Effect of different light-curing techniques on hardness of a microhybrid dental composite resin

Coordenação de Aperfeicoamento de Pessoal de Nivel Superior (CAPES)

Hydrogen ion and calcium releasing of MTA Fillapex® and MTA-based formulations

MTA is composed of various metal oxides, calcium oxide and bismuth. It has good biological properties and is indicated in cases of endodontic complications. Several commercial formulations are available and further studies are necessary to evaluate these materials. Objective: To evaluate pH and calcium releasing of MTA Fillapex® compared with gray and white MTA. Material and methods: Gray and white MTA (Angelus) and MTA Fillapex® (Angelus) were manipulated and placed into polyethylene tubes and immersed in distilled water. The pH of these solutions was measured at 24 hours, 7 days and 14 days. Simultaneously, at these same aforementioned periods, these materials' calcium releasing was quantified, through atomic absorption spectrophotometry. The results were submitted to ANOVA, with level of significance at 5%. Results: Concerning to pH, the materials present similar behaviors among each other at 24 hours (p > 0.05). At 7 and 14 days, MTA Fillapex® provided significantly lower pH values than the other materials (p < 0.05). Regarding to calcium releasing, at 24 hours and 7 days, MTA Fillapex® provided lower releasing than the other materials (p < 0.05). After 14 days, differences were found between MTA Fillapex® and gray MTA (p < 0.05). Conclusion: All materials showed alkaline pH and calcium releasing, with significantly lower values for MTA Fillapex® sealer.

Evaluation of the physicochemical properties and push-out bond strength of mta-based root canal cement

Aim: This study investigated the flowability, setting time, pH, calcium release and bond strength of a MTA-based cement (MTA Fillapex®) compared to AH Plus and Sealapex. Materials and methods: For the flowability test, the ISO 6876:2001 specification was utilized and for the setting time test, the ASTM C266-03 specification was utilized. For the pH and calcium release measurements, 10 samples were prepared for each group and analyzed for several different periods. For the push-out test, dentin disks were distributed into three groups, according to the cement utilized and into three subgroups, according to the root third (n = 10). After obturation, the specimens underwent push-out testing. The data were compared statistically using a significance level of 5%. Results: The flowability of all materials was found to be similar (p > 0.05). The setting times were different among the groups tested (MTA Fillapex < Sealapex < AH Plus) (p < 0.05). At days 7 and 28, the MTA Fillapex presented the higher pH values (p < 0.05). At 24 hours and at 14 days, the calcium release of the MTA Fillapex was similar to that of Sealapex (p > 0.05). AH Plus presented the lowest pH and calcium release values (p < 0.05). In all root thirds, the adhesion to the dentin of the MTA Fillapex and Sealapex were significantly lower than that of AH Plus (p < 0.05). Conclusion: MTA Fillapex and Sealapex presented several similar properties and both were found to be different than AH Plus. Clinical significance: This study evaluated the physicochemical and mechanical properties of new MTA-based root canal cement, in order to use this scaler in root canal fillings. MTA Fillapex showed satisfactory properties for clinical use.

Influence of the addition of calcium hydroxide powder on some physical and chemical properties of the sealer MTA fillapex

Objective: This study evaluated the flow, pH and calcium release of MTA Fillapex (G1) or Fillapex plus 10% in weight of calcium hydroxide powder (G2), compared to AH Plus (G3) and Sealapex (G4). Materials and methods:The flow test was performed according to ISO 6876:2001 requirements. The sealers were placed into plastic tubes and immersed in deionized water. After 24 hours, 7, 14 and 28 days, the water of each tube was removed and tested to evaluate the pH values and the level of released calcium. Calcium release values were analyzed statistically by Kruskal Wallis and Dunn tests and pH values analyzed by ANOVA and Tukey tests (? = 5%). Results:G1 presented higher flow among all sealers. The addition of 10% calcium hydroxide into MTA Fillapex reduced the flow (p < 0.05) but, in a level, that is lower than the one recommended for ISO norms. G2 and G4 presented pH values and calcium release higher than G3 (p < 0.05) in all periods. G1 presented pH value higher than G3 (p < 0.05), except in 7 days period (p > 0.05). G4 presented higher pH values than G1 and G2, but the calcium release was similar for all periods (p > 0.05). G3 presented lower calcium release among all groups (p < 0.05). Conclusion: The addition of 10% calcium hydroxide in MTA Fillapex caused reduction in flow and no negative interference in pH and/or calcium release. However, the obtained flow is different from ISO requirements. Clinical relevance: MTA Fillapex presents levels of flow above the ISO norms. The addition of calcium hydroxide is a suggestion for solving this problem, but the impact of these procedures should be carefully evaluated.

