Spray pyrolysed In2S3 thin films: A potential electron selective layer for large area inverted bulk-heterojunction polymer solar cells

In this paper, we report the results of investigations on the potential of spray pyrolysis technique in depositing electron selective layer over larger area for the fabrication of inverted bulk-heterojunction polymer solar cells. The electron selective layer (In2S3) was deposited using spray pyrolysis technique and the linear heterojunction device thus fabricated exhibited good uniformity in photovoltaic properties throughout the area of the device. An MEH-PPV:PCBM inverted bulk-heterojunction device with In2S3 electron selective layer (active area of 3.25 3.25 cm2) was also fabricated and tested under indoor and outdoor conditions. Fromthe indoor measurements employing a tungsten halogen lamp (50mW/cm2 illumination), an opencircuit voltage of 0.41V and a short-circuit current of 5.6mA were obtained. On the other hand, the outdoor measurements under direct sunlight (74mW/cm2) yielded an open-circuit voltage of 0.46V and a short-circuit current of 9.37mA

Photoschaltbare Azobenzol-modifizierte selbstorganisierte Monoschichten auf Gold(111)-Oberflächen

Für die Entwicklung photoschaltbarer selbstorganisierter Monoschichten (SAMs) auf Gold(111)-Oberflächen wurden neue Azobenzol-terminierte Asparagussäure - und Liponsäurederivate synthetisiert. Um den Einfluss lateraler Wasserstoffbrückenbindungen auf Qualität und Orientierungsordnung der Schichten zu untersuchen, wurden Monolagen, die durch amid- und esterverknüpfte Verbindungen gebildet wurden, miteinander verglichen. Die Filmbildung aus der Lösung wurde in situ durch optische Frequenzverdopplung (SHG) untersucht und die Photoreaktivität mittels Kontaktwinkelmessungen, Oberflächen-Plasmonenresonanz (SPR) und Ellipsometrie verfolgt. SAMs auf Gold wurden außerdem mit Hilfe von Röntgenphotoelektronenspektroskopie (XPS), Nahkanten-Reflexions-Röntgenabsorptionsspektroskopie (NEXAFS) und Infrarot-Reflexionsabsorptionsspektroskopie (IRRAS) charakterisiert, um die Filmqualität, die Bindung ans Substrat und Orientierungsordnung im Film zu ermitteln. Da die Chemisorption auf polykristallinem Gold formal der Koordinationschemie von 1,2-Dithiolan-Derivaten gegenüber nullwertigen Edelmetall-Zentralatomen entspricht, wurden etliche Pt-Komplexe durch oxidative Addition an [Pt(PPh3)4] dargestellt. Im Zusammenhang mit der Darstellung der Asparagussäure wurde die Kristallstruktur von [pipH]2[WS4] und der neuen Verbindungen [pipH]3[WS4](HS) und [pipH]4[WS4][WOS3] (pip = Piperidin) bestimmt. Wasserstoffbrückenbindungen zwischen den Piperidinium-Kationen und den Thiowolframat-Anionen spielen eine dominante strukturelle Rolle.

Synthesis and Characterization of Magnetic Nanoparticles with High Magnetization and Good Oxidation Resistibility

Magnetic nanoparticles attract increasing attention because of their current and potential biomedical applications, such as, magnetically targeted and controlled drug delivery, magnetic hyperthermia and magnetic extraction. Increased magnetization can lead to improved performance in targeting and retention in drug delivery and a higher efficiency in biomaterials extraction. We reported an approach to synthesize iron contained magnetic nanoparticles with high magnetization and good oxidation resistibility by pyrolysis of iron pentacarbonyl (Fe(CO)[subscript 5]) in methane (CH[subscript 4]). Using the high reactivity of Fe nanoparticles, decomposition of CH[subscript 4] on the Fe nanoparticles leads to the formation of nanocrystalline iron carbides at a temperature below 260°C. Structural investigation indicated that the as-synthesized nanoparticles contained crystalline bcc Fe, iron carbides and spinel iron oxide. The Mössbauer and DSC results testified that the as-synthesized nanoparticle contained three crystalline iron carbide phases, which converted to Fe[subscript 3]C after a heat treatment. Surface analysis suggested that the as-synthesized and subsequently heated iron-iron carbide particles were coated by iron oxide, which originated from oxidization of surface Fe atoms. The heat-treated nanoparticles exhibited a magnetization of 160 emu/g, which is two times of that of currently used spinel iron oxide nanoparticles. After heating in an acidic solution with a pH value of 5 at 60°C for 20 h, the nanoparticles retained 90 percentage of the magnetization.

