Synthesis and Photoluminescence Behavior of the Eu3+ Ions as a Nanocoating over a Silica Stober Matrix

In this work, a SiO2 spherical were prepared by the Stober Method and then recovered with a single layer of Eu2O3 oxide (SiO2@Eu2O3) obtained by the Polymeric Precursor Method. The SiO2@Eu2O3 powder was heated treated at 100, 300, 400, 500 and 800 A degrees C. The samples were characterized by the Scanning Electonic Microscopy (SEM), Thermal Analysis (TGA/DTA), and the luminescent properties of the SiO2@Eu2O3 powders were studied by their emission and excitation spectra as well as by the lifetime measurements of the Eu3+ D-5(0) -> aEuro parts per thousand F-7(2) transition. The SEM analysis shows that the silica prepared by the Stober Method is spherical with a particle size of 460 nm. The emission spectra of the SiO2@Eu2O3 powders presented the Eu3+ characteristics bands related to the D-5(0) -> aEuro parts per thousand F-7(J) (J = 0, 1, 2, 3, 4) transitions at 577, 591, 616, 649 and 695 nm, respectively. The band related to the D-5(0) -> aEuro parts per thousand F-7(2) transition is the most intense in the spectra, and its intensity decreases with the temperature enhancement. The decay curves of the SiO2@Eu2O3 samples presented monoexponential features, and the obtained lifetime values were higher than the Eu2O3 oxide. It was possible to conclude that the D-5(0) -> aEuro parts per thousand F-7(2) hypersensitive transition is strongly dependent on the Eu3+ surrounding.

Nanomechanical properties of glass-ceramic films obtained by pressure impregnation of oxide powders on commercial float glass surfaces

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Structural and Luminescence Properties of Silica-Based Hybrids Containing New Silylated-Diketonato Europium(III) Complex

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Piezoelectric behavior of SrRuO(3) buffered lanthanum modified bismuth ferrite thin films grown by chemical method

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Adsorption of MX2 (M = Mn, Ni, Cu, Zn, and Cd; X = Cl, Br, and I) and FeCl3 by modified silica surface with imidazolylpropyl group

Silica gel surface modified with imidazolylpropyl group was used to adsorb MX2 (M = Mn, Ni, Cu, Zn, and Cd; X = Cl, Br, and I) and FeCl3 from ethanol and acetone solution. The adsorption capacity and the intensity of the adsorption were determined by using the Langmuir equation. The influences of the solvent, temperature, and degree of functionalization on the adsorption were also studied. The infrared spectra of the functionalized silica were recorded between 1700-1300 cm-1. The bands of the imidazole skeletal vibrations are shifted to higher frequencies upon metal-to-base nitrogen interaction. © 1985.

Small angle X-ray scattering study of structural changes in silica gel modified with organofunctional groups

Silica gel surfaces, organofunctionalized with 2-mercaptobenzimidazole, iminosalicylaldehyde and imidazole groups were examined using the small angle X-ray scattering technique (SAXS). From the scattering intensity data it was concluded that particles have a uniform size after the coupling reaction. The chemical treatment of the silica gel leads to an attachment of the organofunctional groups on the solid-pore interface of the silica with an increase of the mean size of the solid phase and some coalescence of the pores. © 1989.

Temporal variation in C, N and P of the periphyton on the tropical aquatic macrophyte echinochloa polystachya (H.B.K.) hitch. In Jurumirim Reservoir (São Paulo, Brazil)

The temporal variations in C, N and P concentrations of the periphyton on the natural substratum (Echinochloa polystachya) and its relationships to the water's climatological (air temperature and precipitation), hydrodynamic (water discharge and water level), physical (temperature, transparency) and chemical variables (conductivity, total suspended solids, nitrate, nitrite, ammonia, silica, total phosphorus and orthophosphate) were evaluated in a lagoon at the Paranapanema River mouth into the Jurumirim Reservoir (São Paulo, Brazil) from August 1993 to July 1994. An amplitude variation of 2.0 m in water level was observed. Depending on to the hydrologic conditions, the lagoon presents intermediate conditions of lentic and lotic environments. The amplitude variations in C, N and P were 14.5-52.1% C DW-1, 0.5-3.2% N DW-1, and 0.03-0.4% P DW-1, respectively. The periphyton presented a decreased protein content. The environmental trophic degree appears to be decisive in chemical periphyton composition.

