Propriedades reológicas de matérias-primas do Pólo Cerâmico de Santa Gertrudes provenientes da Formação Corumbataí (região de Rio Claro, SP)

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Flotation of blocolloids suspended in liquid phases of different compositions and pH values

The flotation capacity was determined for cells of yeasts strains belonging to the genera Hansenula, Candida and Saccharomyces. A heterogeneous group of yeasts, comprising strains from the three genera, was identified as showing high flotation capacities (degrees of flotation above 50%), which were practically not affected by variations in medium pH in both the synthetic medium and 2% molasses. Thus, the flotation capacity of the cells in this yeast group seemed strongly dependent on the liquid phase properties and/or growth medium composition, more than on the simple variation in pH of the cell suspensions. A second group of strains, belonging to the Saccharomyces genus, including also brewing yeast strains, was identified as having lower flotation capacities (degrees of flotation below 50% at pH 1.5), which showed no alterations or variations significantly affected by the medium pH. Foam volumes obtained with Saccharomyces strains were greater in synthetic media than in molasses owing to the higher air flow rates required for flotation in molasses. The flotation efficiency decreased in molasses in all cases as well as the foam volume, except in the case of Hansenula cells, which showed an increased foam volume. This was probably due to variations in product excretion by the different yeasts and/or differences in cell wall composition.

Relation between quality and rheological properties of lactic beverages

The physicochemical (pH, fat and total solids content), sensory (appearance, consistency and taste), and rheological characteristics of five different commercial brands of lactic beverages were determined. Rheological measurements were obtained at 5 degreesC and 25 degreesC using a Brookfield rheometer. The experimental data were described by the power law and Herschel-Bulkley models. The ANOVA of the results were conducted using an incomplete block design, and using Tukey test. Samples showed a significant difference (P less than or equal to 0.05%) for fat content and pH. There was a significant difference in total solids content only among Nestle (A), Batavo (C), and Parmalat (D) samples. Sensory evaluation showed more global acceptability for Nestle; however, Nestle and Vigor (E) lactic beverages obtained better results for appearance than for consistency and taste. Batavo obtained the best score for taste. All test samples exhibited non-Newtonian behavior, with thixotropy. Upward curves showed pseudoplastic behavior, while downward curves showed dilatant behavior with the exception of the Nestle sample, at 25 degreesC. Lactic beverages from all brands analyzed showed similar rheological behavior. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Formation of zirconia foams using the thermostimulated sol-gel transition

In this paper we describe the production of zirconia-based foams by a novel thermostimulated sol-gel route, that employs the foaming of colloidal suspensions prior to the sol-gel transition promoted by small increase of temperature (congruent to3 degreesC). This method produces gelled bodies having porosity >70% in the wet stage, and can be used to produce complex-shaped components. The effect of a foaming agent (Freon11 or CCl3F) and surfactant content on the formation and stability of the foams was analyzed. The rheologic measurements demonstrate that by increasing the surfactant concentration, the gelation time decreases increasing foam stability. As the surfactant concentration and quantity of foaming agent increase, the density decreases and the porosity increases. Hg porosimetry results show that the dry foam presents a bimodal pore size distribution. The family of sub-micrometer pores was attributed to the formation of a microemulsion between Freon11 and water. Scanning electron microscopy analysis shows that the foam structure consists of a three-dimensional network of spherical pores, which may be open and interconnected or closed, at larger or smaller porosities, respectively. Finally these results show that the thermostimulated sol-gel transition provides a potential route for ceramic foam manufacture. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Evolution of rheological properties and local structure during gelation of siloxane-polymethylmethacrylate hybrid materials

