Penetration of a light-cured glass ionomer and a resin sealant into occlusal fissures and etched enamel.

PURPOSE: To evaluate the penetration of a light-cured glass ionomer and a resin sealant into occlusal fissures and etched enamel. MATERIALS AND METHODS: Forty-eight maxillary and mandibular caries-free premolars scheduled for extraction for orthodontic reasons were isolated, the occlusal surfaces subjected to prophylaxis and acid-etched with orthophosphoric acid prior to the application of the VariGlass VLC glass ionomer and Concise resin sealants. The teeth were extracted, two longitudinal median sectiors from each tooth were ground to a thickness of 80-100 microns, and the sealant penetration into the fissures evaluated. The sections were placed in nitric acid to dissolve the enamel so the lengths of the tags which had penetrated into the etched enamel could be measured at different sites on the walls of the fissures. RESULTS: Both sealants adapted well to the fissures but penetrated deeper into shallow, open fissures than into deep, constricted fissures. The VariGlass VLC tags into etched enamel were generally longer than the Concise projections.

pH changes at the surface of root dentin when using root canal sealers containing calcium hydroxide

The purpose of this study was to investigate long-term pH changes in cavities prepared in root surface dentin of extracted teeth after obturation of the root canal with gutta-percha and a variety of sealers containing calcium hydroxide. After cleaning and shaping, root canals in 50 recently extracted, human single-rooted teeth were divided into five groups. Each of four groups was obturated with gutta-percha and either Sealapex, Sealer 26, Apexit, or CRCS, all of which contain calcium hydroxide. The remaining group served as the control and was not obturated with gutta-percha or sealer. Cavities were prepared in the facial surface of the roots in the cervical and middle regions. The pH was measured in these dentinal cavities at the initiation of the experiment, and 3, 7, 14, 21, 28, 45, 60, 90, and 120 days after obturation. Results indicate that the pH at the surface of the root does not become alkaline when calcium hydroxide cements are used as root canal sealers. Regardless of the sealer used, the observed pattern of pH change was not different from that seen in the control group of roots that were not treated with sealer. It is concluded that calcium hydroxide-containing cements, although suitable for use as root canal sealants, do not produce an alkaline pH at the root surface. If such a pH change is related to treatment of root resorption, these sealants do not contribute to this treatment. Copyright © 1996 by The American Association of Endodontists.

Calcium hydroxide root canal sealers: Evaluation of pH, calcium ion concentration and conductivity

The calcium hydroxide ionization of four root canal sealers (Sealapex, CRCS, Sealer 26, and Apexit) was studied by measuring conductivity and pH and by conducting atomic absorption spectrophotometry. Samples 6 mm in diameter and 15 mm long were prepared from these sealers. After setting and 48 h storage in a desiccator, five samples of each material were placed in 50 mL distilled water and analysed after 0,1,2,4, 6 and 24 h and 5, 15 and 30 days. The results showed that Sealapex was the root canal sealer showing the highest pH, ionic calcium and total calcium values (P<0.05) throughout the experimental period, followed by CRCS, Apexit and Sealer 26.

Surface finishing of glass ionomer

Purpose: To evaluate the surface roughness and staining of a glass ionomer cement when subjected to different finishing procedures. Materials and Methods: Sixty-four discs of Chem-Fil II glass ionomer cement were submitted to staining test with methylene blue by spectrophotometry and roughness test by profilometry. Four groups were evaluated: Mylar matrix (control), Sof-Lex discs, Enhance points, and diamond bur. Results: Staining and roughness test, analyzed by ANOVA and Tukey's test, showed that the best surface was obtained when the material cured in contact with the Mylar matrix strip or when treated with Sof-Lex discs. The poorest results were obtained after using the diamond bur.

Effect of different root canal sealers on periapical repair of teeth with chronic periradicular periodontitis

Teeth with induced chronic periradicular periodontitis in dogs were root canal treated. After the biomechanical preparation, using K files and 5.25% sodium hypochlorite as the irrigant solution, all root canals were dressed with an antibacterial dressing based on calcium hydroxide, which was left in place for 7 days. After this time, the root canals were obturated with lateral condensation of cold gutta-percha with either a calcium hydroxide root canal filling material (Sealapex) or a zinc oxide-eugenol sealer (Fill Canal). After 270 days, histopathological analysis showed better apical and periapical repair in the teeth obturated with Sealapex (P < 0.05).

Inhibition of demineralization in vitro around amalgam restorations

Objective: The purpose of this in vitro study was to evaluate some forms of preventing or avoiding demineralization within enamel cavity walls adjacent to amalgam restorations. Method and materials: Third molar teeth were sectioned to obtain 72 specimens, divided into one control and five experimental groups: amalgam only; varnish plus amalgam; acidulated phosphate fluoride plus amalgam; adhesive amalgam; glass-ionomer cement plus amalgam; control (amalgam only, not subjected to a demineralization challenge). The experimental groups were subjected to pH and thermal cycling and then submitted to enamel hardness determinations. Results: Significant differences between the treatment groups revealed that the bonded amalgam technique offered the best resistance to demineralization. The use of cavity varnish resulted in greater mineral loss than amalgam placed alone. Conclusion: The use of an adhesive system, glass-ionomer cement, or acidulated phosphate fluoride under amalgam restorations may interfere with development of secondary caries.

