Dendritic Arm Spacing Affecting Mechanical Properties and Wear Behavior of Al-Sn and Al-Si Alloys Directionally Solidified under Unsteady-State Conditions

Alloys of Al-Sn and Al-Si are widely used in tribological applications such as cylinder liners and journal bearings. Studies of the influence of the as-cast microstructures of these alloys on the final mechanical properties and wear resistance can be very useful for planning solidification conditions in order to permit a desired level of final properties to be achieved. The aim of the present study was to contribute to a better understanding about the relationship between the scale of the dendritic network and the corresponding mechanical properties and wear behavior. The Al-Sn (15 and 20 wt pct Sn) and Al-Si (3 and 5 wt pct Si) alloys were directionally solidified under unsteady-state heat flow conditions in water-cooled molds in order to permit samples with a wide range of dendritic spacings to be obtained. These samples were subjected to tensile and wear tests, and experimental quantitative expressions correlating the ultimate tensile strength (UTS), yield tensile strength, elongation, and wear volume to the primary dendritic arm spacing (DAS) have been determined. The wear resistance was shown to be significantly affected by the scale of primary dendrite arm spacing. For Al-Si alloys, the refinement of the dendritic array improved the wear resistance, while for the Al-Sn alloys, an opposite effect was observed, i.e., the increase in primary dendrite arm spacing improved the wear resistance. The effect of inverse segregation, which is observed for Al-Sn alloys, on the wear resistance is also discussed.

Citric acid as anti-hydration additive for magnesia containing refractory castables

Magnesia hydration is a key concern in refractory castable processing. The volumetric expansion that follows this reaction can result in cracks or even explosion during the first heating-up. Citric acid (CA) and other chelants can significantly reduce MgO hydration rate in aqueous suspensions by forming an insoluble magnesium citrate protective coating on the magnesia particles` surface. In the present work, the performance of CA as an anti-hydration additive in refractory castables was evaluated by hydration tests, mechanical strength and apparent volumetric expansion (AVE) measurements and thermogravimetry. The results attained have shown that CA effectiveness depends strongly on the amount added and by the interaction with other raw materials in the composition, in particular calcium aluminate cement. (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Production and characterization of boride layers on AISI D2 tool steel

AISI D2 is the most commonly used cold-work tool steel of its grade. It offers high hardenability, low distortion after quenching, high resistance to softening and good wear resistance. The use of appropriate hard coatings on this steel can further improve its wear resistance. Boronizing is a surface treatment of Boron diffusion into the substrate. In this work boride layers were formed on AISI D2 steel using borax baths containing iron-titanium and aluminium, at 800 degrees C and 1000 degrees C during 4 h. The borided treated steel was characterized by optical microscopy, Vickers microhardness, X-ray diffraction (XRD) and glow discharge optical spectroscopy (GDOS) to verify the effect of the bath compositions and treatment temperatures in the layer formation. Depending on the bath composition, Fe(2)B or FeB was the predominant phase in the boride layers. The layers exhibited ""saw-tooth"" morphology at the substrate interface; layer thicknesses varied from 60 to 120 mu m, and hardness in the range of 1596-1744 HV were obtained. (C) 2009 Elsevier Ltd. All rights reserved.

Influence of chloride ion concentration and temperature on the electrochemical properties of passive films formed on a superduplex stainless steel

Polarization measurements were conducted to monitor the corrosion behavior of superduplex stainless steel ASTM A995M-Gr.SA/EN 10283-Mat#1.4469(GX2CrNiMo26-7-4) when exposed to a) an electrolyte containing 22,700 parts per million (ppm) of chloride ions at seven different temperatures and b) an electrolyte at 25 GC and different chloride ion concentrations (5800, 22,700, 58,000 and 80,000 ppm of Cl(-)). The polarization curves indicate that the passive films formed are only slightly affected by NaCl concentration, but the pitting potential decreases drastically increasing the temperature, in particular >60 degrees C. The image analysis of the microstructure after potentiodynamic polarization showed that the pitting number and size vary in function of the temperature of the tested medium. Nyquist diagrams were determined by electrochemical impedance spectroscopy to characterize the resistance of the passive layer. According to Nyquist plots, the arc polarization resistance decreases increasing the temperature due to a catalytic degradation of the oxide passive films. (C) 2009 Elsevier Inc. All rights reserved.