Inherited resistance to arsenate toxicity in two populations of Lumbricus rubellus

No unequivocal evidence exists of genetically inherited resistance to metals/metalloids in field populations of earthworms. We studied cocoon production in adult Lumbricus rubellus Hoffmeister collected from an abandoned arsenic and copper mine (Devon Great Consols, Devon, UK), and abandoned tungsten mine (Carrock Fell, Cumbria, UK) and an uncontaminated cultured population. The earthworms were kept in uncontaminated soil for nine weeks. From a total of 42 L. rubellus from each site, Devon Great Consols adults produced 301 cocoons, of which 42 were viable; Carrock Fell 60 cocoons, of which 11 were viable; and the reference population 101 cocoons, of which 62 were viable. The hatchlings were collected and stored at 4degreesC at weekly intervals. After 12 weeks, all hatchlings were transferred to clean soil and maintained at 15degreesC for 20 weeks until they showed evidence of a clitellum. In toxicity trials, F1 generation L. rubellus were exposed to 2,000 mg As/kg as sodium arsenate or 300 mg Cu/kg as copper chloride for 28 d. The F1 generation L. rubellus from Devon Great Consols mine demonstrated resistance to arsenate but not copper. All L. rubellus from Devon Great Consols kept in soil treated with sodium arsenate remained in good condition over the 28-d period but lost condition rapidly and suffered high mortality in soil treated with copper chloride. The control population suffered high mortality in soil treated with sodium arsenate and copper chloride. Previous work has shown that field-collected adults demonstrate resistance to both arsenate and Cu toxicity under these conditions. Thus, while arsenate resistance may be demonstrated in F1 generation L. rubellus from one of the contaminated sites, Cu resistance is not. The F1 adults and F2 cocoons did not have significantly higher levels of As than the control population, with no residual As tissue burden, suggesting that resistance to As in these populations may be inherited.

The oxadiazolyldiazenido(1-) ligand: a remarkably versatile platform for the synthesis of heteropolynuclear transition metal complexes

Cyclo-condensation of aroyl hydrazides with the cationic tungsten-dichlorodiazomethane complex [BrW(dppe)(2)(N2CCI2)](+) affords neutral oxadiazolyldiazenido(1-) complexes which react readily with a wide range of transition and non-transition metal species to afford a novel series of crystallographically-characterised heteropolynuclear complexes containing bridging oxadiazolyldiazenido(1-) ligands.

Synthesis and characterization of packed mesoporous tungsteno-silicates: application to the catalytic dehydrogenation of 2-propanol

The synthesis of highly ordered mesoporous tungsteno-silicas in which a high percentage of tungsten is introduced into a silica framework is reported hereafter. Powder XRD and TEM have been used to characterize the materials synthesized at room temperature. The materials are shown to be homogeneous as there is no evidence for any crystalline species other than the silica framework. The pore diameter and the surface area of the materials, evaluated from the nitrogen adsorption isotherms and unit cell parameter indicate a pore diameter of about 2 nm and a surface area of 1400 m(2) g(-1) for a content of 10% tungsten. Catalyzed dehydration of 2-propanol has been investigated and the activity of the materials synthesized is significant, even for low tungsten content W-MCM-41 materials. (C) 2003 Elsevier B.V. All rights reserved.

New high technology product development: The case of light emitting diodes

New high technology products usher in novel possibilities to transform the design, production and use of buildings. The high technology companies which design, develop and introduce these new products by generating and applying novel scientific and technical knowledge are faced with significant market uncertainty, technological uncertainty and competitive volatility. These characteristics present unique innovation challenges compared to low- and medium technology companies. This paper reports on an ongoing Construction Knowledge Exchange funded project which is tracking, real time, the new product development process of a new family of light emitting diode (LEDs) technologies. LEDs offer significant functional and environmental performance improvements over incumbent tungsten and halogen lamps. Hitherto, the use of energy efficient, low maintenance LEDs has been constrained by technical limitations. Rapid improvements in basic science and technology mean that for the first time LEDs can provide realistic general and accent lighting solutions. Interim results will be presented on the complex, emergent new high technology product development processes which are being revealed by the integrated supply chain of a LED module manufacture, a luminaire (light fitting) manufacture and end user involved in the project.