Long-term surface hardness and monomer conversion of a nonofilled and a microhybrid composite resin

Objective: This study aims to evaluate the degree of conversion (DC) and hydrolytic degradation through the Vickers hardness test (HV) of a nanofilled (Filtek™ Z-250, 3M) and a microhybrid (Filtek™Supreme-XT, 3M) composite resin. Materials and methods: Eight disk-shaped specimens (4 mm diameter × 2 mm thick, ISO 4049) of each material were prepared for each test. Composites were inserted into single increment in a metallic matrix and light-cured for 40 seconds. VH readings were performed for each specimen at predetermined intervals: immediately after polymerization (control), 1, 2, 3, 7, 14, 21, 30 and 180 days. After curing, initial hardness measurements were performed and the specimens were immersed in artificial saliva at 37°C. For DC (%), specimens were ground, pressed with KBr and analyzed by FT-IR spectrophotometer. Results: Student t-test showed that there was no difference between the resins for DC (p = 0.252). ANOVA analysis revealed that Z-250 VH means were all greater than S-XT, for both top and bottom surfaces, whatever the storage-period in artificial saliva (p < 0.001). After 180 days of storage, the hardness obtained for S-XT was similar with that at the baseline, for both top and bottom surfaces. While for Z-250 hardness was not significantly different from baseline only for top surface, but there was a significant decrease observed in hardness for bottom surface. Conclusion: The materials tested showed no evidence of hydrolytic degradation in a significant way, in a 6-month storagetime in artificial saliva. Nanofilled resin presents a monomer conversion comparable to the conventional microhybrid.

Properties of one modified composite resin by TiO2 nanoparticles

The purpose of this study was to evaluate the compressive strength and color changes of one composite resin modified by TiO2 nanoparticles and their distribution by SEM.

In vivo evaluation of the inflammatory response and IL-6 immunoexpression promoted by Biodentine and MTA Angelus

Aim To evaluate the inflammatory process induced by Biodentine and mineral trioxide aggregate (MTA) in rat subcutaneous tissues. Methodology A polyethylene tube filled with Biodentine (n = 20) or MTA (n = 20) was placed into the dorsal subcutaneous of forty male rats; in the control group (CG; n = 20), empty tubes were implanted. After 7, 15, 30 and 60 days, the polyethylene tubes surrounded by connective tissue were fixed and embedded in paraffin. The number of inflammatory cells was estimated in HE-stained sections; numerical density of interleukin-6 (IL-6)-immunolabelled cells was also performed. The differences amongst the groups were analysed statistically by Tukey's test (P ≤ 0.05). Results A high number of inflammatory cells and IL-6-positive cells were observed at 7 days, in all groups; however, in the Biodentine group, the number of inflammatory cells and IL-6-immunolabelled cells was significantly higher (P ≤ 0.05) in comparison with the other groups at 7 and 15 days. In the capsules of animals from all groups, a gradual and significant reduction (P ≤ 0.05) of these parameters was seen over time. At 60 days, the capsules exhibited numerous fibroblasts and bundles of collagen fibres; in addition, the number of IL-6-positive cells was not significantly different amongst Biodentine, MTA and control groups. Conclusions There was a significant regression in the inflammatory reaction in the capsules indicating, therefore, that Biodentine is a biocompatible material.