Hybrid siloxane-polymethylmethacrylate (PMMA) nanocomposites with covalent bonds between the inorganic (siloxane) and organic (polymer) phases were prepared by the sot gel process through hydrolysis and polycondensation of 3-(trimethoxysilyl)propylmethacrylate (TMSM) and polymerization of methylmethacrylate (MMA) using benzoyl peroxide (BPO) as initiator. The effect of MMA, BPO and water contents on the viscoelastic behaviour of these materials was analysed during gelation by dynamic rheological measurements. The changes in storage (G') and loss moduli (G), complex viscosity (eta*) and phase angle (6) were measured as a function of the reaction time showing the viscous character of the sot in the initial step of gelation and its progressive transformation to an elastic gel. This study was complemented by Si-29 and C-13 solid-state nuclear magnetic resonance (NMR/MAS) measurements of dried gel. The analysis of the experimental results shows that linear chains are formed in the initial step of the gelation followed by a growth of branched structures and formation of a three-dimensional network. Near the gel point this hybrid material demonstrates the typical scaling behaviour expected from percolation theory.

Structure of redispersible SnO2 nanoparticles

Suspensions of undoped SnO2 nanoparticles and containing Eu3+ ions were prepared by a sol-gel procedure. Using the classical synthesis method ( precipitation), the particles tend to grow by a coarsening process in order to minimize the surface free energy. This effect can strongly be reduced by the addition of an amide and surfactant during the synthesis, which decreases the surface free energy of the colloidal particles. These additives promote the formation of powders composed of very small primary particles formed by a crystallite of 10 Angstrom, and exhibit good redispersion properties. The local and long order structures of the redispersible powder were studied by X-rays absorption spectroscopy at Sn L-I edge and X-rays diffraction, respectively. The structure of the colloidal aggregates in suspension was investigated by small angle X-rays scattering (SAXS). SAXS results indicate the sol are composed by a polidisperse system of hard spheres resulting of agglomeration of the primary particles and their size increasing by agglomeration for progressively higher Eu3+ content.

Chitinolytic activities in the gut of Aedes aegypti (Diptera : Culicidae) larvae and their role in digestion of chitin-rich structures

Mosquito larvae are believed to be capable of digesting chitin, an insoluble polysaccharide of N-acetylglucosamine, for their nutritional benefit. Studies based on physiological and biochemical assays were conducted in order to detect the presence of chitinase activities in the gut of the detritus-feeding Aedes aegypti larvae. Larvae placed for 24 h in suspensions of chitin azure were able to digest the ingested chitin. Semi-denaturing PAGE using glycol chitin and two fluorogenic substrate analogues showed the presence of two distinct chitinase activities: an endochitinase that catalyzed the hydrolysis of chitin and an endochitinase that cleaved the short substrates [4MU(GlcNAc)(3)] and [4MU(GlcNAc)(2)] that hydrolyzed the chitobioside [4MU(GlcNAc)(2)]. The endochitinase had an extremely broad pH-activity against glycol chitin and chitin azure, pH ranging from 4.0 to 10.0. When the substrate [4MU(GlcNAc)(3)] was used, two activities were observed at pH ranges 4.0-6.0 and 8.0-10.0. Chitinase activity against [4MU(GlcNAc)(3)] was detected throughout the gut with the highest specific activity in the hindgut. The pH of the gut contents was determined by observing color changes in gut after feeding the larvae with color indicator dyes. It was observed a correlation between the pH observed in the gut of feeding larvae (pH 10-6.0) and the optimum pH for gut chitinase activities. In this work, we report that gut chitinases may be involved in the digestion of chitin-containing structures and also in the partial degradation of the chitinous peritrophic matrix in the hindgut. (C) 2003 Elsevier B.V. All rights reserved.

Preparation of SnO2 supported membranes with ultrafine pores

The colloidal route of the sol-gel process was used to prepare supported SnO2 membranes. The influence of the sol and monoelectrolyte concentrations on the formation of the gel layer by sol-casting on the top of macroporous alpha-Al2O3 support was described. The stability of the colloidal suspension as a function of the concentrations was analyzed from creep-recovery measurements. The calcined supported membranes were characterized by nitrogen adsorption-desorption isotherms and scanning electron microscopy. The set of results show that homogeneous membrane layers containing the smallest quantity of cracks are formed in a critical interval of sol (1.01 less than or equal to[SnO2]less than or equal to 1.4 M) and electrolyte (2.O less than or equal to[Cl-]less than or equal to 4.0 mM) concentrations. The samples prepared from concentrated suspensions present a lot of interconnected cracks which favors the peeling of the coated layer. The membranes have pores of average diameter of about 1 nm.

