Influence of microwave polymerization method and thickness on porosity of acrylic resin

Purpose: This study evaluated the influence of polymerization cycle and thickness of maxillary complete denture bases on the porosity of acrylic resin. Materials and Methods: Two heat-activated denture base resins - one conventional (Clássico) and one designed for microwave polymerization (Onda-Cryl) - were used. Four groups were established, according to polymerization cycles: A (Onda-Cryl, short microwave cycle), B (Onda-Cryl, long microwave cycle), C (Onda-Cryl, manufacturing microwave cycle), and T (Clássico, water bath). Porosity was evaluated for different thicknesses (2.0, 3.5, and 5.0 mm; thicknesses I, II, and III, respectively) by measurement of the specimen volume before and after its immersion in water. The percent porosity data were submitted to Kruskal-Wallis for comparison among the groups. Results: The Kruskal-Wallis test detected that the combinations of the different cycles and thicknesses showed significant differences, and the mean ranks of percent porosity showed differences only in the thinnest (2.0 mm) microwave-polymerized specimens (A = 53.55, B = 40.80, and C = 90.70). Thickness did not affect the results for cycle T (I = 96.15, II = 70.20, and III = 82.70), because porosity values were similar in the three thicknesses. Conclusions: Microwave polymerization cycles and the specimen thickness of acrylic resin influenced porosity. Porosity differences were not observed in the polymerized resin bases in the water bath cycle for any thickness. © 2007 by The American College of Prosthodontists.

Influence of thermal and mechanical cycling on the flexural strength of ceramics with titanium or gold alloy frameworks

Objectives: The aim of this study was to evaluate the effect of thermal and mechanical cycling alone or in combination, on the flexural strength of ceramic and metallic frameworks cast in gold alloy or titanium. Methods: Metallic frameworks (25 mm × 3 mm × 0.5 mm) (N = 96) cast in gold alloy or commercial pure titanium (Ti cp) were obtained using acrylic templates. They were airborne particle-abraded with 150 μm aluminum oxide at the central area of the frameworks (8 mm × 3 mm). Bonding agent and opaque were applied on the particle-abraded surfaces and the corresponding ceramic for each metal was fired onto them. The thickness of the ceramic layer was standardized by positioning the frameworks in a metallic template (height: 1 mm). The specimens from each ceramic-metal combination (N = 96, n = 12 per group) were randomly assigned into four experimental fatigue conditions, namely water storage at 37 °C for 24 h (control group), thermal cycling (3000 cycles, between 4 and 55 °C, dwell time: 10 s), mechanical cycling (20,000 cycles under 10 N load, immersion in distilled water at 37 °C) and, thermal and mechanical cycling. A flexural strength test was performed in a universal testing machine (crosshead speed: 1.5 mm/min). Data were statistically analyzed using two-way ANOVA and Tukey's test (α = 0.05). Results: The mean flexural strength values for the ceramic-gold alloy combination (55 ± 7.2 MPa) were significantly higher than those of the ceramic-Ti cp combination (32 ± 6.7 MPa) regardless of the fatigue conditions performed (p < 0.05). Mechanical and thermo-mechanical fatigue decreased the flexural strength results significantly for both ceramic-gold alloy (52 ± 6.6 and 53 ± 5.6 MPa, respectively) and ceramic-Ti cp combinations (29 ± 6.8 and 29 ± 6.8 MPa, respectively) compared to the control group (58 ± 7.8 and 39 ± 5.1 MPa, for gold and Ti cp, respectively) (p < 0.05) (Tukey's test). While ceramic-Ti cp combinations failed adhesively at the metal-opaque interface, gold alloy frameworks exhibited a residue of ceramic material on the surface in all experimental groups. Significance: Mechanical and thermo-mechanical fatigue conditions decreased the flexural strength values for both ceramic-gold alloy and ceramic-Ti cp combinations with the results being significantly lower for the latter in all experimental conditions. © 2007 Academy of Dental Materials.

