Failure analysis of prestressed anchor bars

Three broken steel bars from a sewed crack in a dam are reported. The inspection of the fracture surfaces of the prestressed bars suggests that fractures were triggered by small cracks and by the inherent brittleness of the bars, as fracture toughness was about 40 MPa m1/2. The analysis of the failures shows that the usual design requirements for prestressing bars fail to warn against brittle failures if some damage exists. Some recommendations, based on the concept of damage tolerance, are suggested to avoid similar unfortunate incidents.

Tuning the properties of carbon fiber-reinforced poly (phenylene sulphide) laminates via incorporation of inorganic fullerene-like WS2 nanoparticles

Novel carbon fiber (CF)-reinforced poly(phenylene sulphide) (PPS) laminates incorporating inorganic fullerene-like tungsten disulfide (IF-WS2) nanoparticles were prepared via melt-blending and hot-press processing. The influence of the IF-WS2 on the morphology, thermal, mechanical and tribological properties of PPS/CF composites was investigated. Efficient nanoparticle dispersion within the matrix was attained without using surfactants. A progressive rise in thermal stability was found with increasing IF-WS2 loading, as revealed by thermogravimetric analysis. The addition of low nanoparticle contents retarded the crystallization of the matrix, whereas concentrations equal or higher than 1.0 wt% increased both the crystallization temperature and degree of crystallinity compared to those of PPS/CF. Mechanical tests indicated that with only 1.0 wt% IF-WS2 the flexural modulus and strength of PPS/CF improved by 17 and 14%, respectively, without loss in toughness, ascribed to a synergistic effect between the two fillers. A significant enhancement in the storage modulus and glass transition temperature was also observed. Moreover, the wear rate and coefficient of friction strongly decreased, attributed to the lubricant role of the IF-WS2 combined with their reinforcing effect. These inorganic nanoparticles show great potential to improve the mechanical and tribological properties of conventional thermoplastic/CF composites for structural applications.

Mechanical Characterization of Multicrystalline Silicon Substrates for Solar Cell Applications

The possibility of using more economical silicon feedstock, i.e. as support for epitaxial solar cells, is of interest when the cost reduction and the properties are attractive. We have investigated the mechanical behaviour of two blocks of upgraded metallurgical silicon, which is known to present high content of impurities even after being purified by the directional solidification process. These impurities are mainly metals like Al and silicon compounds. Thus, it is important to characterize their effect in order to improve cell performance and to ensure the survival of the wafers throughout the solar value chain. Microstructure and mechanical properties were studied by means of ring on ring and three point bending tests. Additionally, elastic modulus and fracture toughness were measured. These results showed that it is possible to obtain marked improvements in toughness when impurities act as microscopic internal crack arrestors. However, the same impurities can be initiators of damage due to residual thermal stresses introduced during the crystallization process.

Towards the development of poly (phenylene sulphide) based nanocomposites with enhanced mechanical, electrical and tribological properties

Novel poly(phenylene sulphide) (PPS) nanocomposites reinforced with an aminated derivative (PPS-NH2) covalently attached to acid-treated single-walled carbon nanotubes (SWCNTs) were prepared via simple melt-blending technique. Their morphology, viscoelastic behaviour, electrical conductivity, mechanical and tribological properties were investigated. Scanning electron microscopy revealed that the grafting process was effective in uniformly dispersing the SWCNTs within the matrix. The storage and loss moduli as a function of frequency increased with the SWCNT content, tending to a plateau in the low-frequency regime. The electrical conductivity of the nanocomposites was considerably enhanced in the range 0.1?0.5 wt% SWCNTs; electrical and rheological percolation thresholds occurred at similar nanotube concentrations. Mechanical tests demonstrated that with only 1.0 wt% SWCNTs the Young's modulus and tensile strength of the matrix improved by 51 and 37%, respectively, without decrement in toughness, ascribed to a very efficient load transfer. A moderate decrease in the friction coefficient and a 75% reduction in wear rate were found for the abovementioned nanotube loading, indicating that PPS-NH2-g-SWCNTs are good tribological additives for thermoplastic polymers. Based on the promising results obtained in this work, it is expected that these nanofillers will be used to develop high-performance thermoplastic/CNT nanocomposites for structural applications.