VEGETABLE OIL STRUCTURE AND ANTIOXIDANTS

Five vegetable oils: canola, soybean, corn, cottonseed and sunflower oils were characterized with respect to their composition by gas chromatography and viscosity. The compositions of the vegetable oils suggest that they exhibit substantially different propensity for oxidation following the order of: canola < corn < cottonseed < sunflower approximate to soybean. Viscosities at 40 degrees C and 100 degrees C and the viscosity index (VI) values were determined for the vegetable oils and two petroleum oil quenchants: Microtemp 157 (a conventional slow oil) and Microtemp 153B (an accelerated or fast oil). The kinematic viscosities of the different vegetable and petroleum oils at 40 degrees C were similar. The VI values for the different vegetable oils were very close and varied between 209-220 and were all much higher than the VI values obtained for Microtemp 157 (96) and Microtemp 153B (121). These data indicate that the viscosity variations of these vegetable oils are substantially less sensitive to temperature variation than are the parafinic oil based Microtemp 157 and Microtemp 153B. Although these data suggest that any of the vegetable oils evaluated could be blended with minimal impact on viscosity, the oxidative stability would surely be substantially impacted. Cooling curve analysis was performed on these vegetable oils at 60 degrees C under non-agitated conditions. These results were compared with cooling curves obtained for Microtemp 157, a conventional, unaccelerated petroleum oil, and Microtemp 153B, an accelerated petroleum oil under the same conditions. The results showed that cooling profiles of the different vegetable oils were similar as expected from the VI values. However, no boiling was observed wit any of the vegetable oils and heat transfer occurs only by convection since there is no full-film boiling and nucleate boiling process as typically observed for petroleum oil quenchants, including those of this study. Therefore, high-temperature cooling is considerable faster for vegetable oils as a class. The cooling properties obtained suggest that vegetable oils would be especially suitable fur quenching low-hardenability steels such as carbon steels.

Crystallisation behaviours of Al-based metallic glasses: Compositional and topological aspects

The different types of thermal crystallisation behaviours observed during continuous heating of M-based metallic glasses have been successfully associated with the topological instability. criterion, which is simply calculated from the alloy composition and metallic radii of the alloying elements and aluminium. In the present work, we report on new results evidencing the correlation between the values of X and the crystallisation behaviours in Al-based alloys of the Al-Ni-Ce system and we compare the glass-forming abilities of alloys designed with compositions corresponding to the same topological instability condition. The results are discussed in terms of compositional and topological aspects emphasizing the relevance of the different types of clusters in the amorphous phase in defining the stability of the glass and the types of thermal crystallisation. (C) 2008 Elsevier B.V. All rights reserved.

Sigma phase morphologies in cast and aged super duplex stainless steel

Solution annealed and water quenched duplex and super duplex stainless steels are thermodynamically metastable systems at room temperature. These systems do not migrate spontaneously to a thermodynamically stable condition because an energy barrier separates the metastable and stable states. However, any heat input they receive, for example through isothermal treatment or through prolonged exposure to a voltaic arc in the welding process, cause them to reach a condition of stable equilibrium which, for super duplex stainless steels, means precipitation of intermetallic and carbide phases. These phases include the sigma phase, which is easily identified from its morphology, and its influence on the material`s impact strength. The purpose of this work was to ascertain how 2-hour isothermal heat treatments at 920 degrees C and 980 degrees C affect the microstructure of ASTM A890/A890M GR 6A super duplex stainless steel. The sigma phase morphologies were found to be influenced by these two aging temperatures, with the material showing a predominantly lacy microstructure when heat treated at 920 degrees C and block-shaped when heat treated at 980 degrees C. (C) 2009 Elsevier Inc. All rights reserved.

