V2O5/TiO2 catalyst xerogels: Method of preparation and characterization

This work describes a modified sol-gel method for the preparation of V2O5/TiO2 catalysts. The samples have been characterized by N-2 adsorption at 77 K, X-ray Diffractometry (XRD), Scanning Electronic Microscopy (SEM/EDX) and Fourier Transform Infrared Spectroscopy (FT-IR). The surface area increases with the vanadia loading from 24 m(2) g(-1) for pure TiO2 to 87 m(2) g(-1) for 9 wt% of V2O5. The rutile form is predominant for pure TiO2 but becomes enriched with anatase phase when vanadia loading is increased. No crystalline V2O5 phase was observed in the diffractograms of the catalysts. Analysis by SEM showed heterogeneous granulation of particles with high vanadium dispersion. Two species of surface vanadium were observed by FT-IR spectroscopy: a monomeric vanadyl and polymeric vanadates. The vanadyl/vanadate ratio remains practically constant. Ethanol oxidation was used as a catalytic test in a temperature range from 350 to 560 K. The catalytic activity starts around 380 K. For the sample with 9 wt% of vanadia, the conversion of ethanol into acetaldehyde as the main product was approximately 90% at 473 K.

Synthesis and characterization of TiO2 chemically modified by Pd(II) 2-aminothiazole complex for the photocatalytic degradation of phenol

An investigation was made into the photocatalytic activity of in situ synthesized TiO2 chemically modified by Pd(II) 2-aminothiazole complex for phenol degradation at different pH values. At longer reaction times, the bare titania presented far poorer pbotoactivity than the modified catalysts in the entire range of pH studied. The catalyst complexed with Pd(II) was more efficient than the metal-free Pd, irrespective of pH and reaction time, suggesting that metal plays an important role. A cooperative mechanism is proposed, involving the possible photoactivation of both TiO2 and sensitizer. (C) 2007 Elsevier B.V. All rights reserved.

Efficient robust optimization based on polynomial chaos and tabu search algorithm

The study of robust design methodologies and techniques has become a new topical area in design optimizations in nearly all engineering and applied science disciplines in the last 10 years due to inevitable and unavoidable imprecision or uncertainty which is existed in real word design problems. To develop a fast optimizer for robust designs, a methodology based on polynomial chaos and tabu search algorithm is proposed. In the methodology, the polynomial chaos is employed as a stochastic response surface model of the objective function to efficiently evaluate the robust performance parameter while a mechanism to assign expected fitness only to promising solutions is introduced in tabu search algorithm to minimize the requirement for determining robust metrics of intermediate solutions. The proposed methodology is applied to the robust design of a practical inverse problem with satisfactory results.

Electron Transport in Dye-Sensitized Solar Cells Based on ZnO Nanotubes: Evidence for Highly Efficient Charge Collection and Exceptionally Rapid Dynamics

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Efficient microwave-assisted hydrothermal synthesis of CuO sea urchin-like architectures via a mesoscale self-assembly

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

An efficient microwave-assisted hydrothermal synthesis of BaZrO3 microcrystals: growth mechanism and photoluminescence emissions

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Effects of Alloyed and Oxide Phases on Methanol Oxidation of Pt-Ru/C Nanocatalysts of the Same Particle Size

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Fabrication of coaxial TiO2/Sb2S3 nanowire hybrids for efficient nanostructured organic- inorganic thin film photovoltaics

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of the catalyst MCM-41 on the kinetic of the thermal decomposition of poly(ethylene terephthalate)

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Cobalt phthalocyanine as a biomimetic catalyst in the amperometric quantification of dipyrone using FIA

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Sol-gel synthesis of titania-alumina catalyst supports

Titanium oxide is a good candidate as new support for hydrotreating (HDT) catalysts, but has the inconvenience of presenting small surface area and poor thermal stability. To overcome these handicaps TiO2-Al2O3 mixed oxides were proposed as catalyst support. Here, the results concerning the preparation, characterization and testing of molybdenum catalyst supported on titania-alumina are presented. The support was prepared by sol-gel route using titanium and aluminum isopropoxides, chelated with acetylacetone (acac) to promote similar hydrolysis ratio for both the alcoxides. The effect of nominal complexing ratios [acac]/[Ti] and of sol aging temperature on the structural features of nanometric particles was analyzed by quasi-elastic light scattering (QELS) and N-2 adsorption isotherm measurements. These characterizations have shown that the addition of acac and the increase of aging temperature favor the full dispersion of primary nanoparticles in mother acid solution. The dried powder presents a monomodal distribution of slit-shaped micropores, formed by irregular packing of platelet primary particles, surface area superior to 200 m(2) g(-1) and mean pore size of about 1 nm. These characteristics of porous texture are preserved after firing at 673 K. The diffraction patterns of sample fired above 973 K show only the presence of anatase crystalline phase. The crystalline structure of the support remained unaltered after molybdenum adsorption, but the surface area and the micropore volume were drastically reduced. (C) 2002 Published by Elsevier B.V. B.V.

