Investigation on the properties of high reflective mirror prepared by ion-beam sputtering

The single-sided and dual-sided high reflective mirrors were deposited with ion-beam sputtering (IBS). When the incident light entered with 45 degrees, the reflectance of p-polarized light at 1064 nm exceeded 99.5%. Spectrum was gained by spectrometer and weak absorption of coatings was measured by surface thermal lensing (STL) technique. Laser-induced damage threshold (LIDT) was determined and the damage morphology was observed with Lecia-DMRXE microscope simultaneously. The profile of coatings was measured with Mark III-GPI digital interferometer. It was found that the reflectivity of mirror exceeded 99.9% and its absorption was as low as 14 ppm. The reflective bandwidth of the dual-sided sample was about 43 nm wider than that of single-sided sample, and its LIDT was as high as 28 J/cm2, which was 5 J/cm2 higher than that of single-sided sample. Moreover, the profile of dual-sided sample was better than that of substrate without coatings.

High laser-induced damage threshold HfO2 films prepared by ion-assisted electron beam evaporation

HfO2 films were deposited by electron beam evaporation with different deposition parameters. The properties such as refractive index, weak absorption, and laser induced damage thresholds (LIDTs) of these films have been investigated. It was found that when pulsed Nd:YAG 1064 nm laser is used to investigate LIDT of films: Metallic character is the main factor that influences LIDTs of films obtained from Hf starting material by ion-assisted reaction, and films prepared with higher momentum transfer parameter P have fewer metallic character; The ion-assisted reaction parameters are key points for preparing high LIDT films and if the parameters are chose properly, high LIDT films can be obtained. (c) 2004 Elsevier B.V. All rights reserved.

Annealing effects on electron-beam evaporated Al2O3 films

The effects of post-deposited annealing on structure and optical properties of electron-beam evaporated Al2O3 single layers were investigated. The films were annealed in air for 1.5 h at different temperatures from 250 to 400 degrees C. The optical constants and cut-off wavelength were deduced. Microstructure of the samples was characterized by X-ray diffraction (XRD). Profile and surface roughness measurement instrument was used to determine the rms surface roughness. It was found that the cut-off wavelength shifted to short wavelength as the annealing temperature increased and the total optical loss decreased. The film structure remained amorphous even after annealing at 400 degrees C temperature and the samples annealed at higher temperature had the higher rms surface roughness. The decreasing total optical loss with annealing temperature was attributed to the reduction of absorption owing to oxidation of the film by annealing. Guidance to reduce the optical loss of excimer laser mirrors was given. (c) 2004 Elsevier B.V. All rights reserved.

Comparison of TiO2 and ZrO2 films deposited by electron-beam evaporation and by sol-gel process

TiO2 and ZrO2 films are deposited by electron-beam (EB) evaporation and by sol-gel process. The film properties are characterized by visible and Fourier-transform infrared spectrometry, x-ray diffraction analysis, surface roughness measure, absorption and laser-induced damage threshold (LIDT) test. It is found that the sol-gel Elms have lower refractive index, packing density and roughness than EB deposited films due to their amorphous structure and high OH group concentration in the film. The high LIDT of sol-gel films is mainly due to their amorphous and porous structure, and low absorption. LIDT of EB deposited film is considerably affected by defects in the Elm, and LIDT of sol-gel deposited film is mainly effected by residual organic impurities and solvent trapped in the film.

Influences of oxygen partial pressure on structure and related properties of ZrO2 thin films prepared by electron beam evaporation deposition

ZrO2 thin films were prepared by electron beam evaporation at different oxygen partial pressures. The influences of oxygen partial pressure on structure and related properties of ZrO2 thin films were studied. Transmittance, thermal absorption, structure and residual stress of ZrO2 thin films were measured by spectrophotometer, surface thermal lensing technique (STL), X-ray diffraction and optical interferometer, respectively. The results showed that the structure and related properties varied progressively with the increase of oxygen partial pressure. The refractive indices and the packing densities of the thin films decreased when the oxygen partial pressure increased. The tetragonal phase fraction in the thin films decreased gradually as oxygen partial pressure increased. The residual stress of film deposited at base pressure was high compressive stress, the value decreased with the increase of oxygen partial pressure, and the residual stress became tensile with the further increase of oxygen pressure, which was corresponding to the evolution of packing densities and variation of interplanar distances. (c) 2007 Elsevier B.V. All rights reserved.

Optical and electrical properties of TiOx thin films deposited by electron beam evaporation

The TiOx thin films were prepared by electron beam evaporation using TiO as the starting material. The effect of the annealing temperature on the optical and electrical properties was investigated. The spectra of X-ray photoelectron spectroscopy reveal that Ti in the films mainly exist in the forms of Ti2+ and Ti3+ below 400 degrees C 24h annealing. The charge transfer between different titanium ion contribute greatly to the color, absorption, and electrical resistance of the films. (c) 2006 Elsevier Ltd. All rights reserved.