First Results with the RISING active stopper

This paper outlines some of the physics opportunities available with the GSI RISING active stopper and presents preliminary results from an experiment aimed at performing beta-delayed gamma-ray spectroscopic studies in heavy-neutron-rich nuclei produced following the projectile fragmentation of a 1 GeV per nucleon 208Pb primary beam. The energy response of the silicon active stopping detector for both heavy secondary fragments and beta-particles is demonstrated and preliminary results on the decays of neutron-rich Tantalum (Ta) to Tungsten (W) isotopes are presented as examples of the potential of this technique to allow new structural studies in hitherto experimentally unreachable heavy, neutron-rich nuclei. The resulting spectral information inferred from excited states in the tungsten daughter nuclei are compared with results from axially symmetric Hartree–Fock calculations of the nuclear shape and suggest a change in ground state structure for the N = 116 isotone 190W compared to the lighter isotopes of this element.

Adhesion to Er : YAG laser-prepared dentin after long-term water storage and thermocycling

This in vitro study evaluated the microtensile bond strength of a resin composite to Er:YAG-prepared dentin after long-term storage and thermocycling. Eighty bovine incisors were selected and their roots removed. The crowns were ground to expose superficial dentin. The samples were randomly divided according to cavity preparation method (I-Er:YAG laser and II-carbide bur). Subsequently, an etch & rinse adhesive system was applied and the samples were restored with a resin composite. The samples were subdivided according to time of water storage (WS)/number of thermocycles (TC) performed: A) 24 hours WS/no TC; B) 7 days WS/500 TC; C) 1 month WS/2,000 TC; D) 6 months WS/12,000 TC. The teeth were sectioned in sticks with a cross-sectional area of 1.0-mm(2), which were loaded in tension in a universal testing machine. The data were subjected to two-way ANOVA, Scheffe and Fisher`s tests at a 5% level. In general, the bur-prepared group displayed higher microtensile bond strength values than the laser-treated group. Based on one-month water storage and 2,000 thermocycles, the performance of the tested adhesive system to Er:YAG-laser irradiated dentin was negatively affected (Group IC), while adhesion of the bur-prepared group decreased only within six months of water storage combined with 12,000 thermocycles (Group IID). It may be concluded that adhesion to the Er:YAG laser cavity preparation was more affected by the methods used for simulating degradation of the adhesive interface.

The extreme physical properties of the CoRoT-7b super-Earth

The search for rocky exoplanets plays an important role in our quest for extra-terrestrial life. Here, we discuss the extreme physical properties possible for the first characterised rocky super-Earth, CoRoT-7b (R(pl) = 1.58 +/- 0.10 R(Earth), M(pl) = 6.9 +/- 1.2 M(Earth)). It is extremely close to its star (a = 0.0171 AU = 4.48 R(st)), with its spin and orbital rotation likely synchronised. The comparison of its location in the (M(pl), R(pl)) plane with the predictions of planetary models for different compositions points to an Earth-like composition, even if the error bars of the measured quantities and the partial degeneracy of the models prevent a definitive conclusion. The proximity to its star provides an additional constraint on the model. It implies a high extreme-UV flux and particle wind, and the corresponding efficient erosion of the planetary atmosphere especially for volatile species including water. Consequently, we make the working hypothesis that the planet is rocky with no volatiles in its atmosphere, and derive the physical properties that result. As a consequence, the atmosphere is made of rocky vapours with a very low pressure (P <= 1.5 Pa), no cloud can be sustained, and no thermalisation of the planet is expected. The dayside is very hot (2474 +/- 71 K at the sub-stellar point) while the nightside is very cold (50-75 K). The sub-stellar point is as hot as the tungsten filament of an incandescent bulb, resulting in the melting and distillation of silicate rocks and the formation of a lava ocean. These possible features of CoRoT-7b could be common to many small and hot planets, including the recently discovered Kepler-10b. They define a new class of objects that we propose to name ""Lava-ocean planets"". (C) 2011 Elsevier Inc. All rights reserved.

High-power diode laser in the disinfection in depth of the root canal dentin

Objective. The objective of this study was to evaluate the disinfection degree of dentine caused by the use of diode laser after biomechanical procedures. Study design. Thirty teeth were sectioned and roots were autoclaved and incubated for 4 weeks with a suspension of Enterococcus faecalis. The specimens were randomly divided into 3 groups (n = 10): G1, instrumented with rotary files, irrigated with 0.5% sodium hypochlorite and 17% EDTA-T, and then irradiated by 830-nm diode laser at 3 W; G2, the same procedures as G1 but without laser irradiation; and G3, irrigation with saline solution (control). Dentin samples of each third were collected with carbide burs and aliquots were sowed to count viable cells. Results. The disinfection degree achieved was 100% in G1 and 98.39% in G2, when compared to the control group (G3). Conclusion. Diode laser irradiation provided increased disinfection of the deep radicular dentin in the parameters and samples tested.