Yttrium oxysulfide nanosized spherical particles doped with Yb and Er or Yb and Tm: efficient materials for up-converting phosphor technology field

This work reports on the preparation, structural and luminescent studies of nanosized up-converter phosphors Y2O2S:Yb(4%), Er(0.1%) and Y2O2S:Yb(4%), Tm(0.1%),both from polymeric and basic carbonate precursors. The precursors were submitted to a sulphuration process that was previously developed for oxysulfide preparation from basic carbonate. From XRD data, all phosphors presented the oxysulfide phase and the mean crystallite size estimated from the Scherrer formula in the range of 15-20 nm. Polymeric precursor leads to the smallest crystallite size independent on the doping ion. SEM and TEM results confirmed that basic carbonate leads to spherical particles with narrow size distribution and mean diameter of 150 nm, and polymeric precursor smaller spherical particles with diameter between 20 and 40 nm. Up-conversion studies under 980 nm laser excitation showed that Er-doped phosphors present strong green emission related to H-2(11/2), S-4(3/2) --> I-4(15/2) Er transitions as well as the red ones, F-4(9/2) --> I-4(15/2). Tm-doped samples show strong blue emission assigned to (1)G(4) --> H-3(6) and also the red ones, related to (1)G(4) --> F-3(4). Therefore, the sulphuration method was successfully applied to prepare nanosized and nanostructured blue and green up-converter oxysulfide phosphors starting from basic carbonate and polymeric precursors. (C) 2003 Elsevier B.V. All rights reserved.

Characterization of the porosity developed in a new titania-alumina catalyst support prepared by the sol gel route

Titanium oxide (TiO2) is a good candidate for support of hydrotreating catalysts but has the disadvantage of presenting a low surface area and a poor thermal stability when compared with Al2O3. A mixed TiO2-Al2O3 support was proposed as an alternative that is expected to be free from these drawbacks. The variation during firing of the nanoporous texture of supports composed of TiO2-Al2O3, TiO2 and Al2O3 was studied by small angle X-ray scattering (SAXS). The supports were prepared by the sol-gel route using Ti and Al isopropoxides. We have particularly analyzed the effects of acid and basic hydrolysis on the nanostructural features of catalyst supports fired at different temperatures. The nanopore radius distribution functions were determined from SAXS results assuming a simple model of spherical nanopores embedded in a homogeneous solid matrix. The modal pore radius in both pure TiO2 and pure Al2O3 supports grows from 1.3 to 2.2 nm as the firing temperature increases from 673 to 973 K. on the other hand, the modal pore radius in the mixed TiO2-Al2O3 support remains below 1.2 nm over the same range of firing temperatures. These results demonstrate the good thermal stability of the nanoporous texture of mixed TiO2-Al2O3 supports.

Picrosirius-polarization staining method as an efficient histopathological tool for collagenolysis detectin in vesical prolapse lesions

The Picrosirius-polarization method has been indicated as a selective histochemical stain for collagen detection in tissue sections. This method can also be of value for studying collagen degradation given that, under polarized light, collagen displays birefringence due to its molecular order. The aim of this study is to highlight this staining method as an additional instrument for a rapid and excellent confirmatory diagnosis of the presence of collagenolysis in connective tissue in the vaginal wall with vesical prolapse lesion, in tissue sections. Dramatic changes in collagen morphology were found in vaginal mucosa in vesical prolapse disorder: they were weakly stained by Sirius red and under polarized light appeared as thin, pale (weakly birefringent), greenish, and with fibers more scattered, while the histoarchitecture of the organ showed a disrupted appearance. Thus, in the present study, we showed in vaginal mucosa in the vesicle prolapse that corroded collagenous framework appears as fragmentary and irregularly separated collagenous structures, that are weakly birefringent, corresponding to a molecular disorganization of these fibers caused by collagenolysis. (C) 2006 Elsevier Ltd. All rights reserved.

An efficient geometric parameterization technique for the continuation power flow

Continuation methods have been shown as efficient tools for solving ill-conditioned cases, with close to singular Jacobian matrices, such as the maximum loading point of power systems. Some parameterization techniques have been proposed to avoid matrix singularity and successfully solve those cases. This paper presents a new geometric parameterization scheme that allows the complete tracing of the P-V curves without ill-conditioning problems. The proposed technique associates robustness to simplicity and, it is of easy understanding. The Jacobian matrix singularity is avoided by the addition of a line equation, which passes through a point in the plane determined by the total real power losses and loading factor. These two parameters have clear physical meaning. The application of this new technique to the IEEE systems (14, 30, 57, 118 and 300 buses) shows that the best characteristics of the conventional Newton's method are not only preserved but also improved. (C) 2006 Elsevier B.V. All rights reserved.