Connective tissue responses to calcium hydroxide-based root canal medicaments

Aim: The objective of the present study was to evaluate the tissue inflammatory response induced by calcium hydroxide pastes, with or without paramonochlorophenol and camphor. Methodology: Isogenic BALB/c mice were inoculated into the subcutaneous tissue with either 0.1 mL of a suspension of Calen, Calen with camphorated paramonochlorophenol, Calen with paramonochlorophenol, Calasept paste or phosphate-buffered saline (control). After 6, 12 and 24 h and 2, 3, 5, 7 and 15 days, three animals in each group were sacrificed and the excised lesions processed for histopathological evaluation of the inflammatory response. Events monitored and graded included the assessment of vascular congestion, oedema, haemorrhage, inflammatory infiltrate, necrosis and tissue repair. Results: The pastes induced an inflammatory response at every observation period, although the intensity, duration and extension of inflammation varied. Calen paste always produced an initial short-term inflammatory response whilst the other pastes produced extended reactions. All pastes allowed repair to take place by the end of the experimental period, although the speed of this process varied between the materials. Calen presented the best biocompatibility; the phenolic compound caused greater tissue response, which was even more severe in the absence of camphor. Calasept paste was damaging and the repair process slower. Conclusions: All calcium hydroxide formulations caused an inflammatory response. The severity and longevity of the responses varied between pastes as a result of the various antiseptic agents. Although irritating, repair was apparent with all formulations.

Microleakage evaluation of pit and fissure sealants done with different procedures, materials, and laser after invasive technique

This study evaluated the microleakage of pit and fissure sealants after different surface preparation (invasive technique and laser irradiation) and the use of different materials (fluoride resin-filled sealant, resin-modified glass ionomer cement and adhesive system). Eighty-four pre molars were used in this study, which were divided into seven groups. After the accomplishment of the different treatments, these were submitted to thermocycling process and assess for microleakage by examination under an epifluorescent microscope and scored zero to seven. Two specimens of each group were observed under scanning electron microscope (SEM). The results showed that laser irradiation did not lessen microleakage in pit and fissures when using a filled-resin sealant with fluoride or a resin-modified glass ionomer cement. The use of laser irradiation and adhesive system, followed by a resin-filled sealant with fluoride, showed the lowest microleakage scores in pit and fissures. Comparing this group to the resin-modified glass ionomer cement group, there was statistical significance. The use of a adhesive system decreased microleakage when using a fluoride resin-filled sealant with or without previous laser irradiation; although it was not statistically significant.

Reaction of dogs' teeth to root canal filling with mineral trioxide aggregate or a glass ionomer sealer

This study was conducted to observe the reaction of apical tissues of dogs' teeth after root canal filling with gutta-percha and mineral trioxide aggregate (MTA) or a glass ionomer (Ketac-Endo) as a sealer. The root canals were instrumented and filled by the lateral condensation technique with the sealers studied. Animals were killed 6 months later, and the specimens were removed and prepared for histological analysis. Results showed no inflammatory reaction of apical tissue and total closure of the apical foramen of all the teeth sealed with MTA. The teeth sealed with Ketac-Endo showed two cases of partial closure and different degrees of chronic inflammatory reaction. In conclusion, MTA exhibited better biological properties than Ketac-Endo. Copyright © 1999 by The American Association of Endodontists.

Use of one-bottle adhesive as an intermediate bonding layer to reduce sealant microleakage on saliva-contaminated enamel

Purpose: To evaluate the influence of three different adhesives, each used as an intermediary layer, on microleakage of sealants applied under condition of salivary contamination. Materials and Methods: Six different experimental conditions were compared, 3 with adhesives and 3 without. After prophylaxis and acid etching of enamel, salivary contamination was placed for 10 s. In Group SC the sealant was applied after saliva without bonding agent and then light-cured. In Group SCA, after saliva, the surface was air dried, and then the sealant was applied and cured. In Groups ScB, SB and PB, a bonding agent (Scotchbond Dual Cure/3M, Single Bond/3M and Prime & Bond 2.1/Dentsply, respectively) was applied after the saliva and prior to the sealant application and curing. After storage in distilled water at 37°C for 24 hrs, the teeth were submitted to 500 thermal cycles (5°C and 55°C), and silver nitrate was used as a leakage tracer. Leakage data were collected on cross sections as percentage of total enamel-sealant interface length. Representative samples were evaluated under SEM. Results: Sealants placed on contaminated enamel with no bonding agent showed extensive microleakage (94.27% in SC; 42.65% in SCA). The SEM revealed gaps as wide as 20 μm in areas where silver nitrate leakage could be visualized. In contrast, all bonding agent groups showed leakage less than 6.9%. Placement of sealant with a dentin-bonding agent on contaminated enamel significantly reduced microleakage (P< 0.0001). The use of a bonding agent as an intermediary layer between enamel and sealant significantly reduced saliva's effect on sealant microleakage.