Mechanical characterization of multicrystalline silicon wafers

The possibility of using more economical silicon feedstock, i.e. as support for epitaxial solar cells, is of interest when the cost reduction and the properties are attractive. We have investigated the mechanical behavior of two blocks of upgraded metallurgical silicon, which is known to present high content of impurities even after being purified by the directional solidification process. The impurities are mainly metals like Al and silicon compounds. Thus, it is important to characterize their effect in order to improve cell performance and to ensure the survival of the wafers throughout the solar value chain. Microstructure and mechanical properties were studied by means of ring on ring and three point bending tests. Additionally, Young’s modulus, hardness and fracture toughness were measured. These results showed that it is possible to obtain marked improvements in toughness when impurities act as microscopic internal crack arrestors. However, the same impurities can be initiators of damage due to residual thermal stresses introduced during the crystallization process.

Mechanical behavior of tungsten-vanadium-lanthana alloys as function of temperature

The mechanical behavior of three tungsten (W) alloys with vanadium (V) and lanthana (La2O3) additions (W–4%V, W–1%La2O3, W–4%V–1%La2O3) processed by hot isostatic pressing (HIP) have been compared with pure-W to analyze the influence of the dopants. Mechanical characterization was performed by three point bending (TPB) tests in an oxidizing air atmosphere and temperature range between 77 (immersion tests in liquid nitrogen) and 1273 K, through which the fracture toughness, flexural strength, and yield strength as function of temperature were obtained. Results show that the V and La2O3 additions improve the mechanical properties and oxidation behavior, respectively. Furthermore, a synergistic effect of both dopants results in an extraordinary increase of the flexure strength, fracture toughness and resistance to oxidation compared to pure-W, especially at higher temperatures. In addition, a new experimental method was developed to obtain a very small notch tip radius (around 5–7 μm) and much more similar to a crack through the use of a new machined notch. The fracture toughness results were lower than those obtained with traditional machining of the notch, which can be explained with electron microscopy, observations of deformation in the rear part of the notch tip. Finally, scanning electron microscopy (SEM) examination of the microstructure and fracture surfaces was used to determine and analyze the relationship between the macroscopic mechanical properties and the micromechanisms of failure involved, depending on the temperature and the dispersion of the alloy.

Superplastic deformation of directionally solidified nanofibrillar Al2O3-Y3Al5O12-ZrO2 eutectics

Nanofibrillar Al2O3–Y3Al5O12–ZrO2 eutectic rods were manufactured by directional solidification from the melt at high growth rates in an inert atmosphere using the laser-heated floating zone method. Under conditions of cooperative growth, the ternary eutectic presented a homogeneous microstructure, formed by bundles of single-crystal c-oriented Al2O3 and Y3Al5O12 (YAG) whiskers of ≈100 nm in width with smaller Y2O3-doped ZrO2 (YSZ) whiskers between them. Owing to the anisotropic fibrillar microstructure, Al2O3–YAG–YSZ ternary eutectics present high strength and toughness at ambient temperature while they exhibit superplastic behavior at 1600 K and above. Careful examination of the deformed samples by transmission electron microscopy did not show any evidence of dislocation activity and superplastic deformation was attributed to mass-transport by diffusion within the nanometric domains. This combination of high strength and toughness at ambient temperature together with the ability to support large deformations without failure above 1600 K is unique and shows a large potential to develop new structural materials for very high temperature structural applications.

Mechanical and thermal behaviour of isotactic polypropylene reinforced with inorganic fullerene-like WS2 nanoparticles: Effect of filler loading and temperature

The thermal and mechanical behaviour of isotactic polypropylene (iPP) nanocomposites reinforced with different loadings of inorganic fullerene-like tungsten disulfide (IF-WS2) nanoparticles was investigated. The IF-WS2 noticeably enhanced the polymer stiffness and strength, ascribed to their uniform dispersion, the formation of a large nanoparticle?matrix interface combined with a nucleating effect on iPP crystallization. Their reinforcement effect was more pronounced at high temperatures. However, a drop in ductility and toughness was found at higher IF-WS2 concentrations. The tensile behaviour of the nanocomposites was extremely sensitive to the strain rate and temperature, and their yield strength was properly described by the Eyring s equation. The activation energy increased while the activation volume decreased with increasing nanoparticle loading, indicating a reduction in polymer chain motion. The nanoparticles improved the thermomechanical properties of iPP: raised the glass transition and heat deflection temperatures while decreased the coefficient of thermal expansion. The nanocomposites also displayed superior flame retardancy with longer ignition time and reduced peak heat release rate. Further, a gradual rise in thermal conductivity was found with increasing IF-WS2 loading both in the glassy and rubbery states. The results presented herein highlight the benefits and high potential of using IF-nanoparticles for enhancing the thermomechanical properties of thermoplastic polymers compared to other nanoscale fillers.

