Effectiveness of surface protection for resin-modified glass-ionomer materials

Objective: the purpose of this study was to evaluate the effectiveness of various surface treatments for resin-modified glass-ionomer restorative materials by determining dye uptake spectrophotometrically. Method and materials: Two hundred twenty-four specimens, 4.1 mm in diameter and 2.0 mm thick, were made of 3 materials: Vitremer, Fuji II LC, and Photac-Fil Aplicap. Specimens were divided into 15 groups. The positive and negative control specimens remained unprotected, while the experimental specimens were protected with Heliobond light-activated bonding resin, Colorama nail varnish, or surface coatings indicated by the manufacturers of the glass-ionomer materials. Finishing Gloss for Vitremer, Fuji Varnish for Fuji II LC, and Ketac Glaze for Photac-Fil. The disks were immersed in 0.05% methylene blue for 24 hours except for the negative control group, which was immersed in deionized water. After 24 hours, the disks were removed, washed, and individually placed in 1 mL of 65% nitric acid for 24 hours. The solutions were centrifuged and the spectrophotometric absorbance was determined at 606 nm. The dye uptake was expressed in micrograms of dye per milliliter, and the results were analyzed with the Kruskal-Wallis test. Results: There were no differences in dye uptake among the 3 resin-modified glass-ionomer restorative materials, however, all of them required surface protection. Conclusion: the best surface protection for the 3 evaluated materials was obtained with Heliobond light-activated bonding resin.

Development of a new epoxy resin for superconducting magnet impregnation

A novel epoxy resin system based on a low viscosity Bisphenol-A (DGEBA)/Bisphenol-F (DGEBF) blend has been investigated for use in tight-wound superconducting magnet impregnation. The principle is to decrease the Bisphenol-A resin system viscosity by adding the low viscosity Bisphenol-F resin. The rheological and mechanical properties of the blend system are compared to the pure Bisphenol-A resin and also to the Bisphenol-F resin both cured with acid anhydride. For the vacuum/pressure impregnation, both the pure Bisphenol-F resin system and DGEBA/DGEBF blend system can be applied without S-glass fabric between coil layers due to its higher rigidity at low temperature and good resistance to thermal shock. This resin system have been tested for impregnation of copper and NbTi wire wound coils whilst Bisphenol-A resin system have been used for testing Nb3Sn coil impregnation where S-glass braid is present as wire insulation.

Microleakage of hydrophilic adhesive systems in Class V composite restorations

Purpose: To investigate the microleakage of four hydrophilic adhesive systems: one multiple-bottles (Scotchbond Multi-Purpose Plus); two one-bottle (Single Bond, Stae); and one self-etching (Etch & Prime 3.0). Materials and Methods: 120 bovine incisor teeth were divided into four groups (n = 30) and Class V cavities were prepared at the cemento-enamel junction. The cavities were restored with the adhesive systems and with Z100 composite. The teeth were thermocycled 1,000 times between 5 +/- 2 degreesC and 55 +/- 2 degreesC with a dwell time of 1 min, and then placed in a 2% methylene blue dye (pH 7.0) for 4 hrs, washed and sectioned vertically through the center of the restorations. The qualitative evaluation was made by three examiners who distributed pre-established scores (0-4) for each tooth using a stereomicroscope at x30 magnification. Results: In enamel margins little microleakage was observed and the Kruskal-Wallis analysis did not show differences. In dentin margins the KruskaI-Wallis and multiple comparison analyses were applied: microleakage was significantly greater with Stae (median 3) and Scotchbond MP Plus (median 4). Single Bond (median 1) and Etch & Prime 3.0 (median 2) showed the best results in dentin margins, and the statistical analysis did not demonstrate differences in microleakage among these groups.

EPR investigation of the influence of side chain protecting groups on peptide-resin solvation of the Asx and Glx model containing peptides

In spite of all progressive efforts aiming to optimize SPPS, serious problems mainly affecting the assembly of aggregating sequences have persisted. Following the study intended to unravel the complex solvation phenomenon of peptide-resin beads, the XING and XAAAA model aggregating segments were labeled with a paramagnetic probe and studied via EPR spectroscopy. Low and high substituted resins were also comparatively used, with the X residue being Asx or Glx containing the main protecting groups used in the SPPS. Notably, the cyclo-hexyl group used for Asp and Glu residues in Boc-chemistry induced greater chain immobilization than its tert-butyl partner-protecting group of the Fmoc strategy. Otherwise, the most impressive peptide chain immobilization occurred when the large trytil group was used for Asn and Gln protection in Fmoc-chemistry. These surprising results thus seem to stress the possibility of the relevant influence of the amino-acid side chain protecting groups in the overall peptide synthesis yield. (C) 2007 Elsevier Ltd. All rights reserved.