Effect of Surface Treatments on the Bond Strength between Composite Resin and Acrylic Resin Denture Teeth

Purpose: This investigation studied the effects of 3 surface treatments on the shear bond strength of a light-activated composite resin bonded to acrylic resin denture teeth. Materials and Methods: The occlusal surfaces of 30 acrylic resin denture teeth were ground flat with up to 400-grit silicon carbide paper. Three different surface treatments were evaluated: (1) the flat ground surfaces were primed with methyl methacrylate (MMA) monomer for 180 seconds; (2) light-cured adhesive resin was applied and light polymerized according to the manufacturer's instructions; and (3) treatment 1 followed by treatment 2. The composite resin was packed on the prepared surfaces using a split mold. The interface between tooth and composite was loaded at a cross-head speed of 0.5 mm/min until failure. Results: Analysis of variance indicated significant differences between the surface treatments. Results of mean comparisons using Tukey's test showed that significantly higher shear bond strengths were developed by bonding composite resin to the surfaces that were previously treated with MMA and then with the bonding agent when compared to the other treatments. Conclusion: Combined surface treatment of MMA monomer followed by application of light-cured adhesive resin provided the highest shear bond strength between composite resin and acrylic resin denture teeth.

Reaction of rat connective tissue to implanted dentin tube filled with mineral trioxide aggregate, Portland cement or calcium hydroxide.

The subject of this study was to observe the rat subcutaneous connective tissue reaction to implanted dentin tubes filled with mineral trioxide aggregate, Portland cement or calcium hydroxide. The animals were sacrificed after 7 or 30 days and the undecalcified specimens were prepared for histological analysis with polarized light and Von Kossa technique for mineralized tissues. The results were similar for the studied materials. At the tube openings, there were Von Kossa-positive granules that were birefringent to polarized light. Next to these granulations, there was an irregular tissue like a bridge that was Von Kossa-positive. The dentin walls of the tubes exhibited in the tubules a structure highly birefringent to polarized light, usually like a layer and at different depths. The mechanism of action of the studied materials has some similarity.

Healing process of dog dental pulp after pulpotomy and pulp covering with mineral trioxide aggregate or Portland cement.

Considering several reports about the similarity between the chemical compositions of the mineral trioxide aggregate (MTA) and Portland cement (PC), the subject of this investigation was to analyze the behavior of dog dental pulp after pulpotomy and direct pulp protection with these materials. After pulpotomy, the pulp stumps of 26 roots of dog teeth were protected with MTA or PC. Sixty days after treatment, the animal was sacrificed and the specimens removed and prepared for histomorphological analysis. There was a complete tubular hard tissue bridge in almost all specimens. In conclusion, MTA and PC show similar comparative results when used in direct pulp protection after pulpotomy.

Microleakage in primary teeth restored by conventional or bonded amalgam technique.

The aim of this in vitro study was to evaluate marginal leakage in class V restorations in primary teeth restored with amalgam, using three different techniques. Thirty maxillary anterior primary teeth, clinically sound and naturally exfoliated, were used. In group 1 (n = 10), two thin layers of a copal varnish (Cavitine) were applied. In group 2 (n = 10), Scotchbond Multi-Purpose Plus, a dual adhesive system, was used according to manufacturer instructions. In group 3 (n = 10), One-Step adhesive system in combination with a low-viscosity resin (Resinomer) were used according to manufacturer instructions. All samples were restored with a high-copper dental amalgam alloy (GS 80, SDI). After restoration, the samples were stored in normal saline at 37 degrees C for 72 h. The specimens were polished, thermocycled (500 cycles, 5 degrees and 55 degrees C, 30-s dwell time) and impermeabilized with fingernail polish to within 1.0 mm of the restoration margins. The teeth were then placed in 0.5% methylene blue for 4 h. Finally, the samples were sectioned and evaluated for marginal leakage. The Kruskal-Wallis test showed that the filled adhesive resin (group 3) had the least microleakage. There was no significant difference between groups 1 and 2.

Treatment of traumatized permanent incisors with crown and root fractures: A case report

A case report of the treatment of permanent incisors with crown and root fractures is presented. A radiolucent lesion at the fracture lines was treated with calcium hydroxide in the coronal fragments for 18 months. Clinically, the teeth became firm and the radiographic results after 2 years showed healing of the lesion and hard tissue filling in the space at the fracture lines. © Munksgaard, 2001.