Identification and dynamics of polyglycine II nanocrystals in Argiope trifasciata flagelliform silk

Spider silks combine a significant number of desirable characteristics in one material, including large tensile strength and strain at breaking, biocompatibility, and the possibility of tailoring their properties. Major ampullate gland silk (MAS) is the most studied silk and their properties are explained by a double lattice of hydrogen bonds and elastomeric protein chains linked to polyalanine β-nanocrystals. However, many basic details regarding the relationship between composition, microstructure and properties in silks are still lacking. Here we show that this relationship can be traced in flagelliform silk (Flag) spun by Argiope trifasciata spiders after identifying a phase consisting of polyglycine II nanocrystals. The presence of this phase is consistent with the dominant presence of the –GGX– and –GPG– motifs in its sequence. In contrast to the passive role assigned to polyalanine nanocrystals in MAS, polyglycine II nanocrystals can undergo growing/collapse processes that contribute to increase toughness and justify the ability of Flag to supercontract.

Determination of the hoop fracture properties of unirradiated hydrogen-charged nuclear fuel cladding from ring compression tests

In this work, a new methodology is devised to obtain the fracture properties of nuclear fuel cladding in the hoop direction. The proposed method combines ring compression tests and a finite element method that includes a damage model based on cohesive crack theory, applied to unirradiated hydrogen-charged ZIRLOTM nuclear fuel cladding. Samples with hydrogen concentrations from 0 to 2000 ppm were tested at 20 �C. Agreement between the finite element simulations and the experimental results is excellent in all cases. The parameters of the cohesive crack model are obtained from the simulations, with the fracture energy and fracture toughness being calculated in turn. The evolution of fracture toughness in the hoop direction with the hydrogen concentration (up to 2000 ppm) is reported for the first time for ZIRLOTM cladding. Additionally, the fracture micromechanisms are examined as a function of the hydrogen concentration. In the as-received samples, the micromechanism is the nucleation, growth and coalescence of voids, whereas in the samples with 2000 ppm, a combination of cuasicleavage and plastic deformation, along with secondary microcracking is observed.

Estudio del comportamiento mecánico y en fractura de un hormigón autocompactante con fibras de poliolefina

El uso de hormigón autocompactante se ha convertido en algo habitual desde su aparición a finales de la década de los 80 gracias a la reducción de costes de mano de obra, la buena calidad del acabado superficial y su uso en piezas fuertemente armadas. Por otro lado, los hormigones reforzados con fibras aportan una mejora en las propiedades mecánicas que puede permitir la reducción de armados y, en general, mejorar la respuesta del material ante todo tipo de solicitaciones, especialmente de tracción. En este trabajo se ha estudiado el comportamiento mecánico de un hormigón autocompactante con fibras de poliolefina. Se han obtenido resultados de caracterización mecánica y de fractura de un hormigón autocompactante de referencia sin fibras y de tres dosificaciones con fibras desde 3 kg/m³ hasta 6 kg/m³. Estos resultados han proporcionado un notable incremento en los valores de resistencia post-fisuración y de energía de fractura sin perjuicio de sus propiedades autocompactantes en estado fresco. Since the development of the first Self-Compacting Concrete in the late 80’s, its use has become widespread due to the reduction of the labor costs, the good finishing quality and the achieving of the necessary fluidity for congested reinforced pieces. Furthermore, Fiber Reinforced Concrete provides improvements of the mechanical properties which may even permit the reduction of the reinforcement. The mechanical behavior of a Self-Compacting Concrete with polyolefin fibers has been explored in this research. Results for mechanical properties and for fracture and post-cracking toughness have been obtained. The experimental campaign has been performed for a plain Self-Compacting Concrete and for three different fiber dosages from 3 kg/m³ to 6 kg/m³. These results show a significant enhancement of the post-cracking strength and the fracture energy without harming in the concrete self-compacting properties in fresh state.