Marine catfish sting causing fatal heart perforation in a fisherman

Many marine catfish have serrated bony stings (spines), which are used in defense against predators, on the dorsal and pectoral fins. While catfish-induced injuries are generally characterized by the pain associated with envenomation, the stings in some species are sufficiently long and sharp to cause severe penetrating trauma. Most injuries are to the hands of victims, commonly fishermen. We report the death of a fisherman caused by myocardial perforation from a catfish sting. To our knowledge, this is the first such description in the medical literature.

Effectiveness of six different disinfectants on removing five microbial species and effects on the topographic characteristics of acrylic resin

Purpose: The aim of this study was to evaluate the effectiveness of disinfectant solutions (1% sodium hypochlorite, 2% chlorhexidine digluconate, 2% glutaraldehyde, 100% vinegar, tabs of sodium perborate-based denture cleanser, and 3.8% sodium perborate) in the disinfection of acrylic resin specimens (n = 10/group) contaminated in vitro by Candida albicans, Streptococcus mutans, S. aureus, Escherichia coli, or Bacillus subtilis as measured by residual colony-forming unit (CFU). In a separate experiment, acrylic resin was treated with disinfectants to monitor potential effects on surface roughness, Ra (μm), which might facilitate microbial adherence. Materials and Methods: Three hundred fifty acrylic resin specimens contaminated in vitro with 1×10 6 cells/ml suspensions of standard strains of the cited microorganisms were immersed in the disinfectants for 10 minutes; the control group was not submitted to any disinfection process. Final counts of microorganisms per ml were performed by plating method for the evaluation of microbial level reduction. Results were compared statistically by ANOVA and Tukey's test (p ≤ 0.05). In a parallel study aiming to evaluate the effect of the tested disinfectant on resin surface, 60 specimens were analyzed in a digital rugosimeter before and after ten cycles of 10-minute immersion in the disinfectants. Measurements of superficial roughness, Ra (μm), were compared statistically by paired t-test (p ≤ 0.05). Results: The results showed that 1% sodium hypochlorite, 2% glutaraldehyde, and 2% chlorhexidine digluconate were most effective against the analyzed microorganisms, followed by 100% vinegar, 3.8% sodium perborate, and tabs of sodium perborate-based denture cleanser. Superficial roughness of the specimens was higher after disinfection cycles with 3.8% sodium perborate (p = 0.03) and lower after the cycles with 2% chlorhexidine digluconate (p = 0.04). Conclusion: Within the limits of this experiment, it could be concluded that 1% sodium hypochlorite, 2% glutaraldehyde, 2% chlorexidine, 100% vinegar, and 3.8% sodium perborate are valid alternatives for the disinfection of acrylic resin. © 2008 by The American College of Prosthodontists.

Superação da dormência em sementes de Murdannia nudiflora (L.) Brenan

The objective of this study was to identify treatments capable of promoting and standardizing the germination of Murdannia nudiflora (L.) Brenan seeds. The seeds of this weed were submitted to the following treatments: mechanical abrasion with 220-grit sandpaper (20, 30 and 40 frictions); immersion in sulfuric acid (90% for 30 and 40 seconds), followed by washing in running water; immersion in sodium hypochlorite (2.5% for 8 and 12 hours) and lye (5 minutes), followed by five washings in distilled water; immersion in KNO 3 (1% for 24 hours); preheating at 40°C in a humid or dry substrate for 2, 3 and 4 weeks. The statistical design was totally randomized, with four repetitions. The number of germinated seeds was counted every other day. The most favorable treatments were preheating at 40°C in humid substrate for 3 weeks, followed by mechanical abrasion after 40 frictions and immersion in sulfuric acid for 40 seconds.

The role of coarse intermetallics in the localized corrosion behaviour of AA 2024-T3 in low concentrated chloride media

Aluminium alloy (AA) 2024-T3 is an important engineering material due to its widespread use in the aerospace industry. However, it is very prone to localized corrosion attack in chloride containing media, which has been mainly associated to the presence of coarse intermetallics (IMs). In this work the corrosion behaviour of aluminium alloy 2024-T3 in low concentrated chloride media was investigated using microscopy and electrochemical methods. SEM observations have shown that intermetallics with the same nominal composition present heterogeneous reaction rates, and that both types of coarse IMs normally found in the AA 2024-T3 microstructure corrode. Moreover, EDS analyses have shown important compositional changes in the corroded IMs, evidencing the selective corrosion of their more active constituents and the onset of an intense oxygen peak, irrespective to the IM nature. TEM/EDS observations on non-corroded samples have evidenced the heterogeneous composition within the IMs. On the other hand, the results of the electrochemical investigations, in accordance with the SEM/EDS observations, have evidenced that IMs corrosion dominates the electrochemical response of the alloy during the first hours of immersion in the test electrolyte. © 2009 by NACE International.