Planar waveguides based on nanocrystalline and Er3+ doped SnO2

Luminescent SnO2: x%mol Er3+ (x=0.1-2.0) thin films have been spin coated on borosilicate and silica substrates from water colloidal suspensions that could be prepared containing up to 40% in weight SnO2 nanocrystalline powders. High Resolution Transmission Electron Microscopy results show the well known SnO2 cassiterite structure and nanocrystallites around 10 nm in diameter, corroborating results from X-ray diffraction. Mono and multi layers have been prepared from the stable colloidal suspensions and films thickness was observed to increase linearly, up to 200 nm, with the colloidal suspensions nanoparticles amount. Excitation and emission spectra have been measured and Er3+ ions were found to be essentially incorporated into the cassiterite structure, substituting for Sn4+, for doping concentration lower than 0.05 mol%. Er3+ ions also appear segregated at the grains surface for higher doping concentration. The optical parameters (refractive index, thickness and propagating modes) of a waveguide sample were measured at 632.8 and 543.4 nm by the prism coupling technique. A monomodal waveguide was obtained with attenuation loss of 3.5 dB/cm along a 2.5 cm optical path.

Study of synthesis variables in the nanocrystal growth behavior of tin oxide processed by controlled hydrolysis

Tin dioxide nanoparticle suspensions were synthesized at room temperature by the hydrolysis reaction of tin chloride (II) dissolved in ethanol. The effect of the initial tin (II) ion concentration, in the ethanolic solution, on the mean particle size of the nanoparticles was studied. The Sn2+ concentration was varied from 0.0025 to 0.1 M, and all other synthesis parameters were kept fixed. Moreover, an investigation of the effect of agglomeration on the nanoparticle characteristics (i.e., size and morphology) was also done by modifying the pH of the SnO2 suspensions. The different samples were characterized by transmission electron microscopy, optical absorption spectroscopy in the ultraviolet range, and photoluminescence measurements. The results show that higher initial ion concentrations and agglomeration lead to larger nanoparticles. The concentration effect is explained by enhanced growth due to a higher supersaturation of the liquid medium. However, it was observed that the agglomeration of the nanoparticles in suspension induce coarsening by the oriented-attachment mechanism.

Small angle X-ray scattering study of surface modified tin oxide nanoparticles prepared by sol-gel route

The surface properties of SnO2 nanoparticles were modified by grafting ionic (Tiron (R). (OH)(2)C6H2(SO3Na)(2)(H2O)-H-.) or non-ionic (Catechol (R). C6H4-1,2-(OH)(2)) capping Molecules during aqueous sol-gel processing to improve the redispersibility of powdered xerogel. The effect of the amount of grafted organic molecules on the redispersibility of powders in aqueous solution at several basic pH values was Studied. The nanostructural features of the colloidal suspensions were analyzed by small angle X-ray scattering (SAXS) measurements. Irrespective of the nature and amount of grafted molecules, complete redispersion was obtained in aqueous solution at pH = 13. The redispersion at pH = 11 results in a mixture of dispersed primary particles and aggregates. The proportion of well dispersed nanoparticles and aggregates (and their average size) can be tuned by the quantity of grafted ionic molecules.