Comportamiento mecánico de nuevas aleaciones de wolframio en función de la temperatura

La presente memoria de tesis tiene como objetivo principal la caracterización mecánica en función de la temperatura de nueve aleaciones de wolframio con contenidos diferentes en titanio, vanadio, itria y lantana. Las aleaciones estudiadas son las siguientes: W-0.5%Y2O3, W-2%Ti, W-2% Ti-0.5% Y2O3, W-4% Ti-0.5% Y2O3, W-2%V, W- 2%Vmix, W-4%V, W-1%La2O3 and W-4%V-1%La2O3. Todos ellos, además del wolframio puro se fabrican mediante compresión isostática en caliente (HIP) y son suministradas por la Universidad Carlos III de Madrid. La investigación se desarrolla a través de un estudio sistemático basado en ensayos físicos y mecánicos, así como el análisis post mortem de las muestras ensayadas. Para realizar dicha caracterización mecánica se aplican diferentes ensayos mecánicos, la mayoría de ellos realizados en el intervalo de temperatura de 25 a 1000 º C. Los ensayos de caracterización que se llevan a cabo son: • Densidad • Dureza Vicker • Módulo de elasticidad y su evolución con la temperatura • Límite elástico o resistencia a la flexión máxima, y su evolución con la temperatura • Resistencia a la fractura y su comportamiento con la temperatura. • Análisis microestructural • Análisis fractográfico • Análisis de la relación microestructura-comportamiento macroscópico. El estudio comienza con una introducción acerca de los sistemas en los que estos materiales son candidatos para su aplicación, para comprender las condiciones a las que los materiales serán expuestos. En este caso, el componente que determina las condiciones es el Divertor del reactor de energía de fusión por confinamiento magnético. Parece obvio que su uso en los componentes del reactor de fusión, más exactamente como materiales de cara al plasma (Plasma Facing Components o PFC), hace que estas aleaciones trabajen bajo condiciones de irradiación de neutrones. Además, el hecho de que sean materiales nuevos hace necesario un estudio previo de las características básicas que garantice los requisitos mínimos antes de realizar un estudio más complejo. Esto constituye la principal motivación de la presente investigación. La actual crisis energética ha llevado a aunar esfuerzos en el desarrollo de nuevos materiales, técnicas y dispositivos para la aplicación en la industria de la energía nuclear. El desarrollo de las técnicas de producción de aleaciones de wolframio, con un punto de fusión muy alto, requiere el uso de precursores de sinterizado para lograr densificaciones más altas y por lo tanto mejores propiedades mecánicas. Este es el propósito de la adición de titanio y vanadio en estas aleaciones. Sin embargo, uno de los principales problemas de la utilización de wolframio como material estructural es su alta temperatura de transición dúctil-frágil. Esta temperatura es característica de materiales metálicos con estructura cúbica centrada en el cuerpo y depende de varios factores metalúrgicos. El proceso de recristalización aumenta esta temperatura de transición. Los PFC tienen temperaturas muy altas de servicio, lo que facilita la recristalización del metal. Con el fin de retrasar este proceso, se dispersan partículas insolubles en el material permitiendo temperaturas de servicio más altas. Hasta ahora se ha utilizado óxidos de torio, lantano e itrio como partículas dispersas. Para entender cómo los contenidos en algunos elementos y partículas de óxido afectan a las propiedades de wolframio se estudian las aleaciones binarias de wolframio en comparación con el wolframio puro. A su vez estas aleaciones binarias se utilizan como material de referencia para entender el comportamiento de las aleaciones ternarias. Dada la estrecha relación entre las propiedades del material, la estructura y proceso de fabricación, el estudio se completa con un análisis fractográfico y micrográfico. El análisis fractográfico puede mostrar los mecanismos que están implicados en el proceso de fractura del material. Por otro lado, el estudio micrográfico ayudará a entender este comportamiento a través de la identificación de las posibles fases presentes. La medida del tamaño de grano es una parte de la caracterización microestructural. En esta investigación, la medida del tamaño de grano se llevó a cabo por ataque químico selectivo para revelar el límite de grano en las muestras preparadas. Posteriormente las micrografías fueron sometidas a tratamiento y análisis de imágenes. El documento termina con una discusión de los resultados y la compilación de las conclusiones más importantes que se alcanzan