Changes on transmittance mode of different composite resins

The purpose of this study was to evaluate the transmittance of seven different composite resins. Ten specimens were prepared (10 mm diameter, 2 mm thickness) for each experimental group, as follows: G1- Charisma® A 2 (Heraeus-Kulzer); G2- Filtek™ Supreme A 2E (3M/ESPE); G3- Filtek™ Supreme A2B (3M/ESPE); G4-Filtek™ Supreme YT (3M/ESPE); G5- Esthet-X® A2 (Dentsply); G6- Esthet-X® YE (Dentsply); G7- Durafill® A 2 (Heraeus-Kulzer) and G8- Filtek™ Z-100 A2 (3M/ESPE). The transmittance mode was measured using a UV-visible spectrophotometer (Cary Instruments) at 400-760 nm. The specimens were evaluated at three different times: zero hour (initial), 24 hours and 10 days after immersion in artificial saliva. The differences in transmittance were determined by two-way analysis of variance (ANOVA) and Tukey's test. The various composite resins showed significant differences in the wavelength dependence of transmittance. The mean values of transmittance increased significantly, with wavelengths increasing from 400 to 760 nm. The performance of the experimental groups was similar in terms of immersion time, considering that at time zero and after 10 days, all the groups showed similar results, which were statistically higher than the values obtained after 24 hours of immersion. The Filtek™ Supreme YT composite resin presented the highest mean transmittance values along the wavelengths at the three measured times. Esthet-X® YE and Durafill® yielded similar mean transmittance values, which were higher than those of the other groups. This study shows that the transmittance values of composite resins are directly related with the type, size and amount of inorganic filler particles.

The effect of chloride ions and A. ferrooxidans on the oxidative dissolution of the chalcopyrite evaluated by electrochemical noise analysis (ENA)

It is believed that the dissolution of chalcopyrite (CuFeS2) in acid medium can be accelerated by the addition of Cl- ions, which modify the electrochemical reactions in the leaching system. Electrochemical noise analysis (ENA) was utilized to evaluate the effect of the Cl- ions and Acidithiobacillus ferrooxidans on the oxidative dissolution of a CPE-chalcopyrite (carbon paste electrode modified with chalcopyrite) in acid medium. The emphasis was on the analysis of the admittance plots (Ac) calculated by ENA. In general, a stable passive behavior was observed, mainly during the initial stages of CPE-chalcopyrite immersion, characterized by a low passive current and a low dispersion of the Ac plots, mainly after bacteria addition. This can be explained by the adhesion of bacterial cells on the CPE-chalcopyrite surface acting as a physical barrier. The greater dispersions in the Ac plots occurred immediately after the Cl- ions addition, in the absence of bacteria characterizing an active-state. In the presence of bacteria the addition of Clions only produced some effect after some time due to the barrier effect caused by bacteria adhesion. © (2009) Trans Tech Publications.

