation chemistry is limited by oxygen diffusion. (C) 2001 Elsevier Science Ltd. All rights reserved.

Simultaneous administration of a cocktail of markers to measure renal drug elimination pathways: absence of a pharmacokinetic interaction between fluconazole and sinistrin, p-aminohippuric acid and pindolol

Aims Previous studies suggest that estimated creatinine clearance, the conventional measure of renal function, does not adequately reflect charges in renal drug handling in some patients, including the immunosuppressed. The aim of this study was to develop and validate a cocktail of markers. to be given in a single administration, capable of detecting alterations in the renal elimination pathways of glomerular filtration, tubular secretion and tubular reabsorption. Methods Healthy male subjects (n = 12) received intravenously infused 2500 mg sinistrin (glomerular filtration) and 440 mg p-aminohippuric acid (PAH; anion secretion), and orally administered 100 mg fluconazole (reabsorption) and 15 mg rac-pindolol (cation secretion). The potential interaction between these markers was investigated in a pharmacokinetic study where markers (M) or fluconazole (F) were administered alone or together (M + F). Validated analytical methods were used to measure plasma and urine concentrations in order to quantify the renal handling of each marker. Plasma protein binding of fluconazole was measured by ultrafiltration. All subjects had an estimated creatinine clearance within the normal range. The renal clearance of each marker (Mean +/- s.d.) was calculated as the ratio of the amount excreted in urine and thearea-under-the-concentration-time curve. Statistical comparisons were made using a paired t-test and 95% confidence intervals were reported. Results The renal clearances of sinistrin (M: 119 +/- 31 ml min(-1); M + F: 130 +/- 40 ml min(-1); P = 0.32), PAH (M: 469 +/- 145 ml min(-1); M + F: 467 +/- 146 ml min(-1); P = 0.95), R-pindolol (M: 204 +/- 41 ml min(-1); M + F: 190 +/- 41 ml min(-1); P = 0.39; n = 11), S-pindolol (M: 225 +/- 55 ml min(-1); M + F: 209 +/- 60 ml min(-1); P = 0.27; n = 11) and fluconazole (F: 14.9 +/-3.8 ml min(-1); M + F: 13.6 +/- 3.4 ml min(-1); P = 0.16) were similar when the markers or fluconazole were administered alone (M or F) or as a cocktail (M + F). Conclusions This study found no interaction between markers and fluconazole in healthy male subjects, suggesting that a single administration of this cocktail of markers of different renal processes call be used to simultaneously investigate pathways of renal drug elimination.

Photosensitization of the sunscreen octyl p-dimethylaminobenzoate by UVA in human melanocytes but not in keratinocytes

Sunscreens penetrate human epidermis and modify the biology of proliferating cells. This study addressed the question whether the UV response of cultured human cells is affected by direct treatment with nontoxic levels of sunscreens. Cell survival following exposure to UVC or unfiltered UVB was not altered by preincubation with 25 μg/mL of octyl p-dimethylaminobenzoate (o-PABA), 2-ethylhexyl p-methoxycinnamate (EHMC) or oxybenzone. However, UVA or UVB filtered to reproduce the solar UV spectrum penetrating to the basal layer of the epidermis, highly sensitized cells to killing by o-PABA but not by its hydrolysis product, 4-dimethylaminobenzoic acid. Sensitization was found in all cell types tested, except normal keratinocytes, and could be prevented by certain antioxidants particularly pyruvate and the hydroxyl radical scavenger mannitol. o-PABA and EHMC applied without UV reduced the adherence of cells. The results indicate that sunscreens may increase cell mobility and the combination of o-PABA with solar UV may selectively damage melanocytes in the skin.

How cracks in SiOx-coated polyester films affect gas permeation

In this paper theoretical models have been established that can account for the gas transmission through nanocomposite laminates, consisting of an oxide layer of finite permeability containing defects, on a polymer sheet of finite thickness. The defect shapes can either be in the form of long cracks or rectangular holes. The models offer a choice of exact numerical calculations or fast and intuitive analytical approximations. The experimental measurements of oxygen permeation through four different SiOx/poly (ethylene terephthalate) samples that were strained to produce distributions or cracks showed good agreement when compared with predicted results from the approximate analytic model. As a consequence of this observation, a key practical conclusion is that, because of the logarithmic dependence of transmission on the width of a crack, for a given strain it is better to have a small number of large cracks rather than a large number of small cracks. (C) 2001 Elsevier Science B.V. All rights reserved.

Techniques to determine ignition, flame stability and burnout of blended coals in p.f. power station boilers

The blending of coals has become popular to improve the performance of coals, to meet specifications of power plants and, to reduce the cost of coals, This article reviews the results and provides new information on ignition, flame stability, and carbon burnout studies of blended coals. The reviewed studies were conducted in laboratory-, pilot-, and full-scale facilities. The new information was taken in pilot-scale studies. The results generally show that blending a high-volatile coal with a low-volatile coal or anthracite can improve the ignition, flame stability and burnout of the blends. This paper discusses two general methods to predict the performance of blended coals: (1) experiment; and (2) indices. Laboratory- and pilot-scale tests, at least, provide a relative ranking of the combustion performance of coal/blends in power station boilers. Several indices, volatile matter content, heating value and a maceral index, can be used to predict the relative ranking of ignitability and flame stability of coals and blends. The maceral index, fuel ratio, and vitrinite reflectance can also be used to predict the absolute carbon burnout of coal and blends within limits. (C) 2000 Elsevier Science Ltd. All rights reserved.