Topological instability, average electronegativity difference and glass forming ability of amorphous alloys

In this paper, we report the remarkable agreement of the glass forming ability of binary alloys with a new criterion that combines the topological instability parameter (lambda) and the average electronegativity difference among the elements of an alloy, assuming both exert a synergetic effect. The best glass forming compositions for Zr-Cu and Ti-Ni systems are well predicted by this new approach. Although the new criterion needs further refinement, it is concluded that the proposed approach is a promising and simple tool to guide and reduce the tedious and labour intensive work to find good glass former compositions in metallic systems. (C) 2008 Elsevier Ltd. All rights reserved.

Mechanical and tribological properties of a sintered glass-ceramic compared to granite and porcelainized stoneware

Mechanical and tribological properties of a partially crystallized sintered glass-ceramic were compared to two commercial floor tiles: black granite and porcelainized stoneware. Mechanical properties, hardness and elastic modulus were evaluated by instrumented indentation. Friction coefficient and wear characterization were evaluated using a reciprocating ball-on-flat tribometer in two controlled environments: air with relative humidity of 53% and under running water at 23 degrees C. The sintered glass-ceramic and porcelainized stoneware presented similar mechanical and tribological properties. Regarding the mechanical and tribological properties, the results suggest that this glass-ceramic is suitable to be used as industrial tile. (C) 2011 Elsevier B.V. All rights reserved.

Microstructural characteristics and corrosion behavior of a super duplex stainless steel casting

The machining of super duplex stainless steel castings is usually complicated by the difficulty involved in maintaining the dimensional tolerances required for given applications. Internal stresses originating from the solidification process and from subsequent heat treatments reach levels that exceed the material`s yield strength, promoting plastic strain. Stress relief heat treatments at 520 degrees C for 2 h are an interesting option to solve this problem, but because these materials present a thermodynamically metastable condition, a few precautions should be taken. The main objective of this work was to demonstrate that, after solution annealing at 1130 degrees C and water quenching, stress relief at 520 degrees C for 2 h did not alter the duplex microstructure or impair the pitting corrosion resistance of ASTM A890/A890M Grade 6A steel. This finding was confirmed by microstructural characterization techniques, including light optical and scanning electron microscopy, and X-ray diffraction. Corrosion potential measurements in synthetic sea water containing 20,000 ppm of chloride ions were also conducted at three temperatures: 5 degrees C, 25 degrees C and 60 degrees C. (c) 2008 Elsevier Inc. All rights reserved.

Thermodynamic and topological instability approaches for forecasting glass-forming ability in the ternary Al-Ni-Y system

A thermodynamic approach to predict bulk glass-forming compositions in binary metallic systems was recently proposed. In this approach. the parameter gamma* = Delta H-amor/(Delta H-inter - Delta H-amor) indicates the glass-forming ability (GFA) from the standpoint of the driving force to form different competing phases, and Delta H-amor and Delta H-inter are the enthalpies for-lass and intermetallic formation, respectively. Good glass-forming compositions should have a large negative enthalpy for glass formation and a very small difference for intermetallic formation, thus making the glassy phase easily reachable even under low cooling rates. The gamma* parameter showed a good correlation with GFA experimental data in the Ni-Nb binary system. In this work, a simple extension of the gamma* parameter is applied in the ternary Al-Ni-Y system. The calculated gamma* isocontours in the ternary diagram are compared with experimental results of glass formation in that system. Despite sonic misfitting, the best glass formers are found quite close to the highest gamma* values, leading to the conclusion that this thermodynamic approach can lie extended to ternary systems, serving as a useful tool for the development of new glass-forming compositions. Finally the thermodynamic approach is compared with the topological instability criteria used to predict the thermal behavior of glassy Al alloys. (C) 2007 Elsevier B. V. All rights reserved.