利用等效层的消偏振宽带减反膜设计

分析了倾斜入射条件下导致光学薄膜产生偏振的原因, 针对不同偏振态的等效导纳与等效相位进行了分析, 并计算了对称膜层在45°入射条件下不同偏振态的等效折射率与等效相位厚度, 采用等效层方法设计了光学性能良好的600～900 nm波段消偏振宽带减反膜。最后利用电子束蒸发技术制备了薄膜样品, 样品的光谱性能完全能够满足使用要求。其中在600～900 nm波段范围内, 平均反射率均小于1.38%, 反射率的偏振度均低于0.89％。另外, 通过对其理论及实验光学性能、角度敏感性、膜层厚度误差敏感性等方面的分析结果可

三倍频分光膜在1064 nm的破斑特性研究

采用电子束蒸发方式制备了两种不同材料组合的分光膜,分别对其在波长1064 nm激光辐照下的损伤阈值进行了测试,用Alpha-Step 500台阶仪对破斑进行了深度测量。实验结果表明,破斑呈现出表面层的剥落和深坑破坏两种形态。表面层的剥落深度在一定范围内不随能量密度的变化而变化；深坑破坏深浅不一,是膜内缺陷融化、汽化及喷发的综合作用的结果,是损伤阈值降低的主要原因。

Influence of oxygen plasma treatment on properties of ZrO2 films prepared by e-beam evaporation techniques

Zirconia films were prepared by e-beam evaporation, and oxygen plasma treatment was used to modify film properties. Spectrophotometry, x-ray diffractometry (XRD), and atomic force microscopy were used to characterize refractive index, extinction coefficient, rnicrostructure, and surface roughness, respectively. The experimental results indicate that both refractive index and extinction coefficient of the films were reduced slightly after oxygen plasma treatment, with the decrease of intrinsic stress and surface roughness. From XRD spectra, the intensity decrease of the T(110) diffraction peak was clearly observed after the treatment, which was caused by the restructuring of the film atoms. (C) 2008 Elsevier Ltd. All rights reserved.

Working pressure dependence of properties of Al2O3 thin films prepared by electron beam evaporation

The effects of working pressure on properties of Al2O3 thin films are investigated. Transmittance of the Al2O3 thin film is measured by a Lambda 900 spectrometer. Laser-induced damage threshold (LIDT) is measured by a Nd:YAG laser at 355nm with a pulse width of 7ns. Microdefects were observed under a Nomarski microscope. The samples are characterized by optical properties and defect, as well as LIDT under the 355 nm Nd: YAG laser radiation. It is found that the working pressure has fundamental effect on the LIDT. It is the absorption rather than the microdefect that plays an important role on the LID T of Al2O3 thin film.

Al2O3/SiO2 films prepared by electron-beam evaporation as UV antireflection coatings on 4H-SiC

Al2O3/SiO2 films have been deposited as UV antireflection coatings on 4H-SiC by electron-beam evaporation and characterized by reflection spectrum, scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS). The reflectance of the Al2O3/SiO2 films is 0.33% and 10 times lower than that of a thermally grown SiO2 single layer at 276 nm. The films are amorphous in microstructure and characterize good adhesion to 4H-SiC substrate. XPS results indicate an abrupt interface between evaporated SiO2 and 4H-SiC substrate free of Si-suboxides. These results make the possibility for 4H-SiC based high performance UV optoelectronic devices with Al2O3/SiO2 films as antireflection coatings. (C) 2007 Elsevier B.V. All rights reserved.

Y2O3 stabilized ZrO2 thin films deposited by electron-beam evaporation: Optical properties, structure and residual stresses

This paper describes the preparation and the characterization Of Y2O3 stabilized ZrO2 thin films produced by electric-beam evaporation method. The optical properties, microstructure, surface morphology and the residual stress of the deposited films were investigated by optical spectroscopy, X-ray diffraction (XRD), scanning probe microscope and optical interferometer. It is shown that the optical transmission spectra of all the YSZ thin films are similar with those of ZrO2 thin film, possessing high transparency in the visible and near-infrared regions. The refractive index of the samples decreases with increasing of Y2O3 content. The crystalline structure of pure ZrO2 films is a mixture of tetragonal phase and monoclinic phase, however, Y2O3 stabilized ZrO2 thin films only exhibit the cubic phase independently of how much the added Y2O3 content is. The surface morphology spectrum indicates that all thin films present a crystalline columnar texture with columnar grains perpendicular to the substrate and with a predominantly open microporosity. The residual stress of films transforms tensile from compressive with the increasing Of Y2O3 molar content, which corresponds to the evolutions of the structure and packing densities. (C) 2008 Elsevier Ltd. All rights reserved.

SiO2保护层和退火对Ta2O5薄膜激光损伤阈值影响的对比研究

Ta2O5薄膜采用传统的电子束蒸发方法沉积在BK7基底上。文中对SiO2保护层和退火对Ta2O5薄膜的激光损伤阈值的不同影响进行了研究。结果表明，SiO2保护层不会影响薄膜内的电场分布，薄膜微结构和微缺陷密度，但是会使薄膜的吸收稍微增大；而退火对降低薄膜的微缺陷密度和吸收较有效。SiO2保护层和退火都有利于提高Ta2O5薄膜的抗激光损伤能力，并且退火对提高阈值的影响更为明显。此外，采用SiO2保护层和退火结合的方法，获得了具有最大激光损伤阈值的薄膜。