Investigation of New Ion Conducting Ormolytes Silica-Polypropyleneglycol

Two groups of hybrid organic-inorganic composites exhibiting ionic conduction properties, so called ORMOLYTES (organically modified electrolytes), have been prepared by the sol-gel process. The first group has been prepared from mixture of a lithium salt and 3-isocyanatopropyltriethoxysilane(IsoTrEOS),O,O′-bis(2-aminopropyl) polypropyleneglycol. These materials produce chemical bonds between the organic (polymer) and the inorganic (silica) phases. The second group has been prepared by an ultrasonic method from a mixture of tetraethoxysilane (TEOS), polypropyleneglycol and a lithium salt. The organic and inorganic phases are not chemically bonded in these samples. The Li+ ionic conductivity, σ, of all these materials has been studied by AC impedance spectroscopy up to 100°C. Values of σ up to 10-6 Ω-1·cm-1 have been found at room temperature. A systematic study of the effects of lithium concentration, polymer chain length and the polymer to silica weight ratio on σ shows that there is a strong dependence of σ on the preparation conditions. The dynamic properties of the Li+ ion and the polymer chains as a function of temperature between -100 and 120°C were studied using 7Li solid-state NMR measurements. The ionic conductivity of both families are compared and particular attention is paid to the nature of the bonds between the organic and inorganic components.

Chromium-containing silica materials

Chromium-containing silica samples were obtained from soluble sodium silicate solutions in the presence of different chromium nitrate concentrations. Precipitation was carried out in ethanolic media. Gel precipitate was dried by liophylization and samples measured by transmission electron microscopy (TEM), X-ray energy-dispersive spectrometer, X-ray mapping, X-ray photoemission spectroscopy (XPS), and particle size analysis. Spherical chromium containing silica particles with 3.5% and 4.8% (at.%) of chromium were obtained. Particle size analysis results showed that with increased addition of chromium in sodium silicate solutions produces agglomerates whose sizes range from 1 to 0.2 μm. Chromium mapping and XPS results show that chromium oxide is preferentially segregated on particle surfaces. Chromium oxide was detected on particle surface with a binding energy of 576.77 ± 0.05 eV as obtained from XPS analysis. During the hydrolysis and condensation processes chromium oxide precipitates on the silica surface and it affects the silica chain size. © 2000 Elsevier Science B.V. All rights reserved.

Temperature and stoichiometry effect on microstructural and ferroelectric properties of Pb(Zr1-xTix)O3 thin films prepared by chemical soulution deposition

Lead zirconate titanate (PZT) solutions were prepared using a polymeric precursor method, Zr n-propoxide and Ti i-propoxide were used as starting materials with ethylene glycol and water as solvents. The PZT solution was spin-coated on Pt/Ti/SiO2/Si substrates, baked on a hot plate, and finally heat-treated in a tube furnace between 400 and 800°C. The surface morphology and grain size of the films were characterized by atomic force microscopy (AFM), using a tapping mode with amplitude modulation. The films, thermal annealed at temperatures higher than 500°C, exhibited a dense microstructure, without noticeable cracks or voids. Electrical properties were investigated as a function of composition and annealing temperature.

Nucleation and crystallization of titania nanoparticles in silica titania planar waveguides: A study by low frequency Raman scattering

SiO2 (1-x) - TiO2 (x) waveguides, with the mole fraction x in the range 0.07 - 0.20 and thickness of about 0.4 μm, were deposited on silica substrates by a dip-coating technique. The thermal treatments at 700-900°C, used to fully densify the xerogels, produce nucleation of TiO2 nanocrystals even for the lowest TiO2 content. The nucleation of TiO2 nanocrystals and their growth by thermal annealing up to 1300°C were studied by waveguide Raman spectroscopy, for the SiO2 (0.8) - TiO2 (0.2) composition. By increasing the annealing temperature, the Raman spectrum evolves from that typical of the silica-titania glass to that of anatase, but brookite phase is dominant at intermediate temperatures. In the low. frequency region (5-50 cm-1) of the Raman spectra, acoustic vibrations of the nanocrystals are observed. From the measured line shapes, we can deduce the size distribution of the particles. The results are compared with those obtained from the line widths in the X-ray diffraction patterns. Nanocrystals with a mean size in the range 4-20 nm are obtained, by thermal annealing in a corresponding range of 800-1300°C.

Effect of ceramic surface treatment on the microtensile bond strength between a resin cement and an alumina-based ceramic

Purpose: The objective of this study was to test the following hypothesis: the silica coating on ceramic surface increases the bond strength of resin cement to a ceramic. Materials and Methods: In-Ceram Alumina blocks were made and the ceramic surface was treated: G1 - sandblasting with 110-μm aluminum oxide particles; G2 - Rocatec System: tribochemicai silica coating (Rocatec-Pre powder + Rocatec-Plus powder + Rocatec-Sil); G3 - CoJet System: silica coating (CoJet-Sand) + ESPE-Sil. The ceramic blocks were cemented to composite blocks with Panavia F resin cement (under a load of 750 g/1 min). The cemented blocks were stored in distilled water at 37°C for 7 days and sectioned along the x and y axes with a diamond disk. Samples with an adhesive area of ca 0.8 mm 2 (n = 45) were obtained. The samples were attached to an adapted device for the microtensile test, which was performed in a universal testing machine (EMIC) at a crosshead speed of 1 mm/min. Results: The obtained results were submitted to ANOVA and Tukey's test. Mean values of tensile strength (MPa) and standard deviation values were: (G1) 16.8 ± 3.2; (G2) 30.6 ± 4.5; (G3) 33.0 ± 5.0. G2 and 63 presented greater tensile strength than G1. There was no significant difference between G2 and G3. All the failures took place at the ceramic/resin cement interface. Conclusion: The silica coating (Rocatec or CoJet systems) of the ceramic surface increased the bond strength between the Panavia F resin cement and alumina-based ceramic.