Thixocasting of an A356 alloy: Fluidity, porosity distribution and thermomechanical fatigue behavior

An extensive set of experiments was performed on a semi-solid A356 alloy in order to assess its flow behavior, mechanical properties, microstructural evolution and porosity level. Three different microstructural conditioning techniques (raw material preparation) were employed: deformation recrystallization, magnetohydrodynamic stirring and low temperature pouring. Measurement of microstructural parameters such as Al-alpha particle size, shape factor, contiguity and entrapped liquid showed a relative equivalency among the various conditioning techniques. It was found that the strongest influence on semi-solid slurry fluidity is exerted by the mould temperature. Tensile properties and porosity levels were measured on a demonstration part produced with different slurry ingate velocities. Results showed similar strength levels among all thixocast samples, a strong correlation between elongation and pore volume fraction and porosity levels much lower than the typical figure for permanent mould or die cast Al-Si alloys. Finally, thermomechanical fatigue tests results were much more favorable to the semi-solid material when compared with the conventionally cast alloy, a result attributed to lower porosity, spheroidal shape of the Al-alpha phase, and refined Si eutectic particles. alpha 2007 Elsevier B.V. All rights reserved.

Evaluation of austenitic-ferritic stainless steel wires for orthodontic applications

Several studies have shown that austenitic stainless steels are suitable for use in the final phases of orthodontic treatments, such as finishing and retention. These steels demonstrate appropriate mechanical properties, such as high ultimate tensile strength and good corrosion resistance. A new class of materials, the austenic-ferritic stainless steels, is substituting for austenitic stainless steels in several industrial applications where these properties are necessary. This work supports the hypothesis that orthodontic wires of austenic-ferritic stainless steels can replace austenitic stainless steels. The advantages are cost reduction and decrease of the nickel hypersensitivity effect in patients undergoing orthodontic treatments. The object of this study was to evaluate wires of austenitic-ferritic stainless steel SEW 410 Nr. 14517 (Cr26Ni6Mo3Cu3) produced by cold working through rolling and drawing processes. Tests were performed to evaluate the ultimate tensile strength, hardness, ductility, and formability. In accordance with technical standards the wires exhibited ultimate tensile strength and ductility suitable for orthodontic clinical applications. These austenitie-ferritic wires can be an alternative to substitute the common commercial wires of austenic stainless steels with the advantage of decreasing the nickel content.

Predicting glass-forming compositions in the Al-La and Al-La-Ni systems

In this work, a criterion considering the topological instability (lambda) and the differences in the electronegativity of the constituent elements (Delta e) was applied to the Al-La and Al-Ni-La systems in order to predict the best glass-forming compositions. The results were compared with literature data and with our own experimental data for the Al-La-Ni system. The alloy described in the literature as the best glass former in the Al-La system is located near the point with local maximum for the lambda.Delta e criterion. A good agreement was found between the predictions of the lambda.Delta e criterion and literature data in the Al-La-Ni system, with the region of the best glass-forming ability (GFA) and largest supercooled liquid region (Delta T(x)) coinciding with the best compositional region for amorphization indicated by the lambda.Delta e criterion. Four new glassy compositions were found in the Al-La-Ni system, with the best predicted composition presenting the best glass-forming ability observed so far for this system. Although the lambda.Delta e criterion needs further refinements for completely describe the glass-forming ability in the Al-La and Al-La-Ni systems, the results demonstrated that this criterion is a good tool to predict new glass-forming compositions. (C) 2010 Elsevier B. V. All rights reserved.

Porous alumina-spinel ceramics for high temperature applications

In order to reduce energy costs, high-temperature insulation porous refractory ceramics have been subjected to increasing demands. Among the techniques used to produce these materials (such as the addition of foaming agents and organic compounds), the pore generation via phase transformation presents key aspects, such as easy processing and the absence of toxic volatiles. In this study, this technique was applied to produce porous ceramics by decomposing an aluminum magnesium hydro-carbonate known as hydrotalcite (Mg(6)Al(2)(CO(3))(OH)(16)center dot 4H(2)O). It was found out that by using this complex compound, a large fraction of pores can be generated and kept at high temperatures (above 1300 degrees C) due to the in situ formation of spinel-like phases (MgAl(2)O(4)). (C) 2011 Elsevier Ltd and Techna Group S.r.l. All rights reserved.