Can repair increase the longevity of composite resins? Results of a 10-year clinical trial

The aim of this double-blind clinical trial was to assess the longevity of repairs to localized clinical defects in composite resin restorations that were initially planned to be treated with a restoration replacement. Methods Twenty-eight patients aged 18–80 years old with 50 composite resin restorations (CR) were recruited. The restorations with localized, marginal, anatomical deficiencies and/or secondary caries adjacent to CR that were “clinically judged” to be suitable for repair or replacement according to the USPHS criteria were randomly assigned to Repair (n = 25) or Replacement (n = 25) groups, and the quality of the restorations was scored according to the modified USPHS criteria. The restorations were blind and two examiners scored them at baseline (Cohen Kappa agreement score 0.74) and at ten years (Cohen Kappa agreement score 0.87) restorations. Wilcoxon tests were performed for comparisons within the same group (95% CI), and Friedman tests were utilized for multiple comparisons between the different years within each group. Results Over the decade, the two groups behaved similarly on the parameters of marginal adaptation (MA) (p > 0.05), secondary caries (SC) (p > 0.05), anatomy (A) (p < 0.05), and colour (C) (p > 0.05). Conclusions Given that the MA, SC, A and C parameters behaved similarly in both groups, the repair of composite resins should be elected when clinically indicated, because it is a minimally invasive treatment that can consistently increase the longevity of restorations. Clinical significance The repair of defective composite resins as an alternative treatment to increase their longevity proved to be a safe and effective treatment in the long term.

Sealing composite with defective margins, good care or over treatment? results of a 10-year clinical trial

Purpose: The objective of this study was to clinically evaluate sealed composite restorations after 10 years and compare their behavior with respect to controls. Methods and Materials: The cohort consisted of 20 patients aged 18 to 80 years with 80 composite restorations. All participants in the sealing and no-treatment groups presented with clinical features for the marginal adaptation that deviated from the ideal and were rated Bravo (United States Public Health Service criteria). Composites with Alfa values for the marginal adaptation were used as the positive control. Results: The marginal adaptation behavior was similar between the sealing and control (+) groups, with a high frequency of Bravo values in the 10th year (80% and 51%, respectively). Most of the no-treatment (-) group maintained the Bravo values (91%) for 10 years, although some restorations (9%) progressed to Charlie values. The anatomy parameter differed significantly between the first and 10th years, with deterioration in all three groups (p,0.05). The secondary caries parameter had a similar behavior in the three groups (p.0.05). Conclusions: Sealing the margins of the composite resin restorations had no significant effect compared with the control groups, under the conditions of this study. Sealing the restorations substantially improved the marginal staining and marginal adaptation parameters, although by the tenth year they were similar to the group without intervention.

MTA versus Portland cement: review of literature

Introduction: Both Mineral Trioxide Aggregate (MTA) and Portland cement (PC) have been highlighted because of their favorable biological properties, with extensive applications in Endodontics, including the possibility of using into root canal filling. Objective: This article reviews literature related to MTA and PC comparing their physical, chemical and biological properties, as well as their indications. Literature review: Literature reports studies revealing the similarities between these materials’ properties, including both biocompatibility and bone repair induction. Moreover, there is the need for the development of a root canal sealer based on these materials (MTA and PC). Conclusion: MTA and CP show promissory perspective both in Dentistry and Endodontics.

Influence of light source and immersion media in surface roughness and hardness of a nanofilled composite resin

The study evaluated the influence of light curing units and immersion media on superficial roughness and microhardness of the nanofilled composite resin Supreme XT (3M/ESPE). Light curing units used were: XL 3000 (3M/ESPE), Jet Lite 4000 Plus (JMorita) and Ultralume Led 5 (Ultradent) and immersion media were artificial saliva, Coke®, tea and coffee, totaling 12 experimental groups. Specimens (10mm x 2mm) were immersed in each respective solution for 5 seconds, three times a day, during 60 days and so, were submitted to measure of superficial roughness (Ra) and Vickers hardness. Data were subjected to two-way ANOVA test (p<0.05). Results showed that only the light source factor showed statistically difference for hardness. It was observed that the hardness of the composite resin Filtek Supreme XT (3M/ESPE) was influenced by the light source (p<0.01) independently of the immersion media (p= 0.35) and the Jet Lite 4000 Plus (JMorita) was the light curing unit that presented lower values. In relation to surface roughness, it was noted no-significant statistical difference for light source (p=0.84), when specimens were immersed in different beverages (p=0.35).