Effect of surface treatments on the resin bond to zirconium-based ceramic

Purpose: This study tested the hypothesis that the tribochemical silica coating on ceramic surfaces increases the bond strength of resin cement to a glass-infiltrated zirconium-based ceramic. Materials and Methods: Fifteen blocks of In-Ceram Zirconia from CEREC InLab (5 per group) and 15 composite blocks (Z-250) 5 mm x 5 mm x 4 mm were made. The ceramic surfaces were polished, and the blocks were divided into three groups: (1) airborne abrasion with 110-μm aluminum oxide particles; (2) Rocatec system, tribochemical silica coating; and (3) CoJet system, tribochemical silica coating. The ceramic blocks were cemented to the composite blocks using Panavia F according to the manufacturer's specifications. All samples were stored in 37°C distilled water for 7 days and later sectioned in two axes using a diamond disk under cooling to obtain specimens with a cross-sectional area of approximately 1 mm2 (n = 45). Each specimen was then attached with cyanoacrylate glue to an adapted device for the microtensile test, which was carried out on a universal testing machine. Results: The results were subjected to ANOVA and Tukey's test. Group 2 (23.0 ± 6.7 MPa) and group 3 (26.8 ± 7.4 MPa) showed greater bond strength than group 1 (15.1 ± 5.3 MPa). There was no significant difference between groups 2 and 3. All failures were in the adhesive zone. Conclusion: The hypothesis was confirmed - the tribochemical systems increased the bond strength between Panavia F and In-Ceram Zirconia.

Adsorption of silanes bearing nitrogenated Lewis bases on SiO 2/Si (100) model surfaces

The present paper describes the one-pot procedure for the formation of self-assembled thin films of two silanes on the model oxidized silicon wafer, SiO2/Si. SiO2/Si is a model system for other surfaces, such as glass, quartz, aerosol, and silica gel. MALDI-TOF MS with and without a matrix, XPS, and AFM have confirmed the formation of self-assembled thin films of both 3-imidazolylpropyltrimethoxysilane (3-IPTS) and 4-(N- propyltriethoxysilane-imino)pyridine (4-PTSIP) on the SiO2/Si surface after 30 min. Longer adsorption times lead to the deposition of nonreacted 3-IPTS precursors and the formation of agglomerates on the 3-IPTS monolayer. The formation of 4-PTSIP self-assembled layers on SiO2/Si is also demonstrated. The present results for the flat SiO2/Si surface can lead to a better understanding of the formation of a stationary phase for affinity chromatography as well as transition-metal-supported catalysts on silica and their relationship with surface roughness and ordering. The 3-IPTS and 4-PTSIP modified SiO2/Si wafers can also be envisaged as possible built-on-silicon thin-layer chromatography (TLC) extraction devices for metal determination or N-heterocycle analytes, such as histidine and histamine, with on-spot MALDI-TOF MS detection. © 2005 Elsevier Inc. All rights reserved.

An ultrafiltration membrane, prepared with MSU-type mesoporous silica: Preparation and specific filtration behavior

We report preparation and the singular filtration properties of an ultrafiltration membrane made with MSU-type mesoporous silica that exhibits cylindrical pores aligned mostly normal to the support. This membrane supported on tubular commercial macroporous alumina supports was prepared by the interfacial growth mechanism between stable silica-surfactant hybrid micelles made of the association of silica oligomers with polyethyleneoxide-based (PEO) surfactants and sodium fluoride, a well-known silica condensation catalyst. It appears that the combined effect of the silica nature of the membrane, whose surface charge can be easily adjusted by changing the pH and the non-connected cylindrical shape of the pores provides a new behavior in the retention properties, as proved by the filtration of polyoxyethylene polymers (PEO) with different molecular weights. Depending on the filtration conditions, a rejection rate of 80 % and a steep cut-off at 2,000 Da can be obtained or, on the reverse, polymers three times bigger than the pore diameter can diffuse through the membrane. This new filtration mechanism, which opens up new modes of separation modes, is explained in the light of both topology of the porous network and pH-dependent interactions between PEO polymers and silica porous media. © 2005 Elsevier B.V. All rights reserved.