después del estudio. Actualmente, el desarrollo de nuevos materiales para aplicación en los componentes de cara al plasma continúa. El estudio de estos materiales ayudará a completar una base de datos de características que permita hacer una selección de ellos más fiable. The main goal of this dissertation is the mechanical characterization as a function of temperature of nine tungsten alloys containing different amounts of titanium, vanadium and yttrium and lanthanum oxide. The alloys under study were the following ones: W-0.5%Y2O3, W-2%Ti, W-2% Ti-0.5% Y2O3, W-4% Ti-0.5% Y2O3, W-2%V, W- 2%Vmix, W-4%V, W-1%La2O3 and W-4%V-1%La2O3. All of them, besides pure tungsten, were manufactured using a Hot Isostatic Pressing (HIP) process and they were supplied by the Universidad Carlos III de Madrid. The research was carried out through a systematic study based on physical and mechanical tests as well as the post mortem analysis of tested samples. Diverse mechanical tests were applied to perform this characterization; most of them were conducted at temperatures in the range 25-1000 ºC. The following characterization tests were performed: • Density • Vickers hardness • Elastic modulus • Yield strength or ultimate bending strength, and their evolution with temperature • Fracture toughness and its temperature behavior • Microstructural analysis • Fractographical analysis • Microstructure-macroscopic relationship analysis This study begins with an introduction regarding the systems where these materials could be applied, in order to establish and understand their service conditions. In this case, the component that defines the conditions is the Divertor of magnetic-confinement fusion reactors. It seems obvious that their use as fusion reactor components, more exactly as plasma facing components (PFCs), makes these alloys work under conditions of neutron irradiation. In addition to this, the fact that they are novel materials demands a preliminary study of the basic characteristics which will guarantee their minimum requirements prior to a more complex study. This constitutes the motivation of the present research. The current energy crisis has driven to join forces so as to develop new materials, techniques and devices for their application in the nuclear energy industry. The development of production techniques for tungsten-based alloys, with a very high melting point, requires the use of precursors for sintering to achieve higher densifications and, accordingly, better mechanical properties. This is the purpose of the addition of titanium and vanadium to these alloys. Nevertheless, one of the main problems of using tungsten as structural material is its high ductile-brittle transition temperature. This temperature is characteristic of metallic materials with body centered cubic structure and depends on several metallurgical factors. The recrystallization process increases their transition temperature. Since PFCs have a very high service temperature, this facilitates the metal recrystallization. In order to inhibit this process, insoluble particles are dispersed in the material allowing higher service temperatures. So far, oxides of thorium, lanthanum and yttrium have been used as dispersed particles. Tungsten binary alloys are studied in comparison with pure tungsten to understand how the contents of some elements and oxide particles affect tungsten properties. In turn, these binary alloys are used as reference materials to understand the behavior of ternary alloys. Given the close relationship between the material properties, structure and manufacturing process, this research is completed with a fractographical and micrographic analysis. The fractographical analysis is aimed to show the mechanisms that are involved in the process of the material fracture. Besides, the micrographic study will help to understand this behavior through the identification of present phases. The grain size measurement is a crucial part of the microstructural characterization. In this work, the measurement of grain size was carried out by chemical selective etching to reveal the boundary grain on prepared samples. Afterwards, micrographs were subjected to both treatment and image analysis. The dissertation ends with a discussion of results and the compilation of the most important conclusions reached through this work. The development of new materials for plasma facing components application is still under study. The analysis of these materials will help to complete a database of the features that will allow a more reliable materials selection.

