Transformation of vaterite into calcite in the absence and the presence of copper(II) species. Thermal analysis, IR and EPR study

The transformation of vaterite into calcite may be performed by heating in the presence and the absence of oxygen. Vaterite remains thermally stable until a calcination temperature of 450°C. It transforms progressively to calcite up to 500°C giving two exothermic peaks: 1) at 481°C due to the transformation of vaterite surface which is in contact with a small amount of calcite phase already formed with the time on the solid surface from the humidity atmosphere; 2) at 491°C due to the transformation of pure vaterite bulk. The calcite phase remains stable until 700°C. Above this temperature the formation of CaO is observed.

The transformation of cyclohexane on Zn/H-ZSM-5 zeolites

Samples of Zn/H-ZSM-5 zeolite were prepared by impregnation of the parent zeolite with Zn(NO3)(2). The state of zinc in the samples was analyzed by XPS measurements, (ald the degree of reduction for the zinc oxide on the ZSM-5 zeolite surface in hydrogen atmosphere was determined, as well as the influence of this reducing treatment upon the activity and selectivity for aromatics of zeolites in aromatization of cyclohexane. It resulted that the degree of reduction depends on the concentration of zinc in the zeolite and is influenced by the presence of alumina binder. The results of the activity and selectivity to aromatics were correlated with the reduction of zinc oxide.