Evaluation of alternative methods for the disinfection of toothbrushes

The aim of this study was to evaluate alternative methods for the disinfection of toothbrushes considering that most of the previously proposed methods are expensive and cannot be easily implemented. Two-hundred toothbrushes with standardized dimensions and bristles were included in the study. The toothbrushes were divided into 20 experimental groups (n=10), according to microorganism considered and chemical agent used. The toothbrushes were contaminated in vitro by standardized suspensions of Streptococcus mutans, Streptococcus pyogenes, Staphylococcus aureus or Candida albicans. The following disinfectants were tested: 0.12% chlorhexidine digluconate, 50% white vinegar, a triclosan-containing dentifrice solution, and a perborate-based tablet solution. The disinfection method was immersion in the disinfectant for 10min. After the disinfection procedure, the number of remaining microbial cells was evaluated. The values of cfu/toothbrush of each group of microorganism after disinfection were compared by Kruskal-Wallis ANOVA and Dunn's test for multiple comparisons (5%). The chlorhexidine digluconate solution was the most effective disinfectant. The triclosan-based dentifrice solution promoted a significant reduction of all microorganisms' counts in relation to the control group. As to the disinfection with 50% vinegar, a significant reduction was observed for all the microorganisms, except for C. albicans. The sodium perborate solution was the less effective against the tested microorganisms. Solutions based on triclosan-containing dentifrice may be considered effective, nontoxic, cost-effective, and an easily applicable alternative for the disinfection of toothbrushes. The vinegar solution reduced the presence of S. aureus, S. mutans and S. pyogenes on toothbrushes.

Effect of storage in artificial saliva and thermal cycling on Knoop hardness of resin denture teeth

Purpose: This study aimed to evaluate the effect of different storage periods in artificial saliva and thermal cycling on Knoop hardness of 8 commercial brands of resin denture teeth. Methods: Eigth different brands of resin denture teeth were evaluated (Artplus group, Biolux group, Biotone IPN group, Myerson group, SR Orthosit group, Trilux group, Trubyte Biotone group, and Vipi Dent Plus group). Twenty-four teeth of each brand had their occlusal surfaces ground flat and were embedded in autopolymerized acrylic resin. After polishing, the teeth were submitted to different conditions: (1) immersion in distilled water at 37 ± 2 °C for 48 ± 2. h (control); (2) storage in artificial saliva at 37 ± 2 °C for 15, 30 and 60 days, and (3) thermal cycling between 5 and 55 °C with 30-s dwell times for 5000 cycles. Knoop hardness test was performed after each condition. Data were analyzed with two-way ANOVA and Tukey's test (α= .05). Results: In general, SR Orthosit group presented the highest statistically significant Knoop hardness value while Myerson group exhibited the smallest statistically significant mean (P< .05) in the control period, after thermal cycling, and after all storage periods. The Knoop hardness means obtained before thermal cycling procedure (20.34 ± 4.45 KHN) were statistically higher than those reached after thermal cycling (19.77 ± 4.13 KHN). All brands of resin denture teeth were significantly softened after storage period in artificial saliva. Conclusion: Storage in saliva and thermal cycling significantly reduced the Knoop hardness of the resin denture teeth. SR Orthosit denture teeth showed the highest Knoop hardness values regardless the condition tested. © 2010 Japan Prosthodontic Society.

Dental arches multi-projection system with semantic descriptions

This paper presents the development of an multi-projection stereoscopic dental arches application with semantic descriptions. The first section presents the concepts of the used technologies. Applications and examples are demonstrated. Finally, is presented the physical structure and the developed system, where a 3D dental arch is used as a model and can be viewed in multi-projection, thereby, providing greater user's immersion. ©2010 IEEE.

Effectiveness of three solvents and two associations of solvents on gutta-percha and Resilon

This study evaluated the effectiveness of 3 solvents (Citrol orange oil, Eucalyptol and Tetrachloroethylene) and 2 associations of solvents (Citrol orange oil+Tetrachloroethylene and Eucalyptol+Tetrachloroethylene) on 3 types of gutta-percha (conventional, thermoplastic and EndoREZ) and Resilon. Ten discs (10 mm diameter x 1 mm thick) from each material were prepared using standard metallic molds. Each specimen was weighed to determinate its initial mass. The specimens were immersed in the solvents for 10 min, followed by immersion in distilled water for 20 min, and were then reweighed to obtain the final mass. The mean weight loss determined the solvent capacity. Data were analyzed by ANOVA and Tukey's test at 5% significance level. Tetrachloroethylene was the most effective on conventional gutta-percha (p<0.05). Tetrachloroethylene was also the most effective on thermoplastic gutta-percha, but it was not significantly different (p>0.05) from Eucalyptol+Tetrachloroethylene, Citrol+Tetrachloroethylene, and Citrol. All solvents and associations presented little effectiveness on Resilon. The association Eucalyptol+Tetrachloroethylene was the most effective on EndoREZ, but it did not differ significantly (p>0.05) from Citrol+Tetrachloroethylene and Tetrachloroethylene. All evaluated substances presented solvent action. Tetrachloroethylene improved the effectiveness of both Citrol and Eucalyptol.