Mechanical behaviour of laminated functionally graded fibre-reinforced self-compacting cementitious composites

El hormigón autocompactante (HAC) es una nueva tipología de hormigón o material compuesto base cemento que se caracteriza por ser capaz de fluir en el interior del encofrado o molde, llenándolo de forma natural, pasando entre las barras de armadura y consolidándose únicamente bajo la acción de su peso propio, sin ayuda de medios de compactación externos, y sin que se produzca segregación de sus componentes. Debido a sus propiedades frescas (capacidad de relleno, capacidad de paso, y resistencia a la segregación), el HAC contribuye de forma significativa a mejorar la calidad de las estructuras así como a abrir nuevos campos de aplicación del hormigón. Por otra parte, la utilidad del hormigón reforzado con fibras de acero (HRFA) es hoy en día incuestionable debido a la mejora significativa de sus propiedades mecánicas tales como resistencia a tracción, tenacidad, resistencia al impacto o su capacidad para absorber energía. Comparado con el HRFA, el hormigón autocompactante reforzado con fibras de acero (HACRFA) presenta como ventaja una mayor fluidez y cohesión ofreciendo, además de unas buenas propiedades mecánicas, importantes ventajas en relación con su puesta en obra. El objetivo global de esta tesis doctoral es el desarrollo de nuevas soluciones estructurales utilizando materiales compuestos base cemento autocompactantes reforzados con fibras de acero. La tesis presenta una nueva forma de resolver el problema basándose en el concepto de los materiales gradiente funcionales (MGF) o materiales con función gradiente (MFG) con el fin de distribuir de forma eficiente las fibras en la sección estructural. Para ello, parte del HAC se sustituye por HACRFA formando capas que presentan una transición gradual entre las mismas con el fin de obtener secciones robustas y exentas de tensiones entre capas con el fin de aplicar el concepto “MGF-laminados” a elementos estructurales tales como vigas, columnas, losas, etc. El proceso incluye asimismo el propio método de fabricación que, basado en la tecnología HAC, permite el desarrollo de interfases delgadas y robustas entre capas (1-3 mm) gracias a las propiedades reológicas del material. Para alcanzar dichos objetivos se ha llevado a cabo un amplio programa experimental cuyas etapas principales son las siguientes: • Definir y desarrollar un método de diseño que permita caracterizar de forma adecuada las propiedades mecánicas de la “interfase”. Esta primera fase experimental incluye: o las consideraciones generales del propio método de fabricación basado en el concepto de fabricación de materiales gradiente funcionales denominado “reología y gravedad”, o las consideraciones específicas del método de caracterización, o la caracterización de la “interfase”. • Estudiar el comportamiento mecánico sobre elementos estructurales, utilizando distintas configuraciones de MGF-laminado frente a acciones tanto estáticas como dinámicas con el fin de comprobar la viabilidad del material para ser usado en elementos estructurales tales como vigas, placas, pilares, etc. Los resultados indican la viabilidad de la metodología de fabricación adoptada, así como, las ventajas tanto estructurales como en reducción de costes de las soluciones laminadas propuestas. Es importante destacar la mejora en términos de resistencia a flexión, compresión o impacto del hormigón autocompactante gradiente funcional en comparación con soluciones de HACRFA monolíticos inclusos con un volumen neto de fibras (Vf) doble o superior. Self-compacting concrete (SCC) is an important advance in the concrete technology in the last decades. It is a new type of high performance concrete with the ability of flowing under its own weight and without the need of vibrations. Due to its specific fresh or rheological properties, such as filling ability, passing ability and segregation resistance, SCC may contribute to a significant improvement of the quality of concrete structures and open up new field for the application of concrete. On the other hand, the usefulness of steel fibre-reinforced concrete (SFRC) in civil engineering applications is unquestionable. SFRC can improve significantly the hardened mechanical properties such as tensile strength, impact resistance, toughness and energy absorption capacity. Compared to SFRC, self-compacting steel fibre-reinforced concrete (SCSFRC) is a relatively new type of concrete with high flowability and good cohesiveness. SCSFRC offers very attractive economical and technical benefits thanks to SCC rheological properties, which can be further extended, when combined with SFRC for improving their mechanical characteristics. However, for the different concrete structural elements, a single concrete mix is selected without an attempt to adapt the diverse fibre-reinforced concretes to the stress-strain sectional properly. This thesis focused on the development of high performance cement-based structural composites made of SCC with and without steel fibres, and their applications for enhanced mechanical properties in front of different types of load and pattern configurations. It presents a new direction for tackling the mechanical problem. The approach adopted is based on the concept of functionally graded cementitious composite (FGCC) where part of the plain SCC is strategically replaced by SCSFRC in order to obtain laminated functionally graded self-compacting cementitious composites, laminated-FGSCC, in single structural elements as beams, columns, slabs, etc. The approach also involves a most suitable casting method, which uses SCC technology to eliminate the potential sharp interlayer while easily forming a robust and regular reproducible graded interlayer of 1-3 mm by controlling the rheology of the mixes and using gravity at the same time to encourage the use of the powerful concept for designing more performance suitable and cost-efficient structural systems. To reach the challenging aim, a wide experimental programme has been carried out involving two main steps: • The definition and development of a novel methodology designed for the characterization of the main parameter associated to the interface- or laminated-FGSCC solutions: the graded interlayer. Work of this first part includes: o the design considerations of the innovative (in the field of concrete) production method based on “rheology and gravity” for producing FG-SCSFRC or as named in the thesis FGSCC, casting process and elements, o the design of a specific testing methodology, o the characterization of the interface-FGSCC by using the so designed testing methodology. • The characterization of the different medium size FGSCC samples under different static and dynamic loads patterns for exploring their possibilities to be used for structural elements as beams, columns, slabs, etc. The results revealed the efficiency of the manufacturing methodology, which allow creating robust structural sections, as well as the feasibility and cost effectiveness of the proposed FGSCC solutions for different structural uses. It is noticeable to say the improvement in terms of flexural, compressive or impact loads’ responses of the different FGSCC in front of equal strength class SCSFRC bulk elements with at least the double of overall net fibre volume fraction (Vf).