Chemical and morphological features of nanofilled composite resin: influence of finishing and polishing procedures and fluoride solutions

This study evaluated the influence of finishing and polishing procedures and differ-ent fluoride solutions on superficial morphology and chemistry of the nanofilled composite resinSupreme XT (3M) through the EDX analysis and SEM evaluation. Circular specimens (n 5 30) of 10mm diameter and 2 mm thickness were prepared, with half of the sample assays finished and polishedwith Super-Snap1sandpaper. The experimental groups were divided according to the presence or ab-sence of finishing and polishing and solutions (arti ficial saliva, 0.0 5% of manipulated sodium fluoridesolution, Fluordent Re ach, Oral B, Fluorgard). Specimens were immersed in each respective solutionfor 1 min per day, during 60 days and stored in artificial saliva at 37 6 18C between immersion peri-ods. Topography and chemical analysis was qualitative. It was observed that specimens submitted tofinishing and polishing procedures had lower superficial degradation. Fluoride solutio ns promoted su-perficial alterations on specimens, being the highest degradation obtained with Fluordent Reach. Itca n be concluded that finishing and polishing procedures and the immersion media influence the su-perficial morphology of composite resin tested; the Fluordent Reach was the flu oride solution thatmo st affected the material’s surface.

Influence of light curing units and fluoride mouthrinse on morphological surface and color stability of a nanofilled composite resin

Composite resin is a dental material susceptible to color change over time which limits the longevity of restorations made with this material. The influence of light curing units and different fluoride mouthrinses on superficial morphology and color stability of a nanofilled composite resin was evaluated. Specimens (N = 150) were prepared and polished. The experimental groups were divided according to the type of light source (halogen and LED) and immersion media (artificial saliva, 0.05% sodium fluoride solution-manipulated, Fluordent Reach, Oral B, Fluorgard). Specimens remained in artificial saliva for 24-h baseline. For 60 days, they were immersed in solutions for 1 min. Color readout was taken at baseline and after 60 days of immersion. Surface morphology was analyzed by Scanning Electron Microscopy (SEM) after 60 days of immersion. Color change data were submitted to two-way Analysis of Variance and Tukey tests (α = 0.05). Surface morphology was qualitatively analyzed. The factor light source presented no significant variability (P = 0.281), the immersion media, significant variability (P < 0.001) and interaction between factors, no significant variability (P = 0.050). According to SEM observations, no difference was noted in the surface of the specimens polymerized by different light sources, irrespective of the immersion medium. It was concluded that the light source did not influence the color stability of composite, irrespective of the immersion media, and among the fluoride solutions analyzed, Fluorgard was the one that promoted the greatest color change, however, this was not clinically perceptible. The immersion media did not influence the morphology of the studied resin. Microsc. Res. Tech. 77:941–946, 2014. © 2014 Wiley Periodicals, Inc.

Chemical and morphological features of dental composite resin: influence of light curing units and immersion media

Aims: The study evaluated the influence of light curing units and immersionmedia on superficial morphology and chemistry of the nanofilled composite resin Supreme XT (3M)through the EDX analysis and SEM evaluation. Light curing units with different power densitiesand mode of application used were XL 3000 (480 mW/cm2), Jet Lite 4000 Plus (1230mW/cm2), andUltralume Led 5 (790 mW/cm2) and immersion media were artificial saliva, Coke1, tea and coffee,totaling 12 experimental groups. Specimens (10 mm 3 2 mm) were immersed in each respectivesolution for 5 min, three times a day, during 60 days and stored in artificial saliva at 378C 6 18Cbetween immersion periods. Topography and chemical analysis was qualitative. Findings: Groupsimmersed in artificial saliva, showed homogeneous degradation of matrix and deposition of calciumat the material surface. Regarding coffee, there was a reasonable chemical degradation with loss ofload particles and deposition of ions. For tea, superficial degradation occurred in specific areaswith deposition of calcium, carbon, potassium and phosphorus. For Coke1, excessive matrix degra-dation and loss of load particles with deposition of calcium, sodium, and potassium. Conclusion:Light curing units did not influence the superficial morphology of composite resin tested, but theimmersion beverages did. Coke1affected material’s surface more than did the other tested drinks.Microsc. Res. Tech. 73:176–181, 2010.