X-ray photoelectron spectroscopy analysis of zirconium nitride-like films prepared on Si(100) substrates by ion beam assisted deposition

Thin zirconium nitride films were prepared on Si(l 00) substrates at room temperature by ion beam assisted deposition with a 2 keV nitrogen ion beam. Arrival rate ratios ARR(N/Zr) used were 0.19, 0.39, 0.92, and 1.86. The chemical composition and bonding structure of the films were analyzed with X-ray photoelectron spectroscopy (XPS). Deconvolution results for Zr 3d, Zr 3p(3/2), N 1s, O 1s, and C 1s XPS spectra indicated self-consistently the presence of metal Zr-0, nitride ZrN, oxide ZrO2, oxymnide Zr2N2O, and carbide ZrC phases, and the amounts of these compounds were influenced by ARR(N/Zr). The chemical composition ratio N/Zr in the film increased with increasing ARR(N/Zr) until ARR(N/Zr) reached 0.92, reflecting the high reactivity of nitrogen in the ion beam, and stayed almost constant for ARR(N/Zr) >= 1, the excess nitrogen being rejected from the growing film. A considerable incorporation of contaminant oxygen and carbon into the depositing film was attributed to the getter effect of zirconium. (C) 2007 Elsevier B.V. All rights reserved.

Assessment the Health Hazard from (222)Rn in Old Metalliferous Mines in San Luis, Argentina

Radon levels in two old mines in San Luis, Argentina, are reported and analyzed. The radiation dose and environmental health risk of (222)Rn concentrations to both guides and visitors were estimated. CR-39 nuclear track detectors were used for this purpose. The values for the (222)Rn concentration at each monitoring site ranged from 0.43 +/- 0.04 to 1.48 +/- 0.12 kBq m(-3) in the Los Cndores wolfram mine and from 1.8 +/- 0.1 to 6.0 +/- 0.5 kBq center dot m(-3) in the La Carolina gold mine, indicating that, in this mine, the radon levels exceed up to four times the action level of 1.5 kBq m(-3) recommended by the International Commission on Radiological Protection. The patterns of the radon transport process revealed that the La Carolina gold mine can be interpreted as a gas confined into a single tube with constant cross-section and air velocity. Patterns of radon activity, taking into account the chimney-effect winds, were used to detect tributary currents of air from shafts or larger fissures along the main adit of the Los Cndores mine, showing that radon can be used as an important tracer of tributary air currents stream out from fissures and smaller voids in the rock of the mine.

Influence of pre-heat treatment and different light-curing units on Vickers hardness of a microhybrid composite resin

The aim of this study was to evaluate the hardness of a dental composite resin submitted to temperature changes before photo-activation with two light-curing unite (LCUs). Five samples (4 mm in diameter and 2 mm in thickness) for each group were made with pre-cure temperatures of 37, 54, and 60A degrees C. The samples were photo-activated with a conventional quartz-tungsten-halogen (QTH) and blue LED LCUs during 40 s. The hardness Vickers test (VHN) was performed on the top and bottom surfaces of the samples. According to the interaction between light-curing unit and different pre-heating temperatures of composite resin, only the light-curing unit provided influences on the mean values of initial Vickers hardness. The light-curing unit based on blue LED showed hardness mean values more homogeneous between the top and bottom surfaces. The hardness mean values were not statistically significant difference for the pre-cure temperature used. According to these results, the pre-heating of the composite resin provide no influence on Vickers hardness mean values, however the blue LED showed a cure more homogeneous than QTH LCU.

Thin films prepared from tungstate glass matrix

Vitreous samples containing high concentrations of WO3 (above 40% M) have been used as a target to prepare thin films. Such films were deposited using the electron beam evaporation method onto soda-lime glass substrates. These films were characterized by X-ray diffraction (XRD), perfilometry, X-ray energy dispersion spectroscopy (EDS), M-Lines and UV-vis absorption spectroscopy. In this work, experimental parameters were established to obtain stable thin films showing a chemical composition close to the glass precursor composition and with a high concentration of WO3. These amorphous thin films of about 4 mu m in thickness exhibit a deep blue coloration but they can be bleached by thermal treatment near the glass transition temperature. Such bleached films show several guided modes in the visible region and have a high refractive index. Controlled crystallization was realized and thus it was possible to obtain WO3 microcrystals in the amorphous phase. (C) 2007 Elsevier B.V. All rights reserved.