Mechanical behavior of 2G REBCO HTS at 77 and 300 K

El gran esfuerzo realizado durante la última década con el fin de integrar los diferentes materiales superconductores en el campo de los sistemas eléctricos y en otras aplicaciones tecnológicas ha dado lugar a un campo de investigación amplio y prometedor. El comportamiento eléctrico de los Superconductores de Alta Temperatura (SAT) crítica (masivo y cintas) depende de diferentes parámetros desde su fabricación hasta la aplicación final con imanes o cables. Sin embargo, las aplicaciones prácticas de estos materiales están fuertemente vinculadas con su comportamiento mecánico tanto a temperatura ambiente (manipulación durante fabricación o instalación) como a temperaturas criogénicas (condiciones de servicio). En esta tesis se ha estudiado el comportamiento mecánico de materiales masivos y cintas de alta temperatura crítica a 300 y 77 K (utilizando nitrógeno líquido). Se han obtenido la resistencia en flexión, la tenacidad de fractura y la resistencia a tracción a la temperatura de servicio y a 300 K. Adicionalmente, se ha medido la dureza mediante el ensayo Vickers y nanoindentación. El módulo Young se midió mediante tres métodos diferentes: 1) nanoindentación, 2) ensayos de flexión en tres puntos y 3) resonancia vibracional mediante grindosonic. Para cada condición de ensayo, se han analizado detalladamente las superficies de fractura y los micromecanismos de fallo. Las propiedades mecánicas de los materiales se han comparado con el fin de entender la influencia de las técnicas de procesado y de las características microestructurales de los monocristales en su comportamiento mecánico. Se ha estudiado el comportamiento electromecánico de cintas comerciales superconductoras de YBCO mediante ensayos de tracción y fatiga a 77 y 300 K. El campo completo de deformaciones en la superficie del material se ha obtenido utilizando Correlación Digital de Imágenes (DIC, por sus siglas en inglés) a 300 K. Además, se realizaron ensayos de fragmentación in situ dentro de un microscopio electrónico con el fin de estudiar la fractura de la capa superconductora y determinar la resistencia a cortante de la intercara entre el substrato y la capa cerámica. Se ha conseguido ver el proceso de la fragmentación aplicando tensión axial y finalmente, se han implementado simulaciones mediante elementos finitos para reproducir la delaminación y el fenómeno de la fragmentación. Por último, se han preparado uniones soldadas entre las capas de cobre de dos cintas superconductoras. Se ha medido la resistencia eléctrica de las uniones con el fin de evaluar el metal de soldadura y el proceso. Asimismo, se ha llevado a cabo la caracterización mecánica de las uniones mediante ensayos "single lap shear" a 300 y 77 K. El efecto del campo magnético se ha estudiado aplicando campo externo hasta 1 T perpendicular o paralelo a la cinta-unión a la temperatura de servicio (77 K). Finalmente, la distribución de tensiones en cada una de las capas de la cinta se estudió mediante simulaciones de elementos finitos, teniendo en cuenta las capas de la cinta mecánicamente más representativas (Cu-Hastelloy-Cu) que influyen en su comportamiento mecánico. The strong effort that has been made in the last years to integrate the different superconducting materials in the field of electrical power systems and other technological applications led to a wide and promising research field. The electrical behavior of High Temperature Superconducting (HTS) materials (bulk and coated conductors) depends on different parameters since their processing until their final application as magnets or cables. However, practical applications of such materials are strongly related with their mechanical performance at room temperature (handling) as well as at cryogenic temperatures (service conditions). In this thesis, the mechanical behavior of HTS bulk and coated conductors was investigated at 300 and 77 K (by immersion in liquid nitrogen). The flexural