Phase equilibrium data and liquidus for the system "MnO"-CaO-(Al2O3+SiO2) at Al2O3/SiO2 of 0.41

Phase-equilibrium data and the liquidus for the system. "MnO"-CaO-(Al2O3-SiO2) at a manganese-rich alloy saturation have been determined in the temperature range from 1423 to 1723 K. The results are presented in the form of a pseudoternary section "MnO"-CaO-(Al2O3 + SiO2) with an Al2O3/SiO2 weight ratio of 0.41. The following primary phases are present in the range of conditions investigated:, 3Al(2)O(3).2SiO(2); SiO2; MnO.Al2O3-2SiO(2); (Mn,Ca)O.SiO2; 2(Mn,Ca)O.SiO2; MnO.Al2O3; (Mn,Ca)O; alpha-2CaO.SiO2; alpha'-2CaO.SiO2; 2CaO.Al2O3.SiO2; CaO.SiO2, and CaO.Al2O3.2SiO(2). The presence of alumina in this system is shown to have a significant effect on the liquidus compared to the system "MnO"-CaO-SiO2, leading to, the stabilization of the anorthite and gehlenite phases.

An age hardening model for Al-7Si-Mg casting alloys

Yield strength (YS) ageing curves have been modelled for A356 and A357 aluminium casting alloys below the solvus temperature of the main hardening precipitate. Predictions are based on the Shercliff and Ashby methodology (Acta MetaH. Mater. 38 (1990) 1789) for wrought alloys. Differences between strengthening in wrought and cast Al-Si-Mg alloys are considered. A Brinell hardness to YS conversion incorporating strain hardening has been established to enable YS ageing curves to be predicted with reduced experimental effort. (C) 2002 Elsevier Science B.V. All rights reserved.