Methane dehydro-aromatization over a Mo/phosphoric rare earth-containing penta-sil type zeolite in the absence of oxygen

The dehydro-aromatization of methane over a Mo-modified penta-sil type high-silica zeolite containing phosphoric and rare earth oxide (abbreviated as Mo/HZRP-1) was investigated. As a modification of HZSM-5, HZRP-1 is also a good support for the preparation of Mo-based zeolite catalysts, and is active for methane dehydro-aromatization. Mo/HZRP-1 catalysts are more active at high Mo loadings compared with Mo/HZSM-5 catalysts. Al-27 MAS NMR spectra of Mo/HZRP-1 reveal that there are two kinds of framework Al in HZRP-1. It is suggested that only the tetrahedral coordinated Al atoms in the form of Al-O-Si species in the zeolite, in the proton forms, are responsible for the formation of aromatics.

A high coking-resistance catalyst for methane aromatization

Steaming-dealuminated HZSM-5-supported molybdenum catalysts have been found to be high coking-resistance catalysts for methane aromatization reactions; compared with conventional catalysts, they give a much higher selectivity towards aromatics.

Comparative study by infrared spectroscopy and microcalorimetry of the CO adsorption over supported palladium catalysts

The adsorption of CO on Al(2)O(3), ZrO(2), ZrO(2)-SiO(2), and ZrO(2)-La(2)O(3) supported Pd catalysts was studied by adsorption microcalorimetry and infrared (TR) spectroscopy. Some interesting and new correlations between the results of microcalorimetry and IR spectroscopy have been found. The CO is adsorbed on palladium catalysts in three different modes: multibonded (3-fold), bridged (2-fold), both on Pd(lll) and (100) planes, and linear (1-fold) adsorbed species. The corresponding differential adsorption heats lie in the field of high (210-170 kJ/mol), medium (140-120 kJ/mol), and low (95-60 kJ/mol) values, respectively. The nature of the support, the reduction temperature, and the pretreatment conditions affect the surface structure of the Pd catalysts, resulting in variations in the site energy distribution, i.e., changes in the fraction of sites adsorbing CO with specific heats of adsorption. Moreover, the CeO(2); promoter addition weakens the adsorption strength of CO on palladium. Based on the exposed results, a correctness factor, which considers the percentages of various CO adsorption states, must be introduced when one calculates the Pd dispersion using CO adsorption data.