strength, the fracture toughness and the tensile strength were obtained at service temperature as well as at 300 K. Furthermore, their hardness was determined by Vickers measurements and nanoindentation and the Young's modulus was measured by three different techniques: 1) nanoindentation, 2) three-point bending tests and 3) vibrational resonance with a grindosonic device. The fracture and deformation micromechanics have been also carefully analyzed for each testing condition. The comparison between the studied materials has been performed in order to understand the influence of the main sintering methods and the microstructural characteristics of the single grains on the macroscopic mechanical behavior. The electromechanical behavior of commercial YBCO coated conductors was studied. The mechanical behavior of the tapes was studied under tensile and fatigue tests at 77 and 300 K. The complete strain field on the surface of the sample was obtained by applying Digital Image Correlation (DIC) at 300 K. Addionally, in situ fragmentation tests inside a Scanning Electron Microscope (SEM) were carried out in order to study the fragmentation of the superconducting layer and determine the interfacial shear strength between substrate and ceramic layer. The fragmentation process upon loading of the YBCO layer has been observed and finally, Finite Element Simulations were employed to reproduce delamination and fragmentation phenomena. Finally, joints between the stabilizing Cu sides of two coated conductors have been prepared. The electrical resistivity of the joints was measured for the purpose of qualifying the soldering material and evaluating the soldering process. Additionally, mechanical characterization under single lap shear tests at 300 and 77 K has been carried out. The effect of the applied magnetic field has been studied by applying external magnetic field up to 1 T perpendicular and parallel to the tape-joint at service temperature (77 K). Finally, finite element simulations were employed to study the distribution of the stresses in earch layer, taking into account the three mechanically relevant layers of the coated conductor (Cu-Hastelloy-Cu) that affect its mechanical behavior

Mechanical characterisation of tungsten-1wt.% yttrium oxide as a function of temperature and atmosphere

This study evaluates the mechanical behaviour of an Y2O3-dispersed tungsten (W) alloy and compares it to a pure W reference material. Both materials were processed via mechanical alloying (MA) and subsequent hot isostatic pressing (HIP). We performed non-standard three-point bending (TPB) tests in both an oxidising atmosphere and vacuum across a temperature range from 77 K, obtained via immersion in liquid nitrogen, to 1473 K to determine the mechanical strength, yield strength and fracture toughness. This research aims to evaluate how the mechanical behaviour of the alloy is affected by oxides formed within the material at high temperatures, primarily from 873 K, when the materials undergo a massive thermal degradation. The results indicate that the alloy is brittle to a high temperature (1473 K) under both atmospheres and that the mechanical properties degrade significantly above 873 K. We also used Vickers microhardness tests and the dynamic modulus by impulse excitation technique (IET) to determine the elastic modulus at room temperature. Moreover, we performed nanoindentation tests to determine the effect of size on the hardness and elastic modulus; however, no significant differences were found. Additionally, we calculated the relative density of the samples to assess the porosity of the alloy. Finally, we analysed the microstructure and fracture surfaces of the tested materials via field emission scanning electron microscopy (FE-SEM) and transmission electron microscopy (TEM). In this way, the relationship between the macroscopic mechanical properties and micromechanisms of failure could be determined based on the temperature and oxides formed