Synthesis and luminescence properties of water dispersible Eu3+-doped boehmite nanoparticles

Nanocrystallized boehmite gamma-AlOOH center dot nH(2)O had been synthesized by spray-drying (SD) of a solution of aluminium tri-sec-butoxide peptized by nitric acid. The sub-micronic spherical particles obtained had an average diameter of 500 nm and were built of 100 nm or less platelet-like sub-particles. The average crystallite size calculated from XRD was 1.6 nm following the b axis (i.e. one unit cell) and 3-4 nm perpendicular to b. As a result of the nanometric sizes of crystallites, there was a large surface free for water adsorption and it was found to be n = 1.18 +/- 0.24H(2)O per AlOOH. The SD spheres spontaneously dispersed in water at room temperature and formed stable-over months-suspensions with nanometre-size particles (25-85 nm). Luminescent europium-doped nanocrystallized boehmites AlOOH: Eu (Al0.98Eu0.02OOH center dot nH(2)O) were synthesized the same way by SD and demonstrated the same crystallization properties and morphologies as the undoped powders. It is inferred from the Eu3+ luminescence spectroscopy that partly hydrated europium species are immobilized on the boehmite nanocrystals where they are directly bonded to alpha(OH) groups of the AlOOH surface. The europium coordination is schematically written [Eu3+(OH)(alpha)(H2O)(7-alpha/2)]. The europium-doped boehmite from SD spontaneously dispersed in water: the luminescence spectroscopy proves that most of the Eu3+ ions were detached from the NPs during water dispersion. The AlOOH: Eu nanoparticles were modified by the amine acid asparagine (ASN). The modification aimed to render the NPs compatible for further bio-functionalization. After surface modification, the NPs easily dispersed in water; the luminescence spectra after dispersion prove that the Eu3+ ions were held at the boehmite surface.

Formation of SnO2 supported porous membranes

In this work, the effect of the substrate microstructure on the formation of SnO2 membranes and of the sintering conditions on their porosity have been analysed. Samples have been prepared by colloidal suspensions cast on alumina or kaolin substrates. Supported membranes have been characterized by Hg porosimetry, MEV, XRD and N-2 adsorption-desorption isotherms. The results show that the narrower pore size distribution of alumina substrate allowed to prepare membranes more homogeneous and free of cracks than that supported on kaolin. The crystallite and pore sizes of the membranes could be controlled by adjusting the temperature of sintering, allowing materials with adequate microstructure with application for ultrafiltration process.

Sintering of zirconia composites obtained by slip casting

Composites containing a matrix of nanometric Ce-stabilized zirconia with an addition of micrometric monoclinic zirconia were processed by slip casting and sintered at a relatively low temperature. The ratio between nanometric and micrometric particles was determined according to the viscosity of the suspensions and the final density of the pellets. An optimum amount of micrometric particles was necessary to achieve improved suspension dispersion and higher pellet density. The amount of deflocculant in the suspensions containing the mixture of micrometric and nanometric particles was optimized by viscosity measurements. The pellets were characterized by dilatometry, Hg porosimetry, density measurement (the Archimedes method) and scanning electron microscopy. Despite the low green density obtained (35-38% of the theoretical density), densities as high as 97.5% were achieved after sintering. (C) 2001 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

SrBi2Ta2O9 ferroelectric thick films prepared by electrophoretic deposition using aqueous suspension

SrBi2Ta2O9 ferroelectric thick films were prepared by electrophoretic deposition (EPD). For that, ceramic powders were prepared by chemical method in order to obtain compounds with chemical homogeneity. The polymeric precursor method was used for the synthesis of the SrBi2Ta2O9 powder. The crystallographic structure of the powder was examined by X-ray diffraction, and the surface area was determined by single point BET adsorption. The 0.03 vol.% suspension was formed by dispersing the powder in water using two different polymers as dispersants: an ester polyphosphate (C213) and an ammonium polyacrilate (Darvan 821-A). It was investigated the influence of the different dispersants in the surface properties of the powder by zeta potential measurements. The films were deposited on platinum-coated alumina and Pt/Ti/SiO2/Si substrates by a 4 mA constant current, for 10 min, using two parallel electrodes placed at a separation distance of 3 min in the suspension. Several cycles of deposition-drying of the deposit were carried out until reaching the desired thickness. After thermal treatment at temperatures ranging from 700 to 1000 degreesC, the films were characterized by X-ray diffraction and scanning electron microscopy for the microstructure observation. (C) 2003 Elsevier Ltd. All rights reserved.