Quebra de dormência em sementes de Sesbania virgata (Cav.) Pers

Forest species with hard seeds often pose considerable problems to nursery managers because their hard and impermeable seed coats hinder and delay germination. Therefore, this work aimed to determine the most efficient, practical and low cost methodology to overcome dormancy in Sesbania virgata (Cav.) Pers. Seed, a specie with potential for recovery of degraded areas. The seeds were submitted to chemical scarification by immersion in sulfuric acid during a period of 5, 10, 20 and 30 minutes, mechanical scarification and heat treatment. After the scarification the seeds were submitted to germ test in germination chambers at 25oC and photoperiod of 14 h. Treatment with mechanical scarification showed the highest germination percentage (98%), followed by chemical scarification for 30 minutes (57%). The heat treatment in spite of obtaining a higher germination percentage than the controls had abnormal development of seedlings and is not therefore recommended for seeds of S. virgata. From the parameters utilized in this study, we recommend the use of the mechanical scarification to overcome dormancy of S. virgata seeds.

Morphological alterations on human radicular dentin after exposure to different fruit juice drinks

Purpose: This in vitro study aimed to evaluate the effect of different fruit juice drinks available in the Brazilian market on smear layer removal and dentinal tubules opening, as well as to verify the effect of toothbrushing subsequently to the juices exposure. Methods: Dentin specimens were prepared and randomly distributed into the control group (distilled water) and twelve types of fruit juice drinks (cashew, orange, mandarin, apple, passion fruit, guava, strawberry, grape, mango, pear, peach, pineapple). The following treatments were applied: immersion or immersion + brushing. After preparation for SEM, photomicrographs were assessed using an index of smear layer removal. Results: No significant differences regarding smear layer removal and dentinal tubules exposure could be observed between the groups after both treatments (Kruskal-Wallis, post-hoc paired comparisons, P>0.05). The control solution and the fruit juice drinks were not able to remove smear layer and to open dentinal tubules. Significant difference between the applied treatments was detected only for the mango juice group (Mann-Whitney, P<0.05). Conclusion: Under the experimental conditions, the different fruit juice drinks did not promote significant alterations on human radicular dentin morphology regardless of the subsequent application of brushing procedures. Copyright: © 2011 Zandim et al.

Color stability of resins and nylon as denture base material in beverages

Purpose: Staining of prosthodontic materials may result in patient dissatisfaction and additional expense for replacement. This study aimed to determine the color stability of two heat-cured denture base acrylic (Lucitone 550, Vipi Cril) and one nylon denture base resin (Transflex) after immersion in beverages. Materials and Methods: Forty disks of each resin (20.0-mm diameter, 3.0-mm thick) were prepared and stored in distilled water for 24 hours at 37°C. During that time (T 0), the color of all specimens was spectrophotometrically measured. Each specimen was immersed in coffee, cola, red wine, and distilled water as a means of control. After 15-day (T 1) and 30-day (T 2) periods of immersion, the color of the specimens was measured again. The CIE (Commission Internationale de L' Eclairage) L*a*b* system was used to determine mean ΔE (color changes) values for each material and compared statistically with two-way ANOVA and Bonferroni intervals at 0.95. Results: In ΔET 0T 1 and ΔET 0T 2 the most severe staining was apparent with red wine (p < 0.001), followed by coffee (p < 0.01), when compared to the specimens stored in distilled water. Transflex also showed significant color change after immersion in cola (p < 0.01). In ΔET 1T 2 only red wine promoted significant staining of all resins (p < 0.0001). Conclusion: Chromatic changes were exhibited by specimens immersed in red wine, followed by coffee. For Transflex, cola also promoted color changes. The values of color changes converted to National Bureau of Standard units showed them to be perceivable to the human eye. © 2011